CN104529269A - 一种抗冻性能优异的混凝土 - Google Patents

一种抗冻性能优异的混凝土 Download PDF

Info

Publication number
CN104529269A
CN104529269A CN201410716417.8A CN201410716417A CN104529269A CN 104529269 A CN104529269 A CN 104529269A CN 201410716417 A CN201410716417 A CN 201410716417A CN 104529269 A CN104529269 A CN 104529269A
Authority
CN
China
Prior art keywords
parts
modification
concrete
clay
stir
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410716417.8A
Other languages
English (en)
Inventor
王小波
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201410716417.8A priority Critical patent/CN104529269A/zh
Publication of CN104529269A publication Critical patent/CN104529269A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种抗冻性能优异的混凝土，其是由下述重量份的原料制得：亚硝酸钠1-2、工业盐2.8-3.5、硅酸钠3-4，碳酸钠1-3、羟基乙叉二磷酸1-3,硬脂酸钙0.7-0.9，硫酸铁0.3-0.45、柠檬酸钠0.3-0.6、三聚氰胺1-3、明矾1-3、聚丙乙烯纤维3-5、聚碳酸酯3.5-4.5、水泥40-45、黄砂70-90、改性包覆陶土80-100。

Description

一种抗冻性能优异的混凝土
技术领域
本发明涉及混凝土领域，确切地说是一种抗冻性能优异的混凝土。
背景技术
     混凝土具有原料丰富，价格低廉，生产工艺简单的特点，因而使其用量越来越大。同时混凝土还具有抗压强度高，耐久性好，强度等级范围宽等特点。这些特点使其使用范围十分广泛，不仅在各种土木工程中使用，就是造船业，机械工业，海洋的开发，地热工程等，混凝土也是重要的材料。
发明内容
本发明的目的在于提供一种抗冻性能优异的混凝土。
上述目的通过以下方案实现：
    一种抗冻性能优异的混凝土，其特征在于：其是由下述重量份的原料制得：亚硝酸钠1-2、工业盐2.8-3.5、硅酸钠3-4，碳酸钠1-3、羟基乙叉二磷酸1-3,硬脂酸钙0.7-0.9，硫酸铁0.3-0.45、柠檬酸钠0.3-0.6、三聚氰胺1-3、明矾1-3、聚丙乙烯纤维3-5、聚碳酸酯3.5-4.5、水泥40-45、黄砂70-90、改性包覆陶土80-100;
所述的改性包覆陶土由下述重量份的原料制得：陶土40-50、海藻酸钠0.1-0.3,玉米淀粉3-5、硅酸钠0.4-0.6、硫酸铝0.2-0.4、硬脂酰胺0.4-0.7、硬脂酸钙1.8-2.2、聚乙二醇 1-2、柠檬酸0.2-0.4、二异氰酸酯0.1-0.6；
所述的改性包覆陶土的制备方法为：取玉米淀粉加水搅拌均匀得悬浮液，再加入硅酸钠、硫酸铝、硬脂酰胺，再40-45℃下100-180转/分搅拌50-70min，再加入其余原料，搅拌均匀，静置浆料30-60分钟、干燥，粉碎即得。
所述的一种抗冻性能优异的混凝土，其特征在于：
制备方法包括以下步骤：
（1）亚硝酸钠、工业盐、硅酸钠、碳酸钠、羟基乙叉二磷酸、硬脂酸钙、硫酸铁、柠檬酸钠、三聚氰胺混匀后，加适量水，搅拌均匀，得改性液；
（2)改性液与聚丙乙烯纤维、黄砂搅拌均匀，静置10-20Min，干燥，得改性聚丙乙烯纤维备用；
（3）改性聚丙乙烯纤维再与剩余原料混匀后，50-60℃下搅拌10-30min，即得。
本发明的有益效果为：本发明防冻效果均匀、防冻度高,可以抵抗300次的快速冻融循环作用，改性聚丙乙烯纤维杂乱无章的分布于混凝土中，协助混凝土承担、传递拉应力，抗裂的同时提高了该混凝土抵抗冻融循环的剥落、分离能力。
具体实施方式
一种抗冻性能优异的混凝土，其是由下述重量(kg)的原料制得：亚硝酸钠1、工业盐2.8、硅酸钠3，碳酸钠1、羟基乙叉二磷酸1,硬脂酸钙0.9，硫酸铁0.3、柠檬酸钠0.3、三聚氰胺3、明矾1、聚丙乙烯纤维3、聚碳酸酯3.5、水泥40、黄砂70、改性包覆陶土80;
所述的改性包覆陶土由下述重量(kg)的原料制得：陶土40、海藻酸钠0.1,玉米淀粉5、硅酸钠0.4、硫酸铝0.2、硬脂酰胺0.4、硬脂酸钙1.8、聚乙二醇 1、柠檬酸0.2、二异氰酸酯0.1；
所述的改性包覆陶土的制备方法为：取玉米淀粉加水搅拌均匀得悬浮液，再加入硅酸钠、硫酸铝、硬脂酰胺，再40℃下180转/分搅拌70min，再加入其余原料，搅拌均匀，静置浆料30分钟、干燥，粉碎即得。
所述的一种抗冻性能优异的混凝土，制备方法包括以下步骤：
（1）亚硝酸钠、工业盐、硅酸钠、碳酸钠、羟基乙叉二磷酸、硬脂酸钙、硫酸铁、柠檬酸钠、三聚氰胺混匀后，加适量水，搅拌均匀，得改性液；
（2)改性液与聚丙乙烯纤维、黄砂搅拌均匀，静置15Min，干燥，得改性聚丙乙烯纤维备用；
（3）改性聚丙乙烯纤维再与剩余原料混匀后，60℃下搅拌30min，即得。
    将所有原料加适量水搅拌均匀， 通过筑模、压实振捣、表面弄平整 8 小时后脱模， 再标准自然养护5天，每天洒水两次得混凝土样品，制得混凝土样品执行 GB/T50081-2002标准， 三次试验的平均强度为 26.8Mpa。

Claims (2)

1.一种抗冻性能优异的混凝土，其特征在于：其是由下述重量份的原料制得：亚硝酸钠1-2、工业盐2.8-3.5、硅酸钠3-4，碳酸钠1-3、羟基乙叉二磷酸1-3,硬脂酸钙0.7-0.9，硫酸铁0.3-0.45、柠檬酸钠0.3-0.6、三聚氰胺1-3、明矾1-3、聚丙乙烯纤维3-5、聚碳酸酯3.5-4.5、水泥40-45、黄砂70-90、改性包覆陶土80-100;
所述的改性包覆陶土由下述重量份的原料制得：陶土40-50、海藻酸钠0.1-0.3,玉米淀粉3-5、硅酸钠0.4-0.6、硫酸铝0.2-0.4、硬脂酰胺0.4-0.7、硬脂酸钙1.8-2.2、聚乙二醇 1-2、柠檬酸0.2-0.4、二异氰酸酯0.1-0.6；
所述的改性包覆陶土的制备方法为：取玉米淀粉加水搅拌均匀得悬浮液，再加入硅酸钠、硫酸铝、硬脂酰胺，再40-45℃下100-180转/分搅拌50-70min，再加入其余原料，搅拌均匀，静置浆料30-60分钟、干燥，粉碎即得。
2.根据权利要求1所述的一种抗冻性能优异的混凝土，其特征在于：
制备方法包括以下步骤：
（1）亚硝酸钠、工业盐、硅酸钠、碳酸钠、羟基乙叉二磷酸、硬脂酸钙、硫酸铁、柠檬酸钠、三聚氰胺混匀后，加适量水，搅拌均匀，得改性液；
（2)改性液与聚丙乙烯纤维、黄砂搅拌均匀，静置10-20Min，干燥，得改性聚丙乙烯纤维备用；
（3）改性聚丙乙烯纤维再与剩余原料混匀后，50-60℃下搅拌10-30min，即得。
CN201410716417.8A 2014-12-02 2014-12-02 一种抗冻性能优异的混凝土 Pending CN104529269A (zh)