CN104529268B - 一种凝结时间长的混凝土 - Google Patents

一种凝结时间长的混凝土 Download PDF

Info

Publication number
CN104529268B
CN104529268B CN201410715942.8A CN201410715942A CN104529268B CN 104529268 B CN104529268 B CN 104529268B CN 201410715942 A CN201410715942 A CN 201410715942A CN 104529268 B CN104529268 B CN 104529268B
Authority
CN
China
Prior art keywords
calcium
clay
powder
modification
concrete
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN201410715942.8A
Other languages
English (en)
Other versions
CN104529268A (zh
Inventor
王小波
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Yangxin Hai Mao concrete mixing Co., Ltd.
Original Assignee
王小波
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 王小波 filed Critical 王小波
Priority to CN201410715942.8A priority Critical patent/CN104529268B/zh
Publication of CN104529268A publication Critical patent/CN104529268A/zh
Application granted granted Critical
Publication of CN104529268B publication Critical patent/CN104529268B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种凝结时间长的混凝土，其是由下述重量份的原料制得：改性包覆陶土10-20、水泥30-40、木钙3-5、醋酸钠3-5、明矾1-3、聚丙烯酸酯乳胶粉3-6、氢氧化钙1-3、粘土10-15,烷基多苷0.5-1、山楂酸0.1-0.15、氧化钙0.1-0.3、氧化镁1-2,石英砂40-60，碳化钙粉15-20、氢氧化铝2-3、糖钙1-3、三聚磷酸钠0.1-0.3、大豆卵磷脂0.1-0.3、氧化锆3-5。

Description

一种凝结时间长的混凝土
技术领域
本发明涉及混凝土领域，确切地说是一种凝结时间长的混凝土。
背景技术
混凝土具有原料丰富，价格低廉，生产工艺简单的特点，因而使其用量越来越大。同时混凝土还具有抗压强度高，耐久性好，强度等级范围宽等特点。这些特点使其使用范围十分广泛，不仅在各种土木工程中使用，就是造船业，机械工业，海洋的开发，地热工程等，混凝土也是重要的材料。
发明内容
本发明的目的在于提供一种凝结时间长的混凝土。
上述目的通过以下方案实现：
一种凝结时间长的混凝土，其特征在于：其是由下述重量份的原料制得：
改性包覆陶土10-20、水泥30-40、木钙3-5、醋酸钠3-5、明矾1-3、聚丙烯酸酯乳胶粉3-6、氢氧化钙1-3、粘土10-15、烷基多苷0.5-1、山楂酸0.1-0.15、氧化钙0.1-0.3、氧化镁1-2、石英砂40-60、碳化钙粉15-20、氢氧化铝2-3、糖钙1-3、三聚磷酸钠0.1-0.3、大豆卵磷脂0.1-0.3、氧化锆3-5；
所述的改性包覆陶土由下述重量份的原料制得：陶土40-50、海藻酸钠0.1-0.3、玉米淀粉3-5、硅酸钠0.4-0.6、硫酸铝0.2-0.4、硬脂酰胺0.4-0.7、硬脂酸钙1.8-2.2、聚乙二醇1-2、柠檬酸0.2-0.4、二异氰酸酯0.1-0.6；
所述的改性包覆陶土的制备方法为：取玉米淀粉加水搅拌均匀得悬浮液，再加入硅酸钠、硫酸铝、硬脂酰胺，在40-45℃下100-180转/分搅拌50-70min，再加入其余原料，搅拌均匀，静置浆料30-60分钟、干燥，粉碎即得。
所述的一种凝结时间长的混凝土，其特征在于：
制备方法包括以下步骤：
（1）木钙、醋酸钠、明矾、聚丙烯酸酯乳胶粉、氢氧化钙、粘土、烷基多苷、山楂酸、氧化钙、氧化镁混匀后，加适量水，搅拌成悬浮液备用；
（2)悬浮液与石英砂、碳化钙粉混匀后，调节pH为8-8.5，静置4-8小时后，抽滤干燥，得改性粉料备用；
（3）改性粉料再与剩余原料混匀后，即得。
本发明的有益效果为：本发明中的改性包覆陶土有效的降低混凝土的水化热，各种添加剂能够改善混凝土的工作度，延长混凝土的凝结时间，有效的降低了施工难度，大大缩短了施工工期。
具体实施方式
一种凝结时间长的混凝土，其是由下述重量（kg)的原料制得：
改性包覆陶土16、水泥40、木钙3、醋酸钠5、明矾1.8、聚丙烯酸酯乳胶粉5、氢氧化钙1、粘土10,烷基多苷0.5、山楂酸0.1、氧化钙0.1、氧化镁1,石英砂40，碳化钙粉15、氢氧化铝2、糖钙1、三聚磷酸钠0.1、大豆卵磷脂0.1、氧化锆5；
所述的改性包覆陶土由下述重量（kg)的原料制得：陶土50、海藻酸钠0.1、玉米淀粉3、硅酸钠0.4、硫酸铝0.2、硬脂酰胺0.4、硬脂酸钙1.8、聚乙二醇1、柠檬酸0.2、二异氰酸酯0.4；
所述的改性包覆陶土的制备方法为：取玉米淀粉加水搅拌均匀得悬浮液，再加入硅酸钠、硫酸铝、硬脂酰胺，在42℃下130转/分搅拌50min，再加入其余原料，搅拌均匀，静置浆料60分钟、干燥，粉碎即得。
所述的一种凝结时间长的混凝土，制备方法包括以下步骤：
（1）木钙、醋酸钠、明矾、聚丙烯酸酯乳胶粉、氢氧化钙、粘土、烷基多苷、山楂酸、氧化钙、氧化镁混匀后，加适量水，搅拌成悬浮液备用；
（2)悬浮液与石英砂、碳化钙粉混匀后，调节pH为8.2，静置6小时后，抽滤干燥，得改性粉料备用；
（3）改性粉料再与剩余原料混匀后，即得。
将所有原料加适量水搅拌均匀，通过筑模、压实振捣、表面弄平整12小时后脱模，再标准自然养护8天，每天洒水两次得混凝土样品，制得混凝土样品执行GB/T50081-2002标准，三次试验的平均强度为26.5MPa。

Claims (2)

1.一种凝结时间长的混凝土，其特征在于：其是由下述重量份的原料制得：改性包覆陶土10-20、水泥30-40、木钙3-5、醋酸钠3-5、明矾1-3、聚丙烯酸酯乳胶粉3-6、氢氧化钙1-3、粘土10-15、烷基多苷0.5-1、山楂酸0.1-0.15、氧化钙0.1-0.3、氧化镁1-2、石英砂40-60、碳化钙粉15-20、氢氧化铝2-3、糖钙1-3、三聚磷酸钠0.1-0.3、大豆卵磷脂0.1-0.3、氧化锆3-5；
所述的改性包覆陶土由下述重量份的原料制得：陶土40-50、海藻酸钠0.1-0.3、玉米淀粉3-5、硅酸钠0.4-0.6、硫酸铝0.2-0.4、硬脂酰胺0.4-0.7、硬脂酸钙1.8-2.2、聚乙二醇1-2、柠檬酸0.2-0.4、二异氰酸酯0.1-0.6；
所述的改性包覆陶土的制备方法为：取玉米淀粉加水搅拌均匀得悬浮液，再加入硅酸钠、硫酸铝、硬脂酰胺，在40-45℃下100-180转/分搅拌50-70min，再加入其余原料，搅拌均匀，静置浆料30-60分钟、干燥，粉碎即得。
2.根据权利要求1所述的一种凝结时间长的混凝土，其特征在于：制备方法包括以下步骤：
（1）木钙、醋酸钠、明矾、聚丙烯酸酯乳胶粉、氢氧化钙、粘土、烷基多苷、山楂酸、氧化钙、氧化镁混匀后，加适量水，搅拌成悬浮液备用；
（2)悬浮液与石英砂、碳化钙粉混匀后，调节pH为8-8.5，静置4-8小时后，抽滤干燥，得改性粉料备用；
（3）改性粉料再与剩余原料混匀后，即得。
CN201410715942.8A 2014-12-02 2014-12-02 一种凝结时间长的混凝土 Expired - Fee Related CN104529268B (zh)