CN104877562A - 一种电子领域用紫外光固化高性能防粘剂 - Google Patents
一种电子领域用紫外光固化高性能防粘剂 Download PDFInfo
- Publication number
- CN104877562A CN104877562A CN201510247841.7A CN201510247841A CN104877562A CN 104877562 A CN104877562 A CN 104877562A CN 201510247841 A CN201510247841 A CN 201510247841A CN 104877562 A CN104877562 A CN 104877562A
- Authority
- CN
- China
- Prior art keywords
- parts
- acrylate
- adhesive agent
- release agent
- ultraviolet light
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明属于防粘剂技术领域，特别涉及一种电子领域用紫外光固化高性能防粘剂，由以下原料按质量份组成：丙烯酸酯改性聚硅氧烷预聚体50-60份，芳香族聚氨酯丙烯酸酯15-20份，丙烯酸二甲氨基乙酯5-10份，光引发剂1-6份，流平剂0.2-0.5份，颜料0.5-1份，石墨烯20-25份。本发明采用以二端羟基聚硅氧烷和γ-甲基丙烯酰氧丙基三甲氧基硅烷为单主体制备丙烯酸酯改性聚硅氧烷预聚物，在防粘剂各方面具备高性能。本发明节约能源、有利环保、简化工艺、提高产品质量、具有广阔的发展前景。
Description
技术领域
本发明属于防粘剂技术领域，特别涉及一种电子领域用紫外光固化高性能防粘剂。
背景技术
在压敏基材中，和压敏胶粘剂同样重要的是防粘剂。防粘剂产品中使用最多、技术也较成熟的有例如聚有机硅氧烷。其发展大致经历了三个阶段：溶剂型、乳液型和无溶剂型（热固化和辐射固化两种）。第一种要耗费大量的能源和资源，生产过程中危险性极大，目前发达国家基本上不再使用；第二种虽然克服了危险性和环境污染问题，但仍需要耗费大量能源，且产品质量不稳定。热固化的溶剂型防粘剂避免了前良好总类型的缺陷，制品性能优异，但由于涂布工艺困难以及仍需要高温固化也不适于热敏基材的生产要求。射线固化（紫外光、电子束）的聚有机硅氧烷防粘剂，克服了溶剂型和乳胶剂型防粘剂的主要缺点，可以低温固化，所以特别适宜热敏性基材的防粘处理。
聚硅氧烷防粘涂料对标签产业非常重要，如果没有可靠的防粘剂用于压敏胶，压敏胶中其它组分就不能以现在的形式存在。而随着科技发展，人们生活水准的提高，对于产品质量标准的不断提升，市面上的一般防粘剂已经不能满足日新月异的新标准新需求，因此急需一种高剥离性能的紫外光固化防粘剂。
发明内容
本发明的目的在于提供一种电子领域用紫外光固化高性能防粘剂，本发明采用以二端羟基聚硅氧烷和γ-甲基丙烯酰氧丙基三甲氧基硅烷为单主体制备丙烯酸酯改性聚硅氧烷预聚物，在防粘剂各方面具备高性能。本发明节约能源、有利环保、简化工艺、提高产品质量、具有广阔的发展前景。
本发明采用的技术方案是：
一种电子领域用紫外光固化高性能防粘剂，由以下原料按质量份组成：丙烯酸酯改性聚硅氧烷预聚体50-60份，芳香族聚氨酯丙烯酸酯15-20份，丙烯酸二甲氨基乙酯5-10份，光引发剂1-6份，流平剂0.2-0.5份，颜料0.5-1份，石墨烯20-25份。
进一步地，所述丙烯酸酯改性聚硅氧烷预聚体是由以下步骤制备而成：将二端羟基二甲基聚硅氧烷与γ-甲基丙烯酰氧丙基三甲氧基硅烷混合加入搅拌，再加入二月桂酸二丁基锡，加热至80~100℃，持续8~10h，提纯即得。
作为优选，所述流平剂为有机硅流平剂或丙烯酸酯流平剂。
作为优选，所述光引发剂为1-羟基环己基苯基甲酮、2-羟基-2-甲基-1-苯基-1-丙酮、二苯基-(2,4,6-三甲基苯甲酰)氧磷、二苯甲酮中的一种或几种。
石墨烯是一种由碳原子构成的单层片状结构的新材料。是一种由碳原子以sp2杂化轨道组成六角型呈蜂巢晶格的平面薄膜，只有一个碳原子厚度的二维材料。石墨烯目前是世上最薄却也是最坚硬的纳米材料，它几乎是完全透明的，只吸收2.3％的光；导热系数高达5300W/m·K，高于碳纳米管和金刚石，常温下其电子迁移率超过15000cm2/V·s，又比纳米碳管或硅晶体高，而电阻率只约10-6Ω·cm，比铜或银更低，为目前世上电阻率最小的材料。目前，也有报道称石墨烯无论是直接在铜或镍上制备，或转移到其他金属上，都可提供防腐蚀保护。铜涂层培育单层石墨烯，采用化学气相沉积法，腐蚀会比裸铜慢七倍，镍涂层培育多层石墨烯，腐蚀比裸镍慢20倍以上。单层石墨烯具有相同的防腐蚀保护作用，就像常规有机涂料，但后者要厚五倍以上。添加石墨烯有效防止了防粘剂在使用过程中受环境及外界影响腐蚀，从而丧失其功能功效，对电子领域生产制造造成损失。
本发明以二端羟基聚硅氧烷和γ-甲基丙烯酰氧丙基三甲氧基硅烷为单主体制备丙烯酸酯改性聚硅氧烷预聚物，具备良好的储存稳定性、固化速率、柔韧性及硬度；配合适当的光聚合引发剂、活性稀释剂、助剂等制成防粘涂层，具有适中的涂布粘度、良好的粘附力及较高的粘附残留率。本发明节约能源、有利环保、简化工艺、提高产品质量、具有广阔的发展前景。
本发明的有益效果是如下：
一、本发明具备良好的储存稳定性、固化速率、柔韧性及硬度；具有适中的涂布粘度、良好的粘附力及较高的粘附残留率以及良好的剥离性能；本发明节约能源、有利环保、简化工艺、提高产品质量、具有广阔的发展前景；
二、本发明采用石墨烯具有优秀的防腐能力，与光固化体系具有良好的共同作用，且效果稳定，作用时效长；
三、本发明能快速固化干燥，环保无毒，持久稳定，适于推广。
具体实施方式
下面结合实施例进一步阐述本发明：
实施例1
一种电子领域用紫外光固化高性能防粘剂，由以下原料按质量份组成：丙烯酸酯改性聚硅氧烷预聚体50份，芳香族聚氨酯丙烯酸酯15份，丙烯酸二甲氨基乙酯5份，1-羟基环己基苯基甲酮1份，有机硅流平剂0.2份，颜料0.5份，石墨烯20份。
实施例2
一种电子领域用紫外光固化高性能防粘剂，由以下原料按质量份组成：丙烯酸酯改性聚硅氧烷预聚体60份，芳香族聚氨酯丙烯酸酯20份，丙烯酸二甲氨基乙酯10份，2-羟基-2-甲基-1-苯基-1-丙酮6份，丙烯酸酯流平剂0.5份，颜料1份，石墨烯25份。
实施例3
一种电子领域用紫外光固化高性能防粘剂，由以下原料按质量份组成：丙烯酸酯改性聚硅氧烷预聚体55份，芳香族聚氨酯丙烯酸酯18份，丙烯酸二甲氨基乙酯8份，二苯基-(2,4,6-三甲基苯甲酰)氧磷4份，有机硅流平剂0.4份，颜料1份，石墨烯22份。
以上述依据本发明的理想实施例为启示，通过上述的说明内容，相关工作人员完全可以在不偏离本项发明技术思想的范围内，进行多样的变更以及修改。本项发明的技术性范围并不局限于说明书上的内容，必须要根据权利要求范围来确定其技术性范围。
Claims (4)
1.一种电子领域用紫外光固化高性能防粘剂，其特征在于由以下原料按质量份组成：丙烯酸酯改性聚硅氧烷预聚体50-60份，芳香族聚氨酯丙烯酸酯15-20份，丙烯酸二甲氨基乙酯5-10份，光引发剂1-6份，流平剂0.2-0.5份，颜料0.5-1份，石墨烯20-25份。
2.根据权利要求1所述的一种电子领域用紫外光固化高性能防粘剂，其特征在于：所述丙烯酸酯改性聚硅氧烷预聚体是由以下步骤制备而成：将二端羟基二甲基聚硅氧烷与γ-甲基丙烯酰氧丙基三甲氧基硅烷混合加入搅拌，再加入二月桂酸二丁基锡，加热至80~100℃，持续8~10h，提纯即得。
3.根据权利要求1所述的一种电子领域用紫外光固化高性能防粘剂，其特征在于：所述流平剂为有机硅流平剂或丙烯酸酯流平剂。
4.根据权利要求1所述的一种电子领域用紫外光固化高性能防粘剂，其特征在于：所述光引发剂为1-羟基环己基苯基甲酮、2-羟基-2-甲基-1-苯基-1-丙酮、二苯基-(2,4,6-三甲基苯甲酰)氧磷、二苯甲酮中的一种或几种。