CN104448149A - 用于制备热稳定性聚偏氟乙烯的工艺 - Google Patents
用于制备热稳定性聚偏氟乙烯的工艺 Download PDFInfo
- Publication number
- CN104448149A CN104448149A CN201410731760.XA CN201410731760A CN104448149A CN 104448149 A CN104448149 A CN 104448149A CN 201410731760 A CN201410731760 A CN 201410731760A CN 104448149 A CN104448149 A CN 104448149A
- Authority
- CN
- China
- Prior art keywords
- weight
- parts
- polyvinylidene fluoride
- weight part
- thermal stability
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种用于制备热稳定性聚偏氟乙烯的工艺,包括如下步骤:1)反应釜中投入0.6重量份双氧水、0.9重量份无机碱溶液,混合均匀,再投入15.2重量份六氟乙烷溶剂、0.4重量份丙烯酰氯溶液,在-8.5℃搅拌反应36分钟;2)再通入9.3重量份聚丙烯酸溶液、68重量份偏氟乙烯单体、3.8重量份氯代环戊烷,在34℃搅拌反应,压力下降至0.26MPa以下时终止反应;3)过滤、洗涤、干燥,即得粉末状聚偏氟乙烯。本发明制备的偏氟乙烯具有良好的热稳定性和可加工性,可满足注塑、挤出和拉膜等生产工艺。
Description
技术领域
本发明涉及用于制备热稳定性聚偏氟乙烯的工艺。
背景技术
现有的偏氟乙烯材料,其热稳定性和可加工性有待提高,特别是不能很好的满足注塑、挤出和拉膜等生产工艺。
发明内容
本发明的目的在于提供一种用于制备热稳定性聚偏氟乙烯的工艺,其制备的偏氟乙烯具有良好的热稳定性和可加工性,可满足注塑、挤出和拉膜等生产工艺。
为实现上述目的,本发明的技术方案是设计一种用于制备热稳定性聚偏氟乙烯的工艺,包括如下步骤:
1)反应釜中投入0.6重量份双氧水、0.9重量份无机碱溶液,混合均匀,再投入15.2重量份六氟乙烷溶剂、0.4重量份丙烯酰氯溶液,在-8.5℃搅拌反应36分钟;
2)再通入9.3重量份聚丙烯酸溶液、68重量份偏氟乙烯单体、3.8重量份氯代环戊烷,在34℃搅拌反应,压力下降至0.26MPa以下时终止反应;
3)过滤、洗涤、干燥,即得粉末状聚偏氟乙烯。
本发明的优点和有益效果在于:提供一种用于制备热稳定性聚偏氟乙烯的工艺,其制备的偏氟乙烯具有良好的热稳定性和可加工性,可满足注塑、挤出和拉膜等生产工艺。
具体实施方式
下面结合实施例,对本发明的具体实施方式作进一步描述。以下实施例仅用于更加清楚地说明本发明的技术方案,而不能以此来限制本发明的保护范围。
本发明具体实施的技术方案是:
一种用于制备热稳定性聚偏氟乙烯的工艺,包括如下步骤:
1)反应釜中投入0.6重量份双氧水、0.9重量份无机碱溶液,混合均匀,再投入15.2重量份六氟乙烷溶剂、0.4重量份丙烯酰氯溶液,在-8.5℃搅拌反应36分钟;
2)再通入9.3重量份聚丙烯酸溶液、68重量份偏氟乙烯单体、3.8重量份氯代环戊烷,在34℃搅拌反应,压力下降至0.26MPa以下时终止反应;
3)过滤、洗涤、干燥,即得粉末状聚偏氟乙烯。
以上所述仅是本发明的优选实施方式,应当指出,对于本技术领域的普通技术人员来说,在不脱离本发明技术原理的前提下,还可以做出若干改进和润饰,这些改进和润饰也应视为本发明的保护范围。
Claims (1)
1.用于制备热稳定性聚偏氟乙烯的工艺,其特征在于,包括如下步骤:
1)反应釜中投入0.6重量份双氧水、0.9重量份无机碱溶液,混合均匀,再投入15.2重量份六氟乙烷溶剂、0.4重量份丙烯酰氯溶液,在-8.5℃搅拌反应36分钟;
2)再通入9.3重量份聚丙烯酸溶液、68重量份偏氟乙烯单体、3.8重量份氯代环戊烷,在34℃搅拌反应,压力下降至0.26MPa以下时终止反应;
3)过滤、洗涤、干燥,即得粉末状聚偏氟乙烯。