CN104559415A - 一种轻质弹性外墙保温抗裂腻子 - Google Patents
一种轻质弹性外墙保温抗裂腻子 Download PDFInfo
- Publication number
- CN104559415A CN104559415A CN201510038313.0A CN201510038313A CN104559415A CN 104559415 A CN104559415 A CN 104559415A CN 201510038313 A CN201510038313 A CN 201510038313A CN 104559415 A CN104559415 A CN 104559415A
- Authority
- CN
- China
- Prior art keywords
- wall heat
- heat insulation
- crack
- lightweight flexible
- flexible exterior
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种建筑涂料,特别涉及一种轻质弹性外墙保温抗裂腻子。一种轻质弹性外墙保温抗裂腻子,包括以重量份计的以下组分:聚氨酯硅丙聚合物,轻质隔热材料,无机填料,无机胶凝材料,助剂。发明的轻质弹性外墙保温抗裂腻子的导热系数与保温墙面的导热系数接近,可使得腻子的变形跟保温材料同步,从而降低裂缝出现的可能性,并且,具有普通弹性腻子的弹性抗裂效果,还减轻了墙体的重量,从而降低了剪切应力,能满足新材料的抗裂要求。
Description
技术领域
本发明涉及一种建筑涂料,特别涉及一种轻质弹性外墙保温抗裂腻子。
背景技术
建筑物的内外墙面采用涂料作饰面,是各种饰面做法中最为简便、最为经济实用的一种方法。随着建筑业的蓬勃发展,建筑涂料的需求量迅速增加,近几年外墙涂料发展势头很猛,国家及地方都陆续出台一系列相关的标准或法规以推广涂料的应用。但随着涂饰工程的增多,外墙涂装质量出现问题也增多,主要表现为涂层龟裂、脱落、泛碱、发花等,严重影响了建筑涂料的声誉及快速发展。
很长时间以来,一旦涂饰工程出现问题,大多都将责任归罪于涂料质量不好,很少考虑其他原因,使得涂料工程技术人员无所适从。随着涂装技术的进步及众多工程案例分析,人们逐步认识到:基层处理材料-腻子质量的好坏直接影响涂层的质量,甚至在某种意义上来说是起决定作用的,因此,腻子产品得到了广泛关注。近几年来,有关腻子产品的开发、研究、生产等虽然都有了很大的进步,但仍满足不了迅速发展的建筑业的需求。尤其是近年来,建筑节能保温的要求越来越高,国家积极推广新材料的应用。目前,建筑物均为保温墙面,所有的热量都集中在保温墙面和涂料之间,即在腻子层上,所以对腻子的考验更加严峻。而现有的弹性抗裂腻子的导热系数与保温墙面的导热系数不接近使得腻子的变形跟保温材料不同步,导致裂缝出现的可能性较高,不能满足新材料的抗裂要求。
发明内容
本发明目的在于提供一种轻质弹性外墙保温抗裂腻子,以解决现有技术中弹性抗裂腻子的导热系数与保温墙面的导热系数不接近使得腻子的变形跟保温材料不同步,导致裂缝出现的可能性较高,不能满足新材料的抗裂要求的技术性问题。
本发明目的通过以下技术方案实现:
一种轻质弹性外墙保温抗裂腻子,包括以重量份计的以下组分:
作为优选,所述聚氨酯硅丙聚合物选自硅丙乳液、纯丙乳液、苯丙乳液、互穿网络结构聚合物乳液或苯丙共聚乳液中的一种或几种。其中,互穿网络结构聚合物乳液是指由两种或多种共混的聚合物分子链相互贯穿并以化学键的方式自交联而形成网络结构的乳液,可使腻子具有优质的弹性效果;苯丙共聚乳液是苯乙烯与丙烯酸酯或官能团丙烯酸酯类单体进行乳液聚合的产物,苯丙乳液具有无毒无味、与颜料粘结强度高等优点,配以多种助剂可提高腻子与基层之间的粘结强度。
作为优选,所述轻质隔热材料包括玻化微珠。其中,多种粒径级配的玻化微珠可增加腻子的分子间隙,但不影响连续性,从而达到等体积质量轻且隔热保温的效果。
作为优选,所述玻化微珠的粒径为0.3mm-0.65mm。
作为优选,所述无机胶凝材料包括硅酸盐水泥。
作为优选,所述无机填料选自重钙粉、硅灰粉、石英粉、灰钙粉、粉煤灰或石英砂中的一种或几种。
作为优选,所述助剂选自纤维素、抗裂纤维、分散剂、防腐剂或润湿剂中的一种或几种。其中防腐剂起到保险的作用;而润湿剂和分散剂一样,都是单一的助剂,它的作用就是改善产品表面的张力和渗透性。
作为优选,所述抗裂纤维包括黑、白木质纤维、3mm短纤维。
作为优选,所述分散剂包括聚乙烯醇。其中,多种级配的抗裂纤维、聚乙烯醇与无机胶凝材料组成的链球状分子链接体系可提高腻子的抗拉强度。
与现有技术相比,本发明的轻质弹性外墙保温抗裂腻子的导热系数与保温墙面的导热系数接近,可使得腻子的变形跟保温材料同步,从而降低裂缝出现的可能性,并且,具有普通弹性腻子的弹性抗裂效果,还减轻了墙体的重量,从而降低了剪切应力,能满足新材料的抗裂要求。
具体实施方式
以下结合具体实施例来说明本发明,下列实施例仅用于说明本发明的配方,并不限定本发明的保护范围。
玻化微珠:是一种以天然矿石珍珠岩也叫火山岩为原料,颗粒分30-50,50-70目,经过玻化炉1100°左右,从低温到高温生出来的一种由表面玻化硬壳球体蜂窝状的颗粒产品。其内部为空腔结构,理化性能十分稳定,耐老化、耐候性强,具有轻质、绝热、防火、吸音和吸水率小等优异性能,适合在绝热、防火、吸音和保温的墙体材料中做填充骨料。本发明中,用玻化微珠做轻质骨料,不仅弥补了使用普通膨胀珍珠岩做轻质骨料的诸多缺陷和不足,即克服了珍珠岩吸水率大、易粉化、在搅拌中体积收缩率大、后期保温性能低和易空鼓开裂等缺点,还可提高产品的易流动性和自抗强度,减少材性收缩率,提高产品综合性能,并能降低综合成本。
实施例1
一种轻质弹性外墙保温抗裂腻子,该抗裂腻子由以下组分混合而成:8份硅丙乳液、18份玻化微珠、19.5份重钙粉、22份硅酸盐水泥、6份纤维素、1份抗裂纤维、1份聚乙烯醇、1份防腐剂和1份润湿剂。
实施例2
一种轻质弹性外墙保温抗裂腻子,该抗裂腻子由以下组分混合而成:6份互穿网络结构聚合物乳液、4份纯丙乳液、20份玻化微珠、11份石英粉、10份石英砂、23份硅酸盐水泥、6份纤维素、1份抗裂纤维、2份聚乙烯醇、1份防腐剂和1份润湿剂。
实施例3
一种轻质弹性外墙保温抗裂腻子,该抗裂腻子由以下组分混合而成:12份纯丙乳液、21份玻化微珠、13份硅灰粉、10份灰钙粉、25份硅酸盐水泥、6份纤维素、1份抗裂纤维、2份聚乙烯醇、1份防腐剂和2份润湿剂。
实施例4
一种轻质弹性外墙保温抗裂腻子,该抗裂腻子由以下组分混合而成:7份苯丙共聚乳液、7份纯丙乳液、23份玻化微珠、15份粉煤灰、10份重钙粉、26份硅酸盐水泥、6份纤维素、2份抗裂纤维、1份聚乙烯醇、2份防腐剂和2份润湿剂。
实施例5
一种轻质弹性外墙保温抗裂腻子,该抗裂腻子由以下组分混合而成:15.5份苯丙乳液、24.5份玻化微珠、26.5石英粉、28份硅酸盐水泥、6份纤维素、2份抗裂纤维、2份聚乙烯醇、2份防腐剂和2份润湿剂。
以上公开的内容仅为本申请的几个具体实施例,但本申请并非局限于此,任何本领域的技术人员能思之的变化,都应落在本申请的保护范围内。
Claims (9)
1.一种轻质弹性外墙保温抗裂腻子,其特征在于,包括以重量份计的以下组分:
2.根据利要求1所述的轻质弹性外墙保温抗裂腻子,其特征在于,所述聚氨酯硅丙聚合物选自硅丙乳液、纯丙乳液、苯丙乳液、互穿网络结构聚合物乳液或苯丙共聚乳液中的一种或几种。
3.根据权利要求1所述的轻质弹性外墙保温抗裂腻子,其特征在于,所述轻质隔热材料包括玻化微珠。
4.根据权利要求3所述的轻质弹性外墙保温抗裂腻子,其特征在于,所述玻化微珠的粒径为0.3mm-0.65mm。
5.根据权利要求1所述的轻质弹性外墙保温抗裂腻子,其特征在于,所述无机胶凝材料包括硅酸盐水泥。
6.根据权利要求1所述的轻质弹性外墙保温抗裂腻子,其特征在于,所述无机填料选自重钙粉、硅灰粉、石英粉、灰钙粉、粉煤灰或石英砂中的一种或几种。
7.根据权利要求1所述的轻质弹性外墙保温抗裂腻子,其特征在于,所述助剂选自纤维素、抗裂纤维、分散剂、防腐剂或润湿剂中的一种或几种。
8.根据权利要求7所述的轻质弹性外墙保温抗裂腻子,其特征在于,所述抗裂纤维包括黑、白木质纤维、3mm短纤维。
9.根据权利要求7所述的轻质弹性外墙保温抗裂腻子,其特征在于,所述分散剂包括聚乙烯醇。