CN104844165A - 一种耐腐蚀陶瓷眼 - Google Patents

一种耐腐蚀陶瓷眼 Download PDF

Info

Publication number
CN104844165A
CN104844165A CN201510200431.7A CN201510200431A CN104844165A CN 104844165 A CN104844165 A CN 104844165A CN 201510200431 A CN201510200431 A CN 201510200431A CN 104844165 A CN104844165 A CN 104844165A
Authority
CN
China
Prior art keywords
aluminum oxide
resistant ceramic
corrosion
silicon carbide
acetone
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510200431.7A
Other languages
English (en)
Inventor
刘勇
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ANHUI HANSHAN SHUNTAIN TEXTILE Co Ltd
Original Assignee
ANHUI HANSHAN SHUNTAIN TEXTILE Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ANHUI HANSHAN SHUNTAIN TEXTILE Co Ltd filed Critical ANHUI HANSHAN SHUNTAIN TEXTILE Co Ltd
Priority to CN201510200431.7A priority Critical patent/CN104844165A/zh
Publication of CN104844165A publication Critical patent/CN104844165A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种耐腐蚀陶瓷眼，其是由下述重量份的原料制得：氧化铝50-60、花生油0.5-1、碳化硅1-3、胶粉0.1-0.3，纳米TiC2-4、氧化铜1-3、邻苯二甲酸二辛酯0.1-0.3、硫酸钡3-5、电熔镁砂1-2、环己酮0.3-0.4、乙撑基双硬脂酰胺0.3-0.5、丙酮0.5-0.9，硅酸锆2-4、羟乙基纤维素HEC 0.3-0.5,月桂醇聚氧乙烯醚1-2，去离子水8-12。

Description

一种耐腐蚀陶瓷眼
技术领域
本发明涉及纺织用陶瓷领域，确切地说是一种耐腐蚀陶瓷眼。
背景技术
     陶瓷眼适用于各种绕线机及纺织机械中的过线过丝部件,由精密陶瓷加工，由于硬度较高，表面光滑，漆包线在其表面滑动时顺畅不受损伤。
发明内容
本发明的目的在于提供一种耐腐蚀陶瓷眼。
上述目的通过以下方案实现：
 一种耐腐蚀陶瓷眼，其特征在于：其是由下述重量份的原料制得：氧化铝50-60、花生油0.5-1、碳化硅1-3、胶粉0.1-0.3，纳米TiC2-4、氧化铜1-3、邻苯二甲酸二辛酯0.1-0.3、硫酸钡3-5、电熔镁砂1-2、环己酮0.3-0.4、乙撑基双硬脂酰胺0.3-0.5、丙酮0.5-0.9，硅酸锆2-4、羟乙基纤维素HEC 0.3-0.5,月桂醇聚氧乙烯醚1-2，去离子水8-12。
所述的一种耐腐蚀陶瓷眼，其特征在于：制备方法为：
（1）羟乙基纤维素HEC 、月桂醇聚氧乙烯醚、去离子水于40-50℃下搅拌均匀后，再加入碳化硅，于65-70℃下搅拌均匀后，得复配料备用；
（2）将氧化铝加入所得复配料中，于58-65℃下搅拌均匀，再静置30-50min，过滤，于65-75℃烘干后，300-400℃煅烧8-15min，得包覆氧化铝备用；
（3）硫酸钡、电熔镁砂、硅酸锆混匀后，加入环己酮、乙撑基双硬脂酰胺、丙酮，球磨5-8小时，再加入邻苯二甲酸二辛酯球磨2-5小时，取出，干燥，后与包覆氧化铝以及其余原料混匀，加适量水制得浆料;
(4)所得浆料在100-120 ℃干燥3-4 h，粉碎后过100-200目筛，成型，再在580-600 ℃保温3-6小时排胶；最后烧结，随炉冷却，即得。
本发明的有益效果为：
本发明所得的陶瓷材料所采用的配方组分合理调和，制成的陶瓷眼性能优良，稳定性好，耐高温和耐腐蚀，应用在纺织工业上，使用寿命长；同时本发明通过特殊的复配包膜液，使得碳化硅均匀的包覆在氧化铝表层，增加陶瓷眼的耐磨性和耐腐蚀性，从而增加使用寿命。
具体实施方式
一种耐腐蚀陶瓷眼，其是由下述重量（kg）的原料制得：氧化铝60、花生油0.5、碳化硅3、胶粉0.3，纳米TiC  2.4、氧化铜1.3、邻苯二甲酸二辛酯0.3、硫酸钡3、电熔镁砂1、环己酮0.4、乙撑基双硬脂酰胺0.5、丙酮0.9，硅酸锆2、羟乙基纤维素HEC 0.3,月桂醇聚氧乙烯醚1，去离子水12。
所述的一种耐腐蚀陶瓷眼，制备方法为：
（1）羟乙基纤维素HEC 、月桂醇聚氧乙烯醚、去离子水于43℃下搅拌均匀后，再加入碳化硅，于65℃下搅拌均匀后，得复配料备用；
（2）将氧化铝加入所得复配料中，于65℃下搅拌均匀，再静置50min，过滤，于68℃烘干后，300℃煅烧15min，得包覆氧化铝备用；
（3）硫酸钡、电熔镁砂、硅酸锆混匀后，加入环己酮、乙撑基双硬脂酰胺、丙酮，球磨8小时，再加入邻苯二甲酸二辛酯球磨5小时，取出，干燥，后与包覆氧化铝以及其余原料混匀，加适量水制得浆料;
(4)所得浆料在120 ℃干燥4 h，粉碎后过200目筛，成型，再在600 ℃保温6小时排胶；最后烧结，随炉冷却，即得。
所得陶瓷眼的参数如下：
莫氏硬度 7、导热系数（w/m.K） 33、常温耐压强度(MPa)≥680、常温抗折强度(MPa)≥700、耐火度 （℃）≥2000、最高使用温度(℃)≥1600。

Claims (2)

1.一种耐腐蚀陶瓷眼，其特征在于：其是由下述重量份的原料制得：氧化铝50-60、花生油0.5-1、碳化硅1-3、胶粉0.1-0.3，纳米TiC2-4、氧化铜1-3、邻苯二甲酸二辛酯0.1-0.3、硫酸钡3-5、电熔镁砂1-2、环己酮0.3-0.4、乙撑基双硬脂酰胺0.3-0.5、丙酮0.5-0.9，硅酸锆2-4、羟乙基纤维素HEC 0.3-0.5,月桂醇聚氧乙烯醚1-2，去离子水8-12。
2.根据权利要求1所述的一种耐腐蚀陶瓷眼，其特征在于：制备方法为：
（1）羟乙基纤维素HEC 、月桂醇聚氧乙烯醚、去离子水于40-50℃下搅拌均匀后，再加入碳化硅，于65-70℃下搅拌均匀后，得复配料备用；
（2）将氧化铝加入所得复配料中，于58-65℃下搅拌均匀，再静置30-50min，过滤，于65-75℃烘干后，300-400℃煅烧8-15min，得包覆氧化铝备用；
（3）硫酸钡、电熔镁砂、硅酸锆混匀后，加入环己酮、乙撑基双硬脂酰胺、丙酮，球磨5-8小时，再加入邻苯二甲酸二辛酯球磨2-5小时，取出，干燥，后与包覆氧化铝以及其余原料混匀，加适量水制得浆料;
(4)所得浆料在100-120 ℃干燥3-4 h，粉碎后过100-200目筛，成型，再在580-600 ℃保温3-6小时排胶；最后烧结，随炉冷却，即得。
CN201510200431.7A 2015-04-27 2015-04-27 一种耐腐蚀陶瓷眼 Pending CN104844165A (zh)