CN104745282A - 一种生丝高防锈切削液 - Google Patents

一种生丝高防锈切削液 Download PDF

Info

Publication number
CN104745282A
CN104745282A CN201510168979.8A CN201510168979A CN104745282A CN 104745282 A CN104745282 A CN 104745282A CN 201510168979 A CN201510168979 A CN 201510168979A CN 104745282 A CN104745282 A CN 104745282A
Authority
CN
China
Prior art keywords
parts
minute
add
raw silk
deionized water
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510168979.8A
Other languages
English (en)
Inventor
王贵东
宋睿
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Hefei Ring Macromolecular Material Factory
Original Assignee
Hefei Ring Macromolecular Material Factory
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Hefei Ring Macromolecular Material Factory filed Critical Hefei Ring Macromolecular Material Factory
Priority to CN201510168979.8A priority Critical patent/CN104745282A/zh
Publication of CN104745282A publication Critical patent/CN104745282A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种生丝高防锈切削液，它是由下述重量份的原料组成的：烷基糖苷1-2、椰油酰胺丙基甜菜碱0.6-1、十二烯基丁二酸4-5、苯甲酸钠2-3、聚磷酸铵0.2-0.3、叔丁基对二苯酚0.5-1、甲酰胺0.3-0.5、醋酸亚铁0.1-0.2、聚乙二醇二缩水甘油醚5-7、生丝8-10、聚马来酸酐10-16、去离子水160-200。本发明丝素乳液以蚕丝为主料，无毒无污染，润滑性高，用聚乙二醇二缩水甘油醚进行改性，可以提高乳液形成膜的柔性、亲水性、稳定性，防锈液a中的十二烯基丁二酸具有很好的防锈功效，最后加入的聚马来酸酐可以附着在膜的表面，不仅加固膜，还隔绝了空气，起到进一步的防锈作用。

Description

一种生丝高防锈切削液
技术领域
本发明主要涉及切削液领域，尤其涉及一种生丝高防锈切削液。
背景技术
切削液是一种用在金属切削、磨加工过程中，用来冷却和润滑刀具和加工件的工业用液体，切削液由多种超强功能助剂经科学复合配合而成，同时具备良好的冷却性能、润滑性能、防锈性能、除油清洗功能、防腐功能、易稀释特点。克服了传统皂基乳化液夏天易臭、冬天难稀释、防锈效果差的的毛病，对车床漆也无不良影响，适用于黑色金属的切削及磨加工，属当前最领先的磨削产品。
为减少金属在加工过程中因磨损带来的损失，各生产企业对金属切削液的性能要求越来越高；同时，由于国家对环境保护的重视，提出了清洁生产、节能减排等要求，促使金属切削液朝着环保、节能、高效的方向发展.全合成切削液具有清洁环保、资源广阔、易制备等优点，是今后金属加工液的重点发展方向。
发明内容
本发明目的就是提供一种生丝高防锈切削液。
本发明是通过以下技术方案实现的：
一种生丝高防锈切削液，它是由下述重量份的原料组成的：
烷基糖苷1-2、椰油酰胺丙基甜菜碱0.6-1、十二烯基丁二酸4-5、苯甲酸钠2-3、聚磷酸铵0.2-0.3、叔丁基对二苯酚0.5-1、甲酰胺0.3-0.5、醋酸亚铁0.1-0.2、聚乙二醇二缩水甘油醚5-7、生丝8-10、聚马来酸酐10-16、去离子水160-200。
一种生丝高防锈切削液的制备方法，包括以下步骤：
(1)将上述生丝加入到其重量90-100倍的0.4-0.6wt％的碳酸钠溶液中，在98-100℃下保温浸泡60-80分钟，过滤，烘干，磨成细粉，与烷基糖苷、甲酰胺混合，加入上述去离子水重量的60-70％，搅拌均匀，加入聚乙二醇二缩水甘油醚，混合超声30-35分钟，得丝素乳液；
(2)将十二烯基丁二酸与醋酸亚铁混合，搅拌均匀后加入剩余去离子水重量的50-60％，加入椰油酰胺丙基甜菜碱、60-100转/分搅拌分散4-5分钟，得防锈液a；
(3)将聚马来酸酐加入到剩余的去离子水中，与防锈液a、丝素乳液混合，60-70℃下保温静置30-40分钟，得防锈共混乳液；
(4)将上述防锈共混乳液与聚磷酸铵、苯甲酸钠混合，70-100转/分搅拌分散14-20分钟，加入剩余各原料，700-800转/分搅拌分散20-30分钟，即得所述切削液。
本发明的优点是：
本发明丝素乳液以蚕丝为主料，无毒无污染，润滑性高，用聚乙二醇二缩水甘油醚进行改性，可以提高乳液形成膜的柔性、亲水性、稳定性，防锈液a中的十二烯基丁二酸具有很好的防锈功效，最后加入的聚马来酸酐可以附着在膜的表面，不仅加固膜，还隔绝了空气，起到进一步的防锈作用。
具体实施方式
实施例1：
一种生丝高防锈切削液，它是由下述重量份的原料组成的：
烷基糖苷1、椰油酰胺丙基甜菜碱0.6、十二烯基丁二酸5、苯甲酸钠3、聚磷酸铵0.3、叔丁基对二苯酚0.5、甲酰胺0.5、醋酸亚铁0.2、聚乙二醇二缩水甘油醚7、生丝10、聚马来酸酐16、去离子水200。
一种生丝高防锈切削液的制备方法，包括以下步骤：
(1)将上述生丝加入到其重量100倍的0.6wt％的碳酸钠溶液中，在100℃下保温浸泡80分钟，过滤，烘干，磨成细粉，与烷基糖苷、甲酰胺混合，加入上述去离子水重量的60％，搅拌均匀，加入聚乙二醇二缩水甘油醚，混合超声35分钟，得丝素乳液；
(2)将十二烯基丁二酸与醋酸亚铁混合，搅拌均匀后加入剩余去离子水重量的60％，加入椰油酰胺丙基甜菜碱、100转/分搅拌分散4-5分钟，得防锈液a；
(3)将聚马来酸酐加入到剩余的去离子水中，与防锈液a、丝素乳液混合，60℃下保温静置40分钟，得防锈共混乳液；
(4)将上述防锈共混乳液与聚磷酸铵、苯甲酸钠混合，100转/分搅拌分散20分钟，加入剩余各原料，800转/分搅拌分散30分钟，即得所述切削液。
性能测试：

Claims (2)

1.一种生丝高防锈切削液，其特征在于它是由下述重量份的原料组成的：
烷基糖苷1-2、椰油酰胺丙基甜菜碱0.6-1、十二烯基丁二酸4-5、苯甲酸钠2-3、聚磷酸铵0.2-0.3、叔丁基对二苯酚0.5-1、甲酰胺0.3-0.5、醋酸亚铁0.1-0.2、聚乙二醇二缩水甘油醚5-7、生丝8-10、聚马来酸酐10-16、去离子水160-200。
2.一种如权利要求1所述的生丝高防锈切削液的制备方法，其特征在于包括以下步骤：
（1）将上述生丝加入到其重量90-100倍的0.4-0.6wt%的碳酸钠溶液中，在98-100℃下保温浸泡60-80分钟，过滤，烘干，磨成细粉，与烷基糖苷、甲酰胺混合，加入上述去离子水重量的60-70%，搅拌均匀，加入聚乙二醇二缩水甘油醚，混合超声30-35分钟，得丝素乳液；
（2）将十二烯基丁二酸与醋酸亚铁混合，搅拌均匀后加入剩余去离子水重量的50-60%，加入椰油酰胺丙基甜菜碱、60-100转/分搅拌分散4-5分钟，得防锈液a；
（3）将聚马来酸酐加入到剩余的去离子水中，与防锈液a、丝素乳液混合，60-70℃下保温静置30-40分钟，得防锈共混乳液；
（4）将上述防锈共混乳液与聚磷酸铵、苯甲酸钠混合，70-100转/分搅拌分散14-20分钟，加入剩余各原料，700-800转/分搅拌分散20-30分钟，即得所述切削液。
CN201510168979.8A 2015-04-10 2015-04-10 一种生丝高防锈切削液 Pending CN104745282A (zh)