CN104891975A - 一种高抗折强度镍锌软磁铁氧体材料及其制备方法 - Google Patents

一种高抗折强度镍锌软磁铁氧体材料及其制备方法 Download PDF

Info

Publication number
CN104891975A
CN104891975A CN201510199309.2A CN201510199309A CN104891975A CN 104891975 A CN104891975 A CN 104891975A CN 201510199309 A CN201510199309 A CN 201510199309A CN 104891975 A CN104891975 A CN 104891975A
Authority
CN
China
Prior art keywords
oxide
soft magnetic
magnetic ferrite
zinc
nickel
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510199309.2A
Other languages
English (en)
Inventor
汪义卉
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
MAANSHAN KEXIN CONSULTING CO Ltd
Original Assignee
MAANSHAN KEXIN CONSULTING CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by MAANSHAN KEXIN CONSULTING CO Ltd filed Critical MAANSHAN KEXIN CONSULTING CO Ltd
Priority to CN201510199309.2A priority Critical patent/CN104891975A/zh
Publication of CN104891975A publication Critical patent/CN104891975A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种高抗折强度镍锌软磁铁氧体材料及其制备方法，由以下重量份的原料制成：氧化铁50-70、氧化锌22-25、氧化镍14-18、氧化铜2-4、硼化钽0.2-0.6、氧化锆0.3-0.6、羰基铁粉0.3-0.4、氯化聚乙烯6-10、碳粉0.4-1、木质素磺酸钠1-2、有机硅树脂6-9、去离子水适量；本发明的软磁铁氧体具有高的抗折强度，损耗小，对环境无污染，且工艺简单，易于操作。

Description

一种高抗折强度镍锌软磁铁氧体材料及其制备方法
技术领域
本发明涉及软磁铁氧体材料领域，具体涉及一种高抗折强度镍锌软磁铁氧体材料及其制备方法。
背景技术
镍锌铁氧体是一类生产量大，广泛应用在1MHz以上的高频材料。由于它具有多孔性高电阻率，适宜在高频中应用，是性能最好的一类软磁铁氧体材料之一。随着电子产品的快速升级换代，小型化、薄小化、高组装密度等已成为电子产品的发展趋势，因此如何保证产品在小薄化后具有更好的耐摔打、抗碰撞能力，以适应各种复杂环境下保证产品性能的稳定和使用寿命的延长，将成为各种电子元器件制造商均都面临的挑战。
发明内容
本发明的目的是提供一种高抗折强度镍锌软磁铁氧体材料及其制备方法。
为了实现本发明的目的，本发明通过以下方案实施：
一种高抗折强度镍锌软磁铁氧体材料及其制备方法，由下列重量份的原料制成：氧化铁50-70、氧化锌22-25、氧化镍14-18、氧化铜2-4、硼化钽0.2-0.6、氧化锆0.3-0.6、羰基铁粉0.3-0.4、氯化聚乙烯6-10、碳粉0.4-1、木质素磺酸钠1-2、有机硅树脂6-9、去离子水适量；
本发明所述一种高抗折强度镍锌软磁铁氧体材料及其制备方法，由以下具体步骤制成：
（1）将氧化铁、氧化镍、氧化锌、氧化铜、碳粉和去离子水加到球磨机中进行湿法球磨混合均匀，球磨时间为6h；
（2）将步骤（1）所得的粉末置于烧结炉中在800-1000°C进行预烧，预烧时间为2-3h；
（3）将步骤（2）所得的粉料按质量比添加硼化钽、羰基铁粉和氧化锆，并进行第二次球磨，粒径控制在1.5-3微米；
（4）将有机硅树脂用3-6倍重量份的六甲基二硅氧烷稀释，将步骤（3）所得的粉体加到有机硅树脂溶液中，经机械搅拌混合，箱式干燥炉干燥后，加入其余剩余的成分搅拌分散均匀；
（5）将步骤（4）得到的粉体注入模具中，使用热压成型机，压制成固定形状即可。
本发明的优点是：本发明添加碳粉进行预烧，增加了粉料的表面粗糙度，增大了与有机硅树脂的接触面积，从而增强了坯体的致密性、平整性和绝缘性，降低了损耗，采用热压成型的工艺，操作简单，方便，降低了资源的浪费且满足了常规抗电磁干扰的需求，添加的羰基铁粉增强了添加物与铁氧体的相容性，并且提高了材料的磁性，添加的硼化钽提高铁氧体的烧结密度，降低晶界和晶界内的气孔率，提高起始磁导率，添加的氧化锆促进了晶粒的增长，提高了磁导率，本发明的软磁铁氧体具有具有高的抗折强度，损耗小，对环境无污染，且工艺简单，易于操作。
具体实施方式
下面通过具体实例对本发明进行详细说明。
一种高抗折强度镍锌软磁铁氧体材料及其制备方法，由下列重量份（公斤）的原料制成：氧化铁54、氧化锌23、氧化镍14、氧化铜4、硼化钽0.4、氧化锆0.6、羰基铁粉0.3、氯化聚乙烯8、碳粉0.8、木质素磺酸钠1、有机硅树脂8、去离子水适量；
本发明所述一种高抗折强度镍锌软磁铁氧体材料及其制备方法，由以下具体步骤制成：
（1）将氧化铁、氧化镍、氧化锌、氧化铜、碳粉和去离子水加到球磨机中进行湿法球磨混合均匀，球磨时间为6h；
（2）将步骤（1）所得的粉末置于烧结炉中在1000°C进行预烧，预烧时间为3h；
（3）将步骤（2）所得的粉料按质量比添加硼化钽、羰基铁粉和氧化锆，并进行第二次球磨，粒径控制在2微米；
（4）将有机硅树脂用5倍重量份的六甲基二硅氧烷稀释，将步骤（3）所得的粉体加到有机硅树脂溶液中，经机械搅拌混合，箱式干燥炉干燥后，加入其余剩余的成分搅拌分散均匀；
（5）将步骤（4）得到的粉体注入模具中，使用热压成型机，压制成固定形状即可。
通过上述实施例制得的软磁铁氧体材料的性能数据：
初始磁导率（25±3°C）：5660±25%；
功率损耗（100Kc、200mT，KW/m3）：557（25±2°C），253（100±2°C）；
饱和磁通密度（mT，100°C）：447；
居里温度（°C）＞246。

Claims (2)

1.一种高抗折强度镍锌软磁铁氧体材料及其制备方法，其特征在于，由以下重量份的原料制成：氧化铁50-70、氧化锌22-25、氧化镍14-18、氧化铜2-4、硼化钽0.2-0.6、氧化锆0.3-0.6、羰基铁粉0.3-0.4、氯化聚乙烯6-10、碳粉0.4-1、木质素磺酸钠1-2、有机硅树脂6-9、去离子水适量。
2.根据权利要求1所述一种高抗折强度镍锌软磁铁氧体材料及其制备方法，其特征在于，由以下具体步骤制成：
（1）将氧化铁、氧化镍、氧化锌、氧化铜、碳粉和去离子水加到球磨机中进行湿法球磨混合均匀，球磨时间为6h；
（2）将步骤（1）所得的粉末置于烧结炉中在800-1000°C进行预烧，预烧时间为2-3h；
（3）将步骤（2）所得的粉料按质量比添加硼化钽、羰基铁粉和氧化锆，并进行第二次球磨，粒径控制在1.5-3微米；
（4）将有机硅树脂用3-6倍重量份的六甲基二硅氧烷稀释，将步骤（3）所得的粉体加到有机硅树脂溶液中，经机械搅拌混合，箱式干燥炉干燥后，加入其余剩余的成分搅拌分散均匀；
（5）将步骤（4）得到的粉体注入模具中，使用热压成型机，压制成固定形状即可。
CN201510199309.2A 2015-04-24 2015-04-24 一种高抗折强度镍锌软磁铁氧体材料及其制备方法 Pending CN104891975A (zh)