CN106221050A - A kind of fireproof high-temperature resistant combined wear-resistant tensile removal cable - Google Patents
A kind of fireproof high-temperature resistant combined wear-resistant tensile removal cable Download PDFInfo
- Publication number
- CN106221050A CN106221050A CN201610668162.1A CN201610668162A CN106221050A CN 106221050 A CN106221050 A CN 106221050A CN 201610668162 A CN201610668162 A CN 201610668162A CN 106221050 A CN106221050 A CN 106221050A
- Authority
- CN
- China
- Prior art keywords
- parts
- rubber
- antioxidant
- temperature resistant
- resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
nullThe invention discloses a kind of fireproof high-temperature resistant combined wear-resistant tensile removal cable,Including cable core and restrictive coating,Wherein restrictive coating raw material includes by weight: natural rubber 5 15,CSM 30 60,Butyl rubber 10 18,Chlorohydrin rubber 12 22,Silicone rubber 5 12,Accelerator TTEE 0.5 1.5,Accelerant N a 22 12,Sulfur 12,Vulcanizing agent HTDM 12,Tributyl citrate 0.5 1.6,Epoxy soybean oil 1 1.8,Disproportionated rosin 13,Coumarone indene resin 12,Antioxidant MB Z 0.2 1.2,Antioxidant A W 12,Antioxidant D NP 12,Hexamethoxymethyl melamine resin 0.5 1.2,Zirconium oxide 12,Blanc fixe 0.2 0.8,Graphene nanometer sheet 10 20,Silicon carbide micro-powder 5 15,Glass microballoon 10 20,RF 90 resin 12.
Description
Technical field
The present invention relates to field of cable technology, particularly relate to a kind of fireproof high-temperature resistant combined wear-resistant tensile removal cable.
Background technology
Coal mine moving cable is that the MT818 issued according to State Administration of Quality and Technical Supervision carries out producing, main
The power supply of ore deposit to be used for underground moving coal excavation apparatus connects, and the occasion that coal mine moving cable uses now gets more and more, more
Come the widest.But coal mine moving cable is mainly common cable at present, can not use, the most also must in hot environment
Must meet cable and have fire-resistant, the wear-resisting and requirement of tension, current common cable also cannot meet its demand.
Summary of the invention
The technical problem existed based on background technology, the present invention proposes a kind of combined wear-resistant tensile of fireproof high-temperature resistant and moves
Galvanic electricity cable, has high temperature resistant, wear-resisting, the tensile property of excellence, and fire resistance and good mechanical properties is good, and it is right to can be applicable to
Fireproof high-temperature resistant requires more harsh occasion, halogen-free environmental simultaneously.
A kind of fireproof high-temperature resistant combined wear-resistant tensile removal cable that the present invention proposes, including cable core and restrictive coating, its
Middle restrictive coating raw material includes by weight: natural rubber 5-15 part, CSM 30-60 part, butyl rubber 10-18
Part, chlorohydrin rubber 12-22 part, silicone rubber 5-12 part, accelerator TTEE 0.5-1.5 part, accelerant N a-22 1-2 part, sulfur 1-
2 parts, vulcanizing agent HTDM 1-2 part, tributyl citrate 0.5-1.6 part, epoxy soybean oil 1-1.8 part, disproportionated rosin 1-3 part is ancient
Horse grand resin 1-2 part, antioxidant MB Z 0.2-1.2 part, antioxidant A W 1-2 part, antioxidant D NP 1-2 part, hexakis-methoxy methyl three
Cymel 0.5-1.2 part, zirconium oxide 1-2 part, blanc fixe 0.2-0.8 part, graphene nanometer sheet 10-20 part, carborundum
Micropowder 5-15 part, glass microballoon 10-20 part, RF-90 resin 1-2 part.
Preferably, in restrictive coating raw material, natural rubber, CSM, butyl rubber, chlorohydrin rubber, silicon rubber
The weight ratio of glue is 8-12:40-50:12-16:14-20:6-10.
Preferably, in restrictive coating raw material, accelerator TTEE, accelerant N a-22, sulfur, the weight ratio of vulcanizing agent HTDM are
0.8-1.2:1.3-1.7:1.5-1.8:1.2-1.4.
Preferably, in restrictive coating raw material, tributyl citrate, epoxy soybean oil, disproportionated rosin, the weight of coumarone indene resin
Ratio is 0.7-1.4:1.2-1.6:1.5-2.5:1.5-1.7.
Preferably, in restrictive coating raw material, zirconium oxide, blanc fixe, graphene nanometer sheet, silicon carbide micro-powder, glass microballoon
Weight ratio be 1.4-1.6:0.4-0.6:14-18:3-10:17-19.
Preferably, restrictive coating raw material includes by weight: natural rubber 8-12 part, CSM 40-50 part,
Butyl rubber 12-16 part, chlorohydrin rubber 14-20 part, silicone rubber 6-10 part, accelerator TTEE0.8-1.2 part, accelerant N a-22
1.3-1.7 part, sulfur 1.5-1.8 part, vulcanizing agent HTDM 1.2-1.4 part, tributyl citrate 0.7-1.4 part, epoxy soybean oil
1.2-1.6 part, disproportionated rosin 1.5-2.5 part, coumarone indene resin 1.5-1.7 part, antioxidant MB Z 0.4-1 part, antioxidant A W
1.3-1.6 part, antioxidant D NP 1.4-1.8 part, hexamethoxymethyl melamine resin 0.7-1 part, zirconium oxide 1.4-1.6 part,
Blanc fixe 0.4-0.6 part, graphene nanometer sheet 14-18 part, silicon carbide micro-powder 3-10 part, glass microballoon 17-19 part, RF-90
Resin 1.1-1.3 part.
The present invention uses natural rubber, CSM, butyl rubber, chlorohydrin rubber and silicone rubber to be base material,
Using sulfur, vulcanizing agent HTDM as vulcanizing agent, coordinate interpolation accelerator TTEE and accelerant N a-22 to carry out helping sulfuration, make this
Bright high temperature resistant, wear-resisting, tension, and there is the most fire-resistant and mechanical property;Add tributyl citrate, epoxy soybean oil,
Disproportionated rosin and coumarone indene resin carry out mating reaction, and not only storeroom compatibility is good, good processability, simultaneously fireproof high-temperature resistant
And tensile property is the most excellent;Add silicon carbide micro-powder, graphene nanometer sheet, blanc fixe and glass microballoon further to assist
Same-action, makes the present invention the most cheap, and wearability is good, and can be applicable to the field more harsh to fireproof high-temperature resistant requirement
Closing, halogen-free environmental simultaneously, overall mix homogeneously, organic with other high with the combination degree of inorganic material, pull resistance is good, and it is fire-resistant
And mechanical property further enhances.
Detailed description of the invention
Below, by specific embodiment, technical scheme is described in detail.
Embodiment 1
A kind of fireproof high-temperature resistant combined wear-resistant tensile removal cable that the present invention proposes, including cable core and restrictive coating, its
Middle restrictive coating raw material includes by weight: natural rubber 5 parts, CSM 60 parts, butyl rubber 10 parts, chloropharin rubber
22 parts of glue, 5 parts of silicone rubber, accelerator TTEE 1.5 parts, accelerant N a-221 part, 2 parts of sulfur, vulcanizing agent HTDM 1 part, Fructus Citri Limoniae
Acid tributyl 1.6 parts, epoxy soybean oil 1 part, disproportionated rosin 3 parts, coumarone indene resin 1 part, antioxidant MB Z 1.2 parts, age resistor
AW 1 part, antioxidant D NP 2 parts, hexamethoxymethyl melamine resin 0.5 part, zirconium oxide 2 parts, blanc fixe 0.2 part, graphite
Alkene nanometer sheet 20 parts, silicon carbide micro-powder 5 parts, glass microballoon 20 parts, RF-90 resin 1 part.
Embodiment 2
A kind of fireproof high-temperature resistant combined wear-resistant tensile removal cable that the present invention proposes, including cable core and restrictive coating, its
Middle restrictive coating raw material includes by weight: natural rubber 15 parts, CSM 30 parts, butyl rubber 18 parts, chloropharin
Rubber 12 parts, 12 parts of silicone rubber, accelerator TTEE 0.5 part, accelerant N a-22 2 parts, 1 part of sulfur, vulcanizing agent HTDM 2 parts,
Tributyl citrate 0.5 part, epoxy soybean oil 1.8 parts, disproportionated rosin 1 part, coumarone indene resin 2 parts, antioxidant MB Z 0.2 part,
Antioxidant A W 2 parts, antioxidant D NP 1 part, hexamethoxymethyl melamine resin 1.2 parts, zirconium oxide 1 part, blanc fixe 0.8
Part, graphene nanometer sheet 10 parts, silicon carbide micro-powder 15 parts, glass microballoon 10 parts, RF-90 resin 2 parts.
Embodiment 3
A kind of fireproof high-temperature resistant combined wear-resistant tensile removal cable that the present invention proposes, including cable core and restrictive coating, its
Middle restrictive coating raw material includes by weight: natural rubber 8 parts, CSM 50 parts, butyl rubber 12 parts, chloropharin rubber
20 parts of glue, 6 parts of silicone rubber, accelerator TTEE 1.2 parts, accelerant N a-221.3 part, 1.8 parts of sulfur, vulcanizing agent HTDM 1.2
Part, tributyl citrate 1.4 parts, epoxy soybean oil 1.2 parts, disproportionated rosin 2.5 parts, coumarone indene resin 1.5 parts, antioxidant MB Z
1 part, antioxidant A W 1.3 parts, antioxidant D NP 1.8 parts, hexamethoxymethyl melamine resin 0.7 part, zirconium oxide 1.6 parts, weight
0.4 part of spar powder, graphene nanometer sheet 18 parts, silicon carbide micro-powder 3 parts, glass microballoon 19 parts, RF-90 resin 1.1 parts.
Embodiment 4
A kind of fireproof high-temperature resistant combined wear-resistant tensile removal cable that the present invention proposes, including cable core and restrictive coating, its
Middle restrictive coating raw material includes by weight: natural rubber 12 parts, CSM 40 parts, butyl rubber 16 parts, chloropharin
Rubber 14 parts, 10 parts of silicone rubber, accelerator TTEE 0.8 part, accelerant N a-22 1.7 parts, 1.5 parts of sulfur, vulcanizing agent HTDM
1.4 parts, tributyl citrate 0.7 part, epoxy soybean oil 1.6 parts, disproportionated rosin 1.5 parts, coumarone indene resin 1.7 parts, age resistor
MBZ 0.4 part, antioxidant A W 1.6 parts, antioxidant D NP 1.4 parts, hexamethoxymethyl melamine resin 1 part, zirconium oxide 1.4
Part, blanc fixe 0.6 part, graphene nanometer sheet 14 parts, silicon carbide micro-powder 10 parts, glass microballoon 17 parts, RF-90 resin 1.3 parts.
Embodiment 5
A kind of fireproof high-temperature resistant combined wear-resistant tensile removal cable that the present invention proposes, including cable core and restrictive coating, its
Middle restrictive coating raw material includes by weight: natural rubber 10 parts, CSM 45 parts, butyl rubber 14 parts, chloropharin
Rubber 17 parts, 8 parts of silicone rubber, accelerator TTEE 1 part, accelerant N a-221.5 part, 1.6 parts of sulfur, vulcanizing agent HTDM 1.3
Part, tributyl citrate 1 part, epoxy soybean oil 1.4 parts, disproportionated rosin 2 parts, coumarone indene resin 1.6 parts, antioxidant MB Z 0.7
Part, antioxidant A W 1.5 parts, antioxidant D NP 1.6 parts, hexamethoxymethyl melamine resin 0.8 part, zirconium oxide 1.5 parts, weight
0.5 part of spar powder, graphene nanometer sheet 16 parts, silicon carbide micro-powder 7 parts, glass microballoon 18 parts, RF-90 resin 1.2 parts.
The above, the only present invention preferably detailed description of the invention, but protection scope of the present invention is not limited thereto,
Any those familiar with the art in the technical scope that the invention discloses, according to technical scheme and
Inventive concept equivalent or change in addition, all should contain within protection scope of the present invention.
Claims (6)
1. a fireproof high-temperature resistant combined wear-resistant tensile removal cable, it is characterised in that include cable core and restrictive coating, Qi Zhonghu
Jacket layer raw material includes by weight: natural rubber 5-15 part, CSM 30-60 part, butyl rubber 10-18 part,
Chlorohydrin rubber 12-22 part, silicone rubber 5-12 part, accelerator TTEE 0.5-1.5 part, accelerant N a-22 1-2 part, sulfur 1-2
Part, vulcanizing agent HTDM 1-2 part, tributyl citrate 0.5-1.6 part, epoxy soybean oil 1-1.8 part, disproportionated rosin 1-3 part is ancient
Horse grand resin 1-2 part, antioxidant MB Z 0.2-1.2 part, antioxidant A W 1-2 part, antioxidant D NP 1-2 part, hexakis-methoxy methyl three
Cymel 0.5-1.2 part, zirconium oxide 1-2 part, blanc fixe 0.2-0.8 part, graphene nanometer sheet 10-20 part, carborundum
Micropowder 5-15 part, glass microballoon 10-20 part, RF-90 resin 1-2 part.
Fireproof high-temperature resistant combined wear-resistant tensile removal cable the most according to claim 1, it is characterised in that restrictive coating raw material
In, natural rubber, CSM, butyl rubber, chlorohydrin rubber, the weight ratio of silicone rubber are 8-12:40-50:12-
16:14-20:6-10.
Fireproof high-temperature resistant the most according to claim 1 or claim 2 combined wear-resistant tensile removal cable, it is characterised in that restrictive coating
In raw material, accelerator TTEE, accelerant N a-22, sulfur, the weight ratio of vulcanizing agent HTDM are 0.8-1.2:1.3-1.7:1.5-
1.8:1.2-1.4.
4. according to fireproof high-temperature resistant combined wear-resistant tensile removal cable described in any one of claim 1-3, it is characterised in that protect
In jacket layer raw material, tributyl citrate, epoxy soybean oil, disproportionated rosin, the weight ratio of coumarone indene resin are 0.7-1.4:1.2-
1.6:1.5-2.5:1.5-1.7.
5. according to fireproof high-temperature resistant combined wear-resistant tensile removal cable described in any one of claim 1-4, it is characterised in that protect
In jacket layer raw material, zirconium oxide, blanc fixe, graphene nanometer sheet, silicon carbide micro-powder, the weight ratio of glass microballoon are 1.4-1.6:
0.4-0.6:14-18:3-10:17-19.
6. according to fireproof high-temperature resistant combined wear-resistant tensile removal cable described in any one of claim 1-5, it is characterised in that protect
Jacket layer raw material includes by weight: natural rubber 8-12 part, CSM 40-50 part, butyl rubber 12-16 part,
Chlorohydrin rubber 14-20 part, silicone rubber 6-10 part, accelerator TTEE 0.8-1.2 part, accelerant N a-22 1.3-1.7 part, sulfur
1.5-1.8 part, vulcanizing agent HTDM 1.2-1.4 part, tributyl citrate 0.7-1.4 part, epoxy soybean oil 1.2-1.6 part, disproportionation
Colophonium 1.5-2.5 part, coumarone indene resin 1.5-1.7 part, antioxidant MB Z 0.4-1 part, antioxidant A W 1.3-1.6 part, age resistor
DNP 1.4-1.8 part, hexamethoxymethyl melamine resin 0.7-1 part, zirconium oxide 1.4-1.6 part, blanc fixe 0.4-0.6
Part, graphene nanometer sheet 14-18 part, silicon carbide micro-powder 3-10 part, glass microballoon 17-19 part, RF-90 resin 1.1-1.3 part.