CN104844166A - 一种耐高温陶瓷眼 - Google Patents

一种耐高温陶瓷眼 Download PDF

Info

Publication number
CN104844166A
CN104844166A CN201510200432.1A CN201510200432A CN104844166A CN 104844166 A CN104844166 A CN 104844166A CN 201510200432 A CN201510200432 A CN 201510200432A CN 104844166 A CN104844166 A CN 104844166A
Authority
CN
China
Prior art keywords
silicon carbide
add
aluminum oxide
acetone
hour
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510200432.1A
Other languages
English (en)
Inventor
刘勇
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ANHUI HANSHAN SHUNTAIN TEXTILE Co Ltd
Original Assignee
ANHUI HANSHAN SHUNTAIN TEXTILE Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ANHUI HANSHAN SHUNTAIN TEXTILE Co Ltd filed Critical ANHUI HANSHAN SHUNTAIN TEXTILE Co Ltd
Priority to CN201510200432.1A priority Critical patent/CN104844166A/zh
Publication of CN104844166A publication Critical patent/CN104844166A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种耐高温陶瓷眼，其是由下述重量份的原料制得：氧化铝50-60、氧化锆粉末10-15，有釉废陶瓷熟砂1-2、碳化硅2-4、硼氢化钠0.5-0.9、碳化硅晶须2-4、二氧化硅2-4、陶土5-10、纤维素1-3、三聚磷酸钠0.2-0.4、环己酮0.2-0.4、氯化石蜡0.1-0.3、乙撑基双硬脂酰胺0.5-0.7、丙酮5-8、正硅酸乙酯1-2、乙醇1-2、聚乙二醇1-2、硝酸铝0.3-0.5、去离子水6-12。

Description

一种耐高温陶瓷眼
技术领域
本发明涉及纺织用陶瓷领域，确切地说是一种耐高温陶瓷眼。
背景技术
     陶瓷眼适用于各种绕线机及纺织机械中的过线过丝部件,由精密陶瓷加工，由于硬度较高，表面光滑，漆包线在其表面滑动时顺畅不受损伤。
发明内容
本发明的目的在于提供一种耐高温陶瓷眼。
上述目的通过以下方案实现：
 一种耐高温陶瓷眼，其特征在于：其是由下述重量份的原料制得：氧化铝50-60、氧化锆粉末10-15，有釉废陶瓷熟砂1-2、碳化硅2-4、硼氢化钠0.5-0.9、碳化硅晶须2-4、二氧化硅2-4、陶土5-10、纤维素1-3、三聚磷酸钠0.2-0.4、环己酮0.2-0.4、氯化石蜡0.1-0.3、乙撑基双硬脂酰胺0.5-0.7、丙酮5-8、正硅酸乙酯1-2、乙醇1-2、聚乙二醇1-2、硝酸铝0.3-0.5、去离子水6-12。
所述的一种耐高温陶瓷眼，其特征在于：制备方法为：
（1）正硅酸乙酯、乙醇、硝酸铝于50-60℃下搅拌均匀后，再加入聚乙二醇、去离子水，于65-70℃下搅拌均匀后，调节PH为3.5-4，再加入碳化硅，于60-70℃下40-50转/分搅拌40-60min，得复配料备用；
（2）将氧化铝加入所得复配料中，于60-70℃下搅拌均匀，再静置30-50min，过滤，于65-80℃烘干后，400-500℃煅烧3-5min，得包覆氧化铝备用；
（3）氧化锆粉末、有釉废陶瓷熟砂混匀后，加入环己酮、乙撑基双硬脂酰胺、丙酮，球磨5-8小时，再加入氯化石蜡球磨2-5小时，取出，干燥，后与包覆氧化铝以及其余原料混匀，加适量水制得浆料;
(4)所得浆料在100-120 ℃干燥3-4 h，粉碎后过80-100目筛，成型，再在580-600 ℃保温1-2小时排胶；最后烧结，随炉冷却，即得。
本发明的有益效果为：本发明综上所述，通过在陶瓷粉料中加入适量的氧化锆粉末，硼氢化钠等，能是的陶瓷眼的性能更稳定，强度高，不易变形，耐高温性能优异；同时本发明通过特殊的复配包膜液，使得碳化硅均匀的包覆在氧化铝表层，增加陶瓷眼的耐磨性和耐腐蚀性，从而增加使用寿命。
具体实施方式
一种耐高温陶瓷眼，其是由下述重量（kg）的原料制得：氧化铝60、氧化锆粉末10，有釉废陶瓷熟砂1、碳化硅2、硼氢化钠0.5、碳化硅晶须2、二氧化硅2、陶土10、纤维素1、三聚磷酸钠0.2、环己酮0.4、氯化石蜡0.1、乙撑基双硬脂酰胺0.5、丙酮5、正硅酸乙酯2、乙醇1、聚乙二醇1、硝酸铝0.5、去离子水12。
所述的一种耐高温陶瓷眼，制备方法为：
（1）正硅酸乙酯、乙醇、硝酸铝于60℃下搅拌均匀后，再加入聚乙二醇、去离子水，于65℃下搅拌均匀后，调节PH为4，再加入碳化硅，于60℃下50转/分搅拌40min，得复配料备用；
（2）将氧化铝加入所得复配料中，于70℃下搅拌均匀，再静置50min，过滤，于70℃烘干后， 500℃煅烧5min，得包覆氧化铝备用；
（3）氧化锆粉末、有釉废陶瓷熟砂混匀后，加入环己酮、乙撑基双硬脂酰胺、丙酮，球磨8小时，再加入氯化石蜡球磨5小时，取出，干燥，后与包覆氧化铝以及其余原料混匀，加适量水制得浆料;
(4)所得浆料在120 ℃干燥4 h，粉碎后过100目筛，成型，再在600 ℃保温1小时排胶；最后烧结，随炉冷却，即得。
所得陶瓷眼的参数如下：
莫氏硬度 9、导热系数（w/m.K） 31、常温耐压强度(MPa)≥690、常温抗折强度(MPa)≥720、耐火度 （℃）≥2000、最高使用温度(℃)≥1700。

Claims (2)

1.一种耐高温陶瓷眼，其特征在于：其是由下述重量份的原料制得：氧化铝50-60、氧化锆粉末10-15，有釉废陶瓷熟砂1-2、碳化硅2-4、硼氢化钠0.5-0.9、碳化硅晶须2-4、二氧化硅2-4、陶土5-10、纤维素1-3、三聚磷酸钠0.2-0.4、环己酮0.2-0.4、氯化石蜡0.1-0.3、乙撑基双硬脂酰胺0.5-0.7、丙酮5-8、正硅酸乙酯1-2、乙醇1-2、聚乙二醇1-2、硝酸铝0.3-0.5、去离子水6-12。
2.根据权利要求1所述的一种耐高温陶瓷眼，其特征在于：制备方法为：
（1）正硅酸乙酯、乙醇、硝酸铝于50-60℃下搅拌均匀后，再加入聚乙二醇、去离子水，于65-70℃下搅拌均匀后，调节PH为3.5-4，再加入碳化硅，于60-70℃下40-50转/分搅拌40-60min，得复配料备用；
（2）将氧化铝加入所得复配料中，于60-70℃下搅拌均匀，再静置30-50min，过滤，于65-80℃烘干后，400-500℃煅烧3-5min，得包覆氧化铝备用；
（3）氧化锆粉末、有釉废陶瓷熟砂混匀后，加入环己酮、乙撑基双硬脂酰胺、丙酮，球磨5-8小时，再加入氯化石蜡球磨2-5小时，取出，干燥，后与包覆氧化铝以及其余原料混匀，加适量水制得浆料;
(4)所得浆料在100-120 ℃干燥3-4 h，粉碎后过80-100目筛，成型，再在580-600 ℃保温1-2小时排胶；最后烧结，随炉冷却，即得。
CN201510200432.1A 2015-04-27 2015-04-27 一种耐高温陶瓷眼 Pending CN104844166A (zh)