CN104532542A - 一种亚麻混纱线前处理工艺 - Google Patents
一种亚麻混纱线前处理工艺 Download PDFInfo
- Publication number
- CN104532542A CN104532542A CN201410791544.4A CN201410791544A CN104532542A CN 104532542 A CN104532542 A CN 104532542A CN 201410791544 A CN201410791544 A CN 201410791544A CN 104532542 A CN104532542 A CN 104532542A
- Authority
- CN
- China
- Prior art keywords
- mixed yarn
- flax
- blended yarn
- flax mixed
- flax blended
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种亚麻混纱线前处理工艺,其特征在于:包括以下步骤:(1)先在105℃的温度下烘干亚麻混纱线3个小时,然后接着煮沸5min;(2)煮沸后冷却亚麻混纱线5分钟,对其进行酶精炼,酶失活沸煮10min,进行冷水冲洗;(3)浸漂在NACLO中,对其沥水氧化,再直接淋冲水洗;(4)浸漂在硫酸中,再利用硫代硫酸钠进行脱氯,用冷水冲洗;(5)对亚麻混纱线进行前处理,接着室温入漂,然后升温至95℃保温50min,再直接进行冰醋酸的酸洗,最后在PH为7的水中清洗;(6)对亚麻混纱线进行热水洗,最后再进行110℃的加热烘干;本发明方案的一种本发明的亚麻混纱线前处理加工工艺,通过对亚麻混纱线的多重处理及清洗漂泊,能够达到较好的白度,满足了实际工艺的需求,具有较高的实用价值。
Description
技术领域
本发明涉及一种纱线前处理工艺,尤其涉及一种亚麻混纱线前处理加工工艺。
背景技术
亚麻具有吸湿、散热、透气性强,具有一定的抗静电性能及抗菌性能,亚麻针织物弹性好、挺括、透气、吸湿性优良,穿着舒适凉爽,不粘皮肤。对这类产品的要求,如尺寸稳定性、白度、颜色鲜艳度、色差等级等也越来越高,而这些质量的提高很大程度上取决于前处理工艺,而现有的漂泊工艺其漂泊的效果不佳,无法满足实际工艺的使用需求。
发明内容
针对上述存在的技术问题,本发明的目的是:提出了一种漂泊效果好的亚麻混纱线前处理工艺。
本发明的技术解决方案是这样实现的:一种亚麻混纱线前处理工艺,包括以下步骤:
(1)先在105℃的温度下烘干亚麻混纱线3个小时,然后接着煮沸5min;
(2)煮沸后冷却亚麻混纱线5分钟,对其进行酶精炼,酶失活沸煮10min,进行冷水冲洗;
(3)浸漂在NACLO中,对其沥水氧化,再直接淋冲水洗;
(4)浸漂在硫酸中,再利用硫代硫酸钠进行脱氯,用冷水冲洗;
(5)对亚麻混纱线进行前处理,接着室温入漂,然后升温至95℃保温50min,再直接进行冰醋酸的酸洗,最后在PH为7的水中清洗;
(6)对亚麻混纱线进行热水洗,最后再进行 110℃的加热烘干。
优选的,所述前处理为对亚麻混纱线在95℃的温度下烘干10min。
由于上述技术方案的运用,本发明与现有技术相比具有下列优点:
本发明方案的一种本发明的亚麻混纱线前处理工艺,通过对亚麻混纱线的多重处理及清洗漂泊,能够达到较好的白度,满足了实际工艺的需求,具有较高的实用价值。
具体实施方式
本发明的一种亚麻混纱线前处理工艺,包括以下步骤:
(1)先在105℃的温度下烘干亚麻混纱线3个小时,然后接着煮沸5min;
(2)煮沸后冷却亚麻混纱线5分钟,对其进行酶精炼,酶失活沸煮10min,进行冷水冲洗;
(3)浸漂在NACLO中,对其沥水氧化,再直接淋冲水洗;
(4)浸漂在硫酸中,再利用硫代硫酸钠进行脱氯,用冷水冲洗;
(5)对亚麻混纱线进行前处理,接着室温入漂,然后升温至95℃保温50min,再直接进行冰醋酸的酸洗,最后在PH为7的水中清洗;
(6)对亚麻混纱线进行热水洗,最后再进行 110℃的加热烘干;所述前处理为对亚麻混纱线在95℃的温度下烘干10min。
如上所述的亚麻混纱线前处理加工工艺中,当浸漂在NACLO中是,其中有效氯含量为2.8g/L;当浸漂在硫酸中,其中硫酸的含量为2g/L;对其进行脱氯时,其中硫代硫酸钠的含量为8g/L,对其进行酸洗时,冰醋酸的含量为2ml/L,并在40℃的情况下浸泡10 min;本发明的亚麻混纱线前处理工艺,其分别通过酶洗、氯洗和氧洗,最后再对其烘干,能够达到很好的漂泊效果。
本发明的亚麻混纱线前处理工艺,通过对亚麻混纱线的多重处理及清洗漂泊,能够达到较好的白度,满足了实际工艺的需求,具有较高的实用价值。
上述实施例只为说明本发明的技术构思及特点,其目的在于让熟悉此项技术的人士能够了解本发明的内容并加以实施,并不能以此限制本发明的保护范围,凡根据本发明精神实质所作的等效变化或修饰,都应涵盖在本发明的保护范围内。
Claims (2)
1.一种亚麻混纱线前处理工艺,其特征在于:包括以下步骤:
(1)先在105℃的温度下烘干亚麻混纱线3个小时,然后接着煮沸5min;
(2)煮沸后冷却亚麻混纱线5分钟,对其进行酶精炼,酶失活沸煮10min,进行冷水冲洗;
(3)浸漂在NACLO中,对其沥水氧化,再直接淋冲水洗;
(4)浸漂在硫酸中,再利用硫代硫酸钠进行脱氯,用冷水冲洗;
(5)对亚麻混纱线进行前处理,接着室温入漂,然后升温至95℃保温50min,再直接进行冰醋酸的酸洗,最后在PH为7的水中清洗;
(6)对亚麻混纱线进行热水洗,最后再进行 110℃的加热烘干。
2.一种亚麻混纱线前处理工艺,其特征在于:所述前处理为对亚麻混纱线在95℃的温度下烘干10min。