CN104867641B - 高频变压器用高电感值高磁导率铁氧体磁芯 - Google Patents
高频变压器用高电感值高磁导率铁氧体磁芯 Download PDFInfo
- Publication number
- CN104867641B CN104867641B CN201510310994.1A CN201510310994A CN104867641B CN 104867641 B CN104867641 B CN 104867641B CN 201510310994 A CN201510310994 A CN 201510310994A CN 104867641 B CN104867641 B CN 104867641B
- Authority
- CN
- China
- Prior art keywords
- component
- frequency transformer
- inductance
- inductance value
- ferrite core
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开了一种高频变压器用高电感值高磁导率铁氧体磁芯,包括第一组分、第二组分和烧结助剂;所述第一组分包括Fe2O3、ZnO、MnO和NiO;所述第二组分包括La2O3、Nb2O5、V2O5、CuO、Bi2O3、TiO2和Cs2O;所述第一组分和第二组分的质量比为7~10:0.5~1;所述烧结助剂为所述第一组分和第二组分总质量的3~5%。本发明一种高频变压器用高电感值高磁导率铁氧体磁芯,通过锰、锌、铁、镍元素含量的合理配比及配方设计,使所得的铁氧体磁芯具有优异的电感值和磁导率,综合性能优异,完全适用于变压器对磁芯的电感值和磁通率的要求,应用前景广阔。
Description
技术领域
本发明涉及锰锌铁氧体技术领域,特别是涉及一种高频变压器用高电感值高磁导率铁氧体磁芯。
背景技术
磁芯是指由各种氧化铁混合物组成的一种烧结磁性金属氧化物。例如,锰- 锌铁氧体和镍- 锌铁氧体是典型的磁芯体材料。铁氧体磁芯用于各种电子设备的线圈和变压器中,其是一种高频导磁材料,主要做高频变压器(像开关电源,行输出变压器等),高频磁环(抗干扰用)等等。锰- 锌铁氧体具有高磁导率和高磁通密度的特点,且在低于1MHz 的频率时,具有较低损耗的特性。镍- 锌铁氧体具有极高的阻抗率、不到几百的低磁导率等特性,及在高于1MHz 的频率亦产生较低损耗等。
目前,随着家用电器、高性能电脑和LCD显示器等的开关电源变压器向小型化、轻薄化和多功能化方向的发展,磁芯在这些设备中得到了越来越广泛的应用,并且成为缩小开关电源变压器的体积、降低温升和提高变压器的输出功率不可缺少的组件,但随着技术的进步,现有磁芯的电感值和磁通率相对较低,不能满足日益先进的变压器的使用需求。
发明内容
本发明主要解决的技术问题是提供一种高频变压器用高电感值高磁导率铁氧体磁芯,能够解决现有变压器用磁芯材料存在的不足之处。
为解决上述技术问题,本发明采用的一个技术方案是:提供一种高频变压器用高电感值高磁导率铁氧体磁芯,包括:第一组分、第二组分和烧结助剂;所述第一组分包括Fe2O3、ZnO、MnO和NiO;所述第二组分包括L a2O3、Nb2O5、V2O5 、CuO、Bi2O3、TiO2和Cs2O;所述第一组分和第二组分的质量比为7~10:0.5~1;所述烧结助剂为所述第一组分和第二组分总质量的3~5%。
在本发明一个较佳实施例中,所述第一组分中Fe2O3、ZnO、MnO和NiO的质量百分比为:Fe2O3 50~55%、ZnO 8~15%、MnO 15~25%、NiO 18~22%。
在本发明一个较佳实施例中,所述第二组分中La2O3、Nb2O5、V2O5 、CuO、Bi2O3、TiO2和Cs2O的质量百分比为:La2O3 20~30%、Nb2O5 5~8%、V2O5 15~20%、CuO 15~25%、Bi2O3 10~15%、TiO2 3~5%、Cs2O 3~5%。
在本发明一个较佳实施例中,所述烧结助剂为Li2O。
在本发明一个较佳实施例中,所述铁氧体磁芯的初始磁导率为3800~5100、电感值50~500mH,阻抗率85%以上,25℃时的电阻率为1.3~1.8×104ρ/Ωm。
本发明的有益效果是:本发明一种高频变压器用高电感值高磁导率铁氧体磁芯,通过锰、锌、铁、镍元素含量的合理配比及配方设计,使所得的铁氧体磁芯具有优异的电感值和磁导率,综合性能优异,完全适用于变压器对磁芯的电感值和磁通率的要求,应用前景广阔。
具体实施方式
下面对本发明的较佳实施例进行详细阐述,以使本发明的优点和特征能更易于被本领域技术人员理解,从而对本发明的保护范围做出更为清楚明确的界定。
本发明实施例包括:
实施例1
本发明揭示了一种高频变压器用高电感值高磁导率铁氧体磁芯,由质量比为7~10:0.5~1的第一组分、第二组分和占第一组分和第二组分总质量3~5%的烧结助剂制备而成;其中,第一组分的原料及其质量百分比为:Fe2O3 50~55%、ZnO 8~15%、MnO 15~25%、NiO 18~22%;第二组分的原料及其质量百分比为:La2O3 20~30%、Nb2O5 5~8%、V2O5 15~20%、CuO 15~25%、Bi2O3 10~15%、TiO2 3~5%、Cs2O 3~5%;烧结助剂为Li2O;
具体制备方法为:
称取原料:称取质量百分比为50%的Fe2O3、15%的ZnO、17%的MnO和18%的NiO作为第一组分;称取质量百分比为20%的La2O3、8%的Nb2O5、20%的V2O5、25%的CuO、17%的Bi2O3、5%的TiO2和5%的Cs2O 作为第二组分;称取占所述第一组分和第二组分总质量的3%的Li2O;
混合湿磨:将称取的第一组分和第二组分加入球磨罐中,按照物料:球:水的质量比为1:5:1的比例加入蒸馏水,混合湿磨6h,得到混合物料;
预烧:将混合湿磨后的物料置于马弗炉中,先在80℃下烘干,再在400℃下预烧4h;
混合研磨:将预烧后的混合物料置于球磨机中,再加入配方量的Li2O,混合研磨至物料粒径为0.5~1.0μm;
制备混合浆料:向得到的混合物料中再加入质量浓度为12%占混合物料重量0.1倍的聚乙烯醇水溶液,搅拌混合,得到混合浆料;
烧结成型:将得到的混合浆料在后压制成型,然后连同模具转入带程序升温功能的惰性气体气氛的窑炉中烧结,其中,惰性气体为压力为20Pa,气体流速为3m/min的氦气,烧结工艺为:以150℃/h 的升温速率从室温加热到600℃,保温3h,再在1150℃下烧结保温6h,随后在惰性气氛下自然降温冷却至室温,得到所述高热阻敏感度和热磁敏感度纳米晶锰锌铁氧体。
上述方法所制备的高频变压器用高电感值高磁导率铁氧体磁芯的初始磁导率为3800、电感值50mH,阻抗率85%以上,25℃时的电阻率为1.3×104ρ/Ωm。
实施例2
本发明揭示了一种高频变压器用高电感值高磁导率铁氧体磁芯,由质量比为10:1的第一组分、第二组分和占第一组分和第二组分总质量5%的烧结助剂制备而成;烧结助剂为Li2O;
具体制备方法步骤如下:
称取原料:称取质量百分比为55%的Fe2O3、8%的ZnO、15%的MnO和22%的NiO作为第一组分;称取质量百分比为30%的La2O3、5%的Nb2O5、15%的V2O5、22%的CuO、20%的Bi2O3、3%的TiO2和3%的Cs2O 作为第二组分;称取占所述第一组分和第二组分总质量的5%的Li2O;
混合湿磨:将步骤(1)中称取的第一组分和第二组分加入球磨罐中,按照物料:球:水的质量比为2:3:1的比例加入蒸馏水,混合湿磨6h,得到混合物料;
预烧:将步骤(2)中混合湿磨后的物料置于马弗炉中,先在100℃下烘干,再在600℃下预烧3h;
混合研磨:将步骤(3)中预烧后的混合物料置于球磨机中,再加入配方量的Li2O,混合研磨至物料粒径为0.5~1.0μm;
制备混合浆料:向步骤(4)中得到的混合物料中再加入质量浓度为18%占混合物料重量0.1倍的聚乙烯醇水溶液,搅拌混合,得到混合浆料;
烧结成型:将得到的混合浆料在后压制成型,然后连同模具转入带程序升温功能的惰性气体气氛的窑炉中烧结,其中,惰性气体为压力为10Pa,气体流速为5m/min的氦气,烧结工艺为:以200℃/h 的升温速率从室温加热到800℃,保温2h,再在1200℃下烧结保温5h,随后在惰性气氛下自然降温冷却至室温,得到所述高热阻敏感度和热磁敏感度纳米晶锰锌铁氧体。
上述方法所制备的高频变压器用高电感值高磁导率铁氧体磁芯的初始磁导率为5100、电感值500mH,阻抗率85%以上,25℃时的电阻率为1.8×104ρ/Ωm。
以上所述仅为本发明的实施例,并非因此限制本发明的专利范围,凡是利用本发明说明书内容所作的等效结构或等效流程变换,或直接或间接运用在其他相关的技术领域,均同理包括在本发明的专利保护范围内。
Claims (5)
1.一种高频变压器用高电感值高磁导率铁氧体磁芯,其特征在于,包括:第一组分、第二组分和烧结助剂;所述第一组分包括Fe2O3、ZnO、MnO和NiO ;所述第二组分包括La2O3、Nb2O5、V2O5 、CuO、Bi2O3、TiO2和Cs2O ;所述第一组分和第二组分的质量比为7~10:0.5~1;所述烧结助剂为所述第一组分和第二组分总质量的3~5%。
2.根据权利要求1 所述的高频变压器用高电感值高磁导率铁氧体磁芯,其特征在于,所述第一组分中Fe2O3、ZnO、MnO 和NiO的质量百分比为:Fe2O3 50~55%、ZnO 8~15%、MnO15~25%、NiO 18~22%。
3.根据权利要求1 所述的高频变压器用高电感值高磁导率铁氧体磁芯,其特征在于,所述第二组分中La2O3、Nb2O5、V2O5 、CuO、Bi2O3、TiO2和Cs2O 的质量百分比为:La2O3 20~30%、Nb2O5 5~8%、V2O5 15~20%、CuO 15~25%、Bi2O3 10~15%、TiO2 3~5%、Cs2O 3~5%。
4.根据权利要求1 所述的高频变压器用高电感值高磁导率铁氧体磁芯,其特征在于,所述烧结助剂为Li2O。
5.根据权利要求1 至4 之一所述的高频变压器用高电感值高磁导率铁氧体磁芯,其特征在于,所述铁氧体磁芯的初始磁导率为3800~5100、电感值50~500mH,阻抗率85%以上,25℃时的电阻率ρ为1.3~1.8×104Ωm。