CN104628361A - 一种夜光仿大理石工艺品及其制备方法 - Google Patents
一种夜光仿大理石工艺品及其制备方法 Download PDFInfo
- Publication number
- CN104628361A CN104628361A CN201310546373.4A CN201310546373A CN104628361A CN 104628361 A CN104628361 A CN 104628361A CN 201310546373 A CN201310546373 A CN 201310546373A CN 104628361 A CN104628361 A CN 104628361A
- Authority
- CN
- China
- Prior art keywords
- parts
- polyester resin
- unsaturated polyester
- noctilucence
- parian
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明的目的是提供一种具有大理石的天然纹理、质感平滑、色调丰富多彩,且可在夜间发光的夜光仿大理石工艺品及其制备方法,包括有下列成分:不饱和聚酯树脂150-200份、热稳定剂5-7份、固化剂3-8份、石粉220-340份、引发剂6-10份、发光颜料3-5份。包括以下步骤,按重量份称取各种原料;放入高混机中混合10-20分钟静置消泡,注入模具中成型,置于窑中,在900℃至1000℃的温度烧制12小时,然后再还原焰5小时后,自然冷却出窑;上蜡抛光,即为成品。
Description
所属技术领域
本发明涉及工艺品领域,尤其是一种夜光仿大理石工艺品。
背景技术
随着石材产业不断发展壮大,石材加工企业的剩余( 下脚料、边角料) 越来越多,石材加工产生的粉尘、石渣、边角料随意堆放,日积月累,废料、石粉堆积成山,占据了大量土地,特别是一遇雨天便被雨水冲刷到溪河,严重影响了植被的生长,同时也污染了周边水源。目前大部分石粉、石渣、边角料都用来制造人造大理石板,其局限性大,无法完全将石材废料利用起业;采用石渣石粉制造工艺品,可以有效地对废石渣进行综合利用,保护生态环境、减少污染、化害为利,是一项减少石材加工企业废石渣石粉污染的一条好途径。
发明内容
本发明的目的是提供一种可在夜间发光的夜光仿大理石工艺品及其制备方法。
一种夜光仿大理石工艺品,所述夜光仿大理石工艺品以重量份为单位,包括有下列成分:
不饱和聚酯树脂 150-200 份、 热稳定剂5-7 份、 固化剂3-8 份、
石粉220-340 份、 引发剂 6-10 份、 发光颜料 3-5 份
作为本发明的一种优选技术方案 :所述不饱和聚酯树脂采用不饱和聚酯树脂191、不饱和聚酯树脂 195 或不饱和聚酯树脂 196 中的一种。
作为本发明的一种优选技术方案 :所述热稳定剂采用硬脂酸铅、硬脂酸锌或硬脂酸钡中的一种或多种混合物。
作为本发明的一种优选技术方案 :所述引发剂采用过氧化甲乙酮或过氧化环己酮糊中的一种或多种混合物。
所述一种夜光仿大理石工艺品的制备方法为 :
第一步 :按照上文所述重量份称取各种原料 ;
第二步 :将上述原料放入高混机中混合 10-20 分钟,使各种成分分散均匀,加料顺序为不饱和聚酯树脂、引发剂、固化剂、热稳定剂、石粉和发光颜料 ;
第三步 :将第上述产物静置消泡,注入模具中成型,固化脱模,整形;
第四步:将上述产物置于窑中,在900℃至1000℃的温度烧制12 小时,然后再还原焰5 小时后,自然冷却出窑;
第五步:上蜡抛光,将出窑后上述产物进行研磨、上蜡、抛光后即为成品。
本发明的有益效果是:所得工艺品具有大理石的天然纹理、质感平滑、色调丰富多彩,且可在夜间发光。
具体实施方式
下面结合实施例,对本发明的技术方案作进一步具体的说明。
实施例 1
第一步 :按照下文所述重量份称取各种原料:
不饱和聚酯树脂 150 份、 热稳定剂 7 份、 固化剂 8 份、
石粉 340 份、 引发剂 6 份、 发光颜料 5 份
第二步 :将上述原料放入高混机中混合 10-20 分钟,使各种成分分散均匀,加料顺序为不饱和聚酯树脂、引发剂、固化剂、热稳定剂、石粉和发光颜料 ;
第三步 :将第上述产物静置消泡,注入模具中成型,固化脱模,整形;
第四步:将上述产物置于窑中,在900℃至1000℃的温度烧制12 小时,然后再还原焰5 小时后,自然冷却出窑;
第五步:上蜡抛光,将出窑后上述产物进行研磨、上蜡、抛光后即为成品。
实施例 2
第一步 :按照下文所述重量份称取各种原料:
不饱和聚酯树脂 180 份、 热稳定剂 6 份、 固化剂 3 份、
石粉 290 份、 引发剂 8 份、 发光颜料 4 份
第二步 :将上述原料放入高混机中混合 10-20 分钟,使各种成分分散均匀,加料顺序为不饱和聚酯树脂、引发剂、固化剂、热稳定剂、石粉和发光颜料 ;
第三步 :将第上述产物静置消泡,注入模具中成型,固化脱模,整形;
第四步:将上述产物置于窑中,在900℃至1000℃的温度烧制12 小时,然后再还原焰5 小时后,自然冷却出窑;
第五步:上蜡抛光,将出窑后上述产物进行研磨、上蜡、抛光后即为成品。
实施例 3
第一步 :按照下文所述重量份称取各种原料:
不饱和聚酯树脂 200 份、 热稳定剂 5 份、 固化剂 6 份、
石粉 220 份、 引发剂 10 份、 发光颜料 3 份
第二步 :将上述原料放入高混机中混合 10-20 分钟,使各种成分分散均匀,加料顺序为不饱和聚酯树脂、引发剂、固化剂、热稳定剂、石粉和发光颜料 ;
第三步 :将第上述产物静置消泡,注入模具中成型,固化脱模,整形;
第四步:将上述产物置于窑中,在900℃至1000℃的温度烧制12 小时,然后再还原焰5 小时后,自然冷却出窑;
第五步:上蜡抛光,将出窑后上述产物进行研磨、上蜡、抛光后即为成品。
Claims (5)
1.一种夜光仿大理石工艺品,其特征是:所述夜光仿大理石工艺品以重量份为单位,包括有下列成分:
不饱和聚酯树脂 150-200 份、 热稳定剂5-7 份、 固化剂3-8 份、
石粉220-340 份、 引发剂 6-10 份、 发光颜料 3-5 份。
2.根据权利要求1所述的一种夜光仿大理石工艺品,其特征是:不饱和聚酯树脂采用不饱和聚酯树脂191、不饱和聚酯树脂 195 或不饱和聚酯树脂 196 中的一种。
3.根据权利要求1所述的一种夜光仿大理石工艺品,其特征是:所述热稳定剂采用硬脂酸铅、硬脂酸锌或硬脂酸钡中的一种或多种混合物。
4.根据权利要求1所述的一种夜光仿大理石工艺品,其特征是:所述引发剂采用过氧化甲乙酮或过氧化环己酮糊中的一种或多种混合物。
5.权利要求1所述的一种夜光仿大理石工艺品的制备方法,其特征是:包括以下步骤:
第一步 :按照上文所述重量份称取各种原料 ;
第二步 :将上述原料放入高混机中混合 10-20 分钟,使各种成分分散均匀,加料顺序为不饱和聚酯树脂、引发剂、固化剂、热稳定剂、石粉和发光颜料 ;
第三步 :将第上述产物静置消泡,注入模具中成型,固化脱模,整形;
第四步:将上述产物置于窑中,在900℃至1000℃的温度烧制12 小时,然后再还原焰5 小时后,自然冷却出窑;
第五步:上蜡抛光,将出窑后上述产物进行研磨、上蜡、抛光后即为成品。