CN104479540B - 一种冰冻气候聚醚酰亚胺树脂防水涂料制备方法 - Google Patents

一种冰冻气候聚醚酰亚胺树脂防水涂料制备方法 Download PDF

Info

Publication number
CN104479540B
CN104479540B CN201410741282.0A CN201410741282A CN104479540B CN 104479540 B CN104479540 B CN 104479540B CN 201410741282 A CN201410741282 A CN 201410741282A CN 104479540 B CN104479540 B CN 104479540B
Authority
CN
China
Prior art keywords
parts
polyetherimide resin
water
triethanolamine
ethylene glycol
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN201410741282.0A
Other languages
English (en)
Other versions
CN104479540A (zh
Inventor
李慧
卜荣明
谢军
张阳
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Zhang Heqing
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201410741282.0A priority Critical patent/CN104479540B/zh
Publication of CN104479540A publication Critical patent/CN104479540A/zh
Application granted granted Critical
Publication of CN104479540B publication Critical patent/CN104479540B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及一种冰冻气候聚醚酰亚胺树脂防水涂料制备方法,由下列原料按质量比组成：聚醚酰亚胺树脂80‑90份、三乙醇胺3.5‑4份、三聚氰胺10‑15份、钛白粉5‑10份、膨胀珍珠岩8‑14份、羟乙基纤维素8‑12份、甲基硅醇钠3‑6份、硫酸铝4‑7份、乙二醇15‑20份、水溶性酰胺5‑8份。首先将聚醚酰亚胺树脂与三乙醇胺、乙二醇、水溶性酰胺进行混合，再加入三聚氰胺、钛白粉、膨胀珍珠岩、羟乙基纤维素进行混合成原浆，将甲基硅醇钠、硫酸铝混合调配后加入原浆进行混合，最后依次经挤出机熔融挤出、粉碎得到涂料。

Description

一种冰冻气候聚醚酰亚胺树脂防水涂料制备方法
技术领域
本发明涉及一种防水涂料，具体说是一种冰冻气候聚醚酰亚胺树脂防水涂料其制备方法。
背景技术
聚酯粉末涂料具有良好的物理机械性能，可广泛用于金属表面的装饰和保护，在冰冻气候下的设备要求涂料防水、耐冻、脆性要求较高，现有市场上的聚酯粉末涂料大都只在防水上性能优异，但是无法满足冰冻气候特殊要求的使用。
发明内容
针对现有技术中的上述不足，本发明提供了一种制造方便，成本低，防水、耐冻、脆性较好的一种冰冻气候聚醚酰亚胺树脂防水涂料及制备方法。
本发明采用的技术方案是：一种冰冻气候聚醚酰亚胺树脂防水涂料，由下列原料按质量比组成：聚醚酰亚胺树脂80-90份、三乙醇胺3.5-4份、三聚氰胺10-15份、钛白粉5-10份、膨胀珍珠岩8-14份、羟乙基纤维素8-12份、甲基硅醇钠3-6份、硫酸铝4-7份、乙二醇15-20份、水溶性酰胺5-8份。
一种冰冻气候聚醚酰亚胺树脂防水涂料的制备方法，包括以下步骤：首先将聚醚酰亚胺树脂与三乙醇胺、乙二醇、水溶性酰胺进行混合，再加入三聚氰胺、钛白粉、膨胀珍珠岩、羟乙基纤维素进行混合成原浆，将甲基硅醇钠、硫酸铝混合调配后加入原浆进行混合，最后依次经挤出机熔融挤出、粉碎得到涂料。
本发明在聚醚酰亚胺树脂中加入三乙醇胺、三聚氰胺、钛白粉、膨胀珍珠岩、羟乙基纤维素，配以甲基硅醇钠、硫酸铝、乙二醇和水溶性酰胺，能兼顾防水、耐水、脆性小的要求，适合冰冻气候下特殊使用要求。
具体实施方式
以下结合实施例对本发明作进一步说明。
实施例一
一种冰冻气候聚醚酰亚胺树脂防水涂料，由下列原料按质量比组成：聚醚酰亚胺树脂80份、三乙醇胺3.5份、三聚氰胺10份、钛白粉5份、膨胀珍珠岩8份、羟乙基纤维素8份、甲基硅醇钠3份、硫酸铝4份、乙二醇15份、水溶性酰胺5份。制备方法包括以下步骤：首先将聚醚酰亚胺树脂与三乙醇胺、乙二醇、水溶性酰胺进行混合，再加入三聚氰胺、钛白粉、膨胀珍珠岩、羟乙基纤维素进行混合成原浆，将甲基硅醇钠、硫酸铝混合调配后加入原浆进行混合，最后依次经挤出机熔融挤出、粉碎得到涂料。
实施例二
一种冰冻气候聚醚酰亚胺树脂防水涂料，由下列原料按质量比组成：聚醚酰亚胺树脂90份、三乙醇胺4份、三聚氰胺15份、钛白粉10份、膨胀珍珠岩14份、羟乙基纤维素12份、甲基硅醇钠6份、硫酸铝7份、乙二醇20份、水溶性酰胺8份。制备方法包括以下步骤：首先将聚醚酰亚胺树脂与三乙醇胺、乙二醇、水溶性酰胺进行混合，再加入三聚氰胺、钛白粉、膨胀珍珠岩、羟乙基纤维素进行混合成原浆，将甲基硅醇钠、硫酸铝混合调配后加入原浆进行混合，最后依次经挤出机熔融挤出、粉碎得到涂料。
实施例三
一种冰冻气候聚醚酰亚胺树脂防水涂料，由下列原料按质量比组成：聚醚酰亚胺树脂83份、三乙醇胺3.7份、三聚氰胺12份、钛白粉7份、膨胀珍珠岩10份、羟乙基纤维素9份、甲基硅醇钠4份、硫酸铝5份、乙二醇16份、水溶性酰胺7份。制备方法包括以下步骤：首先将聚醚酰亚胺树脂与三乙醇胺、乙二醇、水溶性酰胺进行混合，再加入三聚氰胺、钛白粉、膨胀珍珠岩、羟乙基纤维素进行混合成原浆，将甲基硅醇钠、硫酸铝混合调配后加入原浆进行混合，最后依次经挤出机熔融挤出、粉碎得到涂料。

Claims (1)

1.一种冰冻气候聚醚酰亚胺树脂防水涂料制备方法，由下列原料按质量比组成：聚醚酰亚胺树脂83份、三乙醇胺3.7份、三聚氰胺12份、钛白粉7份、膨胀珍珠岩10份、羟乙基纤维素9份、甲基硅醇钠4份、硫酸铝5份、乙二醇16份、水溶性酰胺7份;包括以下步骤：首先将聚醚酰亚胺树脂与三乙醇胺、乙二醇、水溶性酰胺进行混合，再加入三聚氰胺、钛白粉、膨胀珍珠岩、羟乙基纤维素进行混合成原浆，将甲基硅醇钠、硫酸铝混合调配后加入原浆进行混合，最后依次经挤出机熔融挤出、粉碎得到涂料。
CN201410741282.0A 2014-12-09 2014-12-09 一种冰冻气候聚醚酰亚胺树脂防水涂料制备方法 Expired - Fee Related CN104479540B (zh)