CN104841863A - 一种新型易溃散覆膜砂及其制备方法 - Google Patents

一种新型易溃散覆膜砂及其制备方法 Download PDF

Info

Publication number
CN104841863A
CN104841863A CN201510229081.7A CN201510229081A CN104841863A CN 104841863 A CN104841863 A CN 104841863A CN 201510229081 A CN201510229081 A CN 201510229081A CN 104841863 A CN104841863 A CN 104841863A
Authority
CN
China
Prior art keywords
parts
sand
add
mixed
precoated sand
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510229081.7A
Other languages
English (en)
Inventor
章功国
王泾文
段宗银
李纯金
陈超
王淑妍
张少伍
王晓芬
谢勇
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Maanshan Hengyi Machinery Manufacturing Co Ltd
Original Assignee
Maanshan Hengyi Machinery Manufacturing Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Maanshan Hengyi Machinery Manufacturing Co Ltd filed Critical Maanshan Hengyi Machinery Manufacturing Co Ltd
Priority to CN201510229081.7A priority Critical patent/CN104841863A/zh
Publication of CN104841863A publication Critical patent/CN104841863A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种新型易溃散覆膜砂，其特征在于，由下列重量份的原料制成：热塑性酚醛树脂4-6、聚甲醛1-2、交联剂TAC 1-1.5、水2.5-3、乌洛托品0.8-1.2、石英砂80-90、二硫化钼3-5、硅藻土8-11、过氧化钙0.4-0.7、硬脂酸钙0.25-0.35、增效剂5-7；本发明添加特殊工艺制成的增效剂，增强了覆膜砂的流动性、透气性、散热性以及强度，表面致密不易开裂变形；还添加了二硫化钼、硅藻土等增加流动性、透气性的成分，过氧化钙等溃散成分，聚甲醛与热塑性酚醛树脂混合增加产品的强度，制成的覆膜砂耐高温、易溃散、不易粘砂、壳型不起层、导热性好、流动性好、铸件表面平整。

Description

一种新型易溃散覆膜砂及其制备方法
技术领域
本发明涉及型砂技术领域，特别是一种新型易溃散覆膜砂及其制备方法。
背景技术
覆膜砂是指造型前在砂粒表面上覆有一层固体树脂膜的型砂或芯砂。近年来广泛使用的是热法用覆膜砂的生产工艺，即把砂预热到一定温度，加树脂使其熔融，搅拌使树脂包覆在砂粒表面，加乌洛托品水溶液及润滑剂，冷却、破碎、筛分得覆膜砂。由于覆膜砂具有强度高、发气量低、生产铸件尺寸精度高、表面光洁、便于保存等优点，近年来应用日益广泛。现有技术中的覆膜砂存在着耐热性较差，粗糙度较大，易在铸件上粘砂，溃散性较差，落砂清理异常困难，增加了劳动强度。因此，必须改善现有覆膜砂的性能，使其满足生产需求。针对各种铸件缺陷生产的覆膜砂，当前根据铸件材质的要求也越来越高，开发的新铸件材质标准也越来越多。
现有很多关于改性覆膜砂的发明，但是本发明通过研究，添加一种增效剂对普通覆膜砂进行改性，该增效剂内含透气良好的玉米秸秆、陶土，散热快的石墨烯等成分，通过特殊工艺制成，增强了覆膜砂的流动性、透气性、散热性以及强度，表面致密不易开裂变形。本发明在配方中还添加了二硫化钼、硅藻土等增加流动性、透气性的成分，过氧化钙等溃散成分，聚甲醛与热塑性酚醛树脂混合增加产品的强度，制成的覆膜砂耐高温、易溃散、不易粘砂。
发明内容
本发明的目的是提供一种新型易溃散覆膜砂及其制备方法。
为了实现本发明的目的，本发明通过以下方案实施：
一种新型易溃散覆膜砂，由下列重量份的原料制成：热塑性酚醛树脂4-6、聚甲醛1-2、交联剂TAC 1-1.5、水2.5-3、乌洛托品0.8-1.2、石英砂80-90、二硫化钼3-5、硅藻土8-11、过氧化钙0.4-0.7、硬脂酸钙0.25-0.35、增效剂5-7；
所述增效剂由以下重量份的原料制备而成：玉米秸秆4-6、淀粉2-3、水玻璃3-5、氢氧化钙1.5-2.5、氯化镁1-2、石墨烯4-5、陶土20-25、锆英粉9-11、邻苯二甲酸二丁酯3-4、水9-12；制备方法如下：将玉米秸秆干燥后粉碎成80-100目的粉末与陶土、淀粉混合搅拌均匀，加入水搅拌均匀，控温在60℃-80℃，保持1-1.5小时，然后加入除水玻璃、邻苯二甲酸二丁酯之外的其余剩余成分，混合20-30分钟，再加入水玻璃、邻苯二甲酸二丁酯，放入混砂机中湿混20-30秒，出砂后烘干，最后粉碎成200-250目即得。
本发明所述一种新型易溃散覆膜砂，其特征在于，由以下具体步骤制成：
（1）将石英砂、二硫化钼、硅藻土放入粉碎机中粉碎，过200-300目筛形成混合砂，然后将沸腾炉加热至160℃，开动沸腾炉内风机，缓慢加入混合砂，将混合砂的温度加热到140℃-150℃；
（2）将加热后的混合砂放到混砂机内，保持160℃恒温，在混碾的同时加入聚甲醛、交联剂TAC与0.6倍量的热塑性酚醛树脂，继续混碾70-80秒后再加入剩余量的热塑性酚醛树脂；
（3）将乌洛托品溶于水形成溶液，然后将溶液的70%缓慢加入到混砂机中，继续热态下混碾75-85秒后，再加入剩余量的溶液，继续混碾10-20秒；
（4）关闭混砂机加热管，吹入冷风冷却混合砂，降温至100℃左右时均匀地加入其余剩余成分，混和30-35秒，然后出砂到破碎机中，风冷至40℃-60℃时破碎，过筛至冷却器中，风冷到35℃以下，出砂装袋备用。
本发明的优异效果是：本发明添加特殊工艺制成的增效剂，增强了覆膜砂的流动性、透气性、散热性以及强度，表面致密不易开裂变形；还添加了二硫化钼、硅藻土等增加流动性、透气性的成分，过氧化钙等溃散成分，聚甲醛与热塑性酚醛树脂混合增加产品的强度，制成的覆膜砂耐高温、易溃散、不易粘砂、壳型不起层、导热性好、流动性好、铸件表面平整。
具体实施方式
下面通过具体实例对本发明进行详细说明。
一种新型易溃散覆膜砂，由下列重量份（公斤）的原料制成：热塑性酚醛树脂4、聚甲醛1、交联剂TAC 1、水2.5、乌洛托品0.8、石英砂80、二硫化钼3、硅藻土8、过氧化钙0.4、硬脂酸钙0.25、增效剂5；
所述增效剂由以下重量份（公斤）的原料制备而成：玉米秸秆4、淀粉2、水玻璃3、氢氧化钙1.5、氯化镁1、石墨烯4、陶土20、锆英粉9、邻苯二甲酸二丁酯3、水9；制备方法如下：将玉米秸秆干燥后粉碎成100目的粉末与陶土、淀粉混合搅拌均匀，加入水搅拌均匀，控温在60℃-80℃，保持1小时，然后加入除水玻璃、邻苯二甲酸二丁酯之外的其余剩余成分，混合20分钟，再加入水玻璃、邻苯二甲酸二丁酯，放入混砂机中湿混20秒，出砂后烘干，最后粉碎成200目即得。
本发明所述一种新型易溃散覆膜砂，其特征在于，由以下具体步骤制成：
（1）将石英砂、二硫化钼、硅藻土放入粉碎机中粉碎，过200目筛形成混合砂，然后将沸腾炉加热至160℃，开动沸腾炉内风机，缓慢加入混合砂，将混合砂的温度加热到140℃-150℃；
（2）将加热后的混合砂放到混砂机内，保持160℃恒温，在混碾的同时加入聚甲醛、交联剂TAC与0.6倍量的热塑性酚醛树脂，继续混碾75秒后再加入剩余量的热塑性酚醛树脂；
（3）将乌洛托品溶于水形成溶液，然后将溶液的70%缓慢加入到混砂机中，继续热态下混碾80秒后，再加入剩余量的溶液，继续混碾10秒；
（4）关闭混砂机加热管，吹入冷风冷却混合砂，降温至100℃左右时均匀地加入其余剩余成分，混和30秒，然后出砂到破碎机中，风冷至40℃-60℃时破碎，过筛至冷却器中，风冷到35℃以下，出砂装袋备用。
本实施例覆膜砂的性能测试如下 ：常温抗弯强度为6.3MPa，热态抗弯强度为3.1MPa，灼烧减量2.8%，熔点为104℃。

Claims (2)

1.一种新型易溃散覆膜砂，其特征在于，由下列重量份的原料制成：热塑性酚醛树脂4-6、聚甲醛1-2、交联剂TAC 1-1.5、水2.5-3、乌洛托品0.8-1.2、石英砂80-90、二硫化钼3-5、硅藻土8-11、过氧化钙0.4-0.7、硬脂酸钙0.25-0.35、增效剂5-7；
所述增效剂由以下重量份的原料制备而成：玉米秸秆4-6、淀粉2-3、水玻璃3-5、氢氧化钙1.5-2.5、氯化镁1-2、石墨烯4-5、陶土20-25、锆英粉9-11、邻苯二甲酸二丁酯3-4、水9-12；制备方法如下：将玉米秸秆干燥后粉碎成80-100目的粉末与陶土、淀粉混合搅拌均匀，加入水搅拌均匀，控温在60℃-80℃，保持1-1.5小时，然后加入除水玻璃、邻苯二甲酸二丁酯之外的其余剩余成分，混合20-30分钟，再加入水玻璃、邻苯二甲酸二丁酯，放入混砂机中湿混20-30秒，出砂后烘干，最后粉碎成200-250目即得。
2.根据权利要求1所述一种新型易溃散覆膜砂，其特征在于，由以下具体步骤制成：
（1）将石英砂、二硫化钼、硅藻土放入粉碎机中粉碎，过200-300目筛形成混合砂，然后将沸腾炉加热至160℃，开动沸腾炉内风机，缓慢加入混合砂，将混合砂的温度加热到140℃-150℃；
（2）将加热后的混合砂放到混砂机内，保持160℃恒温，在混碾的同时加入聚甲醛、交联剂TAC与0.6倍量的热塑性酚醛树脂，继续混碾70-80秒后再加入剩余量的热塑性酚醛树脂；
（3）将乌洛托品溶于水形成溶液，然后将溶液的70%缓慢加入到混砂机中，继续热态下混碾75-85秒后，再加入剩余量的溶液，继续混碾10-20秒；
（4）关闭混砂机加热管，吹入冷风冷却混合砂，降温至100℃左右时均匀地加入其余剩余成分，混和30-35秒，然后出砂到破碎机中，风冷至40℃-60℃时破碎，过筛至冷却器中，风冷到35℃以下，出砂装袋备用。
CN201510229081.7A 2015-05-07 2015-05-07 一种新型易溃散覆膜砂及其制备方法 Pending CN104841863A (zh)