CN104830404B - 一种含离子液体、改性纳米锌粉和石墨烯的润滑油组合物的制备方法 - Google Patents
一种含离子液体、改性纳米锌粉和石墨烯的润滑油组合物的制备方法 Download PDFInfo
- Publication number
- CN104830404B CN104830404B CN201510245446.5A CN201510245446A CN104830404B CN 104830404 B CN104830404 B CN 104830404B CN 201510245446 A CN201510245446 A CN 201510245446A CN 104830404 B CN104830404 B CN 104830404B
- Authority
- CN
- China
- Prior art keywords
- zinc powder
- nano zinc
- graphene
- modified nano
- ionic liquid
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开了一种含离子液体、改性纳米锌粉和石墨烯的润滑油组合物的制备方法。该方法采用基础油、清净剂、分散剂、防腐剂、极压抗磨剂、油性剂、抗氧剂、粘度指数改进剂、防锈剂、降凝剂、抗泡剂、离子液体、改性纳米锌粉和石墨烯复配得到润滑油组合物。该方法生产工艺简单易行，设备投资小，能耗低，无环境污染，有利于推广应用。该方法所制得含离子液体、改性纳米锌粉和石墨烯的润滑油组合物产品可广泛应用于机械工业、汽车工业、精密仪器、电力工业、冶金工业、模具制造与应用工业、钢铁工业、机床工业等工业领域，具有广阔的应用前景。
Description
技术领域
本发明涉及一种含离子液体、改性纳米锌粉和石墨烯的润滑油组合物的制备方法，属于润滑油领域。
背景技术
润滑油主要用于减少运动部件表面间的摩擦，具有润滑作用，同时对机器设备还具有防锈、防腐、绝缘、功率传送、冷却、密封、清洗杂质和缓冲等功能，是一类在机械工业、汽车工业、精密仪器、电力工业、冶金工业、模具制造与应用工业、钢铁工业、机床工业等工业领域不可或缺的化工产品，在上述工业领域具有重要的作用。随着工业的飞速发展，装备技术的不断提升，我国对各种润滑油产品的需求量持续增长，且已成为全球第二大润滑油市场。在润滑油需求量不断上升的同时，也要求润滑油产品质量不断提高。因此，具有多功能的新型润滑剂已成为研究热点。
具有抗磨和自修复功能的抗磨纳米润滑油添加剂是近年来国内外研究热点之一。纳米金属粉体如纳米锌粉备受关注。一方面，纳米锌粉具有优异的极压、抗磨和环境友好性等特性，可在器件摩擦表面形成润滑膜；另一方面，纳米锌粉颗粒在摩擦界面之间可以自由滚动，具有微轴承的作用。因此，纳米锌粉作为新型润滑油添加剂添加到润滑油中，可以大大提高了相互摩擦表面的润滑性能，大幅度降低摩擦系数，显著提高润滑作用，进而提高机械设备的有效动力，延长机械设备的使用寿命，降低机械设备的运转能耗。但纳米锌粉在润滑油中的分散稳定性和热稳定性是目前的一个难题。
离子液体具有：蒸汽压极低或“零”蒸汽压、挥发性小或几乎无挥发性；熔点低(可在-100℃以下)；液程宽(可在200℃以上)；热稳定性优异；电化学窗口宽；导电性和导热性好；静电场强；结构可设计性强，可根据实际需要设计合成某一结构的离子液体；选择性溶解能力强，既有可溶解有机物的离子液体，也有可溶解无机物的离子液体，还有可同时溶解有机物和无机物的离子液体等特点。由于离子液体具有上述独特性能而备受关注，它已被广泛应用于化学研究的各个领域中。目前，离子液体在聚合反应、选择性烷基化和胺化反应、酰基化反应、酯化反应、化学键的重排反应、室温和常压下的催化加氢反应、烯烃的环氧化反应、电化学合成、支链脂肪酸的制备等方面得到应用，并显示出反应速率快、转化率高、反应的选择性高、催化体系可循环重复使用等优点。同时，离子液体在溶剂萃取、物质的分离和纯化、废旧高分子化合物的回收、燃料电池、太阳能电池、锂离子电池、电容器、变压器、工业废气中二氧化碳的提取、地质样品的溶解、核燃料和核废料的分离与处理、用作添加剂等方面也得到了广泛的研究，具有广泛的应用前景。另外，离子液体凭借其熔点低、难燃、抗氧化性好和热稳定性高等特点，将成为理想、绿色、高性能新型润滑剂添加剂。
石墨烯是近年来备受关注的纳米材料之一。2004年英国曼彻斯特大学的AndreGeim和Konstantin Novoselov教授，成功地从石墨中分离出石墨烯，证实它可以单独存在以来，仅仅时隔6年，两人就因“二维石墨烯材料的开创性实验”研究成果，共同获得2010年诺贝尔物理学奖，这足以证明石墨烯在材料科学领域具有举足轻重的地位。
石墨烯是一种二维碳材料，是单层石墨烯、双层石墨烯和少层(3～10层)石墨烯的统称。石墨烯能牢牢地附着在金属表面，石墨烯具有几乎是完全透明、无毒、化学性能优异、润滑性能优异、机械强度大、导热性优异、导电性能极强、比表面积高达2630m2/g和储氢性能优异等特点，使石墨烯在润滑、微电子、超级计算机、超级电容器、锂离子电池、燃料电池、光伏产业、透明电极、印刷电路、传感器、工业催化、储能、储氢和新型石墨烯基复合材料等领域都有着广泛的应用。
本发明首先以纳米锌粉为原料，通过化学方法和物理方法对纳米锌粉进行改性，制备易于分散的改性纳米锌粉；其次，以离子液体、改性纳米锌粉和石墨烯作为新型润滑油添加剂，用基础油、离子液体、改性纳米锌粉、石墨烯和一般润滑油添加剂(一般添加剂为清净剂、分散剂、防腐剂、极压抗磨剂、油性剂、抗氧剂、粘度指数改进剂、防锈剂、降凝剂和抗泡剂)复配得到含离子液体、改性纳米锌粉和石墨烯的润滑油组合物。本发明将为机械工业、汽车工业、精密仪器、电力工业、冶金工业、模具制造与应用工业、钢铁工业、机床工业等工业领域提供一种性能优异的润滑油产品，具有重要的实际意义。目前，国内、外关于同时使用基础油、离子液体、改性纳米锌粉、石墨烯和一般润滑油添加剂复配得到润滑油产品的研究和技术鲜见报道。
发明内容
本发明所述的一种含离子液体、改性纳米锌粉和石墨烯的润滑油组合物的制备方法，提供一种以纳米锌粉为原料，通过化学方法和物理方法对纳米锌粉进行改性，制备易于分散的改性纳米锌粉；再以离子液体、改性纳米锌粉和石墨烯作为新型润滑油添加剂，用基础油、离子液体、改性纳米锌粉、石墨烯和一般润滑油添加剂(一般添加剂为清净剂、分散剂、防腐剂、极压抗磨剂、油性剂、抗氧剂、粘度指数改进剂、防锈剂、降凝剂和抗泡剂)复配得到含离子液体、改性纳米锌粉和石墨烯的润滑油组合物的方法，该方法生产工艺简单易行，设备投资小，能耗低，无环境污染，有利于推广应用。
本发明所述的一种含离子液体、改性纳米锌粉和石墨烯的润滑油组合物的制备方法，所制得的含离子液体、改性纳米锌粉和石墨烯的润滑油组合物可广泛应用于机械工业、汽车工业、精密仪器、电力工业、冶金工业、模具制造与应用工业、钢铁工业、机床工业等工业领域，具有广阔的应用前景。
本发明所述的一种含离子液体、改性纳米锌粉和石墨烯的润滑油组合物的制备方法，采用如下技术方案：
1、改性纳米锌粉的制备：按照纳米锌粉、硫醇、阳离子表面活性剂、缓蚀剂、络合剂与去离子水的质量百分比为(0.001％～85％)∶(0.00001％～85％)∶(0.001％～35％)∶(0.001％～25％)∶(0.001％～15％)∶(0.001％～98％)的比例，依次将硫醇、阳离子表面活性剂、缓蚀剂和络合剂加入去离子水中，在频率为20kHz～1MHz、功率为30W～15kW的超声波分散作用下，搅拌0.1h～1.0h后，再加入纳米锌粉，进一步在频率为20kHz～1MHz、功率为30W～15kW的超声波分散作用下，搅拌反应0.1h～20.0h，然后依次经过离心分离、去离子水洗涤、离心分离、真空干燥、研磨和过筛工艺过程得到改性纳米锌粉，制得的改性纳米锌粉备用；
2、润滑油组合物的制备：按照离子液体、改性纳米锌粉、石墨烯、清净剂、分散剂、防腐剂、极压抗磨剂、油性剂、抗氧剂、粘度指数改进剂、防锈剂、降凝剂、抗泡剂与基础油的质量百分比为(0.00001％～85％)∶(0.001％～65％)∶(0.001％～65％)∶(0.001％～35％)∶(0.001％～25％)∶(0.001％～15％)∶(0.001％～15％)∶(0.001％～15％)∶(0.001％～15％)∶(0.001％～35％)∶(0.001％～15％)∶(0.001％～15％)∶(0.001％～15％)∶(0.001％～98％)的比例，将离子液体、改性纳米锌粉、石墨烯、清净剂、分散剂、防腐剂、极压抗磨剂、油性剂、抗氧剂、粘度指数改进剂、防锈剂、降凝剂、抗泡剂和基础油混合并搅拌均匀，即可制备得到含离子液体、改性纳米锌粉和石墨烯的润滑油组合物。
本发明所述的一种含离子液体、改性纳米锌粉和石墨烯的润滑油组合物的制备方法，其显著的特点之一是：使用两种及两种以上碳链长短不同、分子截面积不同的硫醇改性纳米锌粉时，可以使在纳米锌粉表面生成的一层硫醇锌更加致密，有利于提高纳米锌粉的分散能力。
本发明所述的一种含离子液体、改性纳米锌粉和石墨烯的润滑油组合物的制备方法，其显著的特点之二是：改性纳米锌粉时，同时使用硫醇和缓蚀剂，可以在纳米锌粉表面生成一层硫醇锌的同时，还可在纳米锌粉表面吸附苯并三氮唑或苯并三氮唑衍生物，有利于进一步提高纳米锌粉的分散能力，显著增强了纳米锌粉在润滑油中分散稳定性、热稳定性和耐氧化性能，解决了目前纳米锌粉分散难、热稳定性差和耐氧化性能差的难题。
本发明所述的一种含离子液体、改性纳米锌粉和石墨烯的润滑油组合物的制备方法，其显著的特点之三是：润滑油中添加改性纳米锌粉后，可以大大提高了相互摩擦表面的润滑性能，大幅度降低摩擦系数，显著提高润滑作用，进而提高机械设备的有效动力，延长机械设备的使用寿命，降低机械设备的运转能耗。
本发明所述的一种含离子液体、改性纳米锌粉和石墨烯的润滑油组合物的制备方法，其显著的特点之四是：润滑油中添加离子液体后，可显著提高润滑油的减摩和抗磨性能，提高润滑油的承载能力。
本发明所述的一种含离子液体、改性纳米锌粉和石墨烯的润滑油组合物的制备方法，其显著的特点之五是：由于石墨烯会均匀并且牢牢地附着在金属表面，形成具有优异润滑和保护性能的膜，而且石墨烯自身对离子液体也有很强的吸附作用。因此，用石墨烯与离子液体和纳米锌粉复配润滑油将使润滑油的性能有以下三个方面的改进：第一，可利用石墨烯在纳米锌粉表面的强吸附作用来保护纳米锌粉不受氧化，延长润滑油的使用寿命；第二，可利用石墨烯在轴承、机械设备、机械零部件等需要润滑的金属表面的强吸附作用来形成保护膜，显著提高减摩抗磨性能，降低金属的腐蚀速度，增强轴承、机械设备、机械零部件等的抗损伤能力和自修复能力；第三，可利用石墨烯与离子液体对润滑产生的协同增强作用，使减摩抗磨性能进一步提高，润滑性能显著提高。所以，复配润滑油时，在添加离子液体和纳米锌粉的基础上，再添加石墨烯，润滑油的吸附成膜性能和减摩抗磨性能显著提高，润滑油的使用寿命可提高20％以上。
本发明所述的一种含离子液体、改性纳米锌粉和石墨烯的润滑油组合物的制备方法，其特征在于改性纳米锌粉的制备过程中，所用的硫醇是叔丁基硫醇、正丁基硫醇、特丁基硫醇、正戊基硫醇、正辛基硫醇、正十二烷基硫醇、叔十二烷基硫醇、十四烷基硫醇、十六烷基硫醇、十八烷基硫醇、苄基硫醇和苯乙基硫醇中的任一种或多种。
本发明所述的一种含离子液体、改性纳米锌粉和石墨烯的润滑油组合物的制备方法，其特征在于改性纳米锌粉的制备过程中，所用的阳离子表面活性剂是十二烷基三甲基氯化铵、十二烷基三甲基溴化铵、十二烷基二甲基苄基氯化铵、十二烷基二甲基苄基溴化铵、十四烷基三甲基氯化铵、十四烷基三甲基溴化铵、十四烷基二甲基苄基氯化铵、十四烷基二甲基苄基溴化铵、十六烷基三甲基氯化铵、十六烷基三甲基溴化铵、十六烷基二甲基苄基氯化铵、十六烷基二甲基苄基溴化铵、十八烷基三甲基氯化铵、十八烷基三甲基溴化铵、十八烷基二甲基苄基氯化铵、十八烷基二甲基苄基溴化铵、十四烷基二甲基吡啶氯化铵和十四烷基二甲基吡啶溴化铵中的任一种或多种。
本发明所述的一种含离子液体、改性纳米锌粉和石墨烯的润滑油组合物的制备方法，其特征在于改性纳米锌粉的制备过程中，所用的缓蚀剂是苯并三氮唑、甲基苯并三氮唑、N-羟基苯并三氮唑、1-羟基苯并三氮唑、5-羧基苯并三氮唑和4-羟基苯并三氮唑中的任一种或多种。
本发明所述的一种含离子液体、改性纳米锌粉和石墨烯的润滑油组合物的制备方法，其特征在于改性纳米锌粉的制备过程中，所用的络合剂是乙二胺四乙酸二钠盐、柠檬酸钠、柠檬酸钾、柠檬酸铵、酒石酸钠、酒石酸钾和酒石酸铵中的任一种或多种。
本发明所述的一种含离子液体、改性纳米锌粉和石墨烯的润滑油组合物的制备方法，其特征在于润滑油组合物的制备过程中，所用的离子液体是1-甲基-3-乙基咪唑六氟磷酸盐、1-甲基-3-乙基咪唑四氟硼酸盐、1-甲基-3-丁基咪唑六氟磷酸盐、1-甲基-3-丁基咪唑四氟硼酸盐、1-甲基-3-己基咪唑六氟磷酸盐、1-甲基-3-己基咪唑四氟硼酸盐、1，2-二甲基-3-乙基咪唑六氟磷酸盐、1，2-二甲基-3-乙基咪唑四氟硼酸盐、1，2-二甲基-3-丁基咪唑六氟磷酸盐、1，2-二甲基-3-丁基咪唑四氟硼酸盐、1，2-二甲基-3-己基咪唑六氟磷酸盐、1，2-二甲基-3-己基咪唑四氟硼酸盐、N-乙基吡啶六氟磷酸盐、N-乙基吡啶四氟硼酸盐、N-丁基吡啶六氟磷酸盐、N-丁基吡啶四氟硼酸盐、N-己基吡啶六氟磷酸盐和N-己基吡啶四氟硼酸盐中的任一种或多种。
本发明所述的一种含离子液体、改性纳米锌粉和石墨烯的润滑油组合物的制备方法，其特征在于润滑油组合物的制备过程中，所用的石墨烯是单层石墨烯、双层石墨烯、少层石墨烯(3-10层)中的任一种或多种。
本发明所述的一种含离子液体、改性纳米锌粉和石墨烯的润滑油组合物的制备方法，其特征在于润滑油组合物的制备过程中，所用的清净剂是石油磺酸钙、石油磺酸镁、硫磷化聚异丁烯钡盐、烷基水杨酸钙、环烷酸镁、环烷酸钙和硫化烷基酚钙中的任一种或多种。
本发明所述的一种含离子液体、改性纳米锌粉和石墨烯的润滑油组合物的制备方法，其特征在于润滑油组合物的制备过程中，所用的分散剂是单烯基丁二酰亚胺、双烯基丁二酰亚胺、多烯基丁二酰亚胺和聚异丁烯丁二酰亚胺中的任一种或多种。
本发明所述的一种含离子液体、改性纳米锌粉和石墨烯的润滑油组合物的制备方法，其特征在于润滑油组合物的制备过程中，所用的防腐剂是硫磷烷基酚锌盐、硫磷丁辛基锌盐、硫磷双辛基碱性锌盐和硫磷二烷基锌盐中的任一种或多种。
本发明所述的一种含离子液体、改性纳米锌粉和石墨烯的润滑油组合物的制备方法，其特征在于润滑油组合物的制备过程中，所用的极压抗磨剂是氯化石蜡、酸性亚磷酸二丁酯、磷酸三甲酚酯、硫代磷酸胺盐、异辛基酸性磷酸酯十八胺盐、硫化异丁烯、二苄基二硫化物、环烷酸铅、二丁基二硫代氨基甲酸钼、二丁基二硫代氨基甲酸锑、二丁基二硫代氨基甲酸铅和硼化油酰胺中的任一种或多种。
本发明所述的一种含离子液体、改性纳米锌粉和石墨烯的润滑油组合物的制备方法，其特征在于润滑油组合物的制备过程中，所用的油性剂是硫化鲸鱼油、油酸乙二醇酯、硫化棉籽油、苯并三氮唑脂肪酸胺盐、亚磷酸三苯脂、磷酸三乙酯、油酸丁酯、硬脂酸丁脂、苯二甲酸二辛酯和油酸中的任一种或多种。
本发明所述的一种含离子液体、改性纳米锌粉和石墨烯的润滑油组合物的制备方法，其特征在于润滑油组合物的制备过程中，所用的抗氧剂是2，6-二叔丁基对甲酚、4，4-亚甲基双(2，6-二叔丁基苯酚)、2，6-二叔丁基-α-二甲氨基对甲酚、N-苯基-α-萘胺、二丁基二硫化氨基甲酸锌和二酚基丙烷中的任一种或多种。
本发明所述的一种含离子液体、改性纳米锌粉和石墨烯的润滑油组合物的制备方法，其特征在于润滑油组合物的制备过程中，所用的粘度指数改进剂是聚乙烯基正丁基醚、聚甲基丙烯酸酯、聚异丁烯、聚丙烯酸酯、丁二酰亚胺乙丙共聚物和苯乙烯-双烯共聚物中的任一种或多种。
本发明所述的一种含离子液体、改性纳米锌粉和石墨烯的润滑油组合物的制备方法，其特征在于润滑油组合物的制备过程中，所用的防锈剂是石油磺酸钡、石油磺酸钠、环烷酸锌、二壬基萘磺酸钡、苯并三氮唑、合成磺酸镁、烷基磷酸咪唑啉盐、羊毛脂镁皂、失水山梨糖醇单油酸酯、油酸三乙醇胺酯、磺化蓖麻油和羊毛脂中的任一种或多种。
本发明所述的一种含离子液体、改性纳米锌粉和石墨烯的润滑油组合物的制备方法，其特征在于润滑油组合物的制备过程中，所用的降凝剂是聚丙烯酸酯、聚α-烯烃和烷基萘中的任一种或多种。
本发明所述的一种含离子液体、改性纳米锌粉和石墨烯的润滑油组合物的制备方法，其特征在于润滑油组合物的制备过程中，所用的抗泡剂是二甲基硅油、丙烯酸酯与乙烯基醚共聚物和蓖麻油聚氧乙烯醚中的任一种或多种。
本发明所述的一种含离子液体、改性纳米锌粉和石墨烯的润滑油组合物的制备方法，其特征在于润滑油组合物的制备过程中，所用的超声波分散器的频率为20kHz～1MHz、功率为30W～15kW。
具体实施方式
下面是本发明所述的一种含离子液体、改性纳米锌粉和石墨烯的润滑油组合物的制备方法的非限定性实例。这些实例的给出仅仅是为了说明的目的，并不能理解为对本发明的限定。因为在不脱离本发明的精神和范围的基础上，可以对本发明进行许多变换。在这些实施例中，除非特别说明，所有的百分比都是指质量百分比。
实施例1
改性纳米锌粉的制备：
按照上述质量百分比，依次将叔丁基硫醇、十八烷基硫醇、十八烷基二甲基苄基氯化铵、十二烷基三甲基氯化铵、4-羟基苯并三氮唑、苯并三氮唑、乙二胺四乙酸二钠盐和酒石酸钠加入去离子水中，在频率为24kHz、功率为3kW的超声波分散作用下，搅拌0.4h后，再加入纳米锌粉，进一步在频率为24kHz、功率为3kW的超声波分散作用下，搅拌4.5h，然后经离心分离、去离子水洗涤、离心分离、真空干燥、研磨和过筛工艺过程得到改性纳米锌粉，制得的改性纳米锌粉备用；
润滑油组合物的制备：
按照上述质量百分比，依次将1-甲基-3-丁基咪唑六氟磷酸盐、改性纳米锌粉、双层石墨烯、石油磺酸钙、单烯基丁二酰亚胺、硫磷烷基酚锌盐、酸性亚磷酸二丁酯、油酸乙二醇酯、2，6-二叔丁基对甲酚、聚乙烯基正丁基醚、石油磺酸钡、聚丙烯酸酯、二甲基硅油和基础油混合并搅拌均匀，即可制备得到含离子液体、改性纳米锌粉和石墨烯的润滑油组合物。
实施例2
改性纳米锌粉的制备：
按照上述质量百分比，依次将正丁基硫醇、苯乙基硫醇、十二烷基三甲基溴化铵、十四烷基二甲基吡啶溴化铵、十六烷基二甲基苄基溴化铵、甲基苯并三氮唑、柠檬酸钠和酒石酸钾加入去离子水中，在频率为28kHz、功率为5kW的超声波分散作用下，搅拌0.4h后，再加入纳米锌粉，进一步在频率为28kHz、功率为5kW的超声波分散作用下，搅拌3.0h，然后经离心分离、去离子水洗涤、离心分离、真空干燥、研磨和过筛工艺过程得到改性纳米锌粉，制得的改性纳米锌粉备用；
润滑油组合物的制备：
按照上述质量百分比，依次将1-甲基-3-丁基咪唑四氟硼酸盐、改性纳米锌粉、单层石墨烯、硫磷化聚异丁烯钡盐、双烯基丁二酰亚胺、硫磷丁辛基锌盐、磷酸三甲酚酯、硫化棉籽油、二酚基丙烷、聚甲基丙烯酸酯、环烷酸锌、聚α-烯烃、丙烯酸酯与乙烯基醚共聚物和基础油混合并搅拌均匀，即可制备得到含离子液体、改性纳米锌粉和石墨烯的润滑油组合物。
实施例3
改性纳米锌粉的制备：
按照上述质量百分比，依次将正十二烷基硫醇、正戊基硫醇、十二烷基二甲基苄基氯化铵、十八烷基三甲基溴化铵、N-羟基苯并三氮唑、苯并三氮唑、乙二胺四乙酸二钠盐和柠檬酸钾加入去离子水中，在频率为38kHz、功率为8kW的超声波分散作用下，搅拌0.3h后，再加入纳米锌粉，进一步在频率为38kHz、功率为8kW的超声波分散作用下，搅拌2.5h，然后经离心分离、去离子水洗涤、离心分离、真空干燥、研磨和过筛工艺过程得到改性纳米锌粉，制得的改性纳米锌粉备用；
润滑油组合物的制备：
按照上述质量百分比，依次将N-丁基吡啶六氟磷酸盐、改性纳米锌粉、少层石墨烯、烷基水杨酸钙、多烯基丁二酰亚胺、硫磷双辛基碱性锌盐、异辛基酸性磷酸酯十八胺盐、硬脂酸丁脂、N-苯基-α-萘胺、聚异丁烯、二壬基萘磺酸钡、聚α-烯烃、蓖麻油聚氧乙烯醚和基础油混合并搅拌均匀，即可制备得到含离子液体、改性纳米锌粉和石墨烯的润滑油组合物。
实施例4
改性纳米锌粉的制备：
按照上述质量百分比，依次将正辛基硫醇、十四烷基硫醇、十四烷基三甲基溴化铵、十二烷基二甲基苄基溴化铵、1-羟基苯并三氮唑、苯并三氮唑、乙二胺四乙酸二钠盐和柠檬酸铵加入去离子水中，在频率为58kHz、功率为6kW的超声波分散作用下，搅拌0.6h后，再加入纳米锌粉，进一步在频率为58kHz、功率为6kW的超声波分散作用下，搅拌2.5h，然后经离心分离、去离子水洗涤、离心分离、真空干燥、研磨和过筛工艺过程得到改性纳米锌粉，制得的改性纳米锌粉备用；
润滑油组合物的制备：
按照上述质量百分比，依次将N-丁基吡啶四氟硼酸盐、改性纳米锌粉、双层石墨烯、少层石墨烯、烷基水杨酸钙、聚异丁烯丁二酰亚胺、硫磷二烷基锌盐、二苄基二硫化物、油酸丁酯、二丁基二硫化氨基甲酸锌、聚丙烯酸酯、羊毛脂镁皂、烷基萘、二甲基硅油和基础油混合并搅拌均匀，即可制备得到含离子液体、改性纳米锌粉和石墨烯的润滑油组合物。
实施例5
改性纳米锌粉的制备：
按照上述质量百分比，依次将十六烷基硫醇、苄基硫醇、正丁基硫醇、十四烷基三甲基氯化铵、十六烷基二甲基苄基氯化铵、5-羧基苯并三氮唑、苯并三氮唑、乙二胺四乙酸二钠盐和酒石酸铵加入去离子水中，在频率为40kHz、功率为3.5kW的超声波分散作用下，搅拌0.6h后，再加入纳米锌粉，进一步在频率为40kHz、功率为3.5kW的超声波分散作用下，搅拌4.0h，然后经离心分离、去离子水洗涤、离心分离、真空干燥、研磨和过筛工艺过程得到改性纳米锌粉，制得的改性纳米锌粉备用；
润滑油组合物的制备：
按照上述质量百分比，依次将1-甲基-3-丁基咪唑六氟磷酸盐、1，2-二甲基-3-丁基咪唑四氟硼酸盐、改性纳米锌粉、双层石墨烯、单层石墨烯、石油磺酸镁、单烯基丁二酰亚胺、硫磷二烷基锌盐、酸性亚磷酸二丁酯、二苄基二硫化物、苯并三氮唑脂肪酸胺盐、2，6-二叔丁基对甲酚、聚乙烯基正丁基醚、石油磺酸钡、失水山梨糖醇单油酸酯、聚α-烯烃、二甲基硅油和基础油混合并搅拌均匀，即可制备得到含离子液体、改性纳米锌粉和石墨烯的润滑油组合物。
实施例6
改性纳米锌粉的制备：
按照上述质量百分比，依次将叔十二烷基硫醇、正戊基硫醇、十八烷基二甲基苄基溴化铵、十六烷基三甲基氯化铵、苯并三氮唑、乙二胺四乙酸二钠盐和柠檬酸钾加入去离子水中，在频率为35kHz、功率为2kW的超声波分散作用下，搅拌0.5h后，再加入纳米锌粉，进一步在频率为35kHz、功率为2kW的超声波分散作用下，搅拌7.0h，然后经离心分离、去离子水洗涤、离心分离、真空干燥、研磨和过筛工艺过程得到改性纳米锌粉，制得的改性纳米锌粉备用；
润滑油组合物的制备：
按照上述质量百分比，依次将N-己基吡啶六氟磷酸盐、N-丁基吡啶六氟磷酸盐、1-甲基-3-己基咪唑六氟磷酸盐、改性纳米锌粉、双层石墨烯、单层石墨烯、环烷酸镁、双烯基丁二酰亚胺、硫磷烷基酚锌盐、硫磷二烷基锌盐、磷酸三甲酚酯、氯化石蜡、油酸丁酯、磷酸三丁酯、N-苯基-α-萘胺、二酚基丙烷、聚甲基丙烯酸酯、聚异丁烯、合成磺酸镁、烷基磷酸咪唑啉盐、聚α-烯烃、烷基萘、二甲基硅油、丙烯酸酯与乙烯基醚共聚物和基础油混合并搅拌均匀，即可制备得到含离子液体、改性纳米锌粉和石墨烯的润滑油组合物。
实施例7
改性纳米锌粉的制备：
按照上述质量百分比，依次将正辛基硫醇、正十二烷基硫醇、十六烷基硫醇、十八烷基三甲基氯化铵、十四烷基二甲基苄基氯化铵、十四烷基二甲基吡啶氯化铵、苯并三氮唑、4-羟基苯并三氮唑、乙二胺四乙酸二钠盐和酒石酸钾加入去离子水中，在频率为100kHz、功率为5.5kW的超声波分散作用下，搅拌0.3h后，再加入纳米锌粉，进一步在频率为100kHz、功率为5.5kW的超声波分散作用下，搅拌2.5h，然后经离心分离、去离子水洗涤、离心分离、真空干燥、研磨和过筛工艺过程得到改性纳米锌粉，制得的改性纳米锌粉备用；
润滑油组合物的制备：
按照上述质量百分比，依次将N-己基吡啶四氟硼酸盐、改性纳米锌粉、单层石墨烯、双层石墨烯、少层石墨烯、环烷酸钙、硫化烷基酚钙、多烯基丁二酰亚胺、硫磷丁辛基锌盐、异辛基酸性磷酸酯十八胺盐、二丁基二硫代氨基甲酸锑、邻苯二甲酸二辛酯、油酸、2，6-二叔丁基-α-二甲氨基对甲酚、聚甲基丙烯酸酯、苯乙烯-双烯共聚物、油酸三乙醇胺酯、二壬基萘磺酸钡、烷基萘、蓖麻油聚氧乙烯醚和基础油混合并搅拌均匀，即可制备得到含离子液体、改性纳米锌粉和石墨烯的润滑油组合物。
实施例8
改性纳米锌粉的制备：
按照上述质量百分比，依次将正丁基硫醇、正辛基硫醇、十八烷基硫醇、十二烷基三甲基氯化铵、十四烷基二甲基苄基溴化铵、十六烷基三甲基溴化铵、甲基苯并三氮唑、1-羟基苯并三氮唑、乙二胺四乙酸二钠盐和柠檬酸铵加入去离子水中，在频率为45kHz、功率为3.5kW的超声波分散作用下，搅拌0.5h后，再加入纳米锌粉，进一步在频率为45kHz、功率为3.5kW的超声波分散作用下，搅拌5.5h，然后经离心分离、去离子水洗涤、离心分离、真空干燥、研磨和过筛工艺过程得到改性纳米锌粉，制得的改性纳米锌粉备用；
润滑油组合物的制备：
按照上述质量百分比，依次将1-甲基-3-乙基咪唑六氟磷酸盐、1-甲基-3-己基咪唑四氟硼酸盐、改性纳米锌粉、单层石墨烯、双层石墨烯、少层石墨烯、硫磷化聚异丁烯钡盐、环烷酸镁、单烯基丁二酰亚胺、双烯基丁二酰亚胺、硫磷双辛基碱性锌盐、二丁基二硫代氨基甲酸钼、亚磷酸三苯脂、油酸乙二醇酯、二丁基二硫化氨基甲酸锌、丁二酰亚胺乙丙共聚物、磺化蓖麻油、苯并三氮唑、聚丙烯酸酯、二甲基硅油、丙烯酸酯与乙烯基醚共聚物和基础油混合并搅拌均匀，即制得含离子液体、改性纳米锌粉和石墨烯的润滑油组合物。
Claims (1)
1.一种含离子液体、改性纳米锌粉和石墨烯的润滑油组合物的制备方法，其特征在于含离子液体、改性纳米锌粉和石墨烯的润滑油组合物的制备按照如下质量百分比：
依次将N-己基吡啶四氟硼酸盐、改性纳米锌粉、单层石墨烯、双层石墨烯、少层石墨烯、环烷酸钙、硫化烷基酚钙、多烯基丁二酰亚胺、硫磷丁辛基锌盐、异辛基酸性磷酸酯十八胺盐、二丁基二硫代氨基甲酸锑、邻苯二甲酸二辛酯、油酸、2，6-二叔丁基-α-二甲氨基对甲酚、聚甲基丙烯酸酯、苯乙烯-双烯共聚物、油酸三乙醇胺酯、二壬基萘磺酸钡、烷基萘、蓖麻油聚氧乙烯醚和基础油混合并搅拌均匀，即制备得到含离子液体、改性纳米锌粉和石墨烯的润滑油组合物；
其中，改性纳米锌粉的制备按照如下质量百分比：
依次将正辛基硫醇、正十二烷基硫醇、十六烷基硫醇、十八烷基三甲基氯化铵、十四烷基二甲基苄基氯化铵、十四烷基二甲基吡啶氯化铵、苯并三氮唑、4-羟基苯并三氮唑、乙二胺四乙酸二钠盐和酒石酸钾加入去离子水中，在频率为100kHz、功率为5.5kW的超声波分散作用下，搅拌0.3h后，再加入纳米锌粉，进一步在频率为100kHz、功率为5.5kW的超声波分散作用下，搅拌2.5h，然后经离心分离、去离子水洗涤、离心分离、真空干燥、研磨和过筛工艺过程，即制备得到改性纳米锌粉。