CN104710143A - 一种泡沫混凝土 - Google Patents
一种泡沫混凝土 Download PDFInfo
- Publication number
- CN104710143A CN104710143A CN201310671052.7A CN201310671052A CN104710143A CN 104710143 A CN104710143 A CN 104710143A CN 201310671052 A CN201310671052 A CN 201310671052A CN 104710143 A CN104710143 A CN 104710143A
- Authority
- CN
- China
- Prior art keywords
- parts
- nano
- oxide
- foamed concrete
- diatomite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种泡沫混凝土,由以下质量份数的成份组成:50-80份多晶硅粉体、50-60份玻璃纤维、200-250份高铝水泥、150-200份石英砂、50-100份纳米高岭土、10-30份纳米氧化铜、10-30份纳米氧化锌、10-30份纳米氧化铁、100-120份铝矾土、10-25份聚乳酸、30-40份铁尾矿、25-35份硅藻土、10-25份烷基磺酸钠、10-20份烷基酚聚氧乙烯醚、 15-25份茶皂素发泡剂、200-300份水。该泡沫混凝土具有耐热度高、绿色安全环保,无毒无害、防水性能强、耐久性能好、加工方便、低的弹性模量、隔音耐火、强度高和成本低等优点。
Description
技术领域
本发明涉及混凝土的技术领域,尤其涉及一种泡沫混凝土。
背景技术
泡沫混凝土是通过发泡机的发泡系统将发泡剂用机械方式充分发泡,并将泡沫与水泥浆均匀混合,然后经过发泡机的泵送系统进行现浇施工或模具成型,经自然养护所形成的一种含有大量封闭气孔的新型轻质保温材料。
泡沫混凝土又称为发泡水泥、轻质混泥土等,是一种利废、环保、节能、低廉且具有不燃性的新型建筑节能材料。轻质混凝土(泡沫混凝土)是通过化学或物理的方式根据应用需要将空气或氮气、二氧化碳气、氧气等气体引入混凝土浆体中,经过合理养护成型,而形成的含有大量细小的封闭气孔,并具有相当强度的混凝土制品。轻质混凝土(泡沫混凝土)的制作通常是用机械方法将泡沫剂水溶液制备成泡沫。
泡沫混凝土是一种新型的节能环保型建筑材料,国内外学者对其做了大量的研究开发,使其广泛应用于墙体材料中,但其还存在一定的缺陷,如强度偏低、开裂、吸水等,因而要进一步扩大其应用领域还需在发泡剂、配合比、工艺流程、设备等方面做更进一步的研究。
泡沫混凝土的种类很多,但最常用的是水泥泡沫混凝土。水泥泡沫混凝土根据其掺合料不同又可分为水泥-粉煤灰-石灰型、水泥-矿渣-石灰-石膏型、水泥-粉煤灰-砂-石灰型、水泥一砂一石灰型、水泥-矿渣-粉煤灰-石灰-植物纤维型[4]、水泥-砂-玻璃纤维型等类型。
但是,现有技术的泡沫混凝土稠度较小,其粘稠度不能克服泡沫的表面扩张力,料浆中不同位置的泡沫,其直径随时间而出现不同程度的增大,从而使其部分泡沫直径偏大,而且泡沫直径大小不一,加泡不稳、成泡率能力下降;最终影响成泡的质量。
发明内容
本发明的目的是为了克服上述现有技术的缺点,提供一种泡沫混凝土,该泡沫混凝土具有耐热度高、绿色安全环保,无毒无害、防水性能强、耐久性能好、加工方便、低的弹性模量、隔音耐火、强度高和成本低等优点。
本发明解决其技术问题所采用的技术方案是:一种泡沫混凝土,由以下质量份数的成份组成:50-80份多晶硅粉体、50-60份玻璃纤维、200-250份高铝水泥、150-200份石英砂、50-100份纳米高岭土、10-30份纳米氧化铜、10-30份纳米氧化锌、10-30份纳米氧化铁、100-120份铝矾土、10-25份聚乳酸、30-40份铁尾矿、25-35份硅藻土、10-25份烷基磺酸钠、10-20份烷基酚聚氧乙烯醚、 15-25份茶皂素发泡剂、200-300份水。
进一步的,所述的多晶硅粉体为50份、玻璃纤维为50份、高铝水泥为200份、石英砂为150份、纳米高岭土为50份、纳米氧化铜为10份、纳米氧化锌为10份、纳米氧化铁为10份、铝矾土为100份、聚乳酸为10份、铁尾矿为30份、硅藻土为25份、烷基磺酸钠为10份、烷基酚聚氧乙烯醚为10份、 茶皂素发泡剂为15份、水为200份。
或者是,所述的多晶硅粉体为80份、玻璃纤维为60份、高铝水泥为250份、石英砂为200份、纳米高岭土为100份、纳米氧化铜为30份、纳米氧化锌为30份、纳米氧化铁为30份、铝矾土为120份、聚乳酸为25份、铁尾矿为40份、硅藻土为35份、烷基磺酸钠为25份、烷基酚聚氧乙烯醚为20份、 茶皂素发泡剂为25份、水为300份。
综上所述,本发明的有益效果是:本发明的泡沫混凝土具有耐热度高、绿色安全环保,无毒无害、防水性能强、耐久性能好、加工方便、低的弹性模量、隔音耐火、强度高和成本低等优点。
具体实施方式
实施例1
本实施例1所描述的一种泡沫混凝土,由以下质量份数的成份组成:50份多晶硅粉体、50份玻璃纤维、200份高铝水泥、150份石英砂、50份纳米高岭土、10份纳米氧化铜、10份纳米氧化锌、10份纳米氧化铁、100份铝矾土、10份聚乳酸、30份铁尾矿、25份硅藻土、10份烷基磺酸钠、10份烷基酚聚氧乙烯醚、 15份茶皂素发泡剂、200份水。
实施例2
本实施例2所描述的一种泡沫混凝土,由以下质量份数的成份组成:80份多晶硅粉体、60份玻璃纤维、250份高铝水泥、200份石英砂、100份纳米高岭土、30份纳米氧化铜、30份纳米氧化锌、30份纳米氧化铁、120份铝矾土、25份聚乳酸、40份铁尾矿、35份硅藻土、25份烷基磺酸钠、20份烷基酚聚氧乙烯醚、 25份茶皂素发泡剂、300份水。
以上所述,仅是本发明的较佳实施例而已,并非对本发明的原理和框架作任何形式上的限制。凡是依据本发明的技术实质对以上实施例所作的任何简单修改、等同变化与修饰,均仍属于本发明的技术方案的范围内。
Claims (3)
1.一种泡沫混凝土,其特征在于,由以下质量份数的成份组成:50-80份多晶硅粉体、50-60份玻璃纤维、200-250份高铝水泥、150-200份石英砂、50-100份纳米高岭土、10-30份纳米氧化铜、10-30份纳米氧化锌、10-30份纳米氧化铁、100-120份铝矾土、10-25份聚乳酸、30-40份铁尾矿、25-35份硅藻土、10-25份烷基磺酸钠、10-20份烷基酚聚氧乙烯醚、 15-25份茶皂素发泡剂、200-300份水。
2.根据权利要求1所述的一种泡沫混凝土,其特征在于,所述的多晶硅粉体为50份、玻璃纤维为50份、高铝水泥为200份、石英砂为150份、纳米高岭土为50份、纳米氧化铜为10份、纳米氧化锌为10份、纳米氧化铁为10份、铝矾土为100份、聚乳酸为10份、铁尾矿为30份、硅藻土为25份、烷基磺酸钠为10份、烷基酚聚氧乙烯醚为10份、 茶皂素发泡剂为15份、水为200份。
3.根据权利要求1所述的一种泡沫混凝土,其特征在于,所述的多晶硅粉体为80份、玻璃纤维为60份、高铝水泥为250份、石英砂为200份、纳米高岭土为100份、纳米氧化铜为30份、纳米氧化锌为30份、纳米氧化铁为30份、铝矾土为120份、聚乳酸为25份、铁尾矿为40份、硅藻土为35份、烷基磺酸钠为25份、烷基酚聚氧乙烯醚为20份、 茶皂素发泡剂为25份、水为300份。