CN103509286A - 一种抗老化复配电缆料 - Google Patents

一种抗老化复配电缆料 Download PDF

Info

Publication number
CN103509286A
CN103509286A CN201310405359.2A CN201310405359A CN103509286A CN 103509286 A CN103509286 A CN 103509286A CN 201310405359 A CN201310405359 A CN 201310405359A CN 103509286 A CN103509286 A CN 103509286A
Authority
CN
China
Prior art keywords
parts
density polyethylene
raw material
agent
cable materials
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201310405359.2A
Other languages
English (en)
Other versions
CN103509286B (zh
Inventor
陈太锁
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Anhui Great Electric Limited-Liability Co Of China
Original Assignee
Anhui Great Electric Limited-Liability Co Of China
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Anhui Great Electric Limited-Liability Co Of China filed Critical Anhui Great Electric Limited-Liability Co Of China
Priority to CN201310405359.2A priority Critical patent/CN103509286B/zh
Publication of CN103509286A publication Critical patent/CN103509286A/zh
Application granted granted Critical
Publication of CN103509286B publication Critical patent/CN103509286B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种抗老化复配电缆料，其是由下述重量份的原料制得：SG-3PVC树脂60-68、低密度聚乙烯LDPE 10-20、线性低密度聚乙烯LLDPE 5-7、铝酸酯偶联剂DL-411 1-2、抗紫外剂UV-531 0.1-1、交联剂TAIC 1.5-3、抗氧剂1035 0.9-1.3、抗氧剂168 1.5-1.8、膨润土15-17、凹凸棒土6-8、间苯二甲酸酯1-2、甘油三醋酸酯0.8-1，改性填充料35-45。

Description

一种抗老化复配电缆料
技术领域
本发明涉及电缆料领域，确切地说是一种抗老化复配电缆料。
背景技术
聚氯乙烯（PVC）本色为微黄色半透明状，有光泽。透明度胜于聚乙烯、聚丙烯，差于聚苯乙烯，随助剂用量不同，分为软、硬聚氯乙烯，软制品柔而韧，手感粘，硬制品的硬度高于低密度聚乙烯，而低于聚丙烯，在屈折处会出现白化现象。
随着科技的发展，PVC的各种助剂和填充料的不断发展，也使得PVC电缆料的性能不断完善和提高。
发明内容
本发明的目的在于提供一种抗老化复配电缆料。
上述目的通过以下方案实现：
一种抗老化复配电缆料，其特征在于：其是由下述重量份的原料制得：
SG-3PVC树脂60-68、低密度聚乙烯LDPE10-20、线性低密度聚乙烯LLDPE5-7、铝酸酯偶联剂DL-4111-2、抗紫外剂UV-5310.1-1、交联剂TAIC1.5-3、抗氧剂10350.9-1.3、抗氧剂1681.5-1.8、膨润土15-17、凹凸棒土6-8、间苯二甲酸酯1-2、甘油三醋酸酯0.8-1，改性填充料35-45；
改性填充料由下列重量份的原料制成：
高岭土13-16、稻壳炭2-4，氧化锌1-2、三氧化二锑1-2,硬脂酸镁0.4-0.6，氢氧化镁10-12、柠檬酸三丁酯2-3、氢氧化铝8-10；
改性填充料的制备方法是将高岭土在800-850℃下煅烧1-3小时，然后，取出，与稻壳炭、硬脂酸镁一并加入适量水中研磨，加10-15%盐酸溶液调PH为4-5，研磨浆料至400-500目后，再加氢氧化钠调为中性，喷雾干燥，得粉末；将所得粉末与其它剩余成分混合，研磨混合均匀即得。
所述的一种抗老化复配电缆料，其特征在于：
制备方法为：
（1）取SG-3PVC树脂、抗紫外剂UV-531、交联剂TAIC按重量份混匀，于捏合机中170-180℃下捏合5-10分钟后，取出冷却；
（2）将步骤（1）所得冷却后的胶料与剩余各原料混匀，于双螺杆挤出机中混炼、造粒，控制温度165-175℃，得到成品。
本发明的有益效果为：本发明的工艺简单,设备投资少,产品性能稳定,贮存周期长。
具体实施方式
一种抗老化复配电缆料，其是由下述重量份(kg)的原料制得：
SG-3PVC树脂68、低密度聚乙烯LDPE18、线性低密度聚乙烯LLDPE7、铝酸酯偶联剂DL-4111.2、抗紫外剂UV-5310.8、交联剂TAIC1.8、抗氧剂10351.3、抗氧剂1681.8、膨润土15、凹凸棒土8、间苯二甲酸酯1、甘油三醋酸酯0.8，改性填充料45；
改性填充料由下列重量份的原料制成：
高岭土16、稻壳炭2，氧化锌1、三氧化二锑1,硬脂酸镁0.6，氢氧化镁12、柠檬酸三丁酯3、氢氧化铝10；
改性填充料的制备方法是将高岭土在820℃下煅烧3小时，然后，取出，与稻壳炭、硬脂酸镁一并加入适量水中研磨，加10%盐酸溶液调PH为5，研磨浆料至500目后，再加氢氧化钠调为中性，喷雾干燥，得粉末；将所得粉末与其它剩余成分混合，研磨混合均匀即得。
所述的一种抗老化复配电缆料，制备方法为：
（1）取SG-3PVC树脂、抗紫外剂UV-531、交联剂TAIC按重量份混匀，于捏合机中176℃下捏合7分钟后，取出冷却；
（2）将步骤（1）所得冷却后的胶料与剩余各原料混匀，于双螺杆挤出机中混炼、造粒，控制温度168℃，得到成品。
将本实施例进行性能测试，所得数据如下：
Figure BDA0000378643990000021
从本实施例测试结果可见，本发明的产品经过100℃×168h的老化和80℃×6h高温压力试验，其机械物理性能变化符合相应标注要求，具有良好的物理机械性能，满足不同温度环境变化的需求。

Claims (2)

1.一种抗老化复配电缆料，其特征在于：其是由下述重量份的原料制得：
 SG-3PVC树脂  60-68、低密度聚乙烯LDPE  10-20、线性低密度聚乙烯LLDPE  5-7、铝酸酯偶联剂DL-411 1-2、抗紫外剂UV-531 0.1-1、交联剂 TAIC 1.5-3、抗氧剂1035 0.9-1.3、抗氧剂168 1.5-1.8、膨润土15-17、凹凸棒土6-8、间苯二甲酸酯1-2、甘油三醋酸酯0.8-1，改性填充料35-45；
    改性填充料由下列重量份的原料制成：
高岭土13-16、稻壳炭2-4，氧化锌1-2、三氧化二锑1-2,硬脂酸镁0.4-0.6，氢氧化镁10-12、柠檬酸三丁酯2-3、氢氧化铝8-10；
    改性填充料的制备方法是将高岭土在800-850℃下煅烧1-3小时，然后，取出，与稻壳炭、硬脂酸镁一并加入适量水中研磨，加10-15%盐酸溶液调PH为4-5，研磨浆料至400-500目后，再加氢氧化钠调为中性，喷雾干燥，得粉末；将所得粉末与其它剩余成分混合，研磨混合均匀即得。
2.根据权利要求1所述的一种抗老化复配电缆料，其特征在于：
  制备方法为：
   （1）取SG-3PVC树脂、抗紫外剂UV-531、交联剂 TAIC按重量份混匀，于捏合机中170-180℃下捏合5-10分钟后，取出冷却；
　　（2）将步骤（1）所得冷却后的胶料与剩余各原料混匀，于双螺杆挤出机中混炼、造粒，控制温度165-175℃，得到成品。
CN201310405359.2A 2013-09-06 2013-09-06 一种抗老化复配电缆料 Expired - Fee Related CN103509286B (zh)