CN104829871A - 一种白炭黑分散剂及其制备方法 - Google Patents

一种白炭黑分散剂及其制备方法 Download PDF

Info

Publication number
CN104829871A
CN104829871A CN201510181585.6A CN201510181585A CN104829871A CN 104829871 A CN104829871 A CN 104829871A CN 201510181585 A CN201510181585 A CN 201510181585A CN 104829871 A CN104829871 A CN 104829871A
Authority
CN
China
Prior art keywords
carbon black
white carbon
acid
lipid acid
black dispersant
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201510181585.6A
Other languages
English (en)
Other versions
CN104829871B (zh
Inventor
储云仙
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
YIXING JUJINXIN CHEMICAL CO Ltd
Original Assignee
YIXING JUJINXIN CHEMICAL CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by YIXING JUJINXIN CHEMICAL CO Ltd filed Critical YIXING JUJINXIN CHEMICAL CO Ltd
Priority to CN201510181585.6A priority Critical patent/CN104829871B/zh
Publication of CN104829871A publication Critical patent/CN104829871A/zh
Application granted granted Critical
Publication of CN104829871B publication Critical patent/CN104829871B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种白炭黑分散剂，包括下列重量百分比的原料：碳16～碳18脂肪酸40-65％，脂肪酸锌皂10-20％，无机填料20-40％，活性剂2-4％。本发明还公开了一种白炭黑分散剂制备方法。该白炭黑分散剂制备方法简单，安全可靠，能显著改善白炭黑在胶料中的分散，提高橡胶的物理性能。

Description

一种白炭黑分散剂及其制备方法
技术领域
本发明涉及分散剂领域，具体涉及一种橡胶用白炭黑分散剂及其制备方法。
背景技术
近年来随着“绿色轮胎”的出现和推广，白炭黑在轮胎中的应用得到了大幅度提高，在轮胎胶料中白炭黑部分或全部代替炭黑可有效降低轮胎阻力，同时能提高胎面的抗刺扎、抗崩裂和抗湿滑等性能，白炭黑虽然使胶料具有良好的使用性，但与烃类橡胶分子的相溶性低，加工性能差，究其原因，白炭黑虽然颗粒细、补强效果好，但在练胶过程中容易产生不同程度的自聚结团倾向，而且白炭黑主要来源于大量存在与表面的活性基团，这些基团的表面活性大，倾向于彼此聚集，导致难以分散，因此研究有针对性、效果好的白炭黑分散剂对于白炭黑在橡胶领域的应用意义重大。
发明内容
发明目的：本发明的目的在与提供一种能有效降低混炼能耗、硫化速度快、物理性能稳定的白炭黑分散剂。
技术方案：一种白炭黑分散剂，其特征在于包括下列重量百分比的原料：碳16～碳18脂肪酸40-65％，脂肪酸锌皂10-20％，无机填料20-40％，活性剂2-4％。
优选的，一种白炭黑分散剂，包括下列重量百分比的原料：碳16～碳18脂肪酸45-65％，脂肪酸锌皂15-20％，无机填料20-35％，活性剂3％。
所述的碳16～碳18脂肪酸选自棕榈酸、油酸、亚油酸、牛羊油脂肪酸、大豆油脂肪酸、花生油脂肪酸、月桂酸、氯丁酸中的一种或多种。
所述的活性剂采用多元醇或碱式碳酸盐。
所述的无机填料为碳酸钙、滑石粉、海泡石中的一种或多种。
所述的白炭黑分散剂的制备方法，其特征在于，包括：将计量后的碳16～碳18脂肪酸投置在反应釜中，加热至100℃充分熔融，搅拌15-20分钟，加入脂肪酸锌皂、无机填料和活性剂后加热至150℃恒温，每隔40分钟搅拌3-5分钟直至全部混合均匀，将混合物料自然冷却后得到所述白炭黑分散剂。
有益效果：本发明所述的白炭黑分散剂，可快速降低门尼粘度，缩短混炼时间，提高胶料挤出速度，明显改善胶料的加工性能，尤其是使填充白炭黑的载重子午线轮胎胎面胶易于加工；能加快硫化速度，显著改善白炭黑在胶料中的分散度，提高橡胶的物理性能；工艺简单，安全可靠，有利于大规模生产。
具体实施方式
实施例1：
一种白炭黑分散剂，其特征在于包括下列重量百分比的原料：碳18脂肪酸65％，脂肪酸锌皂10％，无机填料23％，活性剂2％；碳18脂肪酸为棕榈酸；所述的活性剂采用碱式碳酸盐；所述的无机填料为碳酸钙。
该白炭黑分散剂的制备方法，将计量后的碳18脂肪酸投置在反应釜中，加热至100℃充分熔融，搅拌15分钟，加入脂肪酸锌皂、无机填料和活性剂后加热至150℃恒温，每隔40分钟搅拌3分钟直至全部混合均匀，将混合物料自然冷却后得到所述白炭黑分散剂。
实施例2：
一种白炭黑分散剂，包括下列重量百分比的原料：碳16脂肪酸40，脂肪酸锌皂20％，无机填料38％，活性剂2％；所述的碳16脂肪酸为牛羊油脂肪酸；所述的活性剂采用多元醇；所述的无机填料为滑石粉。
上述的白炭黑分散剂的制备方法，将计量后的碳16脂肪酸投置在反应釜中，加热至100℃充分熔融，搅拌20分钟，加入脂肪酸锌皂、无机填料和活性剂后加热至150℃恒温，每隔40分钟搅拌5分钟直至全部混合均匀，将混合物料自然冷却后得到所述白炭黑分散剂。
实施例3：
一种白炭黑分散剂，包括下列重量百分比的原料：花生油脂肪酸50％，脂肪酸锌皂15％，海泡石31％，碱式碳酸盐4％。
上述白炭黑分散剂的制备方法，将计量后的花生油脂肪酸投置在反应釜中，加热至100℃充分熔融，搅拌18分钟，加入脂肪酸锌皂、海泡石和碱式碳酸盐后加热至150℃恒温，每隔40分钟搅拌4分钟直至全部混合均匀，将混合物料自然冷却后得到所述白炭黑分散剂。
实施例4：
一种白炭黑分散剂，包括下列重量百分比的原料：亚油酸23％，月桂酸31％，脂肪酸锌皂13％，滑石粉30％，多元醇3％。
上述白炭黑分散剂的制备方法：将计量后的亚油酸、月桂酸投置在反应釜中，加热至100℃充分熔融，搅拌15分钟，加入脂肪酸锌皂、滑石粉和多元醇后加热至150℃恒温，每隔40分钟搅拌5分钟直至全部混合均匀，将混合物料自然冷却后得到所述白炭黑分散剂。

Claims (6)

1.一种白炭黑分散剂，其特征在于：包括下列重量百分比的原料：碳16～碳18脂肪酸40-65％，脂肪酸锌皂10-20％，无机填料20-40％，活性剂2-4％。
2.根据权利要求1所述的白炭黑分散剂，其特征在于：包括下列重量百分比的原料：碳16～碳18脂肪酸45-65％，脂肪酸锌皂15-20％，无机填料20-25％，活性剂3％。
3.根据权利要求1所述的白炭黑分散剂，其特征在于：所述的碳16～碳18脂肪酸选自棕榈酸、油酸、亚油酸、牛羊油脂肪酸、大豆油脂肪酸、花生油脂肪酸、月桂酸、氯丁酸中的一种或多种。
4.根据权利要求1所述的白炭黑分散剂，其特征在于：所述的活性剂采用多元醇或碱式碳酸盐。
5.根据权利要求1所述的白炭黑分散剂，其特征在于：所述的无机填料为碳酸钙、滑石粉、海泡石中的一种或多种。
6.一种根据权利要求1所述的白炭黑分散剂的制备方法，其特征在于：包括：将计量后的碳16～碳18脂肪酸投置在反应釜中，加热至100℃充分熔融，搅拌15-20分钟，加入脂肪酸锌皂、无机填料和活性剂后加热至150℃恒温，每隔40分钟搅拌3-5分钟直至全部混合均匀，将混合物料自然冷却后得到所述白炭黑分散剂。
CN201510181585.6A 2015-04-16 2015-04-16 一种白炭黑分散剂及其制备方法 Active CN104829871B (zh)