CN106189825A - A kind of fire-resistant anticorrosion paint - Google Patents
A kind of fire-resistant anticorrosion paint Download PDFInfo
- Publication number
- CN106189825A CN106189825A CN201610590943.3A CN201610590943A CN106189825A CN 106189825 A CN106189825 A CN 106189825A CN 201610590943 A CN201610590943 A CN 201610590943A CN 106189825 A CN106189825 A CN 106189825A
- Authority
- CN
- China
- Prior art keywords
- parts
- fire
- anticorrosion paint
- resistant anticorrosion
- paint
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of fire-resistant anticorrosion paint, including the composition of following content ratio: organic siliconresin 15 35 parts, epoxy resin 10 25 parts, carborundum 8 12 parts, boron nitride 5 15 parts, aluminium oxide 10 15 parts, fire retardant 8 15 parts, chromic anhydride 7 12 parts, phosphate 5 10 parts, nickel titanate 15 parts, deionized water 15 35 parts, isopropanol 10 25 parts, polybutadiene 5 15 parts, tetraethyl orthosilicate 10 25 parts.The present invention all has outstanding adhesive force to glass, pottery, steel construction piece, concrete and various types of resins priming paint etc., can be widely used for the exhaustor of automobile, motorcycle, the anticorrosion of chimney gutter etc., leakproof.
Description
Technical field
The present invention relates to paint field, particularly a kind of fire-resistant anticorrosion paint.
Background technology
Use equipment under some hot environments, such as: automobile, the exhaustor of motorcycle, chimney etc., owing to being chronically at height
In temperature rugged environment, cause the service life reduction of equipment, therefore need it is protected.Conventional method is sprayed coating.And
Traditional anticorrosive coating is due to non-refractory, and the life-span is shorter under the high temperature conditions, and containing a large amount of metallic compounds, not only dirty
Dye environment, and the person is harmful to.The most how to prepare a kind of fire resistant anticorrosive paint be those skilled in the art always
The problem making great efforts to solve.
Summary of the invention
The technical problem that present invention mainly solves is to provide a kind of fire-resistant anticorrosion paint, solves being weak to of existing coating
High temperature, corrosion-prone problem.
For solving above-mentioned technical problem, the technical scheme that the present invention uses is: provide a kind of fire-resistant anticorrosion paint,
Composition including following content ratio:
Organic siliconresin 15 35 parts
Epoxy resin 10 25 parts
Carborundum 8 12 parts
Boron nitride 5 15 parts
Aluminium oxide 10 15 parts
Fire retardant 8 15 parts
Chromic anhydride 7 12 parts
Phosphate 5 10 parts
Nickel titanate 15 parts
Deionized water 15 35 parts
Isopropanol 10 25 parts
Polybutadiene 5 15 parts
Tetraethyl orthosilicate 10 25 parts.
The invention has the beneficial effects as follows: providing a kind of fire-resistant anticorrosion paint, coating dried pieces, any surface finish smooths, tool
There is superior decorative effect.And good flame retardation effect, high temperature resistant, corrosion-resistant, in high temperature environments, will not be dry and cracked, flake.
Detailed description of the invention
Below presently preferred embodiments of the present invention is described in detail so that advantages and features of the invention can be easier to by
It will be appreciated by those skilled in the art that thus protection scope of the present invention is made apparent clear and definite defining.
The embodiment of the present invention 1 includes: a kind of fire-resistant anticorrosion paint, including the composition of following content ratio:
Organic siliconresin 35 parts
Epoxy resin 25 parts
Carborundum 12 parts
Boron nitride 15 parts
Aluminium oxide 15 parts
Fire retardant 15 parts
Chromic anhydride 12 parts
Phosphate 10 parts
Nickel titanate 5 parts
Deionized water 35 parts
Isopropanol 25 parts
Polybutadiene 15 parts
Tetraethyl orthosilicate 25 parts.
The embodiment of the present invention 2 includes: a kind of fire-resistant anticorrosion paint, including the composition of following content ratio:
Organic siliconresin 15 parts
Epoxy resin 10 parts
Carborundum 8 parts
Boron nitride 5 parts
Aluminium oxide 10 parts
Fire retardant 8 parts
Chromic anhydride 7 parts
Phosphate 5 parts
Nickel titanate 1 part
Deionized water 15 parts
Isopropanol 10 parts
Polybutadiene 5 parts
Tetraethyl orthosilicate 10 parts.
The embodiment of the present invention 3 includes: a kind of fire-resistant anticorrosion paint, including the composition of following content ratio:
Organic siliconresin 27 parts
Epoxy resin 20 parts
Carborundum 10 parts
Boron nitride 10 parts
Aluminium oxide 12 parts
Fire retardant 13 parts
Chromic anhydride 10 parts
Phosphate 7 parts
Nickel titanate 3 parts
Deionized water 25 parts
Isopropanol 18 parts
Polybutadiene 10 parts
Tetraethyl orthosilicate 17 parts.
Above-described embodiment, only for technology design and the feature of the explanation present invention, its object is to allow person skilled in the art's energy
Solution present disclosure much of that is also carried out, and can not limit the scope of the invention with this, all according to present invention spirit
The equivalence that essence is made changes or modifies, and all should contain within the scope of the present invention.
Claims (1)
1. a fire-resistant anticorrosion paint, it is characterised in that: include the composition of following content ratio:
Organic siliconresin 15 35 parts
Epoxy resin 10 25 parts
Carborundum 8 12 parts
Boron nitride 5 15 parts
Aluminium oxide 10 15 parts
Fire retardant 8 15 parts
Chromic anhydride 7 12 parts
Phosphate 5 10 parts
Nickel titanate 15 parts
Deionized water 15 35 parts
Isopropanol 10 25 parts
Polybutadiene 5 15 parts
Tetraethyl orthosilicate 10 25 parts.