CN104923713B - 一种长保存期三乙胺法冷芯盒固化剂及其生产方法 - Google Patents
一种长保存期三乙胺法冷芯盒固化剂及其生产方法 Download PDFInfo
- Publication number
- CN104923713B CN104923713B CN201510215446.0A CN201510215446A CN104923713B CN 104923713 B CN104923713 B CN 104923713B CN 201510215446 A CN201510215446 A CN 201510215446A CN 104923713 B CN104923713 B CN 104923713B
- Authority
- CN
- China
- Prior art keywords
- diisocyanate
- curing agent
- core box
- storage
- isocyanate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明涉及一种长保存期三乙胺法冷芯盒固化剂及其生产方法，保存期长的冷芯盒固化剂，其成分及重量配比为：异氰酸酯70—91%，环保植物油酯8%—29%，高效磷酸酯类阻燃剂0.2%—1.0%，混合多元醇二元酯0.01%—0.1%；所述异氰酸酯为甲苯二异氰酸酯、二苯基甲烷二异氰酸酯、1,6‑己二异氰酸酯、多亚甲基多苯基多异氰酸酯、三甲基1,6亚己基二异氰酸酯、反式环己烷二异氰酸酯中的一种或其组合。本发明的有益效果在于：加入的植物油脂，较传统的高沸点芳烃溶剂油等材料，毒害小，且树脂砂浇注过程中无黑烟和有毒气体，环保性能好；高效磷酸酯类阻燃剂、混合多元醇二元酯，有效抑制了异氰酸酯基团的活性，延长了固化剂在空气中的保存期，改善生产现场使用、储存性能。
Description
技术领域
本发明涉及固化剂领域，具体涉及一种长保存期三乙胺法冷芯盒固化剂及其生产方法。
背景技术
目前冷芯盒铸造工业中，主要以三乙胺催化为主。该粘结剂体系是由三部分组成：组分一：苯醚型酚醛树脂（树脂）、组分二：异氰酸酯（固化剂）、组分三：三乙胺（催化剂）。组分二中主要组分为异氰酸酯或其聚合物，由于异氰酸酯结构中含有不饱和键，具有很高的反应活性，容易与包含有活泼氢原子的化合物: 胺、水、醇、酸、碱发生反应，形成二聚体或高分子量的聚合物，导致组分二变质、失效。因此，在组分二中加入一些能够阻碍异氰酸酯自聚、有效延长该组分保存期的阻聚物质，就能很好解决上述缺陷。
发明内容
本发明的提供的一种长保存期三乙胺法冷芯盒固化剂及其生产方法，目的是通过加入合适的阻聚物质，钝化异氰酸酯，降低异氰酸酯的活性，延长组分二固化剂的保存期，既便于生产、存储和使用，也避免损失、浪费。
一种长保存期三乙胺法的冷芯盒固化剂，其成分及重量配比为：异氰酸酯70—91%，环保植物油酯8%—29%，高效磷酸酯类阻燃剂0.2%—1.0%，混合多元醇二元酯0.01%—0.1%。
所述异氰酸酯为甲苯二异氰酸酯、二苯基甲烷二异氰酸酯、1,6-己二异氰酸酯、多亚甲基多苯基多异氰酸酯、三甲基1,6亚己基二异氰酸酯、反式环己烷二异氰酸酯中的一种或其组合；
所述环保植物油酯为二甘醇二苯甲酸酯、邻苯二甲酸二辛酯、邻苯二甲酸二丁酯、己二酸二辛酯、柠檬酸三丁酯中的一种或其组合；
所述高效磷酸酯类阻燃剂为三（2,2-二溴甲基-3-溴丙基）磷酸酯、三苯基磷酸酯、甲苯基磷酸二苯酯、三异丙基磷酸酯中的一种或其组合，所述的高效磷酸酯类阻燃剂主要起到改性作用；
所述的混合多元醇二元酯是一种小分子物质。
所述延长三乙胺法冷芯盒固化剂保存期的生产方法，包括以下步骤：
Ⅰ.将异氰酸酯和环保植物油酯用真空泵抽入搪瓷反应釜，启动搅拌；
Ⅱ.搅拌1-1.5小时，加入高效磷酸酯类阻燃剂、混合多元醇二元酯，继续搅拌；
Ⅲ.搅拌1-1.5小时，既得三乙胺法冷芯盒固化剂，检测、包装。
本发明的有益效果在于：该三乙胺法冷芯盒固化剂中加入的植物油脂，较传统的高沸点芳烃溶剂油等材料，毒害小，且树脂砂浇注过程中无黑烟和有毒气体，环保性能好；工艺中加入的高效磷酸酯类阻燃剂、混合多元醇二元酯，有效抑制了异氰酸酯基团的活性，使得该固化剂在空气中的保存期由3天延长到2周左右，改善生产现场使用、储存性能。
具体实施方式
下面结合具体实施例对本发明作详细说明，但并不因此而限制本发明的内容。
实施案例一：
Ⅰ.将异氰酸酯700公斤和环保植物油酯290公斤用真空泵抽入搪瓷反应釜，启动搅拌；
Ⅱ.搅拌1-1.5小时，加入高效磷酸酯类阻燃剂9公斤、混合多元醇二元酯1公斤，继续搅拌；
Ⅲ.搅拌1-1.5小时，即得三乙胺法冷芯盒固化剂，检测、包装。
实施案例二：
Ⅰ.将异氰酸酯780公斤和环保植物油酯215公斤用真空泵抽入搪瓷反应釜，启动搅拌；
Ⅱ.搅拌1-1.5小时，加入高效磷酸酯类阻燃剂4.5公斤、混合多元醇二元酯0.5公斤，继续搅拌；
Ⅲ.搅拌1-1.5小时，即得三乙胺法冷芯盒固化剂，检测、包装。
实施案例三：
Ⅰ.将异氰酸酯910公斤和环保植物油酯87.5公斤用真空泵抽入搪瓷反应釜，启动搅拌；
Ⅱ.搅拌1-1.5小时，加入高效磷酸酯类阻燃剂2.4公斤、混合多元醇二元酯0.1公斤，继续搅拌；
Ⅲ.搅拌1-1.5小时，即得三乙胺法冷芯盒固化剂，检测、包装。
Claims (1)
1.一种长保存期三乙胺法冷芯盒固化剂的生产方法，所述固化剂的成分及重量配比为：异氰酸酯70—91%，环保植物油酯8%—29%，高效磷酸酯类阻燃剂0.2%—1.0%，混合多元醇二元酯0.01%—0.1%；其中，所述的异氰酸酯为甲苯二异氰酸酯、二苯基甲烷二异氰酸酯、1,6-己二异氰酸酯、多亚甲基多苯基多异氰酸酯、三甲基1,6亚己基二异氰酸酯、反式环己烷二异氰酸酯中的一种或几种的组合；所述环保植物油酯为二甘醇二苯甲酸酯、邻苯二甲酸二辛酯、邻苯二甲酸二丁酯、己二酸二辛酯、柠檬酸三丁酯中的一种或几种的组合；所述高效磷酸酯类阻燃剂为三（2,2-二溴甲基-3-溴丙基）磷酸酯、三苯基磷酸酯、甲苯基磷酸二苯酯、三异丙基磷酸酯中的一种或其组合；所述的混合多元醇二元酯是一种小分子物质；其特征在于：所述方法包括以下步骤：
Ⅰ.将异氰酸酯和环保植物油酯用真空泵抽入搪瓷反应釜，启动搅拌；
Ⅱ.搅拌1-1.5小时，加入高效磷酸酯类阻燃剂、混合多元醇二元酯，继续搅拌；
Ⅲ.搅拌1-1.5小时，既得三乙胺法冷芯盒固化剂，检测、包装。