CN104861451A - 一种用于ptt聚酯的环保阻燃母粒及其制备方法 - Google Patents
一种用于ptt聚酯的环保阻燃母粒及其制备方法 Download PDFInfo
- Publication number
- CN104861451A CN104861451A CN201410531956.4A CN201410531956A CN104861451A CN 104861451 A CN104861451 A CN 104861451A CN 201410531956 A CN201410531956 A CN 201410531956A CN 104861451 A CN104861451 A CN 104861451A
- Authority
- CN
- China
- Prior art keywords
- master batch
- environmental protection
- protection flame
- ptt
- flame retardant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种用于PTT聚酯的环保阻燃母粒及其制备方法。本发明的一种用于PTT聚酯的环保阻燃母粒,其组分按质量百分数配比为:PTT树脂20%~50%、阻燃剂20%~40%、纳米蒙脱土5%~30%、增容剂5%~15%、热稳定剂2%~8%、抑烟剂1%~5%、抗氧剂0.1%~1%、分散剂0.5%~3%。本发明的有益效果是,本发明具有环保、无污染、高浓度、高分散、低成本和使用方便等特点,在生产PTT聚酯添加10%~30%质量分数时,将具有良好的无卤、抑烟、环保阻燃的改性效果,而且还明显提高了材料的力学性能、加工性能和耐热性能等,同时降低了成本,提高了生产效率,有助于工业化生产与应用。
Description
技术领域
本发明涉及高分子材料技术领域,具体地说是一种用于PTT聚酯的环保阻燃母粒及其制备方法。
背景技术
聚对苯二甲酸丙二醇酯(简称PTT聚酯)是由对苯二甲酸和1,3-丙二醇缩聚而制得的一种极具发展前途的新型聚酯高分子材料。PTT聚酯属于一种具有较高的熔融温度和玻璃化温度的半结晶性高聚物,具有良好的耐磨性、耐热性和耐化学药品性,广泛应用于合成纤维、薄膜和工程塑料等领域。然而,PTT聚酯自身不能阻燃,其阻燃性差(极限氧指数约为21%),这将大大限制其在有些领域中的应用。
发明内容
本发明的目的在于提供一种浓度高、阻燃性好和使用方便的用于PTT聚酯的环保阻燃母粒及其制备方法。
本发明解决其技术问题所采用的技术方案是:一种用于PTT聚酯的环保阻燃母粒,其组分按质量百分数配比为:PTT树脂20%~50%、阻燃剂20%~40%、纳米蒙脱土5%~30%、增容剂5%~15%、热稳定剂2%~8%、抑烟剂1%~5%、抗氧剂0.1%~1%、分散剂0.5%~3%。
所述PTT树脂为聚对苯二甲酸丙二醇酯。
所述阻燃剂为聚苯基膦酸二苯砜酯、双酚A-双(二苯基磷酸酯)、聚甲基苯基硅氧烷、微胶囊红磷中的一种或几种。
所述增容剂为甲基丙烯酸酯-丙烯酸酯共聚物、甲基丙烯酸甲酯-丁二烯-苯乙烯三元接枝共聚物、马来酸酐接枝乙烯-辛烯共聚物、乙烯-丙烯酸甲酯-甲基丙烯酸缩水甘油酯中的一种。
所述热稳定剂为硬脂酸钡。
所述抑烟剂为表面经过活化改性处理的纳米二氧化硅、纳米氧化锌、钠米二氧化钛、纳米氧化钙中的一种。
所述抗氧剂为抗氧剂1010、抗氧剂1076、抗氧剂1010或抗氧剂1076与抗氧剂168的复配物中的一种。
所述分散剂为硬脂酸钙、硬脂酸锌、白油、超细TAS-2A粉、乙撑双硬脂酰胺、季戊四醇硬脂酸酯中的一种。
上述的一种用于PTT聚酯的环保阻燃母粒的制备方法为:按重量配比称取各组分,并分别加入料筒温度在80℃~120℃、转速不低于3000r/min的高速混合器中,使一起搅拌3~15分钟,待混合均匀后出料加入双螺杆挤出机中,于210℃~260℃温度下经过熔融混炼后挤出造粒,然后进行干燥、包装,即得本发明。
本发明的有益效果是,本发明具有环保、无污染、高浓度、高分散、低成本和使用方便等特点,在生产PTT聚酯添加10%~30%质量分数时,将具有良好的无卤、抑烟、环保阻燃的改性效果,而且还明显提高了材料的力学性能、加工性能和耐热性能等,同时降低了成本,提高了生产效率,有助于工业化生产与应用。
具体实施方式
下面结合具体的优选实施例来进一步说明本发明的技术方案。
实施例1:
一种用于PTT聚酯的环保阻燃母粒,其组分按质量百分数配比为:PTT树脂30%、聚苯基膦酸二苯砜酯30%、纳米蒙脱土20%、甲基丙烯酸酯-丙烯酸酯共聚物10%、硬脂酸钡5%、表面经过活化改性处理的纳米二氧化硅2.5%、抗氧剂1010 0.5%、白油2%。
制备方法:按重量配比称取各组分,并分别加入料筒温度在80℃~120℃、转速不低于3000r/min的高速混合器中,使一起搅拌3~15分钟,待混合均匀后出料加入双螺杆挤出机中,于210℃~260℃温度下经过熔融混炼后挤出造粒,然后进行干燥、包装,即得本发明的一种用于PTT聚酯的环保阻燃母粒。
实施例2:
一种用于PTT聚酯的环保阻燃母粒,其组分按质量百分数配比为:PTT树脂26%、双酚A-双(二苯基磷酸酯)40%、纳米蒙脱土15%、基丙烯酸甲酯-丁二烯-苯乙烯三元接枝共聚物8%、硬脂酸钡4%、表面经过活化改性处理的钠米二氧化钛4%、抗氧剂1076与抗氧剂168的复配物0.5%、超细TAS-2A粉2.5%。
制备方法:按重量配比称取各组分,并分别加入料筒温度在80℃~120℃、转速不低于3000r/min的高速混合器中,使一起搅拌3~15分钟,待混合均匀后出料加入双螺杆挤出机中,于210℃~260℃温度下经过熔融混炼后挤出造粒,然后进行干燥、包装,即得本发明的一种用于PTT聚酯的环保阻燃母粒。
Claims (6)
1.一种用于PTT聚酯的环保阻燃母粒,其特征在于,其组分按质量百分数配比为:PTT树脂20%~50%、阻燃剂20%~40%、纳米蒙脱土5%~30%、增容剂5%~15%、热稳定剂2%~8%、抑烟剂1%~5%、抗氧剂0.1%~1%、分散剂0.5%~3%。
2.根据权利要求1所述的一种用于PTT聚酯的环保阻燃母粒,其特征在于,所述阻燃剂为聚苯基膦酸二苯砜酯、双酚A-双(二苯基磷酸酯)、聚甲基苯基硅氧烷、微胶囊红磷中的一种或几种。
3.根据权利要求1所述的一种用于PTT聚酯的环保阻燃母粒,其特征在于,所述增容剂为甲基丙烯酸酯-丙烯酸酯共聚物、甲基丙烯酸甲酯-丁二烯-苯乙烯三元接枝共聚物、马来酸酐接枝乙烯-辛烯共聚物、乙烯-丙烯酸甲酯-甲基丙烯酸缩水甘油酯中的一种。
4.根据权利要求1所述的一种用于PTT聚酯的环保阻燃母粒,其特征在于,所述热稳定剂为硬脂酸钡。
5.根据权利要求1所述的一种用于PTT聚酯的环保阻燃母粒,其特征在于,所述抑烟剂为表面经过活化改性处理的纳米二氧化硅、纳米氧化锌、钠米二氧化钛、纳米氧化钙中的一种。
6.根据权利要求1所述的一种用于PTT聚酯的环保阻燃母粒的制备方法,其特征在于,包括以下步骤:按重量配比称取各组分,并分别加入料筒温度在80℃~120℃、转速不低于3000r/min的高速混合器中,使一起搅拌3~15分钟,待混合均匀后出料加入双螺杆挤出机中,于210℃~260℃温度下经过熔融混炼后挤出造粒,然后进行干燥、包装,即得本发明。