CN104845078A - 一种耐热增强改性pbt粉末及其制备方法 - Google Patents
一种耐热增强改性pbt粉末及其制备方法 Download PDFInfo
- Publication number
- CN104845078A CN104845078A CN201410592060.7A CN201410592060A CN104845078A CN 104845078 A CN104845078 A CN 104845078A CN 201410592060 A CN201410592060 A CN 201410592060A CN 104845078 A CN104845078 A CN 104845078A
- Authority
- CN
- China
- Prior art keywords
- heat
- powder
- modified pbt
- pbt
- resisting
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种耐热增强改性PBT粉末及其制备方法。本发明的一种耐热增强改性PBT粉末,其组分按质量百分数配比为:PBT60%~80%、玻璃纤维5%~15%、滑石粉2%~10%、阻燃剂8%~15%、TPU3%~8%、铝钛复合偶联剂0.1%~0.3%、季戊四醇硬脂酸酯0.1%~1%、耐热稳定剂0.1%~1%、抗氧剂0.1%~0.5%,所述耐热稳定剂为N,N-4,4-二苯甲烷双马来酰亚胺。本发明的有益效果是,本发明具有高耐热性、高阻燃性、良好力学性能和优异电性能等特点,而且加工性能好,耐化学药品性强,性能稳定,外观质量好,成本低,可适于电子电器、化工机械等的应用领域。
Description
技术领域
本发明涉及高分子材料技术领域,具体地说是一种耐热增强改性PBT粉末及其制备方法。
背景技术
聚对苯二甲酸丁二醇酯(简称PBT)是一种结晶型热塑性聚酯,由于其具有优异的电性能及耐腐蚀性能,目前已被广泛应用于电子电器、化工、机械等领域。但PBT单独使用存在强度低、耐热性不足、阻燃性差等缺点,对其应用受到一定的限制。
发明内容
本发明的目的在于提供一种耐热增强改性PBT粉末及其制备方法。
本发明解决其技术问题所采用的技术方案是:一种耐热增强改性PBT粉末,其组分按质量百分数配比为:PBT 60%~80%、玻璃纤维5%~15%、滑石粉2%~10%、阻燃剂8%~15%、TPU 3%~8%、铝钛复合偶联剂0.1%~0.3%、季戊四醇硬脂酸酯0.1%~1%、耐热稳定剂0.1%~1%、抗氧剂0.1%~0.5%。
所述PBT为聚对苯二甲酸丁二醇酯树脂。
所述玻璃纤维为表面经过硅烷偶联剂KH550处理后的无碱短切玻璃纤维。
所述阻燃剂为质量比1:4的聚二甲基硅氧烷与双酚A-双(二苯基磷酸酯)的复配物。
所述TPU为热塑性聚氨酯。
所述耐热稳定剂为N,N-4,4-二苯甲烷双马来酰亚胺。
所述抗氧剂为质量比1:1的抗氧剂1076与抗氧剂168的复配物。
本发明的一种耐热增强改性PBT粉末的制备方法,包括以下步骤:
(1)、将PBT于120℃~140℃下干燥4~6小时,阻燃剂于80℃~85℃下干燥30~45分钟,待用;
(2)、按质量百分数配比称取滑石粉和铝钛复合偶联剂,加入高速混合器中,在100℃~120℃温度下搅拌30~45分钟,使完全分散和包覆后,冷却至低于40℃出料,待用;
(3)、按质量百分数配比称取步骤(1)得到干燥的PBT和阻燃剂,加入高速混合器中,同时加入按质量百分数配比称取的玻璃纤维、TPU、季戊四醇硬脂酸酯、耐热稳定剂、抗氧剂以及步骤(2)得到的物料,使一起搅拌3~15分钟,待充分混合均匀后,出料;
(4)、将步骤(3)得到的混合料加入双螺杆挤出机熔融挤出,并经过冷却、造粒、干燥后,再由塑料粉碎机碎成细粉并过筛,选取150~220目的组成,即得到本发明。
本发明的有益效果是,本发明具有高耐热性、高阻燃性、良好力学性能和优异电性能等特点,而且加工性能好,耐化学药品性强,性能稳定,外观质量好,成本低,可适于电子电器、化工机械等的应用领域。
具体实施方式
下面结合具体实施例来进一步说明本发明的技术方案。
一种耐热增强改性PBT粉末,其组分按质量百分数配比为:PBT 68%、玻璃纤维10%、滑石粉5%、阻燃剂10%、TPU 5%、铝钛复合偶联剂0.2%、季戊四醇硬脂酸酯1%、N,N-4,4-二苯甲烷双马来酰亚胺0.6%、抗氧剂0.2%。其中,所述PBT为聚对苯二甲酸丁二醇酯树脂;所述玻璃纤维为表面经过硅烷偶联剂KH550处理后的无碱短切玻璃纤维;所述阻燃剂为质量比1:4的聚二甲基硅氧烷与双酚A-双(二苯基磷酸酯)的复配物;所述抗氧剂为质量比1:1的抗氧剂1076与抗氧剂168的复配物。
其制备方法为:(1)、将PBT于120℃~140℃下干燥4~6小时,阻燃剂于80℃~85℃下干燥30~45分钟,待用;(2)、按质量百分数配比称取滑石粉和铝钛复合偶联剂,加入高速混合器中,在100℃~120℃温度下搅拌30~45分钟,使完全分散和包覆后,冷却至低于40℃出料,待用;(3)、按质量百分数配比称取步骤(1)得到干燥的PBT和阻燃剂,加入高速混合器中,同时加入按质量百分数配比称取的玻璃纤维、TPU、季戊四醇硬脂酸酯、N,N-4,4-二苯甲烷双马来酰亚胺、抗氧剂以及步骤(2)得到的物料,使一起搅拌3~15分钟,待充分混合均匀后,出料;(4)、将步骤(3)得到的混合料加入双螺杆挤出机熔融挤出,并经过冷却、造粒、干燥后,再由塑料粉碎机碎成细粉并过筛,选取150~220目的组成,即得到本发明。
Claims (6)
1.一种耐热增强改性PBT粉末,其特征在于,其组分按质量百分数配比为:PBT 60%~80%、玻璃纤维5%~15%、滑石粉2%~10%、阻燃剂8%~15%、TPU 3%~8%、铝钛复合偶联剂0.1%~0.3%、季戊四醇硬脂酸酯0.1%~1%、耐热稳定剂0.1%~1%、抗氧剂0.1%~0.5%。
2.根据权利要求1所述的一种耐热增强改性PBT粉末,其特征在于,所述玻璃纤维为表面经过硅烷偶联剂KH550处理后的无碱短切玻璃纤维。
3.根据权利要求1所述的一种耐热增强改性PBT粉末,其特征在于,所述阻燃剂为质量比1:4的聚二甲基硅氧烷与双酚A-双(二苯基磷酸酯)的复配物。
4.根据权利要求1所述的一种耐热增强改性PBT粉末,其特征在于,所述耐热稳定剂为N,N-4,4-二苯甲烷双马来酰亚胺。
5.根据权利要求1所述的一种耐热增强改性PBT粉末,其特征在于,所述抗氧剂为质量比1:1的抗氧剂1076与抗氧剂168的复配物。
6.根据权利要求1所述的一种耐热增强改性PBT粉末的制备方法,其特征在于,包括以下步骤:
(1)、将PBT于120℃~140℃下干燥4~6小时,阻燃剂于80℃~85℃下干燥30~45分钟,待用;
(2)、按质量百分数配比称取滑石粉和铝钛复合偶联剂,加入高速混合器中,在100℃~120℃温度下搅拌30~45分钟,使完全分散和包覆后,冷却至低于40℃出料,待用;
(3)、按质量百分数配比称取步骤(1)得到干燥的PBT和阻燃剂,加入高速混合器中,同时加入按质量百分数配比称取的玻璃纤维、TPU、季戊四醇硬脂酸酯、耐热稳定剂、抗氧剂以及步骤(2)得到的物料,使一起搅拌3~15分钟,待充分混合均匀后,出料;
(4)、将步骤(3)得到的混合料加入双螺杆挤出机熔融挤出,并经过冷却、造粒、干燥后,再由塑料粉碎机碎成细粉并过筛,选取150~220目的组成,即得到本发明。