CN104496347A - 一种环保型无机高韧性混凝土 - Google Patents
一种环保型无机高韧性混凝土 Download PDFInfo
- Publication number
- CN104496347A CN104496347A CN201410717043.1A CN201410717043A CN104496347A CN 104496347 A CN104496347 A CN 104496347A CN 201410717043 A CN201410717043 A CN 201410717043A CN 104496347 A CN104496347 A CN 104496347A
- Authority
- CN
- China
- Prior art keywords
- parts
- modification
- brucite
- clay
- stir
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种环保型无机高韧性混凝土,其是由下述重量份的原料制得:改性包覆陶土30-57、水镁石20-30、聚酰胺0.2-0.8、碳酸镁1.2-1.8,硫酸钙15-25,玻璃纤维12-14、聚乙烯胶粉5-8、硅酸钠1-2、碳酸钠1-3,葡萄糖酸钠0.2-0.8,玻化微珠40-60,硅酸盐水泥40-50、磷酸0.5-0.8、硫酸钙晶须5-8,氯化石蜡0.1-0.2、乙二醛0.3-0.5,草酸0.1-0.5。
Description
技术领域
本发明涉及混凝土领域,确切地说是一种环保型无机高韧性混凝土。
背景技术
混凝土具有原料丰富,价格低廉,生产工艺简单的特点,因而使其用量越来越大。同时混凝土还具有抗压强度高,耐久性好,强度等级范围宽等特点。这些特点使其使用范围十分广泛,不仅在各种土木工程中使用,就是造船业,机械工业,海洋的开发,地热工程等,混凝土也是重要的材料。
发明内容
本发明的目的在于提供一种环保型无机高韧性混凝土。
上述目的通过以下方案实现:
一种环保型无机高韧性混凝土,其特征在于:其是由下述重量份的原料制得:
改性包覆陶土30-57、水镁石20-30、聚酰胺0.2-0.8、碳酸镁1.2-1.8,硫酸钙15-25,玻璃纤维12-14、聚乙烯胶粉5-8、硅酸钠1-2、碳酸钠1-3,葡萄糖酸钠0.2-0.8,玻化微珠40-60,硅酸盐水泥40-50、磷酸0.5-0.8、硫酸钙晶须5-8,氯化石蜡0.1-0.2、乙二醛0.3-0.5,草酸0.1-0.5;
所述的改性包覆陶土由下述重量份的原料制得:陶土40-50、海藻酸钠0.1-0.3,玉米淀粉3-5、硅酸钠0.4-0.6、硫酸铝0.2-0.4、硬脂酰胺0.4-0.7、硬脂酸钙1.8-2.2、聚乙二醇 1-2、柠檬酸0.2-0.4、二异氰酸酯0.1-0.6;
所述的改性包覆陶土的制备方法为:取玉米淀粉加水搅拌均匀得悬浮液,再加入硅酸钠、硫酸铝、硬脂酰胺,再40-45℃下100-180转/分搅拌50-70min,再加入其余原料,搅拌均匀,静置浆料30-60分钟、干燥,粉碎即得。
所述的一种环保型无机高韧性混凝土,其特征在于:
制备方法包括以下步骤:
(1)聚酰胺、碳酸镁、氯化石蜡、乙二醛、草酸混匀后,加适量水,搅拌均匀,搅拌成改性,备用;
(2)水镁石破碎,再于浓度为3-5%的盐酸溶液浸泡10-12小时,取出,去离子水洗涤后烘干,得水镁石粉备用;
(3)改性液与水镁石粉混匀后,静置4-6小时后,干燥,得改性粉料备用;
(4)改性粉料再与剩余原料混匀后,即得。
本发明的有益效果为:本发明的通过对水镁石粉改性,以及添加聚乙烯胶粉等原料,混凝土可以防止混凝土开裂,提高混凝土抗折强度和韧性,限制的裂缝宽度,抵抗混凝土表面龟裂和抗爆防火能力。
具体实施方式
一种环保型无机高韧性混凝土,其是由下述重量(kg)的原料制得:
改性包覆陶土37、水镁石30、聚酰胺0.5、碳酸镁1.8,硫酸钙15,玻璃纤维14、聚乙烯胶粉8、硅酸钠1、碳酸钠1,葡萄糖酸钠0.2,玻化微珠40,硅酸盐水泥50、磷酸0.5、硫酸钙晶须5,氯化石蜡0.1、乙二醛0.3,草酸0.1;
所述的改性包覆陶土由下述重量(kg)的原料制得:陶土50、海藻酸钠0.3,玉米淀粉3、硅酸钠0.6、硫酸铝0.2、硬脂酰胺0.7、硬脂酸钙2.2、聚乙二醇 1、柠檬酸0.4、二异氰酸酯0.3;
所述的改性包覆陶土的制备方法为:取玉米淀粉加水搅拌均匀得悬浮液,再加入硅酸钠、硫酸铝、硬脂酰胺,再45℃下180转/分搅拌70min,再加入其余原料,搅拌均匀,静置浆料60分钟、干燥,粉碎即得。
所述的一种环保型无机高韧性混凝土,制备方法包括以下步骤:
(1)聚酰胺、碳酸镁、氯化石蜡、乙二醛、草酸混匀后,加适量水,搅拌均匀,搅拌成改性,备用;
(2)水镁石破碎,再于浓度为5%的盐酸溶液浸泡12小时,取出,去离子水洗涤后烘干,得水镁石粉备用;
(3)改性液与水镁石粉混匀后,静置4小时后,干燥,得改性粉料备用;
(4)改性粉料再与剩余原料混匀后,即得。
将所有原料加适量水搅拌均匀, 通过筑模、压实振捣、表面弄平整 8 小时后脱模, 再标准自然养护5天,每天洒水两次得混凝土样品,制得混凝土样品执行 GB/T50081-2002标准, 三次试验的平均强度为 27.6Mpa。
Claims (2)
1.一种环保型无机高韧性混凝土,其特征在于:其是由下述重量份的原料制得:
改性包覆陶土30-57、水镁石20-30、聚酰胺0.2-0.8、碳酸镁1.2-1.8,硫酸钙15-25,玻璃纤维12-14、聚乙烯胶粉5-8、硅酸钠1-2、碳酸钠1-3,葡萄糖酸钠0.2-0.8,玻化微珠40-60,硅酸盐水泥40-50、磷酸0.5-0.8、硫酸钙晶须5-8,氯化石蜡0.1-0.2、乙二醛0.3-0.5,草酸0.1-0.5;
所述的改性包覆陶土由下述重量份的原料制得:陶土40-50、海藻酸钠0.1-0.3,玉米淀粉3-5、硅酸钠0.4-0.6、硫酸铝0.2-0.4、硬脂酰胺0.4-0.7、硬脂酸钙1.8-2.2、聚乙二醇 1-2、柠檬酸0.2-0.4、二异氰酸酯0.1-0.6;
所述的改性包覆陶土的制备方法为:取玉米淀粉加水搅拌均匀得悬浮液,再加入硅酸钠、硫酸铝、硬脂酰胺,再40-45℃下100-180转/分搅拌50-70min,再加入其余原料,搅拌均匀,静置浆料30-60分钟、干燥,粉碎即得。
2.根据权利要求1所述的一种环保型无机高韧性混凝土,其特征在于:
制备方法包括以下步骤:
(1)聚酰胺、碳酸镁、氯化石蜡、乙二醛、草酸混匀后,加适量水,搅拌均匀,搅拌成改性,备用;
(2)水镁石破碎,再于浓度为3-5%的盐酸溶液浸泡10-12小时,取出,去离子水洗涤后烘干,得水镁石粉备用;
(3)改性液与水镁石粉混匀后,静置4-6小时后,干燥,得改性粉料备用;
(4)改性粉料再与剩余原料混匀后,即得。