CN104725763B - 一种耐光照老化abs塑料及其制备方法 - Google Patents
一种耐光照老化abs塑料及其制备方法 Download PDFInfo
- Publication number
- CN104725763B CN104725763B CN201510141313.3A CN201510141313A CN104725763B CN 104725763 B CN104725763 B CN 104725763B CN 201510141313 A CN201510141313 A CN 201510141313A CN 104725763 B CN104725763 B CN 104725763B
- Authority
- CN
- China
- Prior art keywords
- parts
- aging resisting
- illumination aging
- abs plastic
- illumination
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明公开了一种耐光照老化ABS塑料及其制备方法。所述一种耐光照老化ABS塑料,包括下述重量份的组分:ABS树脂100份,复合光稳定剂0.3‑0.5份,所述复合光稳定剂下述重量份的组分组成:2‑[2‑羟基‑4‑(2,2,6,6‑四甲基哌啶‑4‑氧基)羰基甲氧基苯基]‑2H‑苯并三唑40‑60份和N,N’‑双(2,2,6,6‑四甲基‑4‑哌啶基)‑N,N’‑二醛基己二胺40‑60份。本发明耐光照老化性较优异,且制备工艺简单,产品成本低,产品的综合性能较优异。本发明的耐光照老化ABS塑料,可以用注塑工艺轻易加工成各种形状的零件,特别适合于注塑为各种汽车内饰件。
Description
技术领域
本发明涉及一种塑料及其制备方法,尤其涉及一种耐光照老化ABS塑料及其制备方法。
背景技术
ABS树脂(丙烯腈-苯乙烯-丁二烯共聚物,ABS是Acrylonitrile ButadieneStyrene的首字母缩写)是一种强度高、韧性好、易于加工成型的热塑型高分子材料结构。
ABS树脂是丙烯腈、1,3-丁二烯和苯乙烯三种单体的接枝共聚物。它的分子式可以写为(C8H8·C4H6·C3H3N)x,但实际上往往是含丁二烯的接枝共聚物与丙烯腈-苯乙烯共聚物的混合物,其中,丙烯腈占15~35%,丁二烯占5~30%,苯乙烯占40~60%,乳液法ABS最常见的比例是A:B:S=22:17:61,而本体法ABS中B的比例往往较低,约为13%。
ABS是本世纪40年代发展起来的通用热塑性工程塑料,是一个综合力学性能十分优秀的塑料品种,不仅具有良好的刚性、硬度和加工流动性,而且具有高韧性特点,可以注塑、挤出或热成型。
大部分汽车部件都是用注塑成型方法加工的,ABS树脂的优点是抗冲性、隔音性、耐划痕性,耐热性更好,比PP更美观,特别适用于横向抗冲性和使用温度较为严格的部件。ABS树脂是汽车中使用仅次于聚氨脂和聚丙烯的第三大树脂。ABS树脂可用于车内和车外部外壳,方向盘、导油管及把手和按钮等小部件,车外部包括前散热器护栅和灯罩等。
ABS树脂容易加工,加工尺寸稳定性和表面光泽好,容易涂装、着色,还可以进行喷涂金属、电镀、焊接和粘接等二次加工性能,可广泛应用于电子电器领域,包括各种办公和消费性电子/电器,办公电器包括电子数据处理机、办公室设备。近年来在电子电器市场,ABS树脂在要求耐光照老化和高耐热的电子/电器市场中将保持其地位,耐光照老化的ABS树脂在与ABS/PC等工程塑料合金的竞争中具有明显的优势。
然而,目前的ABS树脂的耐光照老化性能并不佳。
中国发明专利申请号201310001206.1公开了一种耐光照老化ABS塑料,包括下述重量份的组分:ABS树脂100份,复合光稳定剂0.3-0.5份,由下述重量份的组分组成:2-[2-羟基-4-(2,2,6,6-四甲基哌啶-4-氧基)羰基甲氧基苯基]-2H-苯并三唑30-50份、N,N’-双(2,2,6,6-四甲基-4-哌啶基)-N,N’-二醛基己二胺20-40份、N,N-二乙酰基己二酰基二酰肼5-15份。耐光照老化性能较好,但是原料较多。
发明内容
针对现有技术中存在的上述不足,本发明所要解决的技术问题之一提供一种耐光照老化ABS塑料,具有良好的耐光照老化性能。
本发明所要解决的技术问题之二提供上述耐光照老化ABS塑料的制备方法。
本发明的技术问题是通过如下技术方案实现的:
一种耐光照老化ABS塑料,包括下述重量份的组分:ABS树脂100份,复合光稳定剂0.3-0.5份;
所述复合光稳定剂下述重量份的组分组成:2-[2-羟基-4-(2,2,6,6-四甲基哌啶-4-氧基)羰基甲氧基苯基]-2H-苯并三唑40-60份、N,N’-双(2,2,6,6-四甲基-4-哌啶基)-N,N’-二醛基己二胺40-60份。
将2-[2-羟基-4-(2,2,6,6-四甲基哌啶-4-氧基)羰基甲氧基苯基]-2H-苯并三唑和N,N’-双(2,2,6,6-四甲基-4-哌啶基)-N,N’-二醛基己二胺搅拌混合均匀,即可制得该光稳定剂。
本发明还提供了上述耐光照老化ABS塑料的制备方法:按配比称取各组分,混合均匀后,熔融混炼、挤出造粒,即获得所述耐光照老化ABS塑料。
具体的,可以为按配比称取各组分,在高速混合机中,室温下控制转速在300-400转/分钟,混合5-10分钟,取出后转入螺杆挤出机中,在160-190℃温度下挤出造粒,即获得所述耐光照老化ABS塑料。
显然,在本发明中为提高产品的其他性能,还可以适应性地添加其他助剂,如阻燃剂、着色剂和抗静电剂等。
具体的,在本发明中:
2-[2-羟基-4-(2,2,6,6-四甲基哌啶-4-氧基)羰基甲氧基苯基]-2H-苯并三唑,分子式为C23H27N4O3。结构式如下:
N,N’-双(2,2,6,6-四甲基-4-哌啶基)-N,N’-二醛基己二胺,别称光稳定剂4050H,又称紫外吸收剂4050H。CAS号:124172-53-8,其分子式为C26H50N4O2。结构式如下:
发明人通过大量实验得出,将光稳定剂2-[2-羟基-4-(2,2,6,6-四甲基哌啶-4-氧基)羰基甲氧基苯基]-2H-苯并三唑和光稳定剂N,N’-双(2,2,6,6-四甲基-4-哌啶基)-N,N’-二醛基己二胺进行合理复配使用,明显优于使用单一光稳定剂,产生协同增效作用,耐光照老化效果明显。特别的,不添加和金属减活剂N,N-二乙酰基己二酰基二酰肼,耐光照老化效果反而更加优异。
本产品的耐光照老化性较优异,且制备工艺简单,产品成本低,产品的综合性能较优异。
本发明的耐光照老化ABS塑料,可以用注塑工艺轻易加工成各种形状的零件,可用于制成汽车用车内和车外部外壳,方向盘、导油管及把手和按钮等小部件,车外部包括前散热器护栅和灯罩等。
具体的,可以用于生产的汽车内饰件如下:预拉伸盖、预拉伸盖螺盖、中间扶手上盖下板、压条、地图带压条、中间扶手支撑塑料件、椅背板、大膝部空间椅背板、后排扶手通道、门焊饰条、嵌饰板骨架、门上装骨架等。
具体实施方式
下面结合实施例对本发明作进一步描述。
实施例1
按照表1中对应实施例1数据称取各原料。
将各组分加入到高速混合机中,室温下控制转速在350转/分钟,混合8分钟,取出后转入螺杆挤出机中,在175℃温度下挤出造粒,即获得所述耐光照老化ABS塑料。
表1:耐光照老化ABS塑料配方表 单位:公斤
对比例1-4
按照表1中对应对比例1-4数据称取各原料。采用实施例1所述的方法制备所述耐光照老化ABS塑料。
测试例
分别将实施例1和对比例1-4和空白例的母料放入硫化机中压制成厚度为1mm的片,再经过冷压成型,切制成2cm×5cm的样品条。
按GB/T16422.2—1999塑料实验室光源曝露试验方法,置于氙灯曝晒光老化试验箱中照射,然后按GB2409—80塑料黄色指数试验方法,测其黄色指数,得到其变黄指数△YI如下表所示。
表2:耐光照老化性能测试表
变黄指数△YI是表征光氧老化性能的一个重要指标,△YI越小,表示耐光照老化性能越好。
发明人通过大量实验得出,将光稳定剂2-[2-羟基-4-(2,2,6,6-四甲基哌啶-4-氧基)羰基甲氧基苯基]-2H-苯并三唑和光稳定剂N,N’-双(2,2,6,6-四甲基-4-哌啶基)-N,N’-二醛基己二胺进行合理复配使用,明显优于使用单一光稳定剂,产生协同增效作用,耐光照老化效果明显。特别的,不添加和金属减活剂N,N-二乙酰基己二酰基二酰肼,耐光照老化效果反而更加优异。
本产品的耐光照老化性较优异,且制备工艺简单,产品成本低,产品的综合性能较优异。
本发明的耐光照老化ABS塑料,可以用注塑工艺轻易加工成各种形状的零件,可用于制成汽车用车内和车外部外壳,方向盘、导油管及把手和按钮等小部件,车外部包括前散热器护栅和灯罩等。
具体的,可以用于生产的汽车内饰件如下:预拉伸盖、预拉伸盖螺盖、中间扶手上盖下板、压条、地图带压条、中间扶手支撑塑料件、椅背板、大膝部空间椅背板、后排扶手通道、门焊饰条、嵌饰板骨架、门上装骨架等。
以上所述,仅为本发明的具体实施方式,但本发明的保护范围并不局限于此,任何熟悉本领域的技术人员在本发明所揭露的技术范围内,可不经过创造性劳动想到的变化或替换,都应涵盖在本发明的保护范围之内。因此,本发明的保护范围应该以权利要求书所限定的保护范围为准。
Claims (2)
1.一种耐光照老化ABS塑料,包括下述重量份的组分:ABS树脂100份,复合光稳定剂0.3-0.5份,其特征在于,
所述复合光稳定剂由 下述重量份的组分组成:2-[2-羟基-4-(2,2,6,6-四甲基哌啶-4-氧基)羰基甲氧基苯基]-2H-苯并三唑40-60份和N,N’-双(2,2,6,6-四甲基-4-哌啶基)-N,N’-二醛基己二胺40-60份。
2.如权利要求1所述的塑料的制备方法,其特征在于:按配比称取各组分,混合均匀后,熔融混炼、挤出造粒。