CN104556861A - 一种可以快速硬化的乳化沥青保温砂浆 - Google Patents

一种可以快速硬化的乳化沥青保温砂浆 Download PDF

Info

Publication number
CN104556861A
CN104556861A CN201410808384.XA CN201410808384A CN104556861A CN 104556861 A CN104556861 A CN 104556861A CN 201410808384 A CN201410808384 A CN 201410808384A CN 104556861 A CN104556861 A CN 104556861A
Authority
CN
China
Prior art keywords
parts
water
stir
attapulgite
polyethylene wax
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410808384.XA
Other languages
English (en)
Inventor
汪国亮
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Tongling Post Building Energy-Saving Technology Ltd Co
Original Assignee
Tongling Post Building Energy-Saving Technology Ltd Co
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Tongling Post Building Energy-Saving Technology Ltd Co filed Critical Tongling Post Building Energy-Saving Technology Ltd Co
Priority to CN201410808384.XA priority Critical patent/CN104556861A/zh
Publication of CN104556861A publication Critical patent/CN104556861A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种可以快速硬化的乳化沥青保温砂浆，其是由下述重量份的原料制得：乳化沥青50-80、水70-110、氧化镁1-2、粉煤灰1-2、木素磺酸钙1-2、硅藻土1-2、膨胀骨料5-15、聚苯乙烯泡沫颗粒8-10、水泥90-130、聚丙烯纤维1-3、金矿尾矿0.5-0.6、羧甲基纤维素0.1-0.3、硅油1-3、改性包覆凹凸棒土30-40、河砂20-40。

Description

一种可以快速硬化的乳化沥青保温砂浆
技术领域
本发明涉及保温砂浆领域，确切地说是一种可以快速硬化的乳化沥青保温砂浆。
背景技术
保温砂浆是以各种轻质材料为骨料，以水泥为胶凝料，掺和一些改性添加剂，经生产企业搅拌混合而制成的一种预拌干粉砂浆。用于构筑建筑表面保温层的一种建筑材料。
乳化沥青是沥青和乳化剂在一定工艺作用下，生成水包油或油包水（具体谁包谁要看乳化剂的种类）的液态沥青。 乳化沥青是将通常高温使用的道路沥青，经过机械搅拌和化学稳定的方法（乳化），扩散到水中而液化成常温下粘度很低、流动性很好的一种道路建筑材料。可以常温使用，也可以和冷、潮湿的石料一起使用。
发明内容
本发明的目的在于提供一种可以快速硬化的乳化沥青保温砂浆。
上述目的通过以下方案实现：
    一种可以快速硬化的乳化沥青保温砂浆，其特征在于：其是由下述重量份的原料制得：
乳化沥青50-80、水70-110、氧化镁1-2、粉煤灰1-2、木素磺酸钙1-2、硅藻土1-2、膨胀骨料5-15、聚苯乙烯泡沫颗粒8-10、水泥90-130、聚丙烯纤维1-3、金矿尾矿0.5-0.6、羧甲基纤维素0.1-0.3、硅油1-3、改性包覆凹凸棒土30-40、河砂20-40；
改性包覆凹凸棒土由下述重量份的原料制得：
凹凸棒土100-200、2，5-二叔丁基对苯二酚1-2、低分子量聚乙烯蜡粉料40-50、硅酸钠10-15、水100-200、阿拉伯胶1-3、烷基苯磺酸钠1-2、偏硅酸钠3-5、苄基酚聚氧乙烯醚1.5-3.8、脂肪酸甘油酯3-6，亚硫酸氢钠1-2；
改性包覆凹凸棒土的制备方法为：
（1）将低分子量聚乙烯蜡粉料、水、阿拉伯胶、烷基苯磺酸钠、偏硅酸钠加入反应釜中，35-45℃下搅拌，再加入苄基酚聚氧乙烯醚、脂肪酸甘油酯、亚硫酸氢钠、300-400转/分搅拌均匀，升温至170-200℃，400-600rpm下搅拌均匀，制成改性聚乙烯蜡乳液；
（2）将凹凸棒土加入到改性聚乙烯蜡乳液中，然后缓慢加入其余原料，40-60转/粉搅拌5-10min后，烘干，即得。
所述的一种可以快速硬化的乳化沥青保温砂浆，其特征在于：
制备方法包括以下步骤：
(1)羧甲基纤维素、硅油、聚丙烯纤维、氧化镁混匀后，加适量水搅拌均匀，再喷于聚苯乙烯泡沫颗粒表面，自然干燥；
(2)将剩余原料搅拌均匀，加剩余的水，20-30℃下，50-70转/分搅拌30-50min，得浆料备用；
(3)将步骤（1）所得物料与步骤（2）所得浆料混匀，在100-200转/分下搅拌1-2h，即得。
本发明的有益效果为：本发明生产工艺简单、生产效率高、产品强度大、热导率低、能够快速凝结硬化,不开裂、不空鼓,使用寿命长。
具体实施方式
一种可以快速硬化的乳化沥青保温砂浆，其是由下述重量（kg)的原料制得：
乳化沥青60、水100、氧化镁1、粉煤灰2、木素磺酸钙1、硅藻土2、膨胀骨料15、聚苯乙烯泡沫颗粒10、水泥90、聚丙烯纤维3、金矿尾矿0.5、羧甲基纤维素0.3、硅油1、改性包覆凹凸棒土40、河砂40；
改性包覆凹凸棒土由下述重量（kg)的原料制得：
凹凸棒土200、2，5-二叔丁基对苯二酚2、低分子量聚乙烯蜡粉料50、硅酸钠15、水200、阿拉伯胶、烷基苯磺酸钠1、偏硅酸钠5、苄基酚聚氧乙烯醚1.8、脂肪酸甘油酯6，亚硫酸氢钠1；
改性包覆凹凸棒土的制备方法为：
（1）将低分子量聚乙烯蜡粉料、水、阿拉伯胶、烷基苯磺酸钠、偏硅酸钠加入反应釜中，45℃下搅拌，再加入苄基酚聚氧乙烯醚、脂肪酸甘油酯、亚硫酸氢钠、400转/分搅拌均匀，升温至170℃，600rpm下搅拌均匀，制成改性聚乙烯蜡乳液；
（2）将凹凸棒土加入到改性聚乙烯蜡乳液中，然后缓慢加入其余原料，60转/粉搅拌10min后，烘干，即得。
所述的一种可以快速硬化的乳化沥青保温砂浆，
制备方法包括以下步骤：
(1)羧甲基纤维素、硅油、聚丙烯纤维、氧化镁混匀后，加适量水搅拌均匀，再喷于聚苯乙烯泡沫颗粒表面，自然干燥；
(2)将剩余原料搅拌均匀，加剩余的水，30℃下，70转/分搅拌50min，得浆料备用；
(3)将步骤（1）所得物料与步骤（2）所得浆料混匀，在200转/分下搅拌2h，即得。
    本实施例涂抹于混凝土墙面，可操作时间为2h,与混凝土墙面基本结合，测试其导热系数为0.048W/(m·K)，28天标准养护下拉伸粘结强度为0.8MPa,28天标准养护下泡于水中七天拉伸粘结强度为0.57MPa，不透水性（0.3MPa,30min)：不透水。抗压强度2.1MPa。

Claims (2)

1.一种可以快速硬化的乳化沥青保温砂浆，其特征在于：其是由下述重量份的原料制得：
乳化沥青50-80、水70-110、氧化镁1-2、粉煤灰1-2、木素磺酸钙1-2、硅藻土1-2、膨胀骨料5-15、聚苯乙烯泡沫颗粒8-10、水泥90-130、聚丙烯纤维1-3、金矿尾矿0.5-0.6、羧甲基纤维素0.1-0.3、硅油1-3、改性包覆凹凸棒土30-40、河砂20-40；
改性包覆凹凸棒土由下述重量份的原料制得：
凹凸棒土100-200、2，5-二叔丁基对苯二酚1-2、低分子量聚乙烯蜡粉料40-50、硅酸钠10-15、水100-200、阿拉伯胶1-3、烷基苯磺酸钠1-2、偏硅酸钠3-5、苄基酚聚氧乙烯醚1.5-3.8、脂肪酸甘油酯3-6，亚硫酸氢钠1-2；
改性包覆凹凸棒土的制备方法为：
（1）将低分子量聚乙烯蜡粉料、水、阿拉伯胶、烷基苯磺酸钠、偏硅酸钠加入反应釜中，35-45℃下搅拌，再加入苄基酚聚氧乙烯醚、脂肪酸甘油酯、亚硫酸氢钠、300-400转/分搅拌均匀，升温至170-200℃，400-600rpm下搅拌均匀，制成改性聚乙烯蜡乳液；
（2）将凹凸棒土加入到改性聚乙烯蜡乳液中，然后缓慢加入其余原料，40-60转/粉搅拌5-10min后，烘干，即得。
2.根据权利要求1所述的一种可以快速硬化的乳化沥青保温砂浆，其特征在于：
制备方法包括以下步骤：
（1）羧甲基纤维素、硅油、聚丙烯纤维、氧化镁混匀后，加适量水搅拌均匀，再喷于聚苯乙烯泡沫颗粒表面，自然干燥；
（2）将剩余原料搅拌均匀，加剩余的水，20-30℃下，50-70转/分搅拌30-50min，得浆料备用；
（3）将步骤（1）所得物料与步骤（2）所得浆料混匀，在100-200转/分下搅拌1-2h，即得。
CN201410808384.XA 2014-12-23 2014-12-23 一种可以快速硬化的乳化沥青保温砂浆 Pending CN104556861A (zh)