CN104891809B - 一种片状玲珑釉 - Google Patents
一种片状玲珑釉 Download PDFInfo
- Publication number
- CN104891809B CN104891809B CN201510294624.3A CN201510294624A CN104891809B CN 104891809 B CN104891809 B CN 104891809B CN 201510294624 A CN201510294624 A CN 201510294624A CN 104891809 B CN104891809 B CN 104891809B
- Authority
- CN
- China
- Prior art keywords
- glaze
- talcum
- size
- small
- quartz
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明涉及一种片状玲珑釉,包括云南高岭土、长石、石英、釉果、滑石粉、方解石、石灰石、滑石子、氧化锌,所述片状玲珑釉料的重量百分比组成为云南高岭土1‑3%、长石4‑6%、石英30‑40%、釉果30‑40%、滑石粉8‑12%、方解石3‑5%、石灰石3‑5%、滑石子3‑5%、氧化锌1‑3%;各组分重量百分比之和为100%,解决了青花玲珑瓷在1300℃至1330℃高温烧制下玲珑釉与坯体的结合,片状玲珑釉与外釉的结合,在高温高压下片状玲珑釉稳定性较好,不流动(流动幅度较小)的高技术难题,使玲珑釉成为青花图案的一部分。
Description
技术领域
本发明涉及陶瓷产品技术领域,特别是涉及一种片状玲珑釉。
背景技术
景德镇青花玲珑瓷是汉族制瓷工艺中的珍品,是明永乐年间在镂空工艺的基础创造和发展起来的,已有500多年的历史。采用镂雕技法先在瓷器坯体上镂出若干一定形状的玲珑眼,用特制的玲珑釉把眼填平,再绘以青花,施釉后高温烧成。是把青花与玲珑在工艺制作和艺术处理上巧妙加以揉合的产物,碧绿透明的玲珑和淡雅青翠的青花相互衬托,其釉面白里泛青,料色青翠欲滴,玲珑碧绿透明,釉中有釉,花里有花,结合得天衣无缝,展示着中国古代汉族制瓷业高度的技术成就和艺术成就。
传统青花玲珑瓷与本发明最接近的材料为高岭土、长石、石英、釉果、石灰石、滑石粉、滑石子、方解石、氧化锌组成。其比列为高岭土4、长石26、石英13、釉果38、石灰石6、滑石粉4、滑石子4、方解石4、氧化锌1。
高岭土、石英、滑石子主要功效为釉料的骨架和定形作用。长石、釉果、石灰石、滑石、方解石、氧化锌主要功效为增加釉料的玻璃相和透明度。
传统青花玲珑玲珑剔透、幽静雅致、精巧细腻、朴素大方的艺术特色,给人以清新明快之感,但其玲珑眼较小,只能以玲珑眼排列组合成各种图案,形式较为单一,已不能适应现代人所追求的自由、奔放的美感。
发明内容
为了解决上述现有技术存在的技术问题和不足,本发明提供了一种片状玲珑釉,具体发明技术方案如下:
一种片状玲珑釉,由玲珑釉料高温焙烧烧制而成,包括云南高岭土、长石、石英、釉果、滑石粉、方解石、石灰石、滑石子、氧化锌,其特征在于:所述片状玲珑釉料的重量百分比组成为 :
云南高岭土 1-3%、 长石 4-6%、石英 30-40%、 釉果30-40%、 滑石粉 8-12%、 方解石 3-5%、 石灰石 3-5%、滑石子 3-5%、氧化锌 1-3%;
各组分重量百分比之和为100%。
进一步的说:所述片状玲珑釉料的重量百分比组成为 :
云南高岭土 2%、 长石 5%、石英 35%、 釉果34%、 滑石粉 10%、 方解石 4%、 石灰石 4%、 滑石子 4%、氧化锌 2%;
各组分重量百分比之和为100%。
本发明与现有技术的有益效果为:本发明解决了玲珑瓷在1300℃至1330℃高温烧制下玲珑釉与坯体的结合,片状玲珑釉与外釉的结合,在高温高压下片状玲珑釉稳定性较好,不流动(流动幅度较小)的高技术难题,使玲珑釉成为青花图案的一部分。
具体实施方式
下面通过具体的实施例,对本发明的技术方案作进一步具体的说明。
本发明根据下述实施例做进一步的描述,本领域技术人员可以明了的是,下述实施例对本发明仅仅起到说明的作用。在不背离本发明精神的前提下,对本发明所做的任意改进和替代均在本发明保护的范围之内。
实施例1:一种片状玲珑釉,由玲珑釉料高温焙烧烧制而成,包括云南高岭土、长石、石英、釉果、滑石粉、方解石、石灰石、滑石子、氧化锌,所述片状玲珑釉料的重量百分比组成为 :
云南高岭土 1%、长石 4%、石英 37%、 釉果30%、 滑石粉 12%、 方解石 5%、石灰石5%、滑石子 4%、氧化锌 2%。
将上述原料混合均匀后,在1520℃熔化,放入冷水中水淬制成熔块,将熔块装入球磨机中,加水、高铝球石和高岭土 5%研磨成釉浆,细度控制在万孔筛余5%左右,然后经80 ~ 100℃烘干,并制成颗粒状过250目筛,将制成的颗粒按照釉料含水率为10 ~ 15%进行混合搅拌均匀即可使用。
实施例2:一种片状玲珑釉,由玲珑釉料高温焙烧烧制而成,包括云南高岭土、长石、石英、釉果、滑石粉、方解石、石灰石、滑石子、氧化锌,所述片状玲珑釉料的重量百分比组成为 :
云南高岭土 3%、 长石 6%、石英 33%、 釉果40%、 滑石粉 8%、 方解石 3%、石灰石3%、滑石子 3%、 氧化锌 1%。
将上述原料混合均匀后,在1520℃熔化,放入冷水中水淬制成熔块,将熔块装入球磨机中,加水、高铝球石和高岭土 5%研磨成釉浆,细度控制在万孔筛余5%左右,然后经80 ~ 100℃烘干,并制成颗粒状过250目筛,将制成的颗粒按照釉料含水率为10 ~ 15%进行混合搅拌均匀即可使用。
实施例3:一种片状玲珑釉,由玲珑釉料高温焙烧烧制而成,包括云南高岭土、长石、石英、釉果、滑石粉、方解石、石灰石、滑石子、氧化锌,所述片状玲珑釉料的重量百分比组成为 :
云南高岭土 2%、长石 5%、石英 35%、 釉果34%、 滑石粉 10%、 方解石 4%、石灰石4%、滑石子 4%、氧化锌 2%;
各组分重量百分比之和为100%。
将上述原料混合均匀后,在1520℃熔化,放入冷水中水淬制成熔块,将熔块装入球磨机中,加水、高铝球石和高岭土 5%研磨成釉浆,细度控制在万孔筛余5%左右,然后经80 ~ 100℃烘干,并制成颗粒状过250目筛,将制成的颗粒按照釉料含水率为10 ~ 15%进行混合搅拌均匀即可使用。
申请人经过上百次的反复试验,从釉料配方摸索并总结了一整套经过理论考证和实践运作出来的经验,并能得心应手地形成规模化 产业化生产玲珑瓷,用片状玲珑釉料制作的玲珑瓷,解决了使片状玲珑釉在高温高压烧制过程中的稳定性较差、易流动的特性,从而达到片状玲珑釉与陶瓷坯体结合,片状玲珑釉与外釉结合的效果 从而提高了玲珑瓷的附加值。
以上所述,仅为本发明较佳的具体实施方式,但本发明保护范围并不局限于此,根据本发明的技术方案及其发明构思加以等同替换或改变,都应涵盖在本发明的保护范围之内。
Claims (2)
1.一种片状玲珑釉,包括云南高岭土、长石、石英、釉果、滑石粉、方解石、石灰石、滑石子、氧化锌,其特征在于:所述片状玲珑釉料的重量百分比组成为 :
云南高岭土 1-3%、 长石 4-6%、石英 30-40%、 釉果30-40%、 滑石粉 8-12%、 方解石3-5%、 石灰石 3-5%、滑石子 3-5%、氧化锌 1-3%;
各组分重量百分比之和为100%。
2.根据权利要求1所述的片状玲珑釉,其特征在于:所述片状玲珑釉料的重量百分比组成为 :云南高岭土 2%、 长石 5%、石英 35%、 釉果 34%、滑石粉 10%、 方解石 4%、石灰石4%、滑石子 4%、氧化锌 2%;
各组分重量百分比之和为100%。