CN104882844A - 一种热缩复合应力管及其生产方法 - Google Patents
一种热缩复合应力管及其生产方法 Download PDFInfo
- Publication number
- CN104882844A CN104882844A CN201510228992.8A CN201510228992A CN104882844A CN 104882844 A CN104882844 A CN 104882844A CN 201510228992 A CN201510228992 A CN 201510228992A CN 104882844 A CN104882844 A CN 104882844A
- Authority
- CN
- China
- Prior art keywords
- pyrocondensation
- parts
- stress
- pipe
- combined
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
测试项目 | 实施例1 | 实施例2 | 实施例3 | 实施例4 | 实施例5 | 实施例6 | 对比例1 | 对比例2 |
体积电阻率(Ω·cm) | 8.2*1010 | 8.7*1010 | 7.9*1010 | 7.6*1010 | 7.5*1010 | 7.6*1010 | 8.5*1010 | 7.4*1010 |
介电常数 | 19.2 | 19.4 | 19.1 | 18.9 | 19.1 | 18.9 | 18.5 | 18.8 |
局部放电1.73U0下,≤10pC | 小于背景局放 | 小于背景局放 | 小于背景局放 | 小于背景局放 | 小于背景局放 | 小于背景局放 | 1500 pC | 50 pC |
交流耐压4.5U0,5min | 无闪络、无击穿 | 无闪络、无击穿 | 无闪络、无击穿 | 无闪络、无击穿 | 无闪络、无击穿 | 无闪络、无击穿 | 无闪络、无击穿 | 无闪络、无击穿 |
Claims (18)