CN102146239B - Multifunctional colorful waterproof and anticorrosion coating - Google Patents
Multifunctional colorful waterproof and anticorrosion coating Download PDFInfo
- Publication number
- CN102146239B CN102146239B CN 201010123822 CN201010123822A CN102146239B CN 102146239 B CN102146239 B CN 102146239B CN 201010123822 CN201010123822 CN 201010123822 CN 201010123822 A CN201010123822 A CN 201010123822A CN 102146239 B CN102146239 B CN 102146239B
- Authority
- CN
- China
- Prior art keywords
- waterproof
- multifunctional
- protections
- anticorrosion coating
- corrosive
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention relates to a waterproof building material, in particular to a multifunctional colorful waterproof and anticorrosion coating. A composition of the multifunctional colorful waterproof and anticorrosion coating mainly comprises a water-based fluorocarbon emulsion resin, an ethylene-vinyl acetate copolymer (VAE), a silicate frit, alumina cement, an ester plasticizer, ethylene glycol, inorganic filler and an organic pigment. The multifunctional colorful waterproof and anticorrosion coating disclosed by the invention has the characteristics of good durability, long maintenance time, good corrosion resistance and the like, is mainly applicable to corrosion protections of nontoxic environments, such as waterworks and the like, in particular to protections of concrete structures of industrial and domestic sewage treatment plants and protections of water pipelines, and is also applicable to corrosion protections and water repellencies of concrete structures of landfill sits.
Description
Technical field
The present invention relates to a kind of building anti-corrosion water-proof material, relate to specifically a kind of multifunctional colour anti-corrosive and waterproof paint.
Background technology
At present, the technology development of anti-corrosive and waterproof paint is very fast, but protective system is the impregnating material of the lysotypes such as glass reinforced plastic, urethane, Resins, epoxy mostly, use inconvenience, price is high, solvent evaporates is arranged during construction, harmful to operator, the most disadvantageously can not construct at wet environment.
Summary of the invention
The object of the invention is to solve the deficiencies in the prior art, provide a kind of price to be lower than glass reinforced plastic, urethane, Resins, epoxy, performance can be accomplished the effect of anticorrosion waterproof on an equal basis, can under wet environment, construct again, have good anticorrosion water-repellancy, film-forming properties, close-burning hydrate colour multifunctional anticorrosive waterproof paint.
Technical scheme of the present invention is achieved in that a kind of multifunctional colour anti-corrosive and waterproof paint, and composition and the parts by weight of its raw material are as follows:
Water-base fluorocarbon emulsion resin 30-60
Ethene one vinegar ethylene copolymer (VAE) 10-20
Silicate glass material 5-10
High-alumina cement 10-20
Ester plasticizer 5-15
Ethylene glycol 0-10
Mineral filler 1-5
Mineral dye 3-10
Compound method is liquid component water-base fluorocarbon emulsion resin, ethene one vinegar ethylene copolymer (VAE), ester plasticizer, ethylene glycol to be mixed be made into the first component, and solid component silicate glass material, high-alumina cement, mineral filler, mineral dye are made into component B; First component and component B put together to stir got final product in about 10 minutes.
This prescription also can not add ethylene glycol, and ethylene glycol can play freeze proof, improves the effect of levelling property.
Described silicate glass material is by silicon-dioxide 35-38%, potassium oxide 5-8%, and Manganse Dioxide 2-5%, boron trioxide 18-22%, Lithium Oxide 98min 2-6%, calcium oxide 8-9%, sodium oxide 10-12%, aluminium sesquioxide 4-5%, nickel oxide 0.1-1.4% forms.
Calcium carbonate is selected in described mineral filler, and kaolin or mica powder can play wear-resisting effect.
Described lipid softening agent is selected dibutylester or dioctyl ester, can improve the shock-resistance that coating is filmed, snappiness, the performances such as sticking power.
Described mineral dye is selected iron oxide pigment, can make the versicolor waterproof paints such as black, redness, green, yellow, because be mineral dye, so light permanency is good.
A kind of multifunctional colour anti-corrosive and waterproof paint of the present invention has good endurance, maintenance time is long, the characteristics such as good corrosion resistance, and the present invention is specially adapted to adopt cold process construction, it is little to have smell, nontoxic, construction is simple, and is convenient and safe, film without seam, elasticity, the advantage such as corrosion-resistant, ageing-resistant, long service life, non-environmental-pollution.Less demanding to the basal plane planeness during construction, can in moist basal plane construction, widen use range.Mainly be applicable to the nontoxic environment such as tap water water factory anticorrosion, be specially adapted to industry and the protection of sanitary sewage disposal factory concrete structure, the protection of water pipe, the also anticorrosion waterproof of applicable landfill concrete structure.
Embodiment
Embodiment one:
Water-base fluorocarbon emulsion resin 40
Ethene one vinegar ethylene copolymer (VAE) 15
Silicate glass material 8
High-alumina cement 10
Dibutylester 7
Ethylene glycol 10
Calcium carbonate 5
Iron oxide pigment 5
Embodiment two:
Water-base fluorocarbon emulsion resin 60
Ethene one vinegar ethylene copolymer (VAE) 10
Silicate glass material 5
High-alumina cement 10
Dioctyl ester 5
Ethylene glycol 6
Kaolin 1
Iron oxide pigment 3
Embodiment three:
Water-base fluorocarbon emulsion resin 30
Ethene one vinegar ethylene copolymer (VAE) 20
Silicate glass material 10
High-alumina cement 15
Dioctyl ester 15
Ethylene glycol 0
Mica powder 3
Iron oxide pigment 7
Embodiment four:
Water-base fluorocarbon emulsion resin 35
Ethene one vinegar ethylene copolymer (VAE) 12
Silicate glass material 7
High-alumina cement 20
Dibutylester 10
Ethylene glycol 2
Calcium carbonate 4
Iron oxide pigment 10
Above-described embodiment is also non exhaustive.The multifunctional colour anti-corrosive and waterproof paint of gained has following technical indicator:
Time of drying (25 ℃): surface drying≤2h does solid work≤6h;
Sticking power: 1.75MPa;
Tensile strength: 1.8MPa;
Unit elongation: 300%;
Watertightness: 0.3MPa (one hour waterproof);
(time of drying (25 ℃): surface drying≤2h does solid work≤6h chemical-resistant reagent;
Sticking power: 1.75MPa;
Tensile strength: 1.8MPa;
Unit elongation: 300%;
Watertightness: 0.3MPa (one hour waterproof);
Chemical-resistant reagent (7d): 2% sulfuric acid is non-foaming, do not come off;
3% sodium hydroxide is non-foaming, do not come off;
2% hydrochloric acid is non-foaming, do not come off;
10% sodium-chlor is non-foaming, do not come off
100% kerosene is non-foaming, do not come off
Gasoline is non-foaming, do not come off
Diesel oil is non-foaming, do not come off.
Claims (4)
1. multifunctional colour anti-corrosive and waterproof paint, it is characterized in that: composition and the parts by weight of its raw material are as follows:
Described silicate glass material is by silicon-dioxide 35-38%, potassium oxide 5-8%, and Manganse Dioxide 2-5%, boron trioxide 18-22%, Lithium Oxide 98min 2-6%, calcium oxide 8-9%, sodium oxide 10-12%, aluminium sesquioxide 4-5%, nickel oxide 0.1-1.4% forms.
2. the multifunctional colour anti-corrosive and waterproof paint described in according to claim 1, it is characterized in that: described ester plasticizer is selected dibutylester or dioctyl ester.
According to claim 1 in the multifunctional colour anti-corrosive and waterproof paint of stating of institute, it is characterized in that: calcium carbonate is selected in described mineral filler, kaolin or mica are native.
4. the multifunctional colour anti-corrosive and waterproof paint described in according to claim 1, it is characterized in that: described mineral dye is selected iron oxide pigment.