CN104592919A - 脲醛胶胶粘剂及其制备方法 - Google Patents

脲醛胶胶粘剂及其制备方法 Download PDF

Info

Publication number
CN104592919A
CN104592919A CN201510041086.7A CN201510041086A CN104592919A CN 104592919 A CN104592919 A CN 104592919A CN 201510041086 A CN201510041086 A CN 201510041086A CN 104592919 A CN104592919 A CN 104592919A
Authority
CN
China
Prior art keywords
urea
parts
formaldehyde
add
glue adhesive
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201510041086.7A
Other languages
English (en)
Other versions
CN104592919B (zh
Inventor
胡忠
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Wuhan Yingtefuyuan Environment Friendly Material Co Ltd
Original Assignee
Wuhan Yingtefuyuan Environment Friendly Material Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Wuhan Yingtefuyuan Environment Friendly Material Co Ltd filed Critical Wuhan Yingtefuyuan Environment Friendly Material Co Ltd
Priority to CN201510041086.7A priority Critical patent/CN104592919B/zh
Publication of CN104592919A publication Critical patent/CN104592919A/zh
Application granted granted Critical
Publication of CN104592919B publication Critical patent/CN104592919B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明提出了一种脲醛胶胶粘剂及其制备方法，按重量份计包括以下组分：甲醛1200-1400份，尿素1170-1370份，三聚氰胺240-340份，石蜡0.5-2份，硅酸盐15-25份，邻苯二甲酸酐2-4份，固化剂50-70份以及增粘剂8-10份，其中所述甲醛为质量百分含量为37％的工业甲醛。将各个组分分层次添加来制备脲醛胶胶粘剂。制备而得的脲醛胶胶粘剂游离甲醛释放量低，符合国家标准。

Description

脲醛胶胶粘剂及其制备方法
技术领域
本发明属于胶合板胶粘剂领域，具体涉及一种脲醛胶胶粘剂及其制备方法。
背景技术
棕垫，即采用天然椰子树的椰壳纤维制成的“棕床垫”，或“棕地席垫”等。制作床垫过程中一般会用到大量的黏合剂或胶水，而这类附加材料中可能含有大量的甲醛。目前常用的胶粘剂有脲醛胶、三聚氰胺甲醛胶和聚醋酸乙烯脂乳胶，应用最广泛的是脲醛胶，其可适应胶合板热压成型，耐水性好，价格便宜。目前脲醛胶制备多数都是一次性的把甲醛含量降低，这种方法制备得到的脲醛胶粘剂中游离甲醛含量大，容易超标。
发明内容
为解决上述现有技术存在的问题，本发明提出一种脲醛胶胶粘剂及其制备方法，该脲醛胶胶粘剂游离甲醛释放量低，符合国家标准。
本发明的技术方案是这样实现的：
一种脲醛胶胶粘剂，按重量份计包括以下组分：
甲醛1200-1400份，尿素1170-1370份，三聚氰胺240-340份，石蜡0.5-2份，硅酸盐15-25份，邻苯二甲酸酐2-4份，固化剂50-70份以及增粘剂8-10份，其中所述甲醛为质量百分含量为37％的工业甲醛。
进一步，按重量份计包括以下组分：
甲醛1300份，尿素1270份，三聚氰胺290份，石蜡1份，硅酸盐20份，邻苯二甲酸酐2份，固化剂50份以及增粘剂8份，其中所述甲醛为质量百分含量为37％的工业甲醛。
进一步，所述硅酸盐为硅酸钠或者硅酸钾。
进一步，所述增粘剂选自凹凸棒土或/和淀粉。
一种脲醛胶胶粘剂的制备方法，包括以下步骤：
1)按重量份计称取1200-1400份质量百分含量为37％的甲醛加入反应釜，加酸调节pH至3.0-3.2，然后加入60-120份三聚氰胺与850-950份尿素；
2)加热升温至58-60℃，迅速加入氢氧化钠调节pH至8.5-9.0，继续升温至78-82℃，停止升温，保温1h-1.5h；
3)然后加酸调节pH至4.6-5.0，反应成白雾状，终止反应；
4)加入氢氧化钠调节pH至8.5-9.0，加入180-220份三聚氰胺、220-280份尿素以及0.5-2份石蜡，反应0.5h；
5)加入100-140份尿素以及15-25份硅酸盐，然后开始降温，降温至40℃以下，然后加入2份邻苯二甲酸酐，50份固化剂以及8份增粘剂，搅拌均匀，放胶，即得脲醛胶。
进一步，所述硅酸盐为硅酸钠或者硅酸钾。
进一步，所述增粘剂选自凹凸棒土或/和淀粉。
进一步，所述调节pH的酸为硫酸或盐酸。
本发明的优点：
1、本发明的脲醛胶胶粘剂中的甲醛释放量≤0.03毫克/小时，远低于国标QB/T 1952.2/2011的规定。
2、。本发明的脲醛胶在使用时需要边使用边加入固化剂，这样可以降低甲醛的释放量。
具体实施方式
实施例1
一种脲醛胶胶粘剂的制备方法，包括以下步骤：
1)按重量份计称取1200份质量百分含量为37％的甲醛加入反应釜，加酸调节pH至3.0-3.2，然后加入60份三聚氰胺与850份尿素；
2)加热升温至58℃，迅速加入氢氧化钠调节pH至8.5-9.0，继续升温至78℃，停止升温，保温1h-1.5h；
3)然后加酸调节pH至4.6-5.0，反应成白雾状，终止反应；
4)加入氢氧化钠调节pH至8.5-9.0，加入180份三聚氰胺、220份尿素以及0.5份石蜡，反应0.5h；
5)加入100份尿素以及15份硅酸钾，然后开始降温，降温至40℃以下，然后加入2份邻苯二甲酸酐，50份固化剂以及8份凹凸棒土，搅拌均匀，放胶，即得脲醛胶。
其中，调节pH的酸为硫酸。
将步骤5)得到脲醛胶涂覆在棕榈垫上面，根据气候箱法测定甲醛释放量为0.01毫克/小时。
实施例2
一种脲醛胶胶粘剂的制备方法，包括以下步骤：
1)按重量份计称取1400份质量百分含量为37％的甲醛加入反应釜，加酸调节pH至3.0-3.2，然后加入120份三聚氰胺与950份尿素；
2)加热升温至60℃，迅速加入氢氧化钠调节pH至8.5-9.0，继续升温至82℃，停止升温，保温1h-1.5h；
3)然后加酸调节pH至4.6-5.0，反应成白雾状，终止反应；
4)加入氢氧化钠调节pH至8.5-9.0，加入220份三聚氰胺、280份尿素以及2份石蜡，反应0.5h；
5)加入140份尿素以及25份硅酸钠，然后开始降温，降温至40℃以下，然后加入2份邻苯二甲酸酐，50份固化剂以及8份淀粉，搅拌均匀，放胶，即得脲醛胶。
其中，调节pH的酸为盐酸。
将步骤5)得到脲醛胶涂覆在棕榈垫上面，根据气候箱法测定甲醛释放量为0.03毫克/小时。
实施例3
一种脲醛胶胶粘剂的制备方法，包括以下步骤：
1)按重量份计称取1300份质量百分含量为37％的甲醛加入反应釜，加酸调节pH至3.0-3.2，然后加入90份三聚氰胺与900份尿素；
2)加热升温至60℃，迅速加入氢氧化钠调节pH至8.5-9.0，继续升温至80℃，停止升温，保温1h-1.5h；
3)然后加酸调节pH至4.6-5.0，反应成白雾状，终止反应；
4)加入氢氧化钠调节pH至8.5-9.0，加入200份三聚氰胺、250份尿素以及1份石蜡，反应0.5h；
5)加入120份尿素以及20份硅酸钠，然后开始降温，降温至40℃以下，然后加入2份邻苯二甲酸酐，50份固化剂以及8份淀粉和凹凸棒土的混合物，搅拌均匀，放胶，即得脲醛胶。
其中，调节pH的酸为盐酸。
将步骤5)得到脲醛胶涂覆在棕榈垫上面，根据气候箱法测定甲醛释放量为0.02毫克/小时。
以上所述仅为本发明的较佳实施例而已，并不用以限制本发明，凡在本发明的精神和原则之内，所作的任何修改、等同替换、改进等，均应包含在本发明的保护范围之内。

Claims (8)

1.一种脲醛胶胶粘剂，其特征在于，按重量份计包括以下组分：
甲醛1200-1400份，尿素1170-1370份，三聚氰胺240-340份，石蜡0.5-2份，硅酸盐15-25份，邻苯二甲酸酐2-4份，固化剂50-70份以及增粘剂8-10份，其中所述甲醛为质量百分含量为37％的工业甲醛。
2.根据权利要求1所述的脲醛胶胶粘剂，其特征在于，按重量份计包括以下组分：
甲醛1300份，尿素1270份，三聚氰胺290份，石蜡1份，硅酸盐20份，邻苯二甲酸酐2份，固化剂50份以及增粘剂8份，其中所述甲醛为质量百分含量为37％的工业甲醛。
3.根据权利要求1或2所述的脲醛胶胶粘剂，其特征在于，所述硅酸盐为硅酸钠或者硅酸钾。
4.根据权利要求1或2所述的脲醛胶胶粘剂，其特征在于，所述增粘剂选自凹凸棒土或/和淀粉。
5.一种脲醛胶胶粘剂的制备方法，其特征在于，包括以下步骤：
1)按重量份计称取1200-1400份质量百分含量为37％的甲醛加入反应釜，加酸调节pH至3.0-3.2，然后加入60-120份三聚氰胺与850-950份尿素；
2)加热升温至58-60℃，迅速加入氢氧化钠调节pH至8.5-9.0，继续升温至78-82℃，停止升温，保温1h-1.5h；
3)然后加酸调节pH至4.6-5.0，反应成白雾状，终止反应；
4)加入氢氧化钠调节pH至8.5-9.0，加入180-220份三聚氰胺、220-280份尿素以及0.5-2份石蜡，反应0.5h；
5)加入100-140份尿素以及15-25份硅酸盐，然后开始降温，降温至40℃以下，然后加入2份邻苯二甲酸酐，50份固化剂以及8份增粘剂，搅拌均匀，放胶，即得脲醛胶。
6.根据权利要求5所述的脲醛胶胶粘剂的制备方法，其特征在于，所述硅酸盐为硅酸钠或者硅酸钾。
7.根据权利要求5所述的脲醛胶胶粘剂的制备方法，其特征在于，所述增粘剂选自凹凸棒土或/和淀粉。
8.根据权利要求5所述的脲醛胶胶粘剂的制备方法，其特征在于，所述调节pH的酸为硫酸或盐酸。
CN201510041086.7A 2015-01-27 2015-01-27 脲醛胶胶粘剂及其制备方法 Expired - Fee Related CN104592919B (zh)