CN1046748C - 聚乙烯和聚丙烯加工改进剂 - Google Patents
聚乙烯和聚丙烯加工改进剂 Download PDFInfo
- Publication number
- CN1046748C CN1046748C CN 90100811 CN90100811A CN1046748C CN 1046748 C CN1046748 C CN 1046748C CN 90100811 CN90100811 CN 90100811 CN 90100811 A CN90100811 A CN 90100811A CN 1046748 C CN1046748 C CN 1046748C
- Authority
- CN
- China
- Prior art keywords
- polyethylene
- processing
- polypropylene
- modifier
- peroxide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明为一种聚乙烯和聚丙烯加工改进剂，其内容包括适用于各种质量规格的聚乙烯(包括高密度，中密度和低密度三种类型树脂)和聚丙烯的熔融加工，特别是改善高密度聚乙烯的熔体流动性能。这种聚乙烯加工改进剂的制造方法是将聚乙烯、聚丙烯和有机过氧化物(0.3-5%)混合造粒。用此改进剂(添加量为1-4%)与聚乙烯(或聚丙烯)掺混均匀，可改善聚乙烯(或聚丙烯)的熔体加工性能。并且可提高生产效率。
Description
本发明属于聚烯烃材料加工性能改进技术。
聚乙烯是高分子材料中大品种之一。其中高密度聚乙烯是一种结晶性较高的聚合物。由于高密度聚乙烯等结晶性较好且分子量等诸种因素，使得其在实际成型或成膜加工过程中存在着加工较困难等问题。
在国内外发表(公开)的专利报道中，采用有机过氧化物及其它化合物来机械、化学共混改性聚乙烯或聚丙烯的专利项目有148项之多。除了聚丙烯或者聚乙烯十有机过氧化物外，其辅助剂为无机化合物(J61-152754)、金属盐(J60-26038)、成核剂(J62-135551)、脂肪酸(J61-190540)、无定形乙一丙共聚体(Jb3-41552)、低密度聚乙烯(或高密度聚乙烯)+EPR(J63-130649)、低密度聚乙烯(J52-121060)、低密度聚乙烯+乙一丙共聚物(J52-138539)、有机硅化合物(J57-125234)等。这些专利申请内容中，唯有J52-121060中所述聚丙烯+低密度聚乙烯+有机过氧化物的内容与本发明申请的有些类似的地方，其主要技术特征和配方是：适用于挤压制造涂料(层)的聚烯烃组合物，其特征在于对聚丙烯100份(重量比)来说，含有低密度聚乙烯3-15份(重量比)和有机过氧化物0.01-1.0份(重量比)。是以聚丙烯为主要组份的组合物。是将熔融树脂用于向塑料膜、玻璃纸、纸和金属箔等基材表面上挤压形成涂层的高速加工方法。也可以使用占聚丙烯或丙烯10％(重量)以下的与其它α烯烃的共聚物，流动指数以5-20g/10分钟较合适。有机过氧化物包括氢过氧化物(hydroperoxide)、二烷基过氧化物(dialkylpeoxide)、二酰基过氧化物(diacyl peroxide)、过氧化酯(peroxyester)、酮过氧化物等类型。二烷基过氧化物包括过氧化二叔丁基等。挤出机的温度为200-250℃。
本发明是在现有生产加工设备和确保产品质量的条件下，解决了聚乙烯加工的困难和提高了生产效率。该改进剂适用于各种质量规格的聚乙烯(包括高密度，中密度和低密度三种类型树脂)和聚丙烯的熔融加工，特别是改善高密度聚乙烯的熔体流动性能。这种加工改进剂的配方不同于上述已有技术，其中有机过氧化物的用量范围较宽。更重要的是，该加工改进剂为固体颗粒状，具有包装长途运输和生产使用等便利条件。这种改进剂中的活性部分可保存二个月以上。由于是固体颗粒形状使用，因而在加工过程中基本上无大量挥发有害气体产生。该发明技术比一般的共混改性方法，更容易实现工业化连续生产。
本发明聚乙烯加工改进剂，是以聚乙烯、聚丙烯和有机过氧化物等所组成。其重要成份配比范围如下：
聚烯烃(即聚乙烯与聚丙烯的混合物) 为99.7～95％
有机过氧化物 为0.3～5％。其中，聚烯烃混合配比范围为聚乙烯占0.1～25％，聚丙烯占99.9～75％；有机过氧化物为过氧化二叔丁基(OTBP)等。
其加工条件为普通螺杆挤出机，加工温度为150℃-285℃。
该改进剂在改善聚乙烯熔体流动性能和提高其产量的基础上，仍可使聚乙烯保持原有的力学性能。如表1中的缺口与非缺口抗冲强度。但是这种聚乙烯加工改进剂添加量超过4％时，其缺口抗冲强度将会有所下降。若其添加量为20％时，其缺口与非缺口抗冲强度有较大的变化。在实际加工生产中，较为经济实用的添加量为3％以下。
表1聚乙烯注射成型样条的抗冲性能
| 样品号 | 聚乙烯加工改进剂添加量(％) | 抗冲强度(kg/cm2)非缺口 缺口 |
| 12345 | 0241020 | 13.40 7.413.8 6.713.8 6.414.4 5.711.6 1.3 |
J52-121060专利未例出有关的力学性能数据。
该聚乙烯加工改进剂对促进聚乙烯加工生产，改善加工工艺条件和稳定化有很好的效果。并且，其原料来源较广，制备工艺简单等优点。
实施例
例1：将有机过氧化物含量为0.6％的该聚乙烯加工改进剂以2％的添加量加入于聚乙烯(高密度聚乙烯)中制造薄膜(编织带)。其结果表明，在维持正常的日产量情况下，可使生产加工温度降低约20℃左右。
例2：在维持正常的加工条件(基本)下，添加1.5％的聚乙烯改进剂(该有机过氧化物含量为1.1％)或者添加2％的聚乙烯改进剂(该有机过氧化物含量为0.6％)，可增加产量20％左右。
上述两实施例所得到的产品质量基本符合后加工及产品使用的要求，如表(2)所示。
表(2)实施例的数据表
| 纤度(旦) | 拉力(Kg) | 伸长率(％) | 相对抗拉(g/旦) | |
| 产品要求实施例一实施例二 | 800-10001000786 | 3.53.93.5 | 15左右25.321.9 | 3.53.934.4 |
Claims (2)
1、一种聚乙烯和聚丙烯加工改进剂，其特征在于所述的加工改进剂是由99.7-95％(重量比)的聚烯烃和0.3-5.0％(重量比)的有机过氧化物组成的固体颗粒，其中所述的聚烯烃是由99.9-75％(重量比)的聚丙烯和0.1-25％(重量比)的聚乙烯组成。
2、如权利要求1所述的聚乙烯和聚丙烯加工改进剂，其特征在于所说的有机过氧化物为过氧化物二叔丁基。