CN104877513A - 一种皮革制品表面喷涂涂料 - Google Patents

一种皮革制品表面喷涂涂料 Download PDF

Info

Publication number
CN104877513A
CN104877513A CN201510375065.9A CN201510375065A CN104877513A CN 104877513 A CN104877513 A CN 104877513A CN 201510375065 A CN201510375065 A CN 201510375065A CN 104877513 A CN104877513 A CN 104877513A
Authority
CN
China
Prior art keywords
minutes
ether
leatherware
mixture
leatherware surface
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510375065.9A
Other languages
English (en)
Inventor
杨高林
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201510375065.9A priority Critical patent/CN104877513A/zh
Publication of CN104877513A publication Critical patent/CN104877513A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种皮革制品表面处理涂料，其配方按质量百分比计算，由以下组分组成：乙酰乙酸基甲基丙烯酸乙酯：10～20％；磷酸三钠：15～45％；聚异丁烯基丁二酰亚胺：10～40％；苍耳子油：1～7％；硼酸：3～13％；聚乙烯吡咯酮：0.1～1％；丙二醇正丁醚：1～9％；尿素：1～10％；其余为去离子水。该发明中，用该涂料处理过的皮革制品具有极佳的柔顺手感，耐化学性，耐磨，具有高拉伸，高伸长率，耐水耐湿，抗紫外线，不黄变、高光；本涂料树脂对皮革制品表面具有高弹力，附着力佳。

Description

一种皮革制品表面喷涂涂料
技术领域
本发明属于皮革制品表面处理技术领域，更具体是涉及一种皮革制品表面喷涂涂料。
背景技术
皮革制品表面进经常需要进行多种多样的处理，以便能够改善皮革制品表面性能，方便其根据需要使用，一般的皮革制品表面处理方式，大多是通过涂料喷涂进行，而一般的涂料制备过程中，需要采用不同的涂料原料予以配置，以便能够改善涂料使用效果.
发明内容
本发明的目的是提供一种皮革制品表面喷涂涂料，该涂料具有成膜柔软，高光的作用，对皮革制品有极佳的柔顺手感。
为达到上述目的，本发明具体的技术方案如下：
一种皮革制品表面喷涂涂料，其配方按质量百分比计算，由以下组分组成：乙酰乙酸基甲基丙烯酸乙酯：10～20％；磷酸三钠：15～45％；聚异丁烯基丁二酰亚胺：10～40％；苍耳子油：1～7％；硼酸：3～13％；聚乙烯吡咯酮：0.1～1％；丙二醇正丁醚：1～9％；尿素：1～10％；其余为去离子水。
其具体制备工艺如下：
(1)先将乙酰乙酸基甲基丙烯酸乙酯、磷酸三钠投入反应釜中，加热到110～120℃，然后抽真空脱水30～60分钟；
(2)将上述混合物降温到85℃，加入有机铋崔化剂搅拌10分钟；
(3)再向上述混合物中加入聚异丁烯基丁二酰亚胺，维持温度70～90℃保温120～180分钟；
(4)然后在上述温合物中加入苍耳子油、硼酸及适量的乙醚，维持温度70～90℃保温180～240分钟继续反应；
(5)然后将上述混合物冷却到40℃，加入丙二醇正丁醚及乙醚，搅拌10～30分钟；
(6)在上述搅拌的同时，加入已混合尿素的去离子水；
(7)继续搅拌60～120分钟，真空抽去乙醚，即可得到成品。
本发明的有益效果在于：该发明中，用该涂料处理过的皮革制品具有极佳的柔顺手感，耐化学性，耐磨，具有高拉伸，高伸长率，耐水耐湿，抗紫外线，不黄变、高光；本涂料树脂对皮革制品表面具有高弹力，附着力佳。
具体实施方式
以下结合具体实施例来对本发明作进一步的描述。
实施例1
本实施例中的皮革制品表面喷涂涂料，其配方按质量百分比计算，由以下组分组成：乙酰乙酸基甲基丙烯酸乙酯：10％；磷酸三钠：15％；聚异丁烯基丁二酰亚胺：40％；苍耳子油：7％；硼酸：3％；聚乙烯吡咯酮：0.1％；丙二醇正丁醚：9％；尿素：10％；其余为去离子水。
其具体制备工艺如下：
(1)先将乙酰乙酸基甲基丙烯酸乙酯、磷酸三钠投入反应釜中，加热到110℃，然后抽真空脱水60分钟；
(2)将上述混合物降温到85℃，加入有机铋崔化剂搅拌10分钟；
(3)再向上述混合物中加入聚异丁烯基丁二酰亚胺，维持温度70℃保温180分钟；
(4)然后在上述温合物中加入苍耳子油、硼酸及适量的乙醚，维持温度90℃保温180分钟继续反应；取样检测异氰酸酯基含量(NCO)，使其含量维持在2％；
(5)然后将上述混合物冷却到40℃，加入丙二醇正丁醚及乙醚，搅拌30分钟；
(6)在上述搅拌的同时，加入已混合尿素的去离子水；
(7)继续搅拌100分钟，真空抽去乙醚，即可得到成品。
实施例2
本实施例中的皮革制品表面喷涂涂料，其配方按质量百分比计算，由以下组分组成：乙酰乙酸基甲基丙烯酸乙酯：20％；磷酸三钠：45％；聚异丁烯基丁二酰亚胺：10；苍耳子油：1；硼酸：13％；聚乙烯吡咯酮：1％；丙二醇正丁醚：1％；尿素：1％；其余为去离子水。
其具体制备工艺如下：
(1)先将乙酰乙酸基甲基丙烯酸乙酯、磷酸三钠投入反应釜中，加热到120℃，然后抽真空脱水30分钟；
(2)将上述混合物降温到85℃，加入有机铋崔化剂搅拌10分钟；
(3)再向上述混合物中加入聚异丁烯基丁二酰亚胺，维持温度90℃保温120分钟；
(4)然后在上述温合物中加入苍耳子油、硼酸及适量的乙醚，维持温度90℃保温180分钟继续反应；取样检测异氰酸酯基含量(NCO)，使其含量维持在0.5％；
(5)然后将上述混合物冷却到40℃，加入丙二醇正丁醚及乙醚，搅拌10分钟；
(6)在上述搅拌的同时，加入已混合尿素的去离子水；
(7)继续搅拌60分钟，真空抽去乙醚，即可得到成品。
实施例3
本实施例中的皮革制品表面喷涂涂料，其配方按质量百分比计算，由以下组分组成：乙酰乙酸基甲基丙烯酸乙酯：15％；磷酸三钠：30％；聚异丁烯基丁二酰亚胺：25％；苍耳子油：4％；硼酸：8％；聚乙烯吡咯酮：0.5％；丙二醇正丁醚：5％；尿素：5％；其余为去离子水。
其具体制备工艺如下：
(1)先将乙酰乙酸基甲基丙烯酸乙酯、磷酸三钠投入反应釜中，加热到115℃，然后抽真空脱水45分钟；
(2)将上述混合物降温到85℃，加入有机铋崔化剂搅拌10分钟；
(3)再向上述混合物中加入聚异丁烯基丁二酰亚胺，维持温度80℃保温150分钟；
(4)然后在上述温合物中加入苍耳子油、硼酸及适量的乙醚，维持温度80℃保温210分钟继续反应；取样检测异氰酸酯基含量(NCO)，使其含量维持在2％；
(5)然后将上述混合物冷却到40℃，加入丙二醇正丁醚及乙醚，搅拌20分钟；
(6)在上述搅拌的同时，加入已混合尿素的去离子水；
(7)继续搅拌90分钟，真空抽去乙醚，即可得到成品。

Claims (2)

1.一种皮革制品表面处理涂料，其特征在于：按质量百分比计算，由以下组分组成：乙酰乙酸基甲基丙烯酸乙酯：10～20％；磷酸三钠：15～45％；聚异丁烯基丁二酰亚胺：10～40％；苍耳子油：1～7％；硼酸：3～13％；聚乙烯吡咯酮：0.1～1％；丙二醇正丁醚：1～9％；尿素：1～10％；其余为去离子水。
2.根据权利要求1所述的用于皮革制品表面处理的涂料，其特征在于：其具体制备工艺如下：
(1)先将乙酰乙酸基甲基丙烯酸乙酯、磷酸三钠投入反应釜中，加热到110～120℃，然后抽真空脱水30～60分钟；
(2)将上述混合物降温到85℃，加入有机铋崔化剂搅拌10分钟；
(3)再向上述混合物中加入聚异丁烯基丁二酰亚胺，维持温度70～90℃保温120～180分钟；
(4)然后在上述温合物中加入苍耳子油、硼酸及适量的乙醚，维持温度70～90℃保温180～240分钟继续反应；
(5)然后将上述混合物冷却到40℃，加入丙二醇正丁醚及乙醚，搅拌10～30分钟；
(6)在上述搅拌的同时，加入已混合尿素的去离子水；
(7)继续搅拌60～120分钟，真空抽去乙醚，即可得到成品。
CN201510375065.9A 2015-07-01 2015-07-01 一种皮革制品表面喷涂涂料 Pending CN104877513A (zh)