CN104862062A - 丝素水基润滑液的制备方法及其制备的丝素水基润滑液 - Google Patents
丝素水基润滑液的制备方法及其制备的丝素水基润滑液 Download PDFInfo
- Publication number
- CN104862062A CN104862062A CN201510211382.7A CN201510211382A CN104862062A CN 104862062 A CN104862062 A CN 104862062A CN 201510211382 A CN201510211382 A CN 201510211382A CN 104862062 A CN104862062 A CN 104862062A
- Authority
- CN
- China
- Prior art keywords
- fibroin
- water
- lubricating liquid
- preparation
- based lubricating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种丝素水基润滑液的制备方法及其制备的丝素水基润滑液，该方法的步骤如下：1）丝素提取，把生丝切片放置于NaOH溶液中脱胶，用离心机分离得到丝素；2）用去离子水洗涤干净后过滤并烘干，用研磨器将脱胶后的丝素研磨成粉末；3）将1重量份～2重量份的丝素置于量杯中加入98重量份～99重量份去离子水，均匀搅拌后并超声分散，得到该丝素水基润滑液。本发明以丝素为添加剂，通过搅拌超声分散制备成纳米级的水基悬浮液，不仅具有良好的润滑性而且具有优异的生物相容性，可被应用于医用医疗器械的机械润滑。
Description
技术领域
本发明涉及一种丝素水基润滑液的制备方法及其制备的丝素水基润滑液。
背景技术
目前，蚕丝是由丝素蛋白和丝胶蛋白组成的天然长纤维蛋白，其中丝素是坚韧而有弹性的蛋白质，占蚕丝纤维总量的70-80%，大分子中存在结晶区和非结晶区，主要成分为乙氨酸、丙氨酸、丝氨酸、脯氨酸、酪氨酸等各类氨基酸组成。丝素本身具有良好的机械性能和理化性质，如良好的柔韧性和抗拉伸强度、透气透湿性、缓释性等。另外，丝素蛋白是一种从蚕丝中提取的蛋白质，具有很好的生物相容性，能制备成膜、凝胶、微胶囊等多种形态的材料，由于它独特的理化性能，目前丝素蛋白材料在生物医学材料领域被广泛的研究，如固定化酶材料、细胞培养基质、药物缓释剂、人工器官等。因此，把丝素蛋白作为水基润滑液的添加剂，研究其生物摩擦学性能具有重要实用价值。
发明内容
本发明所要解决的技术问题是克服现有技术的缺陷，提供一种丝素水基润滑液的制备方法，它以丝素为添加剂，通过搅拌超声分散制备成纳米级的水基悬浮液，不仅具有良好的润滑性而且具有优异的生物相容性，可被应用于医用医疗器械的机械润滑。
实现本发明的技术问题所采取的技术方案是：一种丝素水基润滑液的制备方法，该方法的步骤如下：
1）丝素提取，把生丝切片放置于NaOH溶液中脱胶，用离心机分离得到丝素；
2）用去离子水洗涤干净后过滤并烘干，用研磨器将脱胶后的丝素研磨成粉末；
3）将1重量份～2重量份的丝素置于量杯中加入98重量份～99重量份去离子水，均匀搅拌后并超声分散，得到该丝素水基润滑液。
进一步，所述的步骤1）中，生丝切片放置于1.0 mol/L 的NaOH溶液中，压力2Mpa，温度125℃，煮沸时间1h。
进一步，步骤1）中，离心机转速为2000转/分，分离10min，得丝素。
进一步，所述的步骤2）中，丝素烘干温度为37℃。
进一步，所述的步骤3）中的超声分散的设备的超生频率为70Hz～100Hz。
本发明还提供了一种丝素水基润滑液的制备方法制备的丝素水基润滑液，它的组份以及各组份重量份如下：
丝素：1份～2份；
去离子水：98份～99份。
采用了上述技术方案后，本发明以丝素为添加剂，通过搅拌超声分散制备成纳米级线状微粒的水基悬浮液，不仅具有良好的润滑性而且具有优异的生物相容性，可被应用于医用医疗器械的机械润滑。
具体实施方式
为了使本发明的内容更容易被清楚地理解，下面根据具体实施例，对本发明作进一步详细的说明。
实施例一
一种丝素水基润滑液的制备方法，该方法的步骤如下：
1）丝素提取，把生丝切片放置于NaOH溶液中脱胶，用离心机分离得到丝素；
2）用去离子水洗涤干净后过滤并烘干，用研磨器将脱胶后的丝素研磨成粉末；
3）将1重量份的丝素置于量杯中加入99重量份去离子水，均匀搅拌后并超声分散，得到该丝素水基润滑液。
步骤1）中，生丝切片放置于1.0 mol/L 的NaOH溶液中，压力2Mpa，温度125℃，煮沸时间1h。
步骤1）中，离心机转速为2000转/分，分离10min，得丝素。
步骤2）中，丝素烘干温度为37℃。
步骤3）中的超声分散的设备的超生频率为70Hz～100Hz。
该丝素水基润滑液的制备方法制备的丝素水基润滑液，它的组份以及各组份重量份如下：
丝素：1份；
去离子水： 99份。
实施例二
一种丝素水基润滑液的制备方法，该方法的步骤如下：
1）丝素提取，把生丝切片放置于NaOH溶液中脱胶，用离心机分离得到丝素；
2）用去离子水洗涤干净后过滤并烘干，用研磨器将脱胶后的丝素研磨成粉末；
3）将2重量份的丝素置于量杯中加入98重量份去离子水，均匀搅拌后并超声分散，得到该丝素水基润滑液。
步骤1）中，生丝切片放置于1.0 mol/L 的NaOH溶液中，压力2Mpa，温度125℃，煮沸时间1h。
步骤1）中，离心机转速为2000转/分，分离10min，得丝素。
步骤2）中，丝素烘干温度为37℃。
步骤3）中的超声分散的设备的超生频率为70Hz～100Hz。
该丝素水基润滑液的制备方法制备的丝素水基润滑液，它的组份以及各组份重量份如下：
丝素： 2份；
去离子水：98份。
经过上述两种实施例方法以及多次实验制备的该种水基润滑液，不仅具有良好的润滑性而且具有优异的生物相容性，可被应用于医用医疗器械的机械润滑。
以上所述的具体实施例，对本发明解决的技术问题、技术方案和有益效果进行了进一步详细说明，所应理解的是，以上所述仅为本发明的具体实施例而已，并不用于限制本发明，凡在本发明的精神和原则之内，所做的任何修改、等同替换、改进等，均应包含在本发明的保护范围之内。
Claims (6)
1.一种丝素水基润滑液的制备方法，其特征在于该方法的步骤如下：
1）丝素提取，把生丝切片放置于NaOH溶液中脱胶，用离心机分离得到丝素；
2）用去离子水洗涤干净后过滤并烘干，用研磨器将脱胶后的丝素研磨成粉末；
3）将1重量份～2重量份的丝素置于量杯中加入98重量份～99重量份去离子水，均匀搅拌后并超声分散，得到该丝素水基润滑液。
2.根据权利要求1中所述的丝素水基润滑液的制备方法，其特征在于：所述的步骤1）中，生丝切片放置于1.0 mol/L 的NaOH溶液中，压力2Mpa，温度125℃，煮沸时间1h。
3.根据权利要求1中所述的丝素水基润滑液的制备方法，其特征在于：所述的步骤1）中，离心机转速为2000转/分，分离10min，得丝素。
4.根据权利要求1中所述的丝素水基润滑液的制备方法及其应用，其特征在于：所述的步骤2）中，丝素烘干温度为37℃。
5.根据权利要求1中所述的丝素水基润滑液的制备方法及其应用，其特征在于：所述的步骤3）中的超声分散的设备的超生频率为70Hz～100Hz。
6.一种如权利要求1～5中任一项所述的丝素水基润滑液的制备方法制备的丝素水基润滑液，其特征在于，它的组份以及各组份重量份如下：
丝素：1份～2份；
去离子水：98份～99份。