CN104556863A - 一种含有磁石的高效能乳化沥青保温砂浆 - Google Patents

一种含有磁石的高效能乳化沥青保温砂浆 Download PDF

Info

Publication number
CN104556863A
CN104556863A CN201410808805.9A CN201410808805A CN104556863A CN 104556863 A CN104556863 A CN 104556863A CN 201410808805 A CN201410808805 A CN 201410808805A CN 104556863 A CN104556863 A CN 104556863A
Authority
CN
China
Prior art keywords
parts
powder
water
attapulgite
stir
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410808805.9A
Other languages
English (en)
Inventor
汪国亮
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Tongling Post Building Energy-Saving Technology Ltd Co
Original Assignee
Tongling Post Building Energy-Saving Technology Ltd Co
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Tongling Post Building Energy-Saving Technology Ltd Co filed Critical Tongling Post Building Energy-Saving Technology Ltd Co
Priority to CN201410808805.9A priority Critical patent/CN104556863A/zh
Publication of CN104556863A publication Critical patent/CN104556863A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种含有磁石的高效能乳化沥青保温砂浆，其是由下述重量份的原料制得：板栗壳5-8、水泥20-30、磁石4-8、重晶石2-4、硼酸0.2-0.4、纯碱1-2、电石渣1-3、甲酸钙2-3、玻化微珠30-40、硫酸钙2-4,膨胀石墨粉4-6、正硅酸乙酯1-2、硬脂酸1-2、石灰石5-6、火山灰4-5、石棉纤维4-6、二甲基硅油1-2、脱硫灰1-3、玻化微珠20-25、乳化沥青80-90、水90-130、改性包膜凹凸棒土5-8。

Description

一种含有磁石的高效能乳化沥青保温砂浆
技术领域
本发明涉及保温砂浆领域，确切地说是一种含有磁石的高效能乳化沥青保温砂浆。 
背景技术
保温砂浆是以各种轻质材料为骨料，以水泥为胶凝料，掺和一些改性添加剂，经生产企业搅拌混合而制成的一种预拌干粉砂浆。用于构筑建筑表面保温层的一种建筑材料。
乳化沥青是沥青和乳化剂在一定工艺作用下，生成水包油或油包水（具体谁包谁要看乳化剂的种类）的液态沥青。 乳化沥青是将通常高温使用的道路沥青，经过机械搅拌和化学稳定的方法（乳化），扩散到水中而液化成常温下粘度很低、流动性很好的一种道路建筑材料。可以常温使用，也可以和冷、潮湿的石料一起使用。
发明内容
本发明的目的在于提供一种含有磁石的高效能乳化沥青保温砂浆，。
上述目的通过以下方案实现：
     一种含有磁石的高效能乳化沥青保温砂浆，其特征在于：其是由下述重量份的原料制得：
板栗壳5-8、水泥20-30、磁石4-8、重晶石2-4、硼酸0.2-0.4、纯碱1-2、电石渣1-3、甲酸钙2-3、玻化微珠30-40、硫酸钙2-4,膨胀石墨粉4-6、正硅酸乙酯1-2、硬脂酸1-2、石灰石5-6、火山灰4-5、石棉纤维4-6、二甲基硅油1-2、脱硫灰1-3、玻化微珠20-25、乳化沥青80-90、水90-130、改性包膜凹凸棒土5-8；
改性包膜凹凸棒土由下述重量份的原料制得：
凹凸棒土100-200、2，5-二叔丁基对苯二酚1-2、低分子量聚乙烯蜡粉料40-50、硅酸钠10-15、水100-200、阿拉伯胶1-3、烷基苯磺酸钠1-2、偏硅酸钠3-5、苄基酚聚氧乙烯醚1.5-3.8、脂肪酸甘油酯3-6，亚硫酸氢钠1-2；
改性包膜凹凸棒土的制备方法为：
（1）将低分子量聚乙烯蜡粉料、水、阿拉伯胶、烷基苯磺酸钠、偏硅酸钠加入反应釜中，35-45℃下搅拌，再加入苄基酚聚氧乙烯醚、脂肪酸甘油酯、亚硫酸氢钠、300-400转/分搅拌均匀，升温至170-200℃，400-600rpm下搅拌均匀，制成改性聚乙烯蜡乳液；
（2）将凹凸棒土加入到改性聚乙烯蜡乳液中，然后缓慢加入其余原料，40-60转/分搅拌5-10min后，烘干，即得。
所述的一种含有磁石的高效能乳化沥青保温砂浆，其特征在于：
制备方法包括以下步骤：
（1）水洗板栗壳去除杂质后，在60-90℃条件下烘24-48h，破碎，筛选出800-1200μm的板栗壳颗粒，即得板栗壳粉备用；
（2）磁石、重晶石混匀后，破碎，过100-120目筛，后再与火山灰、陶砂混匀，得复配矿物粉备用；
（3）将二甲基硅油、脱硫灰、卵磷脂混匀，加适量水配成溶液，再均匀喷于复配矿物粉表面，干燥后，研磨，过100-200目筛，得改性粉料备用；
（4）所得改性粉料与其余原料混匀搅拌后，即得。
本发明的有益效果为：
该发明的优点是具有较强的保温效果，施工简单，含有磁石粉、陶砂、板栗壳粉等原料，使得本发明强度高的同时相容性好，施工结束后不易开鼓、脱落，同时又无毒环保，对人体健康无害。
具体实施方式
  一种含有磁石的高效能乳化沥青保温砂浆，其是由下述重量（kg)的原料制得：
板栗壳8、水泥20、磁石8、重晶石2、硼酸0.4、纯碱1、电石渣1、甲酸钙3、玻化微珠40、硫酸钙4,膨胀石墨粉4、正硅酸乙酯1、硬脂酸2、石灰石6、火山灰4、石棉纤维6、二甲基硅油1、脱硫灰3、玻化微珠20、乳化沥青90、水130、改性包膜凹凸棒土5；
改性包膜凹凸棒土由下述重量（kg)的原料制得：
凹凸棒土150、2，5-二叔丁基对苯二酚1、低分子量聚乙烯蜡粉料50、硅酸钠10、水100、阿拉伯胶1、烷基苯磺酸钠2、偏硅酸钠5、苄基酚聚氧乙烯醚1.5、脂肪酸甘油酯3，亚硫酸氢钠2；
改性包膜凹凸棒土的制备方法为：
（1）将低分子量聚乙烯蜡粉料、水、阿拉伯胶、烷基苯磺酸钠、偏硅酸钠加入反应釜中，38℃下搅拌，再加入苄基酚聚氧乙烯醚、脂肪酸甘油酯、亚硫酸氢钠、350转/分搅拌均匀，升温至180℃，600rpm下搅拌均匀，制成改性聚乙烯蜡乳液；
（2）将凹凸棒土加入到改性聚乙烯蜡乳液中，然后缓慢加入其余原料，60转/分搅拌8min后，烘干，即得。
所述的一种含有磁石的高效能乳化沥青保温砂浆，制备方法包括以下步骤：
（1）水洗板栗壳去除杂质后，在70℃条件下烘24h，破碎，筛选出800-1200μm的板栗壳颗粒，即得板栗壳粉备用；
（2）磁石、重晶石混匀后，破碎，过120目筛，后再与火山灰、陶砂混匀，得复配矿物粉备用；
（3）将二甲基硅油、脱硫灰、卵磷脂混匀，加适量水配成溶液，再均匀喷于复配矿物粉表面，干燥后，研磨，过200目筛，得改性粉料备用；
（4）所得改性粉料与其余原料混匀搅拌后，即得。
    本实施例涂抹于混凝土墙面，可操作时间为1.6h,与混凝土墙面基本结合，测试其导热系数为0.045W/(m·K)，28天标准养护下拉伸粘结强度为0.79MPa,28天标准养护下泡于水中七天拉伸粘结强度为0.54MPa，抗压强度2.4MPa。

Claims (2)

1.一种含有磁石的高效能乳化沥青保温砂浆，，其特征在于：其是由下述重量份的原料制得：
板栗壳5-8、水泥20-30、磁石4-8、重晶石2-4、硼酸0.2-0.4、纯碱1-2、卵磷脂 1-3、甲酸钙2-3、玻化微珠30-40、硫酸钙2-4,膨胀石墨粉4-6、正硅酸乙酯1-2、硬脂酸1-2、石灰石5-6、火山灰4-5、石棉纤维4-6、二甲基硅油1-2、脱硫灰1-3、玻化微珠20-25、乳化沥青80-90、水90-130、改性包膜凹凸棒土5-8；
改性包膜凹凸棒土由下述重量份的原料制得：
凹凸棒土100-200、2，5-二叔丁基对苯二酚1-2、低分子量聚乙烯蜡粉料40-50、硅酸钠10-15、水100-200、阿拉伯胶1-3、烷基苯磺酸钠1-2、偏硅酸钠3-5、苄基酚聚氧乙烯醚1.5-3.8、脂肪酸甘油酯3-6，亚硫酸氢钠1-2；
改性包膜凹凸棒土的制备方法为：
（1）将低分子量聚乙烯蜡粉料、水、阿拉伯胶、烷基苯磺酸钠、偏硅酸钠加入反应釜中，35-45℃下搅拌，再加入苄基酚聚氧乙烯醚、脂肪酸甘油酯、亚硫酸氢钠、300-400转/分搅拌均匀，升温至170-200℃，400-600rpm下搅拌均匀，制成改性聚乙烯蜡乳液；
（2）将凹凸棒土加入到改性聚乙烯蜡乳液中，然后缓慢加入其余原料，40-60转/分搅拌5-10min后，烘干，即得。
2.根据权利要求1所述的一种含有磁石的高效能乳化沥青保温砂浆，，其特征在于：
制备方法包括以下步骤：
（1）水洗板栗壳去除杂质后，在60-90℃条件下烘24-48h，破碎，筛选出800-1200μm的板栗壳颗粒，即得板栗壳粉备用；
（2）磁石、重晶石混匀后，破碎，过100-120目筛，后再与火山灰、陶砂混匀，得复配矿物粉备用；
（3）将二甲基硅油、脱硫灰、卵磷脂混匀，加适量水配成溶液，再均匀喷于复配矿物粉表面，干燥后，研磨，过100-200目筛，得改性粉料备用；
所得改性粉料与其余原料混匀搅拌后，即得。
CN201410808805.9A 2014-12-23 2014-12-23 一种含有磁石的高效能乳化沥青保温砂浆 Pending CN104556863A (zh)