CN104745035A - Simulative sand-containing multicolor paint as well as preparation method and applying method thereof - Google Patents
Simulative sand-containing multicolor paint as well as preparation method and applying method thereof Download PDFInfo
- Publication number
- CN104745035A CN104745035A CN201510121833.8A CN201510121833A CN104745035A CN 104745035 A CN104745035 A CN 104745035A CN 201510121833 A CN201510121833 A CN 201510121833A CN 104745035 A CN104745035 A CN 104745035A
- Authority
- CN
- China
- Prior art keywords
- parts
- emulation
- paint
- water
- sand
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention belongs to the technical field of paint and in particular relates to simulative sand-containing multicolor paint as well as a preparation method and applying method thereof. The paint comprises 150-250 parts of emulsion, 10-15 parts of anti-freezing agent, 13-18 parts of film-forming additive, 0.5-1.5 parts of antifoaming agent, 1-2 parts of preservative, 2-3 parts of pH regulator, 600-700 parts of colored particle solution, 10-20 parts of thickening agent B and 90-160 parts of water by weight. The simulative sand-containing multicolor paint has the beneficial effects that the simulative sand-containing multicolor paint is water-based environment-friendly granite-like paint, not only can be prepared in random colors to achieve the effects of most natural granite and has degree of simulation as high as 90-95% but also is low in cost, is safe to use and convenient to construct, is simple in flow and can be used in construction of concave-convex surfaces compared with natural granite; the simulative sand-containing multicolor paint has higher degree of simulation and better texture than ordinary multicolor paint.
Description
Technical field
The invention belongs to technical field of coatings, be specifically related to a kind of emulation being applicable to external wall and contain sand multicolor finish and preparation method thereof and method of application.
Background technology
The sense organ of exterior finish to building of building plays an important role, and the finishing material of present exterior wall mainly contains following several: emulsion paint, true mineral varnish, aluminium-plastic panel, clad aluminium, cement plate, ceramic tile, glass, stone material etc.Wherein, best with natural ornamental stone decorative effect, and durable and enjoy great popularity.But use natural ornamental stone to come with some shortcomings: natural granite, marmorean decorative pattern and color category are limited, and can have any different between different geographical; Natural granite, marble own wt are comparatively large, external wall uses and has the risk dropped; Lithotome is limited resources, day by day reduces, and overexploitation can damage environment.
Because people adopt the coating of natural-like stone to replace its decorative effect.Although current common multicolor finish on the market can be accomplished with natural granite effect close in color, its surface tactile sensation is larger with natural granite gap all the time.
Summary of the invention
In order to solve the problem, the object of the present invention is to provide a kind of emulation containing sand multicolor finish, on this coating paint exterior wall, not only color is close to the decorative effect of lithotome to make decorated body of wall, and texture is also close to the decorative effect of lithotome.
Two of object of the present invention there is provided the preparation method of described emulation containing sand multicolor finish.
Three of object of the present invention there is provided the method for application of described emulation containing sand multicolor finish.
The present invention is achieved through the following technical solutions:
A kind of emulation, containing sand multicolor finish, comprises the following raw material according to listed as parts by weight:
Wherein, described look grain solution is obtained by the following raw material according to listed as parts by weight:
7% insured's glue solution 400 ~ 500 parts
Colored paint 450 ~ 700 parts
20 ~ 40 parts, water
Described colored paint is the base paint mixture after at least three kinds of color toner; The red base paint of preferred tune 100 ~ 120 parts, adjust grey base paint 180 ~ 210 parts and adjust the mixture of yellow base paint 180 ~ 210 parts, more close with lithotome in such proportioning color.Insured's glue solution is water-soluble silicate compounds, preferred Ke Naiou: S-482, and its weight ratio is 7%, and Main Function is the independence of sematic color grain, makes it have the texture of lithotome.
Wherein said emulsion is organosilicon crylic acid latex, and preferred Ahmedabad is rich: 996AD.The preferred propylene glycol of antifreezing agent, the preferred alcohol ester 12 of film coalescence aid, the preferred mineral oil antifoam agent of defoamer, the preferred broad spectrum type sanitas of sanitas, the preferred AMP-95 of PH conditioning agent, thickening material B preferred hydrophobically-modified alkali swelling type thickening material, the preferred deionized water of water.
Preferably; the preparation method of described look grain solution is specially: first 7% insured's glue solution of described amount and colored paint are stirred 4 ~ 8 minutes under 250 ~ 350rpm; then 10 ~ 30 mesh sieves are crossed; finally the water of sieve gained granular mixture and described amount is stirred 4 ~ 8 minutes under 250 ~ 350rpm, obtained described look grain solution.
Preferably, described colored paint comprises the following raw material according to listed as parts by weight:
Base paint 700 ~ 850 parts
Aqueous color paste 1 ~ 100 part
Quartz sand 100 ~ 250 parts;
Wherein, described quartz sand is 150 ~ 200 orders, the preferred water-based rust slurry of aqueous color paste.
Wherein, the preparation method of described colored paint is: described base paint, aqueous color paste and quartz sand are stirred 8 ~ 15 minutes under 750 ~ 850rpm, obtained described colored paint.
Preferably, described base paint comprises the following raw material according to listed as parts by weight:
Described thickening material A is Mierocrystalline cellulose, the preferred propylene glycol of antifreezing agent, defoamer is mineral oil antifoam agent, dispersion agent is sodium salt dispersion agent, and sanitas is broad spectrum type sanitas, and titanium dioxide is Rutile type Titanium Dioxide, kaolin is calcined kaolin, thickening material A preferred Ke Naiou: HE-10K, the preferred golden fraternal chemical industry of linking agent: KP, mainly provides thixotropy; The preferred alcohol ester 12 of film coalescence aid, the preferred AMP-95 of pH adjusting agent, emulsion is that Ahmedabad is rich: 996AD.
Preferably, described 7% insured's glue solution by weight part be the water of 930 parts and the protecting glue of 70 parts stir under 450 ~ 550rpm 8 ~ 15 minutes modulation form.
Wherein, the preparation method of described base paint is:
First by the antifreezing agent of described amount, defoamer, dispersion agent, sanitas and 400 ~ 450 parts of water in, stir 3 ~ 8 minutes under 250 ~ 350rpm, obtained mixed solution;
Again the titanium dioxide of described amount, kaolin, thickening material A, the glutinous agent of friendship, film coalescence aid and PH conditioning agent and remaining 50 ~ 100 parts of water are joined in mixed solution one, stir 25 ~ 40 minutes under 1000 ~ 1500rpm;
Finally add 7% insured's glue solution and emulsion of described amount, stir 8 ~ 15 minutes under 600 ~ 1000rpm, obtained described base paint.
Prepare the method for described emulation containing sand multicolor finish, first the emulsion of described amount, antifreezing agent, film coalescence aid, defoamer, sanitas, PH conditioning agent and water are stirred 3 ~ 8 minutes under 700 ~ 1000rpm;
Add the look grain solution of described amount, thickening material B and water again, stir 3 ~ 8 minutes under 250 ~ 350rpm, obtained described emulation is containing sand multicolor finish;
Wherein said thickening material B is hydrophobically-modified alkali swelling type thickening material.
Preferably, described look grain solution and thickening material B need slowly add.
Described emulation is containing the method for application of sand multicolor finish, concrete:
Step one, batch scrape exterior wall putty one time, dry 5 ~ 8 days;
Step 2, roller coating or spraying exterior wall seal coat one time, dry 5 ~ 8 hours;
Step 3, roller coating or the real color bottom paint twice of spraying water-based, dry 5 ~ 8 hours;
Step 4, spray described emulation containing sand multicolor finish twice, dry 10 ~ 15 hours;
Step 5, spraying water-based finishing varnish one time, dry 5 ~ 8 hours; Apply complete.。
The present invention is aqueous, environmental protective artificial granite paint, not only arbitrarily can prepare the effect of color and most of natural granite, because adding quartz sand in formula, so fidelity can up to 90% ~ 95%, compared with natural granite low, the use safety of cost, easy construction, flow process simple, can construct at convex-concave surface; And fidelity is higher compared with common multicolor finish, texture is better.Adherence, hardness, weathering resistance etc. all show excellence.Promote the decorative effect of external wall and reduce use cost, replacing natural granite, marble, solving the shortcomings such as grouan high cost, poor stability, effect limitednumber; Meanwhile, compared with common multicolor finish, greatly promote surface tactile sensation and fidelity.
concrete embodiment
Below in conjunction with embodiment, the present invention is described in further detail, understands the present invention to help those skilled in the art.
Embodiment 1
A, 7% insured's glue solution preparation
930kg deionized water and 70kg protecting glue (Ke Naiou: S-482) 500rpm in stirrer are stirred 10 minutes, obtains described 7% insured's glue solution.
B, base paint are prepared
First deionized water 450kg, antifreezing agent 15kg, defoamer 3kg, dispersion agent 3kg and sanitas 3kg are placed in stirrer 300rpm and stir 5 minutes, obtain described base paint;
Drop into titanium dioxide 10kg, kaolin 70kg, thickening material A 4.5kg, linking agent 5kg, film coalescence aid 20kg, pH adjusting agent 1kg and water 75.5kg again, heighten stirring velocity and stir 30 minutes to 1200rpm;
Finally drop into 7% insured's glue solution 40kg and emulsion 300kg, 800rpm stir 15 minutes, obtain described base paint.
C, base paint are mixed colours
By the quartz sand 200kg of the base paint 790kg obtained, red aqueous color paste 10kg and 200 order sizes, stir 10 minutes in 800rpm, obtain adjusting red base paint;
By the quartz sand 200kg of the base paint 790kg, the grey aqueous color paste 10kg that obtain and 200 order sizes, stir 10 minutes in 800rpm, obtain adjusting grey base paint;
By the quartz sand 200kg of the base paint 790kg obtained, yellow aqueous color paste 10kg and 200 order sizes, stir 10 minutes in 800rpm, obtain adjusting yellow base paint.
D, look grain solution preparation
First by 7% insured's glue solution 460kg, adjust red base paint 110kg, adjust grey base paint 200kg and adjust yellow base paint 200kg, stir 5 minutes in 300rpm, then sieve mixture (10 order), becomes granular mixture after sieving; Finally add water 30kg, 300rpm stirs 5 minutes, obtained described look grain solution.
E, emulation are containing the preparation of sand multicolor finish
First by emulsion, (Ahmedabad is rich: 996AD) 200kg, antifreezing agent 13kg, film coalescence aid 15kg, defoamer 1kg, water 7kg, sanitas 1.5kg and pH adjusting agent 2.5kg, stir 5 minutes under 800rpm, then look grain solution 650kg, thickening material B 14.5kg is added and water 95.5kg, 300rpm stir 5 minutes.Obtain final finished emulation containing sand multicolor finish.
Embodiment 2
A, 7% insured's glue solution preparation
930kg deionized water and 70kg protecting glue (Ke Naiou: S-482) 450rpm in stirrer are stirred 8 minutes, obtains described 7% insured's glue solution.
B, base paint are prepared
First deionized water 500kg, antifreezing agent 10kg, defoamer 2kg, dispersion agent 2kg and sanitas 2kg are placed in stirrer 250rpm and stir 3 minutes, obtain described base paint;
Drop into titanium dioxide 8kg, kaolin 60kg, thickening material A 3kg, linking agent 3kg, film coalescence aid 10kg, pH adjusting agent 1kg and water 50kg again, heighten stirring velocity and stir 25 minutes to 1000rpm;
Finally drop into 7% insured's glue solution 30kg and emulsion 319kg, 600rpm stir 8 minutes, obtain described base paint.
C, base paint are mixed colours
By the quartz sand 200kg of the base paint 700kg obtained, red aqueous color paste 100kg and 150 order sizes, stir 8 minutes in 750rpm, obtain adjusting red base paint;
By the quartz sand 200kg of the base paint 790kg, the grey aqueous color paste 100kg that obtain and 150 order sizes, stir 8 minutes in 750rpm, obtain adjusting red base paint;
By the quartz sand 200kg of the base paint 790kg obtained, yellow aqueous color paste 100kg and 150 order sizes, stir 8 minutes in 750rpm, obtain adjusting red base paint.
D, look grain solution preparation
First by 7% insured's glue solution 400kg, adjust red base paint 130kg, adjust grey base paint 220kg and adjust yellow base paint 220kg, stir 10 minutes in 250rpm, then sieve mixture (10 order), becomes granular mixture after sieving; Finally add water 30kg, 250rpm stirs 4 minutes, obtained described look grain solution.
E, emulation are containing the preparation of sand multicolor finish
First by emulsion, (Ahmedabad is rich: 996AD) 150kg, antifreezing agent 15kg, film coalescence aid 18kg, defoamer 1.5kg, water 10kg, sanitas 2kg and pH adjusting agent 3kg, stir 3 minutes under 700rpm, then look grain solution 700kg, thickening material B 205kg is added and water 80.5kg, 250rpm stir 3 minutes.Obtain final finished emulation containing sand multicolor finish.
Embodiment 3
A, 7% insured's glue solution preparation
930kg deionized water and 70kg protecting glue (Ke Naiou: S-482) 550rpm in stirrer are stirred 15 minutes, obtains described 7% insured's glue solution.
B, base paint are prepared
First deionized water 400kg, antifreezing agent 20kg, defoamer 5kg, dispersion agent 5kg and sanitas 5kg are placed in stirrer 350rpm and stir 8 minutes, obtain described base paint;
Drop into titanium dioxide 15kg, kaolin 80kg, thickening material A 5kg, crosslinked 15kg, film coalescence aid 255kg, pH adjusting agent 1kg and water 100kg again, heighten stirring velocity and stir 40 minutes to 1500rpm;
Finally drop into 7% insured's glue solution 45kg and emulsion 289kg, 1000rpm stir 15 minutes, obtain described base paint.
C, base paint are mixed colours
By the quartz sand 250kg of the base paint 749kg obtained, red aqueous color paste 1kg and 200 order sizes, stir 15 minutes in 850rpm, obtain adjusting red base paint;
By the quartz sand 250kg of the base paint 749kg, the grey aqueous color paste 1kg that obtain and 200 order sizes, stir 15 minutes in 850rpm, obtain adjusting red base paint;
By the quartz sand 250kg of the base paint 749kg obtained, yellow aqueous color paste 1kg and 200 order sizes, stir 15 minutes in 850rpm, obtain adjusting red base paint.
D, look grain solution preparation
First by 7% insured's glue solution 500kg, adjust red base paint 120kg, adjust grey base paint 180kg and adjust yellow base paint 1800kg, stir 8 minutes in 350rpm, then sieve mixture (20 order), becomes granular mixture after sieving; Finally add water 20kg, 350rpm stirs 8 minutes, obtained described look grain solution.
E, emulation are containing the preparation of sand multicolor finish
First by emulsion, (Ahmedabad is rich: 996AD) 208.5kg, antifreezing agent 103kg, film coalescence aid 13kg, defoamer 0.5kg, water 5kg, sanitas 1kg and pH adjusting agent 2kg, stir 8 minutes under 1000rpm, then look grain solution 600kg, thickening material B 10kg is added and water 1kg, 3500rpm stir 8 minutes.Obtain final finished emulation containing sand multicolor finish.
Embodiment 4
A, 7% insured's glue solution preparation
930kg deionized water and 70kg protecting glue (Ke Naiou: S-482) 500rpm in stirrer are stirred 10 minutes, obtains described 7% insured's glue solution.
B, base paint are prepared
First deionized water 420kg, antifreezing agent 18kg, defoamer 4kg, dispersion agent 4kg and sanitas 4kg are placed in stirrer 300rpm and stir 5 minutes, obtain described base paint;
Drop into titanium dioxide 12kg, kaolin 75kg, thickening material A 4kg, linking agent 4kg, film coalescence aid 20kg, pH adjusting agent 1kg and water 90kg again, heighten stirring velocity and stir 30 minutes to 1200rpm;
Finally drop into 7% insured's glue solution 40kg and emulsion 300kg, 800rpm stir 15 minutes, obtain described base paint.
C, base paint are mixed colours
By the quartz sand 100kg of the base paint 850kg obtained, red aqueous color paste 50kg and 200 order sizes, stir 10 minutes in 800rpm, obtain adjusting red base paint;
By the quartz sand 100kg of the base paint 850kg, the grey aqueous color paste 50kg that obtain and 200 order sizes, stir 10 minutes in 800rpm, obtain adjusting grey base paint;
By the quartz sand 100kg of the base paint 850kg obtained, yellow aqueous color paste 50kg and 200 order sizes, stir 10 minutes in 800rpm, obtain adjusting yellow base paint.
D, look grain solution preparation
First by 7% insured's glue solution 460kg, adjust red base paint 100kg, adjust grey base paint 190kg and adjust yellow base paint 210kg, stir 5 minutes in 300rpm, then sieve mixture (10 order), becomes granular mixture after sieving; Finally add water 40kg, 300rpm stirs 5 minutes, obtained described look grain solution.
E, emulation are containing the preparation of sand multicolor finish
First by emulsion, (Ahmedabad is rich: 996AD) 200kg, antifreezing agent 14kg, film coalescence aid 12kg, defoamer 1kg, water 8kg, sanitas 1.5kg and pH adjusting agent 2.5kg, stir 5 minutes under 800rpm, then look grain solution 643kg, thickening material B 18kg is added and water 100kg, 300rpm stir 5 minutes.Obtain final finished emulation containing sand multicolor finish.
Above-described embodiment, just preferred embodiment of the present invention, is not used for limiting the scope of the present invention, therefore all equivalences done with the feature described in the claims in the present invention and principle change or modify, and all should be included within the claims in the present invention scope.
Product of the present invention is when using supporting finish paint, and wherein several main physical property is as shown in the table:
As seen from the above table, the present invention not only has appearance and the texture of natural granite, and adherence, water tolerance, alkali resistance are identical with natural granite, and QUV test and cold cycling test in all show the performance identical with natural granite.
Claims (10)
1. emulation is containing a sand multicolor finish, it is characterized in that, comprises the following raw material according to listed as parts by weight:
Wherein, described look grain solution is obtained by the following raw material according to listed as parts by weight:
7% insured's glue solution 400 ~ 500 parts
Colored paint 450 ~ 700 parts
20 ~ 40 parts, water
Described colored paint is the base paint mixture after at least three kinds of color toner.
2. emulation contains sand multicolor finish as claimed in claim 1; it is characterized in that; the preparation method of described look grain solution is specially: first 7% insured's glue solution of described amount and colored paint are stirred 4 ~ 8 minutes under 250 ~ 350rpm; then 10 ~ 30 mesh sieves are crossed; finally the water of sieve gained granular mixture and described amount is stirred 4 ~ 8 minutes under 250 ~ 350rpm, obtained described look grain solution.
3. emulation is containing sand multicolor finish as claimed in claim 1 or 2, and it is characterized in that, described colored paint comprises the following raw material according to listed as parts by weight:
Base paint 700 ~ 850 parts
Aqueous color paste 1 ~ 100 part
Quartz sand 100 ~ 250 parts;
Wherein, described quartz sand is 150 ~ 200 orders.
4. emulation is containing sand multicolor finish as claimed in claim 3, and it is characterized in that, the preparation method of described colored paint is: described base paint, aqueous color paste and quartz sand are stirred 8 ~ 15 minutes under 750 ~ 850rpm, obtained described colored paint.
5., as in claim 2,3 or 4, as described in any one, emulation is containing sand multicolor finish, it is characterized in that, described base paint comprises the following raw material according to listed as parts by weight:
Described thickening material A is Mierocrystalline cellulose.
6. as described in claim 1,2 or 5, emulation containing sand multicolor finish, is characterized in that, described 7% insured's glue solution is that the water of 930 parts and the protecting glue of 70 parts stir to modulate for 8 ~ 15 minutes and form under 450 ~ 550rpm by weight part.
7. emulation is containing sand multicolor finish as claimed in claim 5, and it is characterized in that, the preparation method of described base paint is:
First by the antifreezing agent of described amount, defoamer, dispersion agent, sanitas and 400 ~ 450 parts of water, stir 3 ~ 8 minutes under 250 ~ 350rpm, obtained mixed solution;
Again the titanium dioxide of described amount, kaolin, thickening material A, the glutinous agent of friendship, film coalescence aid and PH conditioning agent and remaining 50 ~ 100 parts of water are joined in mixed solution one, stir 25 ~ 40 minutes under 1000 ~ 1500rpm;
Finally add 7% insured's glue solution and emulsion of described amount, stir 8 ~ 15 minutes under 600 ~ 1000rpm, obtained described base paint.
8. prepare emulation described in any one in claim 1-7, containing the method for sand multicolor finish, to it is characterized in that:
First the emulsion of described amount, antifreezing agent, film coalescence aid, defoamer, sanitas, PH conditioning agent and water are stirred 3 ~ 8 minutes under 700 ~ 1000rpm;
Add the look grain solution of described amount, thickening material B and water again, stir 3 ~ 8 minutes under 250 ~ 350rpm, obtained described emulation is containing sand multicolor finish;
Wherein said thickening material B is hydrophobically-modified alkali swelling type thickening material.
9. emulation, containing the method for sand multicolor finish, is characterized in that: described look grain solution and thickening material B need slowly add as claimed in claim 8..
10. in claim 1-9, described in any one, emulation, containing the method for application of sand multicolor finish, is characterized in that, is specially:
Step one, batch scrape exterior wall putty one time, dry 5 ~ 8 days;
Step 2, roller coating or spraying exterior wall seal coat one time, dry 5 ~ 8 hours;
Step 3, roller coating or the real color bottom paint twice of spraying water-based, dry 5 ~ 8 hours;
Step 4, spray described emulation containing sand multicolor finish twice, dry 10 ~ 15 hours;
Step 5, spraying water-based finishing varnish one time, dry 5 ~ 8 hours; Apply complete.