CN104497459A - 用于生产高稳定性聚四氟乙烯抗滴落剂的工艺 - Google Patents
用于生产高稳定性聚四氟乙烯抗滴落剂的工艺 Download PDFInfo
- Publication number
- CN104497459A CN104497459A CN201410730684.0A CN201410730684A CN104497459A CN 104497459 A CN104497459 A CN 104497459A CN 201410730684 A CN201410730684 A CN 201410730684A CN 104497459 A CN104497459 A CN 104497459A
- Authority
- CN
- China
- Prior art keywords
- weight
- weight part
- parts
- dripping agent
- deionized water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种用于生产高稳定性聚四氟乙烯抗滴落剂的工艺,包括如下步骤:1)在反应釜中投入聚氧乙烯失水山梨醇脂肪酸酯、六偏磷酸钠、过氧化苯甲酰、阁土粉、去离子水、过氧二硫酸铵、二硫八氧酸钾、碳酸钙、甲基丙烯酸丁酯、马来酸酐、水杨酸、甲基三甲氧基硅烷,升温,搅拌反应;2)再在反应釜中投入甲基丙烯酸丁酯、去离子水、过氧化苯甲酰、二硫八氧酸钾、马来酸酐、过氧二硫酸铵,升温,搅拌反应;3)再在反应釜中投入聚四氟乙烯分散液、去离子水,加热进行共混复合,在52℃加入凝聚剂溶液,得到沉淀;4)对沉淀进行离心分离,水洗,再离心分离,烘干粉碎,得到抗滴落剂。本发明制备的聚四氟乙烯抗滴落剂稳定性好。
Description
技术领域
本发明涉及用于生产高稳定性聚四氟乙烯抗滴落剂的工艺。
背景技术
现有的聚四氟乙烯抗滴落剂稳定性有待提高。
发明内容
本发明的目的在于提供一种用于生产高稳定性聚四氟乙烯抗滴落剂的工艺,其制备的聚四氟乙烯抗滴落剂稳定性好。
为实现上述目的,本发明的技术方案是设计一种用于生产高稳定性聚四氟乙烯抗滴落剂的工艺,包括如下步骤:
1)在反应釜中投入2重量份聚氧乙烯失水山梨醇脂肪酸酯、1重量份六偏磷酸钠、2重量份过氧化苯甲酰、5重量份阁土粉、55重量份去离子水、4重量份过氧二硫酸铵、2.6重量份二硫八氧酸钾、2重量份碳酸钙、6重量份甲基丙烯酸丁酯、5重量份马来酸酐、2重量份水杨酸、1重量份甲基三甲氧基硅烷,升温至73℃,搅拌反应52分钟;
2)再在反应釜中投入14重量份甲基丙烯酸丁酯、17重量份去离子水、3重量份过氧化苯甲酰、2重量份二硫八氧酸钾、15重量份马来酸酐、1重量份过氧二硫酸铵,升温至72℃,搅拌反应50分钟;
3)再在反应釜中投入9重量份聚四氟乙烯分散液、28重量份去离子水,加热进行共混复合,在52℃加入凝聚剂溶液,得到沉淀;
4)对沉淀进行离心分离,水洗,再离心分离,烘干粉碎,得到抗滴落剂。
本发明的优点和有益效果在于:提供一种用于生产高稳定性聚四氟乙烯抗滴落剂的工艺,其制备的聚四氟乙烯抗滴落剂稳定性好。
具体实施方式
下面结合实施例,对本发明的具体实施方式作进一步描述。以下实施例仅用于更加清楚地说明本发明的技术方案,而不能以此来限制本发明的保护范围。
本发明具体实施的技术方案是:
一种用于生产高稳定性聚四氟乙烯抗滴落剂的工艺,包括如下步骤:
1)在反应釜中投入2重量份聚氧乙烯失水山梨醇脂肪酸酯、1重量份六偏磷酸钠、2重量份过氧化苯甲酰、5重量份阁土粉、55重量份去离子水、4重量份过氧二硫酸铵、2.6重量份二硫八氧酸钾、2重量份碳酸钙、6重量份甲基丙烯酸丁酯、5重量份马来酸酐、2重量份水杨酸、1重量份甲基三甲氧基硅烷,升温至73℃,搅拌反应52分钟;
2)再在反应釜中投入14重量份甲基丙烯酸丁酯、17重量份去离子水、3重量份过氧化苯甲酰、2重量份二硫八氧酸钾、15重量份马来酸酐、1重量份过氧二硫酸铵,升温至72℃,搅拌反应50分钟;
3)再在反应釜中投入9重量份聚四氟乙烯分散液、28重量份去离子水,加热进行共混复合,在52℃加入凝聚剂溶液,得到沉淀;
4)对沉淀进行离心分离,水洗,再离心分离,烘干粉碎,得到抗滴落剂。
以上所述仅是本发明的优选实施方式,应当指出,对于本技术领域的普通技术人员来说,在不脱离本发明技术原理的前提下,还可以做出若干改进和润饰,这些改进和润饰也应视为本发明的保护范围。
Claims (1)
1.用于生产高稳定性聚四氟乙烯抗滴落剂的工艺,其特征在于,包括如下步骤:
1)在反应釜中投入2重量份聚氧乙烯失水山梨醇脂肪酸酯、1重量份六偏磷酸钠、2重量份过氧化苯甲酰、5重量份阁土粉、55重量份去离子水、4重量份过氧二硫酸铵、2.6重量份二硫八氧酸钾、2重量份碳酸钙、6重量份甲基丙烯酸丁酯、5重量份马来酸酐、2重量份水杨酸、1重量份甲基三甲氧基硅烷,升温至73℃,搅拌反应52分钟;
2)再在反应釜中投入14重量份甲基丙烯酸丁酯、17重量份去离子水、3重量份过氧化苯甲酰、2重量份二硫八氧酸钾、15重量份马来酸酐、1重量份过氧二硫酸铵,升温至72℃,搅拌反应50分钟;
3)再在反应釜中投入9重量份聚四氟乙烯分散液、28重量份去离子水,加热进行共混复合,在52℃加入凝聚剂溶液,得到沉淀;
4)对沉淀进行离心分离,水洗,再离心分离,烘干粉碎,得到抗滴落剂。