CN104556864A - 一种阻燃效果好的乳化沥青保温砂浆 - Google Patents

一种阻燃效果好的乳化沥青保温砂浆 Download PDF

Info

Publication number
CN104556864A
CN104556864A CN201410809788.0A CN201410809788A CN104556864A CN 104556864 A CN104556864 A CN 104556864A CN 201410809788 A CN201410809788 A CN 201410809788A CN 104556864 A CN104556864 A CN 104556864A
Authority
CN
China
Prior art keywords
parts
water
attapulgite
powder
good flame
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410809788.0A
Other languages
English (en)
Inventor
汪国亮
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Tongling Post Building Energy-Saving Technology Ltd Co
Original Assignee
Tongling Post Building Energy-Saving Technology Ltd Co
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Tongling Post Building Energy-Saving Technology Ltd Co filed Critical Tongling Post Building Energy-Saving Technology Ltd Co
Priority to CN201410809788.0A priority Critical patent/CN104556864A/zh
Publication of CN104556864A publication Critical patent/CN104556864A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种阻燃效果好的乳化沥青保温砂浆，其是由下述重量份的原料制得：玻化微珠40-50、乳化沥青50-70、水70-110、水泥40-50、石灰石1-2.4、三氧化二锑25-35、环氧大豆油4-5、高岭土3-5、苯丙乳液5-10、城市道路废水泥路渣30-40、矿物油脂3-5、PP纤维5-10，偏硼酸钡2-4、UNF-5减水剂1-3、海泡石1-3、沸石3-5、氢氧化钠3-5、改性包覆凹凸棒土10-20。

Description

一种阻燃效果好的乳化沥青保温砂浆
技术领域
本发明涉及保温砂浆领域，确切地说是一种阻燃效果好的乳化沥青保温砂浆。
背景技术
保温砂浆是以各种轻质材料为骨料，以水泥为胶凝料，掺和一些改性添加剂，经生产企业搅拌混合而制成的一种预拌干粉砂浆。用于构筑建筑表面保温层的一种建筑材料。
乳化沥青是沥青和乳化剂在一定工艺作用下，生成水包油或油包水（具体谁包谁要看乳化剂的种类）的液态沥青。 乳化沥青是将通常高温使用的道路沥青，经过机械搅拌和化学稳定的方法（乳化），扩散到水中而液化成常温下粘度很低、流动性很好的一种道路建筑材料。可以常温使用，也可以和冷、潮湿的石料一起使用。
发明内容
本发明的目的在于提供一种阻燃效果好的乳化沥青保温砂浆。
上述目的通过以下方案实现：
    一种阻燃效果好的乳化沥青保温砂浆，其特征在于：其是由下述重量份的原料制得：
玻化微珠40-50、乳化沥青50-70、水70-110、水泥40-50、石灰石1-2.4、三氧化二锑25-35、环氧大豆油4-5、高岭土3-5、苯丙乳液5-10、城市道路废水泥路渣30-40、矿物油脂3-5、PP纤维5-10，偏硼酸钡2-4、UNF-5减水剂1-3、海泡石1-3、沸石3-5、氢氧化钠3-5、改性包覆凹凸棒土10-20；
改性包覆凹凸棒土由下述重量份的原料制得：
凹凸棒土100-200、2，5-二叔丁基对苯二酚1-2、低分子量聚乙烯蜡粉料40-50、硅酸钠10-15、水100-200、阿拉伯胶1-3、烷基苯磺酸钠1-2、偏硅酸钠3-5、苄基酚聚氧乙烯醚1.5-3.8、脂肪酸甘油酯3-6，亚硫酸氢钠1-2、；
改性包覆凹凸棒土的制备方法为：
（1）将低分子量聚乙烯蜡粉料、水、阿拉伯胶、烷基苯磺酸钠、偏硅酸钠加入反应釜中，35-45℃下搅拌，再加入苄基酚聚氧乙烯醚、脂肪酸甘油酯、亚硫酸氢钠、300-400转/分搅拌均匀，升温至170-200℃，400-600rpm下搅拌均匀，制成改性聚乙烯蜡乳液；
（2）将凹凸棒土加入到改性聚乙烯蜡乳液中，然后缓慢加入其余原料，40-60转/分搅拌5-10min后，烘干，即得。
所述的一种阻燃效果好的乳化沥青保温砂浆，其特征在于：
制备方法包括以下步骤：
（1）海泡石、沸石、城市道路废水泥路渣混匀后，300-400℃煅烧1-2小时，取出，破碎，过60-80目筛，与高岭土混匀，得复配矿物粉备用；
（2）将苯丙乳液均匀喷于复配矿物粉表面，干燥后，研磨，过100-200目筛，得复配包覆粉料备用；
（3）所得复配包覆粉料与其余原料于30-40℃下搅拌10-40min，即得。
本发明的有益效果为：本发明具有良好的保温隔热性的同时由于添加了三氧化二锑等原料可以使得本发明阻燃效果好、同时原料来源广泛易得，施工方便，附着力强。
具体实施方式
 一种阻燃效果好的乳化沥青保温砂浆，其是由下述重量（kg)的原料制得：
玻化微珠40、乳化沥青50、水110、水泥50、石灰石2.4、三氧化二锑35、环氧大豆油5、高岭土5、苯丙乳液10、城市道路废水泥路渣30、矿物油脂5、PP纤维5，偏硼酸钡4、UNF-5减水剂1、海泡石3、沸石5、氢氧化钠5、改性包覆凹凸棒土20；
改性包覆凹凸棒土由下述重量（kg)的原料制得：
凹凸棒土160、2，5-二叔丁基对苯二酚1、低分子量聚乙烯蜡粉料40、硅酸钠15、水200、阿拉伯胶3、烷基苯磺酸钠2、偏硅酸钠3、苄基酚聚氧乙烯醚3.8、脂肪酸甘油酯3，亚硫酸氢钠2、；
改性包覆凹凸棒土的制备方法为：
（1）将低分子量聚乙烯蜡粉料、水、阿拉伯胶、烷基苯磺酸钠、偏硅酸钠加入反应釜中，45℃下搅拌，再加入苄基酚聚氧乙烯醚、脂肪酸甘油酯、亚硫酸氢钠、400转/分搅拌均匀，升温至180℃，500rpm下搅拌均匀，制成改性聚乙烯蜡乳液；
（2）将凹凸棒土加入到改性聚乙烯蜡乳液中，然后缓慢加入其余原料，60转/分搅拌10min后，烘干，即得。
所述的一种阻燃效果好的乳化沥青保温砂浆，制备方法包括以下步骤：
（1）海泡石、沸石、城市道路废水泥路渣混匀后，400℃煅烧2小时，取出，破碎，过80目筛，与高岭土混匀，得复配矿物粉备用；
（2）将苯丙乳液均匀喷于复配矿物粉表面，干燥后，研磨，过200目筛，得复配包覆粉料备用；
（3）所得复配包覆粉料与其余原料于40℃下搅拌40min，即得。
 本实施例涂抹于混凝土墙面，可操作时间为1.8h,与混凝土墙面基本结合，测试其导热系数为0.046W/(m·K)，28天标准养护下拉伸粘结强度为0.7MPa,28天标准养护下泡于水中七天拉伸粘结强度为0.58MPa,阻燃等级达到A级。

Claims (2)

1.一种阻燃效果好的乳化沥青保温砂浆，其特征在于：其是由下述重量份的原料制得：
玻化微珠40-50、乳化沥青50-70、水70-110、水泥40-50、石灰石1-2.4、三氧化二锑25-35、环氧大豆油4-5、高岭土3-5、苯丙乳液5-10、城市道路废水泥路渣30-40、矿物油脂3-5、PP纤维5-10，偏硼酸钡2-4、UNF-5减水剂1-3、海泡石1-3、沸石3-5、氢氧化钠3-5、改性包覆凹凸棒土10-20；
改性包覆凹凸棒土由下述重量份的原料制得：
凹凸棒土100-200、2，5-二叔丁基对苯二酚1-2、低分子量聚乙烯蜡粉料40-50、硅酸钠10-15、水100-200、阿拉伯胶1-3、烷基苯磺酸钠1-2、偏硅酸钠3-5、苄基酚聚氧乙烯醚1.5-3.8、脂肪酸甘油酯3-6，亚硫酸氢钠1-2；
改性包覆凹凸棒土的制备方法为：
（1）将低分子量聚乙烯蜡粉料、水、阿拉伯胶、烷基苯磺酸钠、偏硅酸钠加入反应釜中，35-45℃下搅拌，再加入苄基酚聚氧乙烯醚、脂肪酸甘油酯、亚硫酸氢钠、300-400转/分搅拌均匀，升温至170-200℃，400-600rpm下搅拌均匀，制成改性聚乙烯蜡乳液；
（2）将凹凸棒土加入到改性聚乙烯蜡乳液中，然后缓慢加入其余原料，40-60转/分搅拌5-10min后，烘干，即得。
2.根据权利要求1所述的一种阻燃效果好的乳化沥青保温砂浆，其特征在于：
制备方法包括以下步骤：
（1）海泡石、沸石、城市道路废水泥路渣混匀后，300-400℃煅烧1-2小时，取出，破碎，过60-80目筛，与高岭土混匀，得复配矿物粉备用；
（2）将苯丙乳液均匀喷于复配矿物粉表面，干燥后，研磨，过100-200目筛，得复配包覆粉料备用；
（3）所得复配包覆粉料与其余原料于30-40℃下搅拌10-40min，即得。
CN201410809788.0A 2014-12-23 2014-12-23 一种阻燃效果好的乳化沥青保温砂浆 Pending CN104556864A (zh)