CN104448644A - 聚四氟乙烯抗滴落剂的制备方法 - Google Patents
聚四氟乙烯抗滴落剂的制备方法 Download PDFInfo
- Publication number
- CN104448644A CN104448644A CN201410730597.5A CN201410730597A CN104448644A CN 104448644 A CN104448644 A CN 104448644A CN 201410730597 A CN201410730597 A CN 201410730597A CN 104448644 A CN104448644 A CN 104448644A
- Authority
- CN
- China
- Prior art keywords
- weight
- weight part
- parts
- dripping agent
- deionized water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种聚四氟乙烯抗滴落剂的制备方法,包括如下步骤:1)在反应釜中投入聚甘油单硬脂酸酯、羟乙基纤维素、去离子水、二硫八氧酸钾、碳酸钙、阁土粉、过氧二硫酸铵、甲基丙烯酸丁酯、过氧化苯甲酰、马来酸酐、苯甲酸、羟基丙基甲基纤维素,升温至73℃,搅拌反应;2)再在反应釜中投入去离子水、二硫八氧酸钾、马来酸酐、过氧化苯甲酰、甲基丙烯酸丁酯、过氧二硫酸铵,升温,搅拌反应68分钟;3)再在反应釜中投入聚四氟乙烯分散液、去离子水,加热进行共混复合,在57℃加入凝聚剂溶液,得到沉淀;4)对沉淀进行离心分离,水洗,再离心分离,烘干粉碎,得到抗滴落剂。本发明制备的聚四氟乙烯抗滴落剂稳定性好。
Description
技术领域
本发明涉及聚四氟乙烯抗滴落剂的制备方法。
背景技术
现有的聚四氟乙烯抗滴落剂稳定性有待提高。
发明内容
本发明的目的在于提供一种聚四氟乙烯抗滴落剂的制备方法,其制备的聚四氟乙烯抗滴落剂稳定性好。
为实现上述目的,本发明的技术方案是设计一种聚四氟乙烯抗滴落剂的制备方法,包括如下步骤:
1)在反应釜中投入2重量份聚甘油单硬脂酸酯、1重量份羟乙基纤维素、35.7重量份去离子水、2.1重量份二硫八氧酸钾、0.8重量份碳酸钙、1.8重量份阁土粉、2.9重量份过氧二硫酸铵、6.4重量份甲基丙烯酸丁酯、0.6重量份过氧化苯甲酰、5.3重量份马来酸酐、2重量份苯甲酸、1重量份羟基丙基甲基纤维素,升温至73℃,搅拌反应64分钟;
2)再在反应釜中投入17.5重量份去离子水、2.1重量份二硫八氧酸钾、8.8重量份马来酸酐、0.8重量份过氧化苯甲酰、18.6重量份甲基丙烯酸丁酯、2.7重量份过氧二硫酸铵,升温至83℃,搅拌反应68分钟;
3)再在反应釜中投入20.8重量份聚四氟乙烯分散液、48.7重量份去离子水,加热进行共混复合,在57℃加入凝聚剂溶液,得到沉淀;
4)对沉淀进行离心分离,水洗,再离心分离,烘干粉碎,得到抗滴落剂。
本发明的优点和有益效果在于:提供一种聚四氟乙烯抗滴落剂的制备方法,其制备的聚四氟乙烯抗滴落剂稳定性好。
具体实施方式
下面结合实施例,对本发明的具体实施方式作进一步描述。以下实施例仅用于更加清楚地说明本发明的技术方案,而不能以此来限制本发明的保护范围。
本发明具体实施的技术方案是:
一种聚四氟乙烯抗滴落剂的制备方法,包括如下步骤:
1)在反应釜中投入2重量份聚甘油单硬脂酸酯、1重量份羟乙基纤维素、35.7重量份去离子水、2.1重量份二硫八氧酸钾、0.8重量份碳酸钙、1.8重量份阁土粉、2.9重量份过氧二硫酸铵、6.4重量份甲基丙烯酸丁酯、0.6重量份过氧化苯甲酰、5.3重量份马来酸酐、2重量份苯甲酸、1重量份羟基丙基甲基纤维素,升温至73℃,搅拌反应64分钟;
2)再在反应釜中投入17.5重量份去离子水、2.1重量份二硫八氧酸钾、8.8重量份马来酸酐、0.8重量份过氧化苯甲酰、18.6重量份甲基丙烯酸丁酯、2.7重量份过氧二硫酸铵,升温至83℃,搅拌反应68分钟;
3)再在反应釜中投入20.8重量份聚四氟乙烯分散液、48.7重量份去离子水,加热进行共混复合,在57℃加入凝聚剂溶液,得到沉淀;
4)对沉淀进行离心分离,水洗,再离心分离,烘干粉碎,得到抗滴落剂。
以上所述仅是本发明的优选实施方式,应当指出,对于本技术领域的普通技术人员来说,在不脱离本发明技术原理的前提下,还可以做出若干改进和润饰,这些改进和润饰也应视为本发明的保护范围。
Claims (1)
1.聚四氟乙烯抗滴落剂的制备方法,其特征在于,包括如下步骤:
1)在反应釜中投入2重量份聚甘油单硬脂酸酯、1重量份羟乙基纤维素、35.7重量份去离子水、2.1重量份二硫八氧酸钾、0.8重量份碳酸钙、1.8重量份阁土粉、2.9重量份过氧二硫酸铵、6.4重量份甲基丙烯酸丁酯、0.6重量份过氧化苯甲酰、5.3重量份马来酸酐、2重量份苯甲酸、1重量份羟基丙基甲基纤维素,升温至73℃,搅拌反应64分钟;
2)再在反应釜中投入17.5重量份去离子水、2.1重量份二硫八氧酸钾、8.8重量份马来酸酐、0.8重量份过氧化苯甲酰、18.6重量份甲基丙烯酸丁酯、2.7重量份过氧二硫酸铵,升温至83℃,搅拌反应68分钟;
3)再在反应釜中投入20.8重量份聚四氟乙烯分散液、48.7重量份去离子水,加热进行共混复合,在57℃加入凝聚剂溶液,得到沉淀;
4)对沉淀进行离心分离,水洗,再离心分离,烘干粉碎,得到抗滴落剂。