CN104591602A - 一种可抗裂外墙乳化沥青复合保温砂浆 - Google Patents
一种可抗裂外墙乳化沥青复合保温砂浆 Download PDFInfo
- Publication number
- CN104591602A CN104591602A CN201410810007.XA CN201410810007A CN104591602A CN 104591602 A CN104591602 A CN 104591602A CN 201410810007 A CN201410810007 A CN 201410810007A CN 104591602 A CN104591602 A CN 104591602A
- Authority
- CN
- China
- Prior art keywords
- parts
- water
- powder
- attapulgite
- insulation mortar
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种可抗裂外墙乳化沥青复合保温砂浆,其是由下述重量份的原料制得:乳化沥青60-70、水90-100、石膏20-30、硝酸钠0.15-0.3,改性包膜凹凸棒土14-18、明矾2-5、柠檬酸钠0.1-0.2、腰果壳油1-2、赤泥3-5、碳酰二胺2-3、羟乙基纤维素0.5-1,玉米淀粉3-6、聚四氟乙烯粉2-3、萤石0.05-0.06、镁橄榄石4-8、铝矾土5-8、莫来砂10-15、陶砂10-20、糊精4-6、氯化铵0.1-0.2、三乙醇胺0.2-0.4、聚酯纤维1-2、玻化微珠20-30。
Description
技术领域
本发明涉及保温砂浆领域,确切地说是一种可抗裂外墙乳化沥青复合保温砂浆。
背景技术
保温砂浆是以各种轻质材料为骨料,以水泥为胶凝料,掺和一些改性添加剂,经生产企业搅拌混合而制成的一种预拌干粉砂浆。用于构筑建筑表面保温层的一种建筑材料。
乳化沥青是沥青和乳化剂在一定工艺作用下,生成水包油或油包水(具体谁包谁要看乳化剂的种类)的液态沥青。 乳化沥青是将通常高温使用的道路沥青,经过机械搅拌和化学稳定的方法(乳化),扩散到水中而液化成常温下粘度很低、流动性很好的一种道路建筑材料。可以常温使用,也可以和冷、潮湿的石料一起使用。
发明内容
本发明的目的在于提供一种可抗裂外墙乳化沥青复合保温砂浆。
上述目的通过以下方案实现:
一种可抗裂外墙乳化沥青复合保温砂浆,其特征在于:其是由下述重量份的原料制得:
乳化沥青60-70、水90-100、石膏20-30、硝酸钠0.15-0.3,改性包膜凹凸棒土14-18、明矾2-5、柠檬酸钠0.1-0.2、腰果壳油1-2、赤泥3-5、碳酰二胺2-3、羟乙基纤维素0.5-1,玉米淀粉3-6、聚四氟乙烯粉2-3、萤石0.05-0.06、镁橄榄石4-8、铝矾土5-8、莫来砂10-15、陶砂10-20、糊精4-6、氯化铵0.1-0.2、三乙醇胺0.2-0.4、聚酯纤维1-2、玻化微珠20-30;
改性包膜凹凸棒土由下述重量份的原料制得:
凹凸棒土100-200、2,5-二叔丁基对苯二酚1-2、低分子量聚乙烯蜡粉料40-50、硅酸钠10-15、水100-200、阿拉伯胶1-3、烷基苯磺酸钠1-2、偏硅酸钠3-5、苄基酚聚氧乙烯醚1.5-3.8、脂肪酸甘油酯3-6,亚硫酸氢钠1-2;
改性包膜凹凸棒土的制备方法为:
(1)将低分子量聚乙烯蜡粉料、水、阿拉伯胶、烷基苯磺酸钠、偏硅酸钠加入反应釜中,35-45℃下搅拌,再加入苄基酚聚氧乙烯醚、脂肪酸甘油酯、亚硫酸氢钠、300-400转/分搅拌均匀,升温至170-200℃,400-600rpm下搅拌均匀,制成改性聚乙烯蜡乳液;
(2)将凹凸棒土加入到改性聚乙烯蜡乳液中,然后加入其余原料,40-60转/分搅拌5-10min后,烘干,即得。
所述的一种可抗裂外墙乳化沥青复合保温砂浆,其特征在于:
制备方法包括以下步骤:
(1)萤石、镁橄榄石混匀后,100-200℃煅烧1-2小时,取出,破碎,过100-120目筛,后再与铝矾土、莫来砂、陶砂混匀,得复配矿物粉备用;
(2)将明矾、柠檬酸钠、腰果壳油、糊精、氯化铵、三乙醇胺,加适量水配成浆料,再均匀喷于复配矿物粉表面,干燥后,研磨,过100-200目筛,得复配包覆粉料备用;
(3)所得复配包覆粉料与其余原料混匀搅拌后,即得。
本发明的有益效果为:本发明通过添加玉米淀粉、糊精、聚四氟乙烯粉等原料,使其具有了非常好的抗裂性能,且通过添加莫来砂等原料使得其强度高,保温性能优异,使用寿命长。
具体实施方式
一种可抗裂外墙乳化沥青复合保温砂浆,其是由下述重量(kg)的原料制得:
乳化沥青70、水100、石膏30、硝酸钠0.15,改性包膜凹凸棒土18、明矾3、柠檬酸钠0.1、腰果壳油1、赤泥3、碳酰二胺2、羟乙基纤维素0.5,玉米淀粉3、聚四氟乙烯粉2、萤石0.05、镁橄榄石8、铝矾土5、莫来砂15、陶砂20、糊精4、氯化铵0.1、三乙醇胺0.2、聚酯纤维1、玻化微珠20;
改性包膜凹凸棒土由下述重量(kg)的原料制得:
凹凸棒土100、2,5-二叔丁基对苯二酚2、低分子量聚乙烯蜡粉料50、硅酸钠15、水100、阿拉伯胶1、烷基苯磺酸钠1、偏硅酸钠3、苄基酚聚氧乙烯醚1.5、脂肪酸甘油酯3,亚硫酸氢钠1;
改性包膜凹凸棒土的制备方法为:
(1)将低分子量聚乙烯蜡粉料、水、阿拉伯胶、烷基苯磺酸钠、偏硅酸钠加入反应釜中,35℃下搅拌,再加入苄基酚聚氧乙烯醚、脂肪酸甘油酯、亚硫酸氢钠、400转/分搅拌均匀,升温至170℃,400rpm下搅拌均匀,制成改性聚乙烯蜡乳液;
(2)将凹凸棒土加入到改性聚乙烯蜡乳液中,然后加入其余原料,60转/分搅拌10min后,烘干,即得。
所述的一种可抗裂外墙乳化沥青复合保温砂浆,
制备方法包括以下步骤:
(1)萤石、镁橄榄石混匀后,140℃煅烧2小时,取出,破碎,过100目筛,后再与铝矾土、莫来砂、陶砂混匀,得复配矿物粉备用;
(2)将明矾、柠檬酸钠、腰果壳油、糊精、氯化铵、三乙醇胺,加适量水配成浆料,再均匀喷于复配矿物粉表面,干燥后,研磨,过100目筛,得复配包覆粉料备用;
(3)所得复配包覆粉料与其余原料混匀搅拌后,即得。
本实施例涂抹于混凝土墙面,可操作时间为2.2h,与混凝土墙面基本结合,测试其导热系数为0.053W/(m·K),28天标准养护下拉伸粘结强度为0.9MPa,28天标准养护下泡于水中七天拉伸粘结强度为0.61MPa。
Claims (2)
1.一种可抗裂外墙乳化沥青复合保温砂浆,其特征在于:其是由下述重量份的原料制得:
乳化沥青60-70、水90-100、石膏20-30、硝酸钠0.15-0.3,改性包膜凹凸棒土14-18、明矾2-5、柠檬酸钠0.1-0.2、腰果壳油1-2、赤泥3-5、碳酰二胺2-3、羟乙基纤维素0.5-1,玉米淀粉3-6、聚四氟乙烯粉2-3、萤石0.05-0.06、镁橄榄石4-8、铝矾土5-8、莫来砂10-15、陶砂10-20、糊精4-6、氯化铵0.1-0.2、三乙醇胺0.2-0.4、聚酯纤维1-2、玻化微珠20-30;
改性包膜凹凸棒土由下述重量份的原料制得:
凹凸棒土100-200、2,5-二叔丁基对苯二酚1-2、低分子量聚乙烯蜡粉料40-50、硅酸钠10-15、水100-200、阿拉伯胶1-3、烷基苯磺酸钠1-2、偏硅酸钠3-5、苄基酚聚氧乙烯醚1.5-3.8、脂肪酸甘油酯3-6,亚硫酸氢钠1-2;
改性包膜凹凸棒土的制备方法为:
(1)将低分子量聚乙烯蜡粉料、水、阿拉伯胶、烷基苯磺酸钠、偏硅酸钠加入反应釜中,35-45℃下搅拌,再加入苄基酚聚氧乙烯醚、脂肪酸甘油酯、亚硫酸氢钠、300-400转/分搅拌均匀,升温至170-200℃,400-600rpm下搅拌均匀,制成改性聚乙烯蜡乳液;
(2)将凹凸棒土加入到改性聚乙烯蜡乳液中,然后加入其余原料,40-60转/分搅拌5-10min后,烘干,即得。
2.根据权利要求1所述的一种可抗裂外墙乳化沥青复合保温砂浆,其特征在于:
制备方法包括以下步骤:
(1)萤石、镁橄榄石混匀后,100-200℃煅烧1-2小时,取出,破碎,过100-120目筛,后再与铝矾土、莫来砂、陶砂混匀,得复配矿物粉备用;
(2)将明矾、柠檬酸钠、腰果壳油、糊精、氯化铵、三乙醇胺,加适量水配成浆料,再均匀喷于复配矿物粉表面,干燥后,研磨,过100-200目筛,得复配包覆粉料备用;
(3)所得复配包覆粉料与其余原料混匀搅拌后,即得。