CN104830119A - 一种环保涂料 - Google Patents
一种环保涂料 Download PDFInfo
- Publication number
- CN104830119A CN104830119A CN201510227150.0A CN201510227150A CN104830119A CN 104830119 A CN104830119 A CN 104830119A CN 201510227150 A CN201510227150 A CN 201510227150A CN 104830119 A CN104830119 A CN 104830119A
- Authority
- CN
- China
- Prior art keywords
- parts
- byk
- environment
- water
- ethanol
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种环保涂料,包括水性环氧酯树脂45-50份;聚醋酸乙烯酯5-10份;聚醚改性硅氧烷8-10份;封端的多异氰酸酯化合物1-3份;二缩三丙二醇二丙烯酸酯10-12份;云母粉2-6份;钦白粉8-10份;磷酸锌4-9份;乙醇3-7份;流平剂1-2份;BYK-180 0.2-0.5份;BYK-025 0.2-0.5份;pH调节剂0.5-3份;去离子水15-20份。本发明所述配方制备得到的环保涂料具有良好的耐油性,耐水性,涂层附着力好,韧性好,防腐性能优异,VOC含量低,节约大量有机溶剂,可有效减少对环境的污染,属于环境友好型涂料。
Description
技术领域
本发明涉及一种涂料,尤其是涉及到一种环保涂料,属于化工技术领域。
背景技术
车间底漆是钢板表面处理后涂刷的第一道油漆,也可称作预处理底漆或保养底漆,主要为了保护钢板在焊接、切割、火工校正等加工过程中少受大气腐蚀。目前主要采用溶剂型防腐底漆,溶剂型防腐底漆中含有大量的有机挥发物(voc),对大气会造成污染,不符合当前环境保护的要求。同时,大量的有机挥发物也对生产和施工人员的身体健康造成相当大的危害。涂料的水性化是目前降低voc排放量的有效方法,也是未来发展的趋势。
水性底漆以水作为溶剂,无毒,无溶剂气味,比溶剂性底漆更环保,由水性树脂、水、颜料及助剂制备而成,其中研究的关键是水性树脂,经过几十年的发展,目前主要的水性树脂体系有水性醇酸、水性丙烯酸、水性环氧、水性聚氨酷树脂、水性无机硅酸盐、水性氟树脂以及它们的改性树脂。
发明内容
为了克服现有技术问题,本发明的目的在于提供一种具有良好的耐油性,耐酸碱性,柔韧性,附着力,防腐蚀性能的环保涂料。
为解决上述技术问题,本发明采用的技术方案为:
一种环保涂料,其特征在于,包括以下组分且各组分重量份数比为:
水性环氧酯树脂 45-50份;
聚醋酸乙烯酯 5-10份;
聚醚改性硅氧烷 8-10份;
封端的多异氰酸酯化合物 1-3份;
二缩三丙二醇二丙烯酸酯 10-12份;
云母粉 2-6份;
钦白粉 8-10份;
磷酸锌 4-9份;
乙醇 3-7份;
流平剂 1-2份;
BYK-180 0.2-0.5份;
BYK-025 0.2-0.5份;
pH调节剂 0.5-3份;
去离子水 15-20份。
进一步优选,所述的环保涂料,包括以下组分且各组分重量份数比为:
水性环氧酯树脂 45份;
聚醋酸乙烯酯 6份;
聚醚改性硅氧烷 10份;
封端的多异氰酸酯化合物 2份;
二缩三丙二醇二丙烯酸酯 11份;
云母粉 4份;
钦白粉 9份;
磷酸锌 6份;
乙醇 5份;
流平剂 2份;
BYK-180 0.4份;
BYK-025 0.3份;
pH调节剂 1份;
去离子水 16份。
且所述的乙醇的浓度为95%。
本发明的有益效果为:本发明所述配方制备得到的环保涂料具有良好的耐油性,耐水性,涂层附着力好,韧性好,防腐性能优异,VOC含量低,节约大量有机溶剂,可有效减少对环境的污染,属于环境友好型涂料。
具体实施方式
下面结合具体实施例详细说明本发明。
实施例1:
将水性环氧酯树脂45份;聚醋酸乙烯酯6份;聚醚改性硅氧烷10份;封端的多异氰酸酯化合物2份;二缩三丙二醇二丙烯酸酯11份;云母粉4份;钦白粉9份;磷酸锌6份;乙醇5份;流平剂2份;BYK-180 0.4份; BYK-025 0.3份;pH调节剂1份;去离子水16份加入到分散机中高速分散30min,最终制备得到环保涂料。
实施例2:
将水性环氧酯树脂50份;聚醋酸乙烯酯8份;聚醚改性硅氧烷9份;封端的多异氰酸酯化合物1份;二缩三丙二醇二丙烯酸酯11份;云母粉6份;钦白粉9份;磷酸锌7份;乙醇7份;流平剂2份;BYK-180 0.4份; BYK-025 0.5份;pH调节剂1份;去离子水19份加入到分散机中高速分散60min,最终制备得到环保涂料。
实施例3:
将水性环氧酯树脂48份;聚醋酸乙烯酯10份;聚醚改性硅氧烷8份;封端的多异氰酸酯化合物3份;二缩三丙二醇二丙烯酸酯10份;云母粉2份;钦白粉10份;磷酸锌9份;乙醇3份;流平剂1份;BYK-180 0.2份; BYK-025 0.2份;pH调节剂3份;去离子水18份加入到分散机中高速分散45min,最终制备得到环保涂料。
本发明按照上述实施例进行了说明应当理解,上述实施例不以任何形式限定本发明,凡采用等同替换或等效变换方式所获得的技术方案,均落在本发明的保护范围之内。
Claims (3)
1. 一种环保涂料,其特征在于,包括以下组分且各组分重量份数比为:
水性环氧酯树脂 45-50份;
聚醋酸乙烯酯 5-10份;
聚醚改性硅氧烷 8-10份;
封端的多异氰酸酯化合物 1-3份;
二缩三丙二醇二丙烯酸酯 10-12份;
云母粉 2-6份;
钦白粉 8-10份;
磷酸锌 4-9份;
乙醇 3-7份;
流平剂 1-2份;
BYK-180 0.2-0.5份;
BYK-025 0.2-0.5份;
pH调节剂 0.5-3份;
去离子水 15-20份。
2.根据权利要求1所述的一种环保涂料,其特征在于,包括以下组分且各组分重量份数比为:
水性环氧酯树脂 45份;
聚醋酸乙烯酯 6份;
聚醚改性硅氧烷 10份;
封端的多异氰酸酯化合物 2份;
二缩三丙二醇二丙烯酸酯 11份;
云母粉 4份;
钦白粉 9份;
磷酸锌 6份;
乙醇 5份;
流平剂 2份;
BYK-180 0.4份;
BYK-025 0.3份;
pH调节剂 1份;
去离子水 16份。
3.根据权利要求1或2所述的一种环保涂料,其特征在于,所述的乙醇的浓度为95%。