CN104877524A - High-temperature-resistant and antistatic coating - Google Patents

High-temperature-resistant and antistatic coating Download PDF

Info

Publication number
CN104877524A
CN104877524A CN201510361227.3A CN201510361227A CN104877524A CN 104877524 A CN104877524 A CN 104877524A CN 201510361227 A CN201510361227 A CN 201510361227A CN 104877524 A CN104877524 A CN 104877524A
Authority
CN
China
Prior art keywords
parts
antistatic coating
coating
resistant
temperature
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
CN201510361227.3A
Other languages
Chinese (zh)
Inventor
任碧龙
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201510361227.3A priority Critical patent/CN104877524A/en
Publication of CN104877524A publication Critical patent/CN104877524A/en
Withdrawn legal-status Critical Current

Abstract

The invention discloses high-temperature-resistant and antistatic coating. The high-temperature-resistant and antistatic coating comprises, by weight, 37-40 parts of organic silicon resin, 15-18 parts of xylene, 12-14 parts of high aluminum fibers, 9-11 parts of magnesium chloride, 8-13 parts of polyisocyanate curing agents, 10-12 parts of nano silicon dioxide, 10-13 parts of cobaltous oxide, 9-13 parts of aluminium oxide, 43-45 parts of epoxy resin, 20-24 parts of conductive powder, 30-35 parts of styrene-acrylic emulsions, 3-4 parts of graphite powder, 2-3 parts of carbon black and 40-50 parts of diluents. The high temperature resisting, oil resisting and antistatic effects of the coating are good and effective in a long term. The surface of the coating is seamless and easy to clean, corrosion resistant performance is good, the preparation technology is simple, and cost is low.

Description

A kind of high-temperature resistant and antistatic coating
Technical field
The present invention relates to coating preparation field, be specifically related to a kind of high-temperature resistant and antistatic coating.
Background technology
High-temperature-resistant antistatic coating has good resistance to elevated temperatures and antistatic property, but the coating of traditional coating is crisp, also there is processing performance difference, the shortcomings such as cost is higher, Corrosion Protection is poor, and hardness is weak.Current high-temperature-resistant antistatic coating function on the market can not meet the needs produced with life.
Summary of the invention
Technical problem to be solved by this invention is, overcome the shortcoming of prior art, there is provided a kind of preparatory technology simple high-temperature resistant and antistatic coating, coating of the present invention has high temperature resistant, oil resistant, and antistatic effect is good and permanently effective, it is easy to clean that coatingsurface is seamless, Corrosion Protection is good, and preparation technology is simple, with low cost.
In order to solve above technical problem, the invention provides a kind of high-temperature resistant and antistatic coating, it is made up of the raw material of following weight part: silicone resin 37-40, dimethylbenzene 15-18, high aluminum fiber 12-14, magnesium chloride 9-11, polyisocyanate curing agent 8-13, nano silicon 10-12, cobalt oxide 10-13, aluminum oxide 9-13, epoxy resin 43-45, conducting powder 20-24, benzene emulsion 30-35, Graphite Powder 99 3-4, carbon black 2-3, thinner 40-50.
The beneficial effect that technical scheme provided by the invention is brought is: a kind of high-temperature resistant and antistatic coating, and this coating has high temperature resistant, oil resistant, and antistatic effect is good and permanently effective, and it is easy to clean that coatingsurface is seamless, and Corrosion Protection is good, and preparation technology is simple, with low cost.
Embodiment
Describe the present invention in detail below in conjunction with specific embodiment, be used for explaining the present invention in this illustrative examples of the present invention and explanation, but not as a limitation of the invention.
Embodiment 1
A kind of high-temperature resistant and antistatic coating in this example is prepared by the raw material of following proportioning: silicone resin 37, dimethylbenzene 18, high aluminum fiber 12, magnesium chloride 11, polyisocyanate curing agent 13, nano silicon 10, cobalt oxide 13, aluminum oxide 9, epoxy resin 43, conducting powder 20, benzene emulsion 35, Graphite Powder 99 4, carbon black 2, thinner 50.
Embodiment 2
A kind of high-temperature resistant and antistatic coating in this example is prepared by the raw material of following proportioning: silicone resin 39, dimethylbenzene 18, high aluminum fiber 14, magnesium chloride 9, polyisocyanate curing agent 8, nano silicon 12, cobalt oxide 10, aluminum oxide 13, epoxy resin 45, conducting powder 24, benzene emulsion 33, Graphite Powder 99 3, carbon black 3, thinner 40.
Embodiment 3
A kind of high-temperature resistant and antistatic coating in this example is prepared by the raw material of following proportioning: silicone resin 38, dimethylbenzene 16, high aluminum fiber 13, magnesium chloride 10, polyisocyanate curing agent 11, nano silicon 11, cobalt oxide 12, aluminum oxide 11, epoxy resin 44, conducting powder 22, benzene emulsion 33, Graphite Powder 99 3.5, carbon black 2.5, thinner 45.
Stirrer for mixing is put in each for above-described embodiment raw material mixing stir and can use.
With above-mentioned according to desirable embodiment of the present invention for enlightenment, by above-mentioned description, relevant staff in the scope not departing from this invention technological thought, can carry out various change and amendment completely.The technical scope of this invention is not limited to the content on specification sheets, must determine its technical scope according to right.

Claims (4)

1. a high-temperature resistant and antistatic coating, is characterized in that: comprise and being made up of the raw material of following parts by weight: silicone resin 37-40, dimethylbenzene 15-18, high aluminum fiber 12-14, magnesium chloride 9-11, polyisocyanate curing agent 8-13, nano silicon 10-12, cobalt oxide 10-13, aluminum oxide 9-13, epoxy resin 43-45, conducting powder 20-24, benzene emulsion 30-35, Graphite Powder 99 3-4, carbon black 2-3, thinner 40-50.
2. high-temperature resistant and antistatic coating according to claim 1, is characterized in that: it is made up of the raw material of following parts by weight: silicone resin 37, dimethylbenzene 18, high aluminum fiber 12, magnesium chloride 11, polyisocyanate curing agent 13, nano silicon 10, cobalt oxide 13, aluminum oxide 9, epoxy resin 43, conducting powder 20, benzene emulsion 35, Graphite Powder 99 4, carbon black 2, thinner 50.
3. high-temperature resistant and antistatic coating according to claim 1, is characterized in that: it is made up of the raw material of following parts by weight: silicone resin 39, dimethylbenzene 18, high aluminum fiber 14, magnesium chloride 9, polyisocyanate curing agent 8, nano silicon 12, cobalt oxide 10, aluminum oxide 13, epoxy resin 45, conducting powder 24, benzene emulsion 33, Graphite Powder 99 3, carbon black 3, thinner 40.
4. high-temperature resistant and antistatic coating according to claim 1, is characterized in that: it is made up of the raw material of following parts by weight: silicone resin 38, dimethylbenzene 16, high aluminum fiber 13, magnesium chloride 10, polyisocyanate curing agent 11, nano silicon 11, cobalt oxide 12, aluminum oxide 11, epoxy resin 44, conducting powder 22, benzene emulsion 33, Graphite Powder 99 3.5, carbon black 2.5, thinner 45.
CN201510361227.3A 2015-06-28 2015-06-28 High-temperature-resistant and antistatic coating Withdrawn CN104877524A (en)