CN104452459A - 一种用于纸淋膜的聚乳酸新材料及其加工工艺 - Google Patents
一种用于纸淋膜的聚乳酸新材料及其加工工艺 Download PDFInfo
- Publication number
- CN104452459A CN104452459A CN201410660641.XA CN201410660641A CN104452459A CN 104452459 A CN104452459 A CN 104452459A CN 201410660641 A CN201410660641 A CN 201410660641A CN 104452459 A CN104452459 A CN 104452459A
- Authority
- CN
- China
- Prior art keywords
- pla
- native starch
- polylactic acid
- acid material
- film
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供一种用于纸淋膜的聚乳酸新材料,由以下成分组成:天然淀粉;聚乳酸;环氧树脂;粘合剂;增白剂和抗氧化剂;所述天然淀粉是玉米天然淀粉、红薯天然淀粉、土豆天然淀粉一种或多种混合物;所述聚乳酸是吹膜级聚乳酸的一种;本发明的有益效果:本发明用于纸淋膜的聚乳酸新材料各组份的原料可全部在市场上购买得到,而且价格便宜,本发明加工工艺简单、制造成本低。
Description
技术领域
本发明涉及用于纸淋膜的聚乳酸新材料及其加工工艺。
背景技术
现有的纸杯生产厂家为了使杯子看上去更白,加入了大量的荧光增白剂,这些有害物质一旦进入人体,会成为潜在的致癌因素。
发明内容
针对现有的技术不足,本发明提供一种用于纸淋膜的聚乳酸新材料。
为了实现上述目的,本发明所采取的技术方案是:
一种用于纸淋膜的聚乳酸新材料,由以下成分组成:天然淀粉;聚乳酸;环氧树脂;粘合剂;增白剂和抗氧化剂;所述天然淀粉是玉米天然淀粉、红薯天然淀粉、土豆天然淀粉一种或多种混合物;所述聚乳酸是吹膜级聚乳酸的一种;所述环氧树脂是环氧树脂类的一种或多种的混合物;所述粘合剂是硼砂、硼酸钠、硼酸钠镁或含硼化合物中的任何一种;所述增白剂是硬脂酸、硬脂酸钙的任何一种;所述抗氧化剂包括山梨酸钾、麦芽酸钾和木酸钾的一种或多种的混合物。
一种用于纸淋膜的聚乳酸新材料的加工工艺,包括以下步骤:①原料干燥:将采购的天然淀粉和聚乳酸分别的加入干燥机中进行干燥,并且将干燥好的天然淀粉和聚乳酸进行密封包装。
②按照原料组分配比将天然淀粉、聚乳酸以及各种助剂称量。
③将称量好的天然淀粉、聚乳酸倒入高速搅拌机,开始以600-800转/分钟的低速搅拌5~9分钟,然后加入称好重量的所述助剂,并以800-1150转/分钟的高速搅拌10~15分钟后,再转入600-800转/分钟的低速搅拌10~15分钟,然后放料即得到所述混合物,在整个混料过程中物料温度控制在≥60℃。
④将从步骤③得到的混合物用双螺杆挤出机造粒,所述挤出机主要控制温度有四段,它们分别是:80~90℃、100~110℃、110~115℃、115~130℃;
⑤将从步骤④挤出的粒料用适合于淋膜纸的淋膜。淋膜工艺的温度为:机体温度:130~140℃、140~150℃、150~160℃、165~175℃模头温度:160~170℃。
本发明的有益效果:本发明用于纸淋膜的聚乳酸新材料各组份的原料可全部在市场上购买得到,而且价格便宜,再加上本发明加工工艺简单、制造成本也低。本发明用于纸淋膜的聚乳酸新材料组份中大部分采用天然淀粉、聚乳酸及少量的催化剂、粘合剂、抗氧化剂等,这样使其性能好、淋膜加工成纸杯后环保,无毒,使用废弃后淋膜层能够被环境中有机微生物降解,是一种具有很大发展潜力和市场需求的用于纸淋膜的聚乳酸新材料。
具体实施方式
实施例;一种用于纸淋膜的聚乳酸新材料,其特征在于所述聚乳酸各组份有如下的重量百分比:
所述天然淀粉是玉米天然淀粉、红薯天然淀粉、土豆天然淀粉一种或多种混合物。
所述聚乳酸是吹膜级聚乳酸的一种。
所述环氧树脂是环氧树脂类的一种或多种的混合物。
所述粘合剂是硼砂、硼酸钠、硼酸钠镁或含硼化合物中的任何一种。
所述增白剂是硬脂酸、硬脂酸钙的任何一种。
所述抗氧化剂包括山梨酸钾、麦芽酸钾和木酸钾的一种或多种的混合物。
一种制造权利要求1所述用于纸淋膜的聚乳酸新材料的加工工艺,其特征在于包括以下步骤:
①原料干燥:将采购的天然淀粉和聚乳酸分别的加入干燥机中进行干燥,并且将干燥好的天然淀粉和聚乳酸进行密封包装。
②按照原料组分配比将天然淀粉、聚乳酸以及各种助剂称量。
③将称量好的天然淀粉、聚乳酸倒入高速搅拌机,开始以600-800转/分钟的低速搅拌5~9分钟,然后加入称好重量的所述助剂,并以800-1150转/分钟的高速搅拌10~15分钟后,再转入600-800转/分钟的低速搅拌10~15分钟,然后放料即得到所述混合物,在整个混料过程中物料温度控制在≥60℃。
④将从步骤③得到的混合物用双螺杆挤出机造粒,所述挤出机主要控制温度有四段,它们分别是:80~90℃、100~110℃、110~115℃、115~130℃;
⑤将从步骤④挤出的粒料用适合于淋膜纸的淋膜。淋膜工艺的温度为:机体温度:130~140℃、140~150℃、150~160℃、165~175℃模头温度:160~170℃。
Claims (2)
1.一种用于纸淋膜的聚乳酸新材料,其特征在于,由以下成分组成:天然淀粉;聚乳酸;环氧树脂;粘合剂;增白剂和抗氧化剂;所述天然淀粉是玉米天然淀粉、红薯天然淀粉、土豆天然淀粉一种或多种混合物;所述聚乳酸是吹膜级聚乳酸的一种;所述环氧树脂是环氧树脂类的一种或多种的混合物;所述粘合剂是硼砂、硼酸钠、硼酸钠镁或含硼化合物中的任何一种;所述增白剂是硬脂酸、硬脂酸钙的任何一种;所述抗氧化剂包括山梨酸钾、麦芽酸钾和木酸钾的一种或多种的混合物。
2.一种制造用于纸淋膜的聚乳酸新材料的加工工艺,其特征在于包括以下步骤:
①原料干燥:将采购的天然淀粉和聚乳酸分别的加入干燥机中进行干燥,并且将干燥好的天然淀粉和聚乳酸进行密封包装。
②按照原料组分配比将天然淀粉、聚乳酸以及各种助剂称量。
③将称量好的天然淀粉、聚乳酸倒入高速搅拌机,开始以600-800转/分钟的低速搅拌5~9分钟,然后加入称好重量的所述助剂,并以800-1150转/分钟的高速搅拌10~15分钟后,再转入600-800转/分钟的低速搅拌10~15分钟,然后放料即得到所述混合物,在整个混料过程中物料温度控制在≥60℃。
④将从步骤③得到的混合物用双螺杆挤出机造粒,所述挤出机主要控制温度有四段,它们分别是:80~90℃、100~110℃、110~115℃、115~130℃;
⑤将从步骤④挤出的粒料用适合于淋膜纸的淋膜。淋膜工艺的温度为:机体温度:130~140℃、140~150℃、150~160℃、165~175℃模头温度:160~170℃。