CN101857405A - 一种高韧性砂浆 - Google Patents

一种高韧性砂浆 Download PDF

Info

Publication number
CN101857405A
CN101857405A CN 201010202056 CN201010202056A CN101857405A CN 101857405 A CN101857405 A CN 101857405A CN 201010202056 CN201010202056 CN 201010202056 CN 201010202056 A CN201010202056 A CN 201010202056A CN 101857405 A CN101857405 A CN 101857405A
Authority
CN
China
Prior art keywords
mortar
cement
sand
parts
tenacity
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN 201010202056
Other languages
English (en)
Inventor
王茹
王培铭
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Tongji University
Original Assignee
Tongji University
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Tongji University filed Critical Tongji University
Priority to CN 201010202056 priority Critical patent/CN101857405A/zh
Publication of CN101857405A publication Critical patent/CN101857405A/zh
Pending legal-status Critical Current

Abstract

本发明属于建筑材料领域,具体涉及一种高韧性砂浆。由水泥、砂、水、聚合物乳胶粉和辅助外加剂组成,其组份的质量比按份数计:水泥100份,砂100-400份,聚合物乳胶粉0.01-40份,辅助外加剂0.01-40份。将这些物质混合均匀,与水拌合,成型,进行一定的养护,即得所需产品。本发明具有如下优点:操作简单,不需要特殊工序;新拌砂浆工作性好;可以制成干混砂浆或预拌砂浆,施工和运输方便;硬化砂浆具有良好的物理力学性能和耐水性,以及较高的韧性。

Description

一种高韧性砂浆
技术领域
[0001] 本发明属于建筑材料领域,具体涉及一种高韧性砂浆。 背景技术
[0002] 砂浆是建筑工程中应用量大、使用面广的建筑材料之一,广泛应用于建筑物的砌 筑与抹面等工程。我国当前的建筑工程中60%以上建筑物仍在沿用砖、砌块等墙体材料,砌 筑、抹灰施工中使用的建筑砂浆仍以水泥砂浆或混合砂浆为主。
[0003] 新型建筑材料的大量运用及现代化施工技术的不断发展对砂浆提出更高要求,普 通砂浆已越来越不能满足需要。人们发现用聚合物乳液改性的水泥砂浆性能优异,但现场 配制要求严格,且乳液需要特殊包装,储存期有限。聚合物乳胶粉(可再分散乳胶粉)的问 世,改变了聚合物以乳液的形式生产和贮放,使用时再掺加到水泥砂浆中的做法,预先将聚 合物通过科学的工艺,进行活化处理,与水凝性粘结剂混合配成预混料,使用时只需要加水 即可,有助于避免现场混配时出现差错,提高产品搬运处理的安全性。聚合物乳胶粉改性水 泥基复合材料中聚合物量可明显小于乳液改性复合材料中聚合物量,从而大幅度地降低材 料成本。另外,商品砂浆作为一种在工厂将所有原料按照一定配比混合好的预混砂浆,同传 统砂浆相比更具优越性,可大幅度提高施工效率,避免环境污染,对建筑业的可持续发展起 到了积极推动作用。
[0004] 在砂浆商品化生产的发展趋势下,上海、北京、广州、深圳等部分大城市已开始大 力推行商品砂浆,并已颁布了各自的地方标准。它是继商品混凝土之后城市建设工程中的 一个新亮点,是提高建设工程质量,改善城市环境的重要举措。预混聚合物乳胶粉商品砂浆 (干粉砂浆)的倍受青睐,凸现了聚合物乳胶粉改性水泥基材料的重要价值。但在某些特殊 场合现有砂浆不能满足韧性和防水的要求。
发明内容
[0005] 本发明的目的是针对现有技术的不足而提供一种高韧性砂浆,
[0006] 本发明提出的高韧性砂浆,由水泥、砂、水、聚合物乳胶粉和辅助外加剂组成,其组 份的质量比如下:
[0007] 组份 份数
[0008] 水泥 100份
[0009]砂 100-400 份
[0010] 聚合物乳胶粉 0.01-40份
[0011] 辅助外加剂 0.01-40份
[0012] 本发明中,所述水泥是指强度不低于42. 5级的硅酸盐水泥、普通硅酸盐水泥、矿 渣硅酸盐水泥、火山灰质硅酸盐水泥粉煤灰硅酸盐水泥或复合硅酸盐水泥中任一种。
[0013] 本发明中,所述砂是指标准砂、石英砂、河砂或人工砂中任一种。
[0014] 本发明中,所述聚合物乳胶粉是指带有五到十五个碳原子长侧链的叔碳酸酯结构单元的叔碳酸酯共聚物乳胶粉中任一种。
[0015] 本发明中,所述辅助外加剂为减水剂、消泡剂、增稠剂或矿物外加剂中任一种或几 种。
[0016] 本发明中,所述水是指饮用水或清洁的天然水中任一种,水的用量以调节拌和料 流动度在170mm左右为宜。
[0017] 本发明提出的高韧性砂浆的制备方法,具体步骤如下:
[0018] (1)按原料配比将水泥、砂、聚合物乳胶粉和辅助外加剂制成均勻混合物;
[0019] (2)将水加入到步骤(1)所述混合物中搅拌均勻;
[0020] (3)将步骤(2)所得拌和料成型,养护至预定龄期,即得所需产品。
[0021] 本发明利用水泥、砂、水、聚合物乳胶粉、辅助外加剂配制砂浆。可以制成干混砂浆 或预拌砂浆。新拌砂浆具有优秀的工作性,硬化砂浆具有优秀的物理力学性能和耐水性,尤 其是优异的韧性。
[0022] 本发明中,所述成型是指将拌和料(新拌砂浆)按需求制备成不同的形状。
[0023] 本发明中,所述养护是指水中养护、空气中养护、标准养护、混合养护中的至少一 种,可以根据实际施工条件而改变。
[0024] 本发明中,所述龄期是指养护时间。
[0025] 本发明具有如下优点:
[0026] (1)操作简单,不需要特殊工序;
[0027] (2)新拌砂浆工作性好;
[0028] (3)可以制成干混砂浆或预拌砂浆,施工和运输方便;
[0029] (4)硬化砂浆具有良好的物理力学性能和耐水性;
[0030] (5)硬化砂浆具有很高的韧性。
具体实施方式
[0031] 下面通过实施例对本发明进行具体描述。有必要在此指出的是以下实施例只用于 对本发明进行进一步说明,不能理解为对本发明保护范围的限制,该领域的技术熟练人员 可以根据上述本发明内容对本发明做出一些非本质的改进和调整。
[0032] 实施例1 :
[0033] 将水泥100份,砂200份,聚合物乳胶粉15份,辅助外加剂1份制成均勻混合物,将 40份水加入到上述混合物中搅拌,制备成新拌砂浆,将新拌砂浆成型,养护至28天后进行 性能测试。结果如下:抗压强度:28MPa ;抗折强度:12MPa ;压折比:2. 3 ;横向变形:2. 5mm ; 24小时毛细孔吸水量:0. 02kg/m2 ;抗渗性检验:无渗透。
[0034] 实施例2 :
[0035] 将水泥100份,砂300份,聚合物乳胶粉5份,辅助外加剂2份制成均勻混合物,将 45份水加入到上述混合物中搅拌,制备成新拌砂浆,将新拌砂浆成型,养护至28天后进行 性能测试。结果如下:抗压强度:24MPa ;抗折强度:10MPa ;压折比:2. 4 ;横向变形:2. 2mm ; 24小时毛细孔吸水量:0. 07kg/m2 ;抗渗性检验:无渗透。

Claims (5)

  1. 一种高韧性砂浆,其特征在于由水泥、砂、水、聚合物乳胶粉和辅助外加剂组成,其组份的质量比如下:组份            份数水泥            100份砂              100-400份聚合物乳胶粉    0.01-40份辅助外加剂      0.01-40份
  2. 2.根据权利要求1所述的高韧性砂浆,其特征在于所述水泥是强度不低于42. 5级的硅 酸盐水泥、普通硅酸盐水泥、矿渣硅酸盐水泥、火山灰质硅酸盐水泥、粉煤灰硅酸盐水泥或 复合硅酸盐水泥中任一种。
  3. 3.根据权利要求1所述的高韧性砂浆,其特征在于所述砂是指标准砂、石英砂、河砂或 人工砂中任一种。
  4. 4.根据权利要求1所述的高韧性砂浆,其特征在于所述聚合物乳胶粉是指带有五到 十五个碳原子长侧链的叔碳酸酯结构单元的叔碳酸酯共聚物乳胶粉中任一种。
  5. 5.根据权利要求1所述的高韧性砂浆,其特征在于所述辅助外加剂为减水剂、消泡剂、 增稠剂或矿物外加剂中任一种或几种。组份 水泥 砂份数 100份 100-400 份
CN 201010202056 2010-06-17 2010-06-17 一种高韧性砂浆 Pending CN101857405A (zh)