CN104479513B - 一种海洋气候端羧基溴碳聚酯树脂防火涂料及制备方法 - Google Patents

一种海洋气候端羧基溴碳聚酯树脂防火涂料及制备方法 Download PDF

Info

Publication number
CN104479513B
CN104479513B CN201410741554.7A CN201410741554A CN104479513B CN 104479513 B CN104479513 B CN 104479513B CN 201410741554 A CN201410741554 A CN 201410741554A CN 104479513 B CN104479513 B CN 104479513B
Authority
CN
China
Prior art keywords
parts
polyester resin
carbon polyester
preparation
end carboxyl
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201410741554.7A
Other languages
English (en)
Other versions
CN104479513A (zh
Inventor
张和庆
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Jiangsu Dayang Marine Equipment Co., Ltd.
Original Assignee
张和庆
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 张和庆 filed Critical 张和庆
Priority to CN201410741554.7A priority Critical patent/CN104479513B/zh
Publication of CN104479513A publication Critical patent/CN104479513A/zh
Application granted granted Critical
Publication of CN104479513B publication Critical patent/CN104479513B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及一种海洋气候端羧基溴碳聚酯树脂防火涂料及制备方法，由下列原料按质量比组成：端羧基溴碳聚酯树脂80‑90份、三乙醇胺3.5‑4份、三聚氰胺10‑15份、钛白粉5‑10份、膨胀珍珠岩8‑14份、羟乙基纤维素8‑12份、甲基硅醇钠3‑6份、硫酸铝4‑7份。首先将端羧基溴碳聚酯树脂与三乙醇胺进行混合，再加入三聚氰胺、钛白粉、膨胀珍珠岩、羟乙基纤维素进行混合成原浆，将甲基硅醇钠、硫酸铝混合调配后加入原浆进行混合，最后依次经挤出机熔融挤出、粉碎得到涂料。

Description

一种海洋气候端羧基溴碳聚酯树脂防火涂料及制备方法
技术领域
本发明涉及一种防火涂料，具体说是一种海洋气候端羧基溴碳聚酯树脂防火涂料及其制备方法。
背景技术
聚酯粉末涂料具有良好的物理机械性能，可广泛用于金属表面的装饰和保护，在海洋气候下船舶上要求涂料防火、耐水、耐腐蚀性能较高，现有市场上的聚酯粉末涂料大都只在防火上性能优异，但是无法满足海洋气候特殊要求的使用。
发明内容
针对现有技术中的上述不足，本发明提供了一种制造方便，成本低，防火、耐水、耐腐蚀性能较好的一种海洋气候端羧基溴碳聚酯树脂防火涂料及制备方法。
本发明采用的技术方案是：一种海洋气候端羧基溴碳聚酯树脂防火涂料，由下列原料按质量比组成：端羧基溴碳聚酯树脂80-90份、三乙醇胺3.5-4份、三聚氰胺10-15份、钛白粉5-10份、膨胀珍珠岩8-14份、羟乙基纤维素8-12份、甲基硅醇钠3-6份、硫酸铝4-7份。
一种海洋气候端羧基溴碳聚酯树脂防火涂料的制备方法，包括以下步骤：首先将端羧基溴碳聚酯树脂与三乙醇胺进行混合，再加入三聚氰胺、钛白粉、膨胀珍珠岩、羟乙基纤维素进行混合成原浆，将甲基硅醇钠、硫酸铝混合调配后加入原浆进行混合，最后依次经挤出机熔融挤出、粉碎得到涂料。
一种海洋气候端羧基溴碳聚酯树脂防火涂料，由下列原料按质量比组成：端羧基溴碳聚酯树脂80-85份、三乙醇胺3.5-4份、三聚氰胺10-15份、钛白粉5-10份、膨胀珍珠岩8-14份、羟乙基纤维素8-12份、甲基硅醇钠3-6份、硫酸铝4-7份。
一种海洋气候端羧基溴碳聚酯树脂防火涂料，由下列原料按质量比组成：端羧基溴碳聚酯树脂85份、三乙醇胺3.6份、三聚氰胺12份、钛白粉7份、膨胀珍珠岩11份、羟乙基纤维素10份、甲基硅醇钠4份、硫酸铝5份。
本发明在端羧基溴碳聚酯树脂中加入三乙醇胺、三聚氰胺、钛白粉、膨胀珍珠岩、羟乙基纤维素，配以甲基硅醇钠和硫酸铝，能兼顾防火、耐水、耐腐蚀性能，适合海洋气候下特殊使用要求。
具体实施方式
以下结合实施例对本发明作进一步说明。
实施例一
一种海洋气候端羧基溴碳聚酯树脂防火涂料，由下列原料按质量比组成：端羧基溴碳聚酯树脂80份、三乙醇胺3.5份、三聚氰胺10份、钛白粉5份、膨胀珍珠岩8份、羟乙基纤维素8份、甲基硅醇钠3份、硫酸铝4份。制备方法包括以下步骤：首先将端羧基溴碳聚酯树脂与三乙醇胺进行混合，再加入三聚氰胺、钛白粉、膨胀珍珠岩、羟乙基纤维素进行混合成原浆，将甲基硅醇钠、硫酸铝混合调配后加入原浆进行混合，最后依次经挤出机熔融挤出、粉碎得到涂料。
实施例二
一种海洋气候端羧基溴碳聚酯树脂防火涂料，由下列原料按质量比组成：端羧基溴碳聚酯树脂90份、三乙醇胺4份、三聚氰胺15份、钛白粉10份、膨胀珍珠岩14份、羟乙基纤维素12份、甲基硅醇钠6份、硫酸铝7份。制备方法包括以下步骤：首先将端羧基溴碳聚酯树脂与三乙醇胺进行混合，再加入三聚氰胺、钛白粉、膨胀珍珠岩、羟乙基纤维素进行混合成原浆，将甲基硅醇钠、硫酸铝混合调配后加入原浆进行混合，最后依次经挤出机熔融挤出、粉碎得到涂料。
实施例三
一种海洋气候端羧基溴碳聚酯树脂防火涂料，由下列原料按质量比组成：端羧基溴碳聚酯树脂85份、三乙醇胺3.6份、三聚氰胺12份、钛白粉7份、膨胀珍珠岩11份、羟乙基纤维素10份、甲基硅醇钠4份、硫酸铝5份。制备方法包括以下步骤：首先将端羧基溴碳聚酯树脂与三乙醇胺进行混合，再加入三聚氰胺、钛白粉、膨胀珍珠岩、羟乙基纤维素进行混合成原浆，将甲基硅醇钠、硫酸铝混合调配后加入原浆进行混合，最后依次经挤出机熔融挤出、粉碎得到涂料。

Claims (1)

1.一种海洋气候端羧基溴碳聚酯树脂防火涂料的制备方法，海洋气候端羧基溴碳聚酯树脂防火涂料由下列原料按质量比组成：端羧基溴碳聚酯树脂85份、三乙醇胺3.6份、三聚氰胺12份、钛白粉7份、膨胀珍珠岩11份、羟乙基纤维素10份、甲基硅醇钠4份、硫酸铝5份；制备方法包括以下步骤：首先将端羧基溴碳聚酯树脂与三乙醇胺进行混合，再加入三聚氰胺、钛白粉、膨胀珍珠岩、羟乙基纤维素进行混合成原浆，将甲基硅醇钠、硫酸铝混合调配后加入原浆进行混合，最后依次经挤出机熔融挤出、粉碎得到涂料。
CN201410741554.7A 2014-12-09 2014-12-09 一种海洋气候端羧基溴碳聚酯树脂防火涂料及制备方法 Active CN104479513B (zh)