CN104556936A - 一种高抗压乳化沥青复合保温砂浆 - Google Patents

一种高抗压乳化沥青复合保温砂浆 Download PDF

Info

Publication number
CN104556936A
CN104556936A CN201410808381.6A CN201410808381A CN104556936A CN 104556936 A CN104556936 A CN 104556936A CN 201410808381 A CN201410808381 A CN 201410808381A CN 104556936 A CN104556936 A CN 104556936A
Authority
CN
China
Prior art keywords
parts
water
powder
attapulgite
compression
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410808381.6A
Other languages
English (en)
Inventor
汪国亮
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Tongling Post Building Energy-Saving Technology Ltd Co
Original Assignee
Tongling Post Building Energy-Saving Technology Ltd Co
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Tongling Post Building Energy-Saving Technology Ltd Co filed Critical Tongling Post Building Energy-Saving Technology Ltd Co
Priority to CN201410808381.6A priority Critical patent/CN104556936A/zh
Publication of CN104556936A publication Critical patent/CN104556936A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种高抗压乳化沥青复合保温砂浆，其是由下述重量份的原料制得：明矾2-4、三聚磷酸钠1-2、松脂岩5-10、SMAC高效低碱膨胀剂1-2、可再分散乳胶粉4-5、SN-T4型防冻减水剂1-3、氟化钙4-6、胡敏酸0.4-0.6、氨基磺酸0.3-0.7、干酪素6-10、芒硝0.3-0.6、水镁石4-8、乳化沥青20-30、水适量、改性包膜凹凸棒土24-38、石膏10-20、水泥20-35。

Description

一种高抗压乳化沥青复合保温砂浆
技术领域
本发明涉及保温砂浆领域，确切地说是一种高抗压乳化沥青复合保温砂浆。
背景技术
保温砂浆是以各种轻质材料为骨料，以水泥为胶凝料，掺和一些改性添加剂，经生产企业搅拌混合而制成的一种预拌干粉砂浆。用于构筑建筑表面保温层的一种建筑材料。
乳化沥青是沥青和乳化剂在一定工艺作用下，生成水包油或油包水（具体谁包谁要看乳化剂的种类）的液态沥青。 乳化沥青是将通常高温使用的道路沥青，经过机械搅拌和化学稳定的方法（乳化），扩散到水中而液化成常温下粘度很低、流动性很好的一种道路建筑材料。可以常温使用，也可以和冷、潮湿的石料一起使用。
发明内容
本发明的目的在于提供一种高抗压乳化沥青复合保温砂浆。
上述目的通过以下方案实现：
    一种高抗压乳化沥青复合保温砂浆，其特征在于：其是由下述重量份的原料制得：明矾2-4、三聚磷酸钠1-2、松脂岩5-10、SMAC高效低碱膨胀剂1-2、可再分散乳胶粉4-5、SN-T4型防冻减水剂1-3、氟化钙4-6、胡敏酸0.4-0.6、氨基磺酸0.3-0.7、干酪素6-10、芒硝0.3-0.6、水镁石4-8、乳化沥青20-30、水适量、改性包膜凹凸棒土24-38、石膏10-20、水泥20-35；
改性包膜凹凸棒土由下述重量份的原料制得：
凹凸棒土100-200、2，5-二叔丁基对苯二酚1-2、低分子量聚乙烯蜡粉料40-50、硅酸钠10-15、水100-200、阿拉伯胶1-3、烷基苯磺酸钠1-2、偏硅酸钠3-5、苄基酚聚氧乙烯醚1.5-3.8、脂肪酸甘油酯3-6，亚硫酸氢钠1-2；
改性包膜凹凸棒土的制备方法为：
（1）将低分子量聚乙烯蜡粉料、水、阿拉伯胶、烷基苯磺酸钠、偏硅酸钠加入反应釜中，35-45℃下搅拌，再加入苄基酚聚氧乙烯醚、脂肪酸甘油酯、亚硫酸氢钠、300-400转/分搅拌均匀，升温至170-200℃，400-600rpm下搅拌均匀，制成改性聚乙烯蜡乳液；
（2）将凹凸棒土加入到改性聚乙烯蜡乳液中，然后缓慢加入其余原料，40-60转/分搅拌5-10min后，烘干，即得。
所述的一种高抗压乳化沥青复合保温砂浆，其特征在于：
制备方法包括以下步骤：
（1）水镁石、松脂岩混匀后，破碎，过100-120目筛，得复配矿物粉备用；
（2）将明矾、三聚磷酸钠、氟化钙、胡敏酸、氨基磺酸、干酪素混匀，加适量水配成溶液，再均匀喷于复配矿物粉表面，干燥后，研磨，过100-200目筛，得改性粉料备用；
（3）所得改性粉料与其余原料混匀搅拌后，即得。
本发明的有益效果为：该发明的优点是通过包膜改性，使砂浆既具施工方便，附着力强的同时保温效果增强，施工结束后不易开鼓、脱落又能有效防水防火，同时具有抗压能力。
具体实施方式
 一种高抗压乳化沥青复合保温砂浆，其是由下述重量（kg)的原料制得：明矾2、三聚磷酸钠1、松脂岩10、SMAC高效低碱膨胀剂2、可再分散乳胶粉5、SN-T4型防冻减水剂3、氟化钙6、胡敏酸0.6、氨基磺酸0.7、干酪素10、芒硝0.6、水镁石8、乳化沥青30、水适量、改性包膜凹凸棒土28、石膏20、水泥25；
改性包膜凹凸棒土由下述重量（kg)的原料制得：
凹凸棒土160、2，5-二叔丁基对苯二酚1、低分子量聚乙烯蜡粉料50、硅酸钠10、水200、阿拉伯胶3、烷基苯磺酸钠2、偏硅酸钠5、苄基酚聚氧乙烯醚1.8、脂肪酸甘油酯6，亚硫酸氢钠2；
改性包膜凹凸棒土的制备方法为：
（1）将低分子量聚乙烯蜡粉料、水、阿拉伯胶、烷基苯磺酸钠、偏硅酸钠加入反应釜中，45℃下搅拌，再加入苄基酚聚氧乙烯醚、脂肪酸甘油酯、亚硫酸氢钠、400转/分搅拌均匀，升温至180℃，600rpm下搅拌均匀，制成改性聚乙烯蜡乳液；
（2）将凹凸棒土加入到改性聚乙烯蜡乳液中，然后缓慢加入其余原料，60转/分搅拌8min后，烘干，即得。
所述的一种高抗压乳化沥青复合保温砂浆，制备方法包括以下步骤：
（1）水镁石、松脂岩混匀后，破碎，过120目筛，得复配矿物粉备用；
（2）将明矾、三聚磷酸钠、氟化钙、胡敏酸、氨基磺酸、干酪素混匀，加适量水配成溶液，再均匀喷于复配矿物粉表面，干燥后，研磨，过200目筛，得改性粉料备用；
(3)所得改性粉料与其余原料混匀搅拌后，即得。
    本实施例涂抹于混凝土墙面，可操作时间为2h,与混凝土墙面基本结合，测试其导热系数为0.052W/(m·K)，28天标准养护下拉伸粘结强度为0.82MPa,28天标准养护下泡于水中七天拉伸粘结强度为0.55MPa，抗压强度3MPa。

Claims (2)

1.一种高抗压乳化沥青复合保温砂浆，其特征在于：其是由下述重量份的原料制得：明矾2-4、三聚磷酸钠1-2、松脂岩5-10、SMAC高效低碱膨胀剂1-2、可再分散乳胶粉4-5、SN-T4型防冻减水剂1-3、氟化钙4-6、胡敏酸0.4-0.6、氨基磺酸0.3-0.7、干酪素6-10、芒硝0.3-0.6、水镁石4-8、乳化沥青20-30、水适量、改性包膜凹凸棒土24-38、石膏10-20、水泥20-35；
改性包膜凹凸棒土由下述重量份的原料制得：
凹凸棒土100-200、2，5-二叔丁基对苯二酚1-2、低分子量聚乙烯蜡粉料40-50、硅酸钠10-15、水100-200、阿拉伯胶1-3、烷基苯磺酸钠1-2、偏硅酸钠3-5、苄基酚聚氧乙烯醚1.5-3.8、脂肪酸甘油酯3-6，亚硫酸氢钠1-2；
改性包膜凹凸棒土的制备方法为：
（1）将低分子量聚乙烯蜡粉料、水、阿拉伯胶、烷基苯磺酸钠、偏硅酸钠加入反应釜中，35-45℃下搅拌，再加入苄基酚聚氧乙烯醚、脂肪酸甘油酯、亚硫酸氢钠、300-400转/分搅拌均匀，升温至170-200℃，400-600rpm下搅拌均匀，制成改性聚乙烯蜡乳液；
（2）将凹凸棒土加入到改性聚乙烯蜡乳液中，然后缓慢加入其余原料，40-60转/分搅拌5-10min后，烘干，即得。
2.根据权利要求1所述的一种高抗压乳化沥青复合保温砂浆，其特征在于：
制备方法包括以下步骤：
（1）水镁石、松脂岩混匀后，破碎，过100-120目筛，得复配矿物粉备用；
（2）将明矾、三聚磷酸钠、氟化钙、胡敏酸、氨基磺酸、干酪素混匀，加适量水配成溶液，再均匀喷于复配矿物粉表面，干燥后，研磨，过100-200目筛，得改性粉料备用；
（3）所得改性粉料与其余原料混匀搅拌后，即得。
CN201410808381.6A 2014-12-23 2014-12-23 一种高抗压乳化沥青复合保温砂浆 Pending CN104556936A (zh)