CN104371289A - 一种新型聚乳酸新材料及加工工艺 - Google Patents
一种新型聚乳酸新材料及加工工艺 Download PDFInfo
- Publication number
- CN104371289A CN104371289A CN201410632711.0A CN201410632711A CN104371289A CN 104371289 A CN104371289 A CN 104371289A CN 201410632711 A CN201410632711 A CN 201410632711A CN 104371289 A CN104371289 A CN 104371289A
- Authority
- CN
- China
- Prior art keywords
- poly
- lactic acid
- biological starch
- mixture
- starch
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种新型聚乳酸新材料,所述聚乳酸各组份有如下的重量百分比:生物淀粉为15%~45%,聚乳酸为40%~80%,树脂为2%~10%,粘合剂为1%~5%,润滑剂为0.5%~1%,抗氧化剂为0.5%~1%;所述生物淀粉是玉米生物淀粉、木薯生物淀粉、土豆生物淀粉一种或多种混合物,所述聚乳酸是吹膜级聚乳酸的一种,所述树脂是树脂类的一种或多种的混合物,所述粘合剂是硼砂、硼酸钠、硼酸钠镁或含硼化合物中的任何一种,所述润滑剂是硬脂酸、硬脂酸钙的任何一种,所述抗氧化剂包括山梨糖醇、麦芽糖醇和木糖醇的一种或多种的混合物。发明的有益效果:本发明用于纸淋膜的聚乳酸新材料各组份的原料可全部在市场上购买得到。
Description
技术领域
本发明涉及一种新材料及加工工艺,特别涉及一种聚乳酸新材料及加工工艺。
背景技术
目前人们普遍使用的是纸塑杯,外面是一层纸,里面则是一层淋膜纸,如果制作时所选用的材质不好或加工工艺不过关,会产生有害物质。此外,有的纸杯生产厂家为了使杯子看上去更白,加入了大量的荧光增白剂,这些有害物质一旦进入人体,会成为潜在的致癌因素。
发明内容
针对现有的技术不足,本发明提供一种新型聚乳酸新材料。
为了实现上述目的,本发明所采取的技术方案是:一种新型聚乳酸新材料,所述聚乳酸各组份有如下的重量百分比:
生物淀粉为15%~45%
聚乳酸为40%~80%
树脂为2%~10%
粘合剂为1%~5%
润滑剂为0.5%~1%
抗氧化剂为0.5%~1%
所述生物淀粉是玉米生物淀粉、木薯生物淀粉、土豆生物淀粉一种或多种混合物。
所述聚乳酸是吹膜级聚乳酸的一种。
所述树脂是树脂类的一种或多种的混合物。
所述粘合剂是硼砂、硼酸钠、硼酸钠镁或含硼化合物中的任何一种。
所述润滑剂是硬脂酸、硬脂酸钙的任何一种。
所述抗氧化剂包括山梨糖醇、麦芽糖醇和木糖醇的一种或多种的混合物。
包括以下步骤:
①原料干燥:将采购的生物淀粉和聚乳酸分别的加入干燥机中进行干燥,并且将干燥好的生物淀粉和聚乳酸进行密封包装。
②按照原料组分配比将生物淀粉、聚乳酸以及各种助剂称量。
③将称量好的生物淀粉、聚乳酸倒入高速搅拌机,开始以600-850转/分钟的低速搅拌6~8分钟,然后加入称好重量的所述助剂,并以1000-1200转/分钟的高速搅拌8~15分钟后,再转入600-850转/分钟的低速搅拌8~15分钟,然后放料即得到所述混合物,在整个混料过程中物料温度控制在≥65℃。
④将从步骤③得到的混合物用双螺杆挤出机造粒,所述挤出机主要控制温度有四段,它们分别是:65~85℃、100~130℃、130~140℃、140~150℃;
⑤将从步骤④挤出的粒料用适合于淋膜纸的淋膜。淋膜工艺的温度为:机体温度:140~150℃、150~165℃、165~175℃、175~185℃模头温度:180~190℃。
本发明的有益效果:本发明用于纸淋膜的聚乳酸新材料各组份的原料可全部在市场上购买得到,而且价格便宜,再加上本发明加工工艺简单、制造成本也低。本发明用于纸淋膜的聚乳酸新材料组份中大部分采用生物淀粉、聚乳酸及少量的催化剂、粘合剂、抗氧化剂等,这样使其性能好、淋膜加工成纸杯后环保,无毒,使用废弃后淋膜层能够被环境中有机微生物降解,是一种具有很大发展潜力和市场需求的用于纸淋膜的聚乳酸新材料。
具体实施方式
实施例;一种新型聚乳酸新材料,所述聚乳酸各组份有如下的重量百分比:
生物淀粉为15%~45%
聚乳酸为40%~80%
树脂为2%~10%
粘合剂为1%~5%
润滑剂为0.5%~1%
抗氧化剂为0.5%~1%
所述生物淀粉是玉米生物淀粉、木薯生物淀粉、土豆生物淀粉一种或多种混合物。
所述聚乳酸是吹膜级聚乳酸的一种。
所述树脂是树脂类的一种或多种的混合物。
所述粘合剂是硼砂、硼酸钠、硼酸钠镁或含硼化合物中的任何一种。
所述润滑剂是硬脂酸、硬脂酸钙的任何一种。
所述抗氧化剂包括山梨糖醇、麦芽糖醇和木糖醇的一种或多种的混合物。
包括以下步骤:
①原料干燥:将采购的生物淀粉和聚乳酸分别的加入干燥机中进行干燥,并且将干燥好的生物淀粉和聚乳酸进行密封包装。
②按照原料组分配比将生物淀粉、聚乳酸以及各种助剂称量。
③将称量好的生物淀粉、聚乳酸倒入高速搅拌机,开始以600-850转/分钟的低速搅拌6~8分钟,然后加入称好重量的所述助剂,并以1000-1200转/分钟的高速搅拌8~15分钟后,再转入600-850转/分钟的低速搅拌8~15分钟,然后放料即得到所述混合物,在整个混料过程中物料温度控制在≥65℃。
④将从步骤③得到的混合物用双螺杆挤出机造粒,所述挤出机主要控制温度有四段,它们分别是:65~85℃、100~130℃、130~140℃、140~150℃;
⑤将从步骤④挤出的粒料用适合于淋膜纸的淋膜。淋膜工艺的温度为:机体温度:140~150℃、150~165℃、165~175℃、175~185℃模头温度:180~190℃。
按以下重量进行原料配比:
生物淀粉为20%,聚乳酸为70%,树脂为8%,粘合剂为3%,润滑剂为1%,抗氧化剂为1%。
所述生物淀粉采用玉米生物淀粉
所述聚乳酸是L-聚乳酸∶Mw=18000;
所述树脂是树脂E-20;
所述粘合剂是硼酸钠镁;
所述润滑剂是硬脂酸;
所述抗氧剂剂是木糖醇。
Claims (2)
1.一种新型聚乳酸新材料,其特征在于所述聚乳酸各组份有如下的重量百分比:
生物淀粉为 15%~45%
聚乳酸为 40%~80%
树脂为 2%~10%
粘合剂为 1%~5%
润滑剂为 0.5%~1%
抗氧化剂为 0.5%~1%;
所述生物淀粉是玉米生物淀粉、木薯生物淀粉、土豆生物淀粉一种或多种混合物;
所述聚乳酸是吹膜级聚乳酸的一种;
所述树脂是树脂类的一种或多种的混合物;
所述粘合剂是硼砂、硼酸钠、硼酸钠镁或含硼化合物中的任何一种;
所述润滑剂是硬脂酸、硬脂酸钙的任何一种;
所述抗氧化剂包括山梨糖醇、麦芽糖醇和木糖醇的一种或多种的混合物。
2.一种新型聚乳酸新材料的加工工艺,其特征在于包括以下步骤:
①原料干燥:将采购的生物淀粉和聚乳酸分别的加入干燥机中进行干燥,并且将干燥好的生物淀粉和聚乳酸进行密封包装;
②按照原料组分配比将生物淀粉、聚乳酸以及各种助剂称量;
③将称量好的生物淀粉、聚乳酸倒入高速搅拌机,开始以600-850转/分钟的低速搅拌6~8分钟,然后加入称好重量的所述助剂,并以1000-1200转/分钟的高速搅拌8~15分钟后,再转入600-850转/分钟的低速搅拌8~15分钟,然后放料即得到所述混合物,在整个混料过程中物料温度控制在≥65℃;
④将从步骤③得到的混合物用双螺杆挤出机造粒,所述挤出机主要控制温度有四段,它们分别是:65~85℃、100~130℃、130~140℃、140~150℃;
⑤将从步骤④挤出的粒料用适合于淋膜纸的淋膜,淋膜工艺的温度为:机体温度:140~150℃、150~165℃、165~175℃、175~185℃模头温度:180~190℃。