CN104562675A - 一种淀粉基纺织浆料及其制备方法 - Google Patents

一种淀粉基纺织浆料及其制备方法 Download PDF

Info

Publication number
CN104562675A
CN104562675A CN201510041690.XA CN201510041690A CN104562675A CN 104562675 A CN104562675 A CN 104562675A CN 201510041690 A CN201510041690 A CN 201510041690A CN 104562675 A CN104562675 A CN 104562675A
Authority
CN
China
Prior art keywords
starch
parts
based textile
preparation
textile size
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201510041690.XA
Other languages
English (en)
Other versions
CN104562675B (zh
Inventor
费芬芳
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shanxi Changqing Biotechnology Co ltd
Original Assignee
Cube Dress Ornament Co Ltd Is Liked In Suzhou
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Cube Dress Ornament Co Ltd Is Liked In Suzhou filed Critical Cube Dress Ornament Co Ltd Is Liked In Suzhou
Priority to CN201510041690.XA priority Critical patent/CN104562675B/zh
Publication of CN104562675A publication Critical patent/CN104562675A/zh
Application granted granted Critical
Publication of CN104562675B publication Critical patent/CN104562675B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种淀粉基纺织浆料及其制备方法，所述的淀粉基纺织浆料包括羟丙基淀粉10-15份、磷酸酯淀粉5-14份、羟丙基二淀粉磷酸酯4-9份、荸荠淀粉3-8份、纳米氮化硅3-6份、瓜尔豆胶为3-9份、聚乙二醇4000为2-5份、月桂醇聚氧乙烯醚为5-10份。制备方法包括以下步骤：(1)首先按重量取羟丙基淀粉、磷酸酯淀粉、羟丙基二淀粉磷酸酯、荸荠淀粉、纳米氮化硅，将上述的各成分均投入分散釜中进行均匀分散，分散至均匀；(2)再向分散釜中加入瓜尔豆胶、聚乙二醇4000、月桂醇聚氧乙烯醚，加热，再进行匀速机械混合，混合至均匀，为制备的淀粉基纺织浆料。

Description

一种淀粉基纺织浆料及其制备方法
技术领域
本发明属于纺织浆料领域，涉及一种纺织浆料及其制备方法，特别是涉及一种淀粉基纺织浆料及其制备方法。
背景技术
浆纱是织造工程的关键工序，浆纱的目的主要是提高纱线的耐磨性，减少毛羽，适当增加纱线的强力，减少伸度，以承受纱在织造过程中复杂的机械作用能力，提高纱线的可织性能。纺织浆料根据其用量的大小和用途分为主浆料(粘着剂)和辅助浆料(助剂)，目前市场上的主浆料有：淀粉和其衍生产品、聚乙烯醇(PVA)、丙烯酸类粘合剂、聚酯类粘合剂。辅助浆料有：油剂类、后上蜡类、分解剂类、防腐剂类、吸湿剂类等。其中淀粉类纺织浆料是其中很重要的一个种类，但是不同的淀粉基纺织浆料的性能也并不相同，应用于经纱上浆中的效果也差异较大。
发明内容
要解决的技术问题：聚乙烯醇(PVA)在纺织浆料领域应用非常广泛，但是聚乙烯醇具有不环保、不易分解的问题，淀粉基纺织浆料的应用范围也越来越广，本发明的目的是提供一种新型的具有较好的断裂强度、较低的耐磨损耗的纺织浆料浆膜及其制备方法。
技术方案：为了解决上述的问题，本发明公开了一种淀粉基纺织浆料，所述的淀粉基纺织浆料包括下述重量份的成分：
进一步的，所述的一种淀粉基纺织浆料，包括下述重量份的成分：
更进一步的，所述的一种淀粉基纺织浆料，包括下述重量份的成分：
所述的一种淀粉基纺织浆料的制备方法，制备方法包括以下步骤：
(1)首先按重量取羟丙基淀粉10-15份、磷酸酯淀粉5-14份、羟丙基二淀粉磷酸酯4-9份、荸荠淀粉3-8份、纳米氮化硅3-6份，将上述的各成分均投入分散釜中进行均匀分散，分散至均匀；
(2)再向分散釜中按重量加入瓜尔豆胶为3-9份、聚乙二醇4000为2-5份、月桂醇聚氧乙烯醚为5-10份，加热，再进行匀速机械混合，混合至均匀，为制备的淀粉基纺织浆料。
进一步的，所述的一种淀粉基纺织浆料的制备方法，羟丙基淀粉为11-14份、磷酸酯淀粉为7-12份、羟丙基二淀粉磷酸酯为5-8份、荸荠淀粉为4-7份、纳米氮化硅为4-5份、瓜尔豆胶为5-8份、聚乙二醇4000为3-4份、月桂醇聚氧乙烯醚为7-9份。
有益效果：用于纺织浆料淀粉多为变性淀粉，其中磷酸酯淀粉有较多的用途，本发明的淀粉基纺织浆料用于经纱上浆具有非常好的耐磨性能和抗断裂的性能，有效地提高了经纱的强度，减少纱线的断头率。尤其是加入了荸荠淀粉和氮化硅后，荸荠淀粉和氮化硅发挥了协同作用，有效的提高了浆料浆膜的断裂强度和耐磨损强度。
具体实施方式
实施例1
(1)首先按重量取羟丙基淀粉15份、磷酸酯淀粉14份、羟丙基二淀粉磷酸酯4份、荸荠淀粉3份、纳米氮化硅6份，将上述的各成分均投入分散釜中进行均匀分散，分散至均匀；
(2)再向分散釜中按重量加入瓜尔豆胶为9份、聚乙二醇4000为5份、月桂醇聚氧乙烯醚为10份，加热，再进行匀速机械混合，混合至均匀，为制备的淀粉基纺织浆料。
实施例2
(1)首先按重量取羟丙基淀粉10份、磷酸酯淀粉5份、羟丙基二淀粉磷酸酯9份、荸荠淀粉8份、纳米氮化硅3份，将上述的各成分均投入分散釜中进行均匀分散，分散至均匀；
(2)再向分散釜中按重量加入瓜尔豆胶为3份、聚乙二醇4000为2份、月桂醇聚氧乙烯醚为5份，加热，再进行匀速机械混合，混合至均匀，为制备的淀粉基纺织浆料。
实施例3
(1)首先按重量取羟丙基淀粉11份、磷酸酯淀粉12份、羟丙基二淀粉磷酸酯5份、荸荠淀粉7份、纳米氮化硅4份，将上述的各成分均投入分散釜中进行均匀分散，分散至均匀；
(2)再向分散釜中按重量加入瓜尔豆胶为8份、聚乙二醇4000为3份、月桂醇聚氧乙烯醚为7份，加热，再进行匀速机械混合，混合至均匀，为制备的淀粉基纺织浆料。
实施例4
(1)首先按重量取羟丙基淀粉14份、磷酸酯淀粉7份、羟丙基二淀粉磷酸酯8份、荸荠淀粉4份、纳米氮化硅5份，将上述的各成分均投入分散釜中进行均匀分散，分散至均匀；
(2)再向分散釜中按重量加入瓜尔豆胶为5份、聚乙二醇4000为4份、月桂醇聚氧乙烯醚为9份，加热，再进行匀速机械混合，混合至均匀，为制备的淀粉基纺织浆料。
实施例5
(1)首先按重量取羟丙基淀粉13份、磷酸酯淀粉10份、羟丙基二淀粉磷酸酯6份、荸荠淀粉5份、纳米氮化硅4份，将上述的各成分均投入分散釜中进行均匀分散，分散至均匀；
(2)再向分散釜中按重量加入瓜尔豆胶为7份、聚乙二醇4000为3份、月桂醇聚氧乙烯醚为8份，加热，再进行匀速机械混合，混合至均匀，为制备的淀粉基纺织浆料。
对比例1
(1)首先按重量取羟丙基淀粉15份、磷酸酯淀粉14份、羟丙基二淀粉磷酸酯4份，将上述的各成分均投入分散釜中进行均匀分散，分散至均匀；
(2)再向分散釜中按重量加入瓜尔豆胶为9份、聚乙二醇4000为5份、月桂醇聚氧乙烯醚为10份，加热，再进行匀速机械混合，混合至均匀，为制备的淀粉基纺织浆料。
对比例2
(1)首先按重量取羟丙基淀粉15份、磷酸酯淀粉14份、羟丙基二淀粉磷酸酯4份、荸荠淀粉3份，将上述的各成分均投入分散釜中进行均匀分散，分散至均匀；
(2)再向分散釜中按重量加入瓜尔豆胶为9份、聚乙二醇4000为5份、月桂醇聚氧乙烯醚为10份，加热，再进行匀速机械混合，混合至均匀，为制备的淀粉基纺织浆料。
实施例1至5和对比例1和2制备得到的浆料浆膜断裂强度和磨耗如下：
实施例5的纺织浆料浆膜的断裂强度和磨耗最高，在加入了荸荠淀粉和氮化硅后，荸荠淀粉和氮化硅发挥了协同作用，有效的提高了浆料浆膜的断裂强度和耐磨损强度。

Claims (5)

1.一种淀粉基纺织浆料，其特征在于，所述的淀粉基纺织浆料包括下述重量份的成分：
2.根据权利要求1所述的一种淀粉基纺织浆料，其特征在于，所述的淀粉基纺织浆料包括下述重量份的成分：
3.根据权利要求1所述的一种淀粉基纺织浆料，其特征在于，所述的淀粉基纺织浆料包括下述重量份的成分：
4.根据权利要求1所述的一种淀粉基纺织浆料的制备方法，其特征在于，所述的淀粉基纺织浆料的制备方法包括以下步骤：
(1)首先按重量取羟丙基淀粉10-15份、磷酸酯淀粉5-14份、羟丙基二淀粉磷酸酯4-9份、荸荠淀粉3-8份、纳米氮化硅3-6份，将上述的各成分均投入分散釜中进行均匀分散，分散至均匀；
(2)再向分散釜中按重量加入瓜尔豆胶为3-9份、聚乙二醇4000为2-5份、月桂醇聚氧乙烯醚为5-10份，加热，再进行匀速机械混合，混合至均匀，为制备的淀粉基纺织浆料。
5.根据权利要求4所述的一种淀粉基纺织浆料的制备方法，其特征在于，所述的淀粉基纺织浆料的制备方法中，羟丙基淀粉为11-14份、磷酸酯淀粉为7-12份、羟丙基二淀粉磷酸酯为5-8份、荸荠淀粉为4-7份、纳米氮化硅为4-5份、瓜尔豆胶为5-8份、聚乙二醇4000为3-4份、月桂醇聚氧乙烯醚为7-9份。
CN201510041690.XA 2015-01-28 2015-01-28 一种淀粉基纺织浆料及其制备方法 Active CN104562675B (zh)