CN104831881B - Building in the style of the ancients concrete component covers or decorate with paint construction method - Google Patents
Building in the style of the ancients concrete component covers or decorate with paint construction method Download PDFInfo
- Publication number
- CN104831881B CN104831881B CN201510190897.3A CN201510190897A CN104831881B CN 104831881 B CN104831881 B CN 104831881B CN 201510190897 A CN201510190897 A CN 201510190897A CN 104831881 B CN104831881 B CN 104831881B
- Authority
- CN
- China
- Prior art keywords
- ash
- parts
- fiber crops
- glue
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a kind of building in the style of the ancients concrete component covers or decorate with paint construction method, comprise the following steps:Concrete floor battle clay prepares that standby, base treatment, logical ash, paste fiber crops, grey, the mellow lime process of pressure fiber crops, fine ash and slurry ash are processed, levigate brick is raw and paint finishing.The present invention selecting in technique, breaks through traditional wood structure surface practice, selects and concrete material performance blends modelled after an antique covers or decorate with paint construction technology it is ensured that covering or decorate with paint quality and the durability of engineering；In terms of material selection, the modern architecture material such as application portland cement, building adhesive, alkali resistance coating, science environmental protection；Compared with covering or decorate with paint construction with traditional timber structure, operation is few, short time limit, task difficulty are little, substantially improves construction operation environment, has saved material and has put into it is ensured that construction safety, has accelerated speed of application, improve construction quality.
Description
Technical field
The present invention relates to a kind of building in the style of the ancients concrete component covers or decorate with paint construction method, belong to building in the style of the ancients surface decoration technique
Field.
Background technology
With the foundation of Chinese's Cultural confidence, various places are imitated the tradition such as large-scale temple, building, Historical Block one after another and are built
Build.In view of a variety of drawbacks such as traditional timber structure cost is high, fire-protection rating is high, timber shortage, various building in the style of the ancients are being built in various places
During, generally substitute traditional timber structure with reinforced concrete structure, not only achieve large span, large space requirement, and right
Traditional gallows timber is optimized and develops, and have accumulated rich experience.But how on reinforced concrete member preferably
Implement to cover or decorate with paint engineering, it is to avoid occur such as holding come off, the quality problems of mouldy etc. " being not acclimatized ", experience still compares shortcoming,
This is a new problem of building in the style of the ancients, is also one of difficult point in construction.
Content of the invention
For solving the deficiencies in the prior art, it is an object of the invention to, provide a kind of building in the style of the ancients concrete component to cover or decorate with paint
Construction method, operation is few, short time limit, task difficulty are little, substantially improves construction operation environment, saved material put into it is ensured that
Construction safety, accelerates speed of application, improves construction quality.
The technical scheme is that：Building in the style of the ancients concrete component covers or decorate with paint construction method, it is characterized in that, walks including following
Suddenly:
(1) preparation of concrete floor battle clay is standby:It is bed material using No. 525 silicate ordinary cements, 108 glue are blending stock,
And add iron oxide pigment and water；
(2) base treatment
A. basic unit's snap the line：Eject concrete component datum line on structured base layer, find out concrete component rejected region, do
Process well labelling；
B. base treatment：Tamp concave face with cement mortar, with hand grinder or emery-cloth polish convex show up, accomplish
No hollowing, cracking, flat smooth；
C. expire brush primer：Treat that concrete base layer picks chisel repairing and completes, after the floating ash dust cleaning on surface finishes, by concrete
Substrate surface completely brushes one glue, and in described glue, the ratio of 108 glue and water is 1: 2；
(3) lead to ash
Carry out logical ash after 108 glue are dried, the concrete floor prepared battle clay are spread at twice, Xian Manpu in step (1), after
Receive light, scraper plate requires flat round directly suitable, the place that scraper plate can not put in place, reexamined neatly with small-sized scraper, after dry, use 60# sand paper
Floating, clean up, brushed lightly only with wet cloth；
(4) fiber crops are pasted
A. beginning slurry：Dip in head slurry brush with paste brush on logical ash, its thickness is can be impregnated with flax silk for degree；
B. fiber crops are glued：Immediately the fiber crops combed in advance are sticked after brushing head slurry, the thickness of fiber crops wants uniformity, and surface will be put down
Whole, corner or junction must not tilt；
C. dry pressure：After fiber crops are stained with, are first set about at seedling angle, line mouth with fiber crops pressure, gradually by fiber crops compacting, press 3～4 times；
D. swill life：Clay is held with concrete floor and water presses 1：1 ratio is mixed well, and is brushed on fiber crops with pasting, is limited with not revealing dry fiber crops；
E. hydraulic pressure：Swill after life, with fiber crops pressure, fiber crops are turned over void, check for the dry fiber crops not being impregnated with, then row is compacted again, and will
Remaining slurry shuts out, and prevents dry rear hollowing；
F. fiber crops are ground：With sandstone polishing after fiber crops are dry, so that numb floss is floated, mill must not be leaked, also flax silk must not be rubbed, to " disconnected speckle "
Till, then the long fiber crops knife having ground is pared off, sweep floating ash with the broom special bags of willow branches, framed by bamboo, for building dykes, brushed lightly only with water cloth；
(5) press fiber crops ash
With leather, concrete floor battle clay is applied on fiber crops, comes and goes to scrape with leather and be stained with reality with fiber crops, then multiple ash, suitable with plank
Horizontal the pushing away of flax silk wraps up in lining, when frame has line angle, will prick out line angle on ash, polishes gray surface with 80# sand paper fine grinding, use broom after doing
The special bags of willow branches, framed by bamboo, for building dykes sweeps floating ash, is brushed lightly only with water cloth；
(6) mellow lime process
After pressing numb ash to parch, the angle after being criticized ash residual at inner corner trim, scraper plate with scraper, tumor scar shovel fall to scabble, with soft
Property scraper plate completely scrape on pressure fiber crops ash mellow lime together, thickness 2～3mm, when having line angle, then with mellow lime binding, dry after polished with sandstone,
Water cloth is brushed lightly only；
(7) fine ash, slurry ash are processed
A. fine ash：After mellow lime drying, with No. 2.5 steel wire cloth sanding components of lumps of wood block bag, taken out with water cloth before upper fine ash and brush lightly
One time, make substrate surface moisten and clean, then with iron plate by seedling angle, frame, upper and lower muffler, frame mouth, line mouth and under do not go
The place fine ash of leather is carefully made uniform, and completely goes up fine ash together with same material again, little face iron plate, big face plate after looking for ash dry
Son, the stupefied use leather of circle, thickness is less than 2mm, and joint can not be stayed and rise on one's feet and obvious position, have and carefully pricked out with fine ash at line angle
Fine rule；
B. starch ash：After fine ash is dried, with No. 1 steel wire cloth sanding, starch grey way identical with fine ash way, to component itself
Due concavo-convex, the grey place of nest, is modified with scraper, shows profile, more grey with Cornu Bovis seu Bubali shovel or grey latex；
(8) levigate brick life
A. levigate：After fine ash is done, it is finely ground to disconnected speckle with sandstone；
B. brick life：After milled, dip in raw Oleum Verniciae fordii with silk head or cover with paint or varnish in time and bore life, when surface oil slick no longer penetrates into, with useless
Oil slick is wiped by numb head, hangs first after preventing from doing, and after all parching, with fine sandpaper polishing, cleans up；
(9) paint finishing
A. emulsion putty is prepared：
Emulsion proportion：100 parts of pigment, 8～12 parts of vinyl polyacetic acid latex, 0.05～0.5 part of sodium hexameta phosphate, carboxymethyl
0.1～0.2 part of cellulose,
Emulsion putty proportioning is：100 parts of Pulvis Talci, 5～6 parts of emulsion, 0.05～0.1 part of sodium hexametaphosphate, concentration 5%
60 parts of cellulose aqueous solution, 1.5～2.5 parts of iron oxide pigment；
B. base treatment：First the side concrete component substrate surface residual is stupefied, float grey, quick sand stone and oil stain removing is net,
Then added water 1 times of mix homogenously brushing bottom with 108 glue；
C. sheaing coating：Its cloth is opened by the emulsion putty coating material scraper plate that step a is prepared, and each thickness is
0.5cm, after first brushing, still needs to deashing one time, to small pitted skin, wind crack position, is mended with emulsion putty and picks up tight, cross water
Cloth, after front layer coating is dried, scratches the second layer, scratches 2～3 times, coating thickness is 80～100 μm；
D. coating surface is processed：After construction coating is to be dried, polished polishing with No. 0 steel wire cloth, surface color after mill
The meeting depth is uneven, repastes brush 108 glue mill base together, brushes 2～3 layers of vinyl chloride-vinylidene chloride copolymer emulsion after being dried.
Further, described concrete floor battle clay the ratio of each component is：100 parts of No. 525 Portland cements, 108
40～50 parts of glue, 3 parts of iron oxide pigment, 5～10 parts of water.
Further, described mellow lime ground battle material the ratio of each component is：100 parts of No. 525 Portland cements,
108 40～50 parts of glue, 3 parts of iron oxide pigment, 5.5～11 parts of water.
Further, described fine ash ground battle material the ratio of each component is：100 parts of No. 525 Portland cements, 108
44～55 parts of glue, 3 parts of iron oxide pigment, 5.5～11 parts of water.
Further, described slurry lacquer putty battle material the ratio of each component is：100 parts of No. 525 Portland cements, 108
46～57.5 parts of glue, 3 parts of iron oxide pigment, 5.75～11.5 parts of water.
Further, the modulator approach of described emulsion putty is：
A. first according to the above ratio carboxymethyl cellulose is soaked in water, soaks 12h, after being completely dissolved into Colloidal fluid, mistake
Sieve sieve is standby；
B. pigment is soaked, pigment：Water is 100：180～200, stir into thick paste, be proportionally added into the glue allocated
Liquid, sodium hexametaphosphate and carboxymethyl cellulose, stirring while adding, to be mixed uniformly afterwards cross 80 mesh steel wire sieve, emulsion completes standby；
C. be proportionally added into allocate Pulvis Talci, emulsion, sodium hexametaphosphate, cellulose aqueous solution, iron oxide pigment, emulsion
Putty is prepared and is completed.
Further, in described step (9), 108 glue mill base match ratios are：108 10 parts of glue, iron oxide pigment 1.5～2.5
Part, 4～5 parts of water.
Further, described outer eaves portion point exposure emulsion putty brushing method is：First painting iron oxide red pigment emulsion, treats
Deashing after drying, with No. 1 steel wire cloth sanding, cleans, crosses water；Second brushing iron oxide red prunus mume (sieb.) sieb.et zucc. pellet emulsion, the pigment composition in emulsion
It is iron oxide red and excellent pellet is 6 parts and 4 parts respectively；After second emulsion is dried, with No. 0 abrasive paper for wood sanding, cleans, cross water；Repaste
The emulsion that extreme trace bright red poster paint is made into Vermilion, the pigment ratio in emulsion is that advertisement is red：Vermilion or toluene glue red be 7：3,
Then through sanding, cleaning, cross water, repaste brush 2～3 road vinyl chloride-vinylidene chloride copolymer emulsion.
The beneficial effect that the present invention is reached：
1. selecting in technique, breaks through traditional wood structure surface practice, and selection and concrete material performance blend
Modelled after an antique cover or decorate with paint construction technology it is ensured that covering or decorate with paint quality and the durability of engineering；
2. in terms of material selection, the modern architecture material such as application portland cement, building adhesive, alkali resistance coating, science
Environmental protection；
3., compared with covering or decorate with paint construction with traditional timber structure, operation is few, short time limit, task difficulty are little, substantially improves construction
Working environment, has saved material and has put into it is ensured that construction safety, accelerated speed of application, improve construction quality.
Specific embodiment
The invention will be further described below.Following examples are only used for the technical side of the present invention is clearly described
Case, and can not be limited the scope of the invention with this.
Building in the style of the ancients concrete component covers or decorate with paint construction method, comprises the following steps:
(1) preparation of concrete floor battle clay is standby:It is bed material using No. 525 silicate ordinary cements, 108 glue are blending stock,
And add iron oxide pigment and water；Described concrete floor battle clay the ratio of each component is：100 parts of No. 525 Portland cements,
108 40～50 parts of glue, 3 parts of iron oxide pigment, 5～10 parts of water.
(2) base treatment
A. basic unit's snap the line：Eject concrete component datum line on structured base layer, find out concrete component rejected region, do
Process well labelling；
B. base treatment：Tamp concave face with cement mortar, with hand grinder or emery-cloth polish convex show up, accomplish
No hollowing, cracking, flat smooth；
C. expire brush primer：Treat that concrete base layer picks chisel repairing and completes, after the floating ash dust cleaning on surface finishes, by concrete
Substrate surface completely brushes one glue, and in described glue, the ratio of 108 glue and water is 1: 2, improves basic unit's cohesion.
(3) lead to ash
Carry out logical ash after 108 glue are dried, the concrete floor prepared battle clay are spread at twice, Xian Manpu in step (1), after
Receive light, scraper plate requires flat round directly suitable, the place that scraper plate can not put in place, reexamined neatly with small-sized scraper, after dry, use 60# sand paper
Floating, clean up, brushed lightly only with wet cloth.
(4) fiber crops are pasted
A. beginning slurry：Dip in head slurry brush with paste brush on logical ash, its thickness is can be impregnated with flax silk for degree；
B. fiber crops are glued：Immediately the fiber crops combed in advance are sticked after brushing head slurry, the thickness of fiber crops wants uniformity, and surface will be put down
Whole, corner or junction must not tilt；
C. dry pressure：After fiber crops are stained with, are first set about at seedling angle, line mouth with fiber crops pressure, gradually by fiber crops compacting, press 3～4 times；
D. swill life：Clay is held with concrete floor and water presses 1：1 ratio is mixed well, and is brushed on fiber crops with pasting, is limited with not revealing dry fiber crops；
E. hydraulic pressure：Swill after life, with fiber crops pressure, fiber crops are turned over void, check for the dry fiber crops not being impregnated with, then row is compacted again, and will
Remaining slurry shuts out, and prevents dry rear hollowing, finally goes through one time, collapses if any seedling angle, stupefied line floats or hemp cut loosens person, should
Fix；
F. fiber crops are ground：With sandstone polishing after fiber crops are dry, so that numb floss is floated, mill must not be leaked, also flax silk must not be rubbed, to " disconnected speckle "
Till, then the long fiber crops knife having ground is pared off, sweep floating ash with the broom special bags of willow branches, framed by bamboo, for building dykes, brushed lightly only with water cloth.
(5) press fiber crops ash
With leather, concrete floor battle clay is applied on fiber crops, comes and goes to scrape with leather and be stained with reality with fiber crops, then multiple ash, suitable with plank
Horizontal the pushing away of flax silk wraps up in lining, when frame has line angle, will prick out line angle on ash, polishes gray surface with 80# sand paper fine grinding, use broom after doing
The special bags of willow branches, framed by bamboo, for building dykes sweeps floating ash, is brushed lightly only with water cloth.
(6) mellow lime process
After pressing numb ash to parch, the angle after being criticized ash residual at inner corner trim, scraper plate with scraper, tumor scar shovel fall to scabble, with soft
Property scraper plate completely scrape on pressure fiber crops ash mellow lime together, thickness 2～3mm, when having line angle, then with mellow lime binding, dry after polished with sandstone,
Water cloth is brushed lightly only, and mellow lime ground battle material the ratio of each component is：100 parts of No. 525 Portland cements, 108 40～50 parts of glue,
3 parts of iron oxide pigment, 5.5～11 parts of water.
(7) fine ash, slurry ash are processed
A. fine ash：After mellow lime drying, with No. 2.5 steel wire cloth sanding components of lumps of wood block bag, taken out with water cloth before upper fine ash and brush lightly
One time, make substrate surface moisten and clean, then with iron plate by seedling angle, frame, upper and lower muffler, frame mouth, line mouth and under do not go
The place fine ash of leather is carefully made uniform, and completely goes up fine ash together with same material again, little face iron plate, big face plate after looking for ash dry
Son, the stupefied use leather of circle, thickness is less than 2mm, and joint can not be stayed and rise on one's feet and obvious position, have and carefully pricked out with fine ash at line angle
Fine rule, battle material in fine ash ground the ratio of each component is：100 parts of No. 525 Portland cements, 108 44～55 parts of glue, ferrum oxide
3 parts of pigment, 5.5～11 parts of water.
B. starch ash：After fine ash is dried, with No. 1 steel wire cloth sanding, starch grey way identical with fine ash way, to component itself
Due concavo-convex, the grey place of nest, is modified with scraper, shows profile, then with Cornu Bovis seu Bubali shovel or grey latex ash, starches the lacquer putty battle each component of material
Proportioning be：100 parts of No. 525 Portland cements, 108 46～57.5 parts of glue, 3 parts of iron oxide pigment, water 5.75～11.5
Part.
(8) levigate brick life
A. levigate：After fine ash is done, it is finely ground to disconnected speckle with sandstone；
B. brick life：After milled, dip in raw Oleum Verniciae fordii with silk head or cover with paint or varnish in time and bore life, when surface oil slick no longer penetrates into, with useless
Oil slick is wiped by numb head, hangs first after preventing from doing, and after all parching, with fine sandpaper polishing, cleans up.
(9) paint finishing
1) emulsion putty is prepared：
Emulsion proportion：100 parts of pigment, 8～12 parts of vinyl polyacetic acid latex, 0.05～0.5 part of sodium hexameta phosphate, carboxymethyl
0.1～0.2 part of cellulose (when joining emulsion, plus the appropriate carboxymethyl cellulose of people and micro sodium hexameta phosphate, to improve putty
Performance, prevents putty cracking and comes off),
Emulsion putty proportioning is：100 parts of Pulvis Talci, 5～6 parts of emulsion, 0.05～0.1 part of sodium hexametaphosphate, concentration 5%
60 parts of cellulose aqueous solution, 1.5～2.5 parts of iron oxide pigment；
The modulator approach of emulsion putty is：
A. first according to the above ratio carboxymethyl cellulose is soaked in water, soaks 12h, after being completely dissolved into Colloidal fluid, mistake
Sieve sieve is standby；
B. pigment is soaked, pigment：Water is 100：180～200, stir into thick paste, be proportionally added into the glue allocated
Liquid, sodium hexametaphosphate and carboxymethyl cellulose, stirring while adding, to be mixed uniformly afterwards cross 80 mesh steel wire sieve, emulsion completes standby；
C. be proportionally added into allocate Pulvis Talci, emulsion, sodium hexametaphosphate, cellulose aqueous solution, iron oxide pigment, emulsion
Putty is prepared and is completed；
2) base treatment：First the side concrete component substrate surface residual is stupefied, float grey, quick sand stone and oil stain removing is net,
Then added water 1 times of mix homogenously brushing bottom with 108 glue；
3) sheaing coating：Its cloth is opened by the emulsion putty coating material scraper plate that step a is prepared, and each thickness is
0.5cm, after first brushing, still needs to deashing one time, to small pitted skin, wind crack position, is mended with emulsion putty and picks up tight, cross water
Cloth, after front layer coating is dried, scratches the second layer, scratches 2～3 times, coating thickness is 80～100 μm；
4) coating surface is processed：After construction coating is to be dried, polished polishing with No. 0 steel wire cloth, surface color after mill
The meeting depth is uneven, repastes brush 108 glue mill base together, brushes 2～3 layers of vinyl chloride-vinylidene chloride copolymer emulsion, 108 glue after being dried
Mill base match ratio is：108 10 parts of glue, 1.5～2.5 parts of iron oxide pigment, 4～5 parts of water.
Outer eaves portion point exposure emulsion putty brushing method is：It is bright red that size connects eaves, and Liang Fang, post are the color such as dark red,
Because redness is not sun-resistant, first painting iron oxide red pigment emulsion, rear deashing to be dried, with No. 1 steel wire cloth sanding, clean, cross water；The
Second painting iron oxide red prunus mume (sieb.) sieb.et zucc. pellet emulsion, it is 6 parts and 4 parts respectively that the pigment in emulsion consists of iron oxide red and excellent pellet；Treat second emulsion
After drying, with No. 0 abrasive paper for wood sanding, clean, cross water；Repaste the emulsion that extreme trace bright red poster paint is made into Vermilion, in emulsion
Pigment ratio be advertisement red：Vermilion or toluene glue red be 7：3, then through sanding, cleaning, cross water, repaste brush 2～3 road vinyl chloride-
Vinylidene chloride copolymer emulsion.So process and can reach that coating is plentiful, there is good weather-proof, the water-fast, property protecting light, protect color
Energy.
The above is only the preferred embodiment of the present invention it is noted that ordinary skill people for the art
For member, on the premise of without departing from the technology of the present invention principle, some improvement can also be made and deform, these improve and deform
Also should be regarded as protection scope of the present invention.
Claims (7)
1. building in the style of the ancients concrete component covers or decorate with paint construction method, it is characterized in that, comprises the following steps:
(1) preparation of concrete floor battle clay is standby:It is bed material using No. 525 silicate ordinary cements, 108 glue are blending stock, and plus
Enter iron oxide pigment and water；
(2) base treatment
A. basic unit's snap the line：Eject concrete component datum line on structured base layer, find out concrete component rejected region, do benefit
Reason labelling；
B. base treatment：Tamp concave face with cement mortar, with hand grinder or emery-cloth polish convex show up, do not accomplish no empty
Drum, cracking, flat smooth；
C. expire brush primer：Treat that concrete base layer picks chisel repairing and completes, after the floating ash dust cleaning on surface finishes, by concrete base layer
One glue is completely brushed on surface, and in described glue, the ratio of 108 glue and water is 1: 2；
(3) lead to ash
Carry out logical ash after 108 glue are dried, the concrete floor prepared battle clay are spread at twice, Xian Manpu, receive afterwards in step (1)
Light, scraper plate requires flat round directly suitable, the place that scraper plate can not put in place, is reexamined neatly with small-sized scraper, is smeared with 60# sand paper after dry
Flat, clean up, brushed lightly only with wet cloth；
(4) fiber crops are pasted
A. beginning slurry：Dip in head slurry brush with paste brush on logical ash, its thickness is can be impregnated with flax silk for degree；
B. fiber crops are glued：Immediately the fiber crops combed in advance are sticked after brushing head slurry, the thickness of fiber crops wants uniformity, and surface is smooth,
Corner or junction must not tilt；
C. dry pressure：After fiber crops are stained with, are first set about at seedling angle, line mouth with fiber crops pressure, gradually by fiber crops compacting, press 3～4 times；
D. swill life：Clay is held with concrete floor and water presses 1：1 ratio is mixed well, and is brushed on fiber crops with pasting, is limited with not revealing dry fiber crops；
E. hydraulic pressure：Swill raw after, with fiber crops pressure, fiber crops are turned over void, check for the dry fiber crops not being impregnated with, then row compacting again, and by remaining slurry
Shut out, prevent dry rear hollowing；
F. fiber crops are ground：With sandstone polishing after fiber crops are dry, so that numb floss is floated, mill must not be leaked, also flax silk must not be rubbed, to " disconnected speckle " be
Only, then the long fiber crops knife having ground is pared off, sweep floating ash with the broom special bags of willow branches, framed by bamboo, for building dykes, brushed lightly only with water cloth；
(5) press fiber crops ash
With leather, concrete floor battle clay is applied on fiber crops, comes and goes to scrape with leather and be stained with reality with fiber crops, then multiple ash, with plank along flax silk
Horizontal pushing away wraps up in lining, when frame has line angle, will prick out line angle on ash, polishes gray surface with 80# sand paper fine grinding, swept with the broom special bags of willow branches, framed by bamboo, for building dykes after doing
Fall and float ash, brushed lightly only with water cloth；
(6) mellow lime process
After pressing numb ash to parch, the angle after being criticized ash residual at inner corner trim, scraper plate with scraper, tumor scar shovel fall to scabble, and are scraped with soft
Plate is completely scraped mellow lime one on pressure fiber crops ash, and thickness 2～3mm, when having line angle, then with mellow lime binding, is polished with sandstone after doing, water cloth
Brush lightly net；
(7) fine ash, slurry ash are processed
A. fine ash：After mellow lime drying, with No. 2.5 steel wire cloth sanding components of lumps of wood block bag, taken out with water cloth before upper fine ash and brush lightly one time,
Make substrate surface moisten and clean, then with iron plate by seedling angle, frame, upper and lower muffler, frame mouth, line mouth and under do not remove leather
Place fine ash is carefully made uniform, and completely goes up fine ash together with same material again after looking for ash dry, little face iron plate, big face plank, circle
Stupefied use leather, thickness is less than 2mm, and joint can not be stayed and rise on one's feet and obvious position, have and carefully prick out fine rule with fine ash at line angle；
B. starch ash：After fine ash is dried, with No. 1 steel wire cloth sanding, the grey way of slurry is identical with fine ash way, and component itself should be had
Concavo-convex, the grey place of nest, modified with scraper, show profile, then with Cornu Bovis seu Bubali shovel or grey latex ash；
(8) levigate brick life
A. levigate：After fine ash is done, it is finely ground to disconnected speckle with sandstone；
B. brick life：After milled, dip in raw Oleum Verniciae fordii with silk head or cover with paint or varnish in time and bore life, when surface oil slick no longer penetrates into, with useless fiber crops head
Oil slick is wiped, after preventing from doing, hangs first, after all parching, with fine sandpaper polishing, clean up；
(9) paint finishing
A. emulsion putty is prepared：
Emulsion proportion：100 parts of pigment, 8～12 parts of vinyl polyacetic acid latex, 0.05～0.5 part of sodium hexameta phosphate, carboxymethyl cellulose
0.1～0.2 part of element,
Emulsion putty proportioning is：100 parts of Pulvis Talci, 5～6 parts of emulsion, 0.05～0.1 part of sodium hexametaphosphate, the fiber of concentration 5%
60 parts of plain aqueous solution, 1.5～2.5 parts of iron oxide pigment；
B. base treatment：First the side concrete component substrate surface residual is stupefied, float grey, quick sand stone and oil stain removing is net, then
Added water 1 times of mix homogenously brushing bottom with 108 glue；
C. sheaing coating：Its cloth is opened by the emulsion putty coating material scraper plate that step a is prepared, and each thickness is 0.5cm,
After first brushing, still need to deashing one time, to small pitted skin, wind crack position, mended with emulsion putty and pick up tight, cross water cloth, treat
After front layer coating is dried, scratch the second layer, scratch 2～3 times, coating thickness is 80～100 μm；
D. coating surface is processed：After construction coating is to be dried, polished polishing with No. 0 steel wire cloth, after mill, surface color can be deep
Shallow inequality, repastes brush 108 glue mill base together, brushes 2～3 layers of vinyl chloride-vinylidene chloride copolymer emulsion after being dried.
2. building in the style of the ancients concrete component according to claim 1 covers or decorate with paint construction method, it is characterized in that, described concrete floor battle
Clay the ratio of each component is：100 parts of No. 525 Portland cements, 108 40～50 parts of glue, 3 parts of iron oxide pigment, water 5～
10 parts.
3. building in the style of the ancients concrete component according to claim 1 covers or decorate with paint construction method, it is characterized in that, described mellow lime ground
Battle material the ratio of each component is：100 parts of No. 525 Portland cements, 108 40～50 parts of glue, 3 parts of iron oxide pigment, water
5.5～11 parts.
4. building in the style of the ancients concrete component according to claim 1 covers or decorate with paint construction method, it is characterized in that, described fine ash ground battle
Material the ratio of each component is：100 parts of No. 525 Portland cements, 108 44～55 parts of glue, 3 parts of iron oxide pigment, water 5.5
～11 parts.
5. building in the style of the ancients concrete component according to claim 1 covers or decorate with paint construction method, it is characterized in that, described slurry lacquer putty battle
Material the ratio of each component is：100 parts of No. 525 Portland cements, 108 46～57.5 parts of glue, 3 parts of iron oxide pigment, water
5.75～11.5 parts.
6. building in the style of the ancients concrete component according to claim 1 covers or decorate with paint construction method, it is characterized in that, described emulsion putty
Modulator approach be：
A. first according to the above ratio carboxymethyl cellulose is soaked in water, soaks 12h, after being completely dissolved into Colloidal fluid, cross sieve sieve
Standby；
B. pigment is soaked, pigment：Water is 100：180～200, stir into thick paste, be proportionally added into allocate glue, six
Metaphosphoric acid is received and carboxymethyl cellulose, stirring while adding, to be mixed uniformly afterwards cross 80 mesh steel wire sieve, emulsion completes standby；
C. be proportionally added into allocate Pulvis Talci, emulsion, sodium hexametaphosphate, cellulose aqueous solution, iron oxide pigment, emulsion putty
Preparation completes.
7. building in the style of the ancients concrete component according to claim 1 covers or decorate with paint construction method, it is characterized in that, described step (9)
In 108 glue mill base match ratios be：108 10 parts of glue, 1.5～2.5 parts of iron oxide pigment, 4～5 parts of water.