CN104448937A - 油漆用超细活性重质碳酸钙的生产方法 - Google Patents

油漆用超细活性重质碳酸钙的生产方法 Download PDF

Info

Publication number
CN104448937A
CN104448937A CN201410656245.XA CN201410656245A CN104448937A CN 104448937 A CN104448937 A CN 104448937A CN 201410656245 A CN201410656245 A CN 201410656245A CN 104448937 A CN104448937 A CN 104448937A
Authority
CN
China
Prior art keywords
calcium carbonate
product
paint
heavy calcium
production method
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410656245.XA
Other languages
English (en)
Inventor
林冬根
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
JIANGSU QUNXIN POWDER MATERIAL Co Ltd
Original Assignee
JIANGSU QUNXIN POWDER MATERIAL Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by JIANGSU QUNXIN POWDER MATERIAL Co Ltd filed Critical JIANGSU QUNXIN POWDER MATERIAL Co Ltd
Priority to CN201410656245.XA priority Critical patent/CN104448937A/zh
Publication of CN104448937A publication Critical patent/CN104448937A/zh
Pending legal-status Critical Current

Abstract

油漆用超细活性重质碳酸钙的生产方法，涉及油漆的生产技术领域，特别是用于生产油漆用的重质碳酸钙的生产工艺技术。本发明将重质碳酸钙进行改性处理，然后再除去团聚的粒子。对表面处理后的产品再次进行处理，以除去表面处理过程中形成的团聚粒子，同时使产品进一步快速冷却，确保不发生再次团聚现象，除去团聚粒子后，更加满足涂料产品的使用要求。另外，采用本发明工艺制成的产品活化度还较原工艺高。

Description

油漆用超细活性重质碳酸钙的生产方法
技术领域
本发明涉及油漆的生产技术领域，特别是用于生产油漆用的重质碳酸钙的生产工艺技术。
背景技术
油漆产品使用超细活性重质碳酸钙时，由于碳酸钙在表面处理时有团聚现象，使油漆产品的成涂性不良，在做涂膜试验时，经常出现不合格现象。
发明内容
本发明目的是针对现有技术的缺陷，提出一种油漆用超细活性重质碳酸钙的生产方法。
本发明将重质碳酸钙进行改性处理，然后再除去团聚的粒子。
对表面处理后的产品再次进行处理，以除去表面处理过程中形成的团聚粒子，同时使产品进一步快速冷却，确保不发生再次团聚现象，除去团聚粒子后，更加满足涂料产品的使用要求。另外，采用本发明工艺制成的产品活化度还较原工艺高。
本发明所述改性处理用材料为硬脂酸。
本发明优选的所述重质碳酸钙的粒径为D97≤10μm。
为了实现全量改性，本发明所述重质碳酸钙与硬脂酸的混合质量比为1000：6～8。
为了达到更好的改性效果，提高改性度，本发明所述改性处理的温度为125℃。
具体实施方式
一、生产工艺
将1000kg、粒径为D97≤10μm的重质碳酸钙与6～8kg的硬脂酸混合，经高速搅拌处理到温度达125℃时出料，经过分级机分级处理除去团聚的粒子后，取得终产品。
二、不同工艺制成的产品数据对照：
  活化度（%） 过200目筛
原有工艺制得的产品    95.0 不能全通过
本发明工艺制得的产品    98.0 全通过
原有产品使用时涂膜试验由于碳酸钙的原因常有不符合现象出现。
改进后的产品使用时涂膜试验由于碳酸钙的原因没有出现不符合现象。

Claims (5)

1.油漆用超细活性重质碳酸钙的生产方法，其特征在于将重质碳酸钙进行改性处理，然后再除去团聚的粒子。
2.根据权利要求1所述生产方法，其特征在于改性处理用材料为硬脂酸。
3.根据权利要求2所述生产方法，其特征在于所述重质碳酸钙的粒径为D97≤10μm。
4.根据权利要求3所述生产方法，其特征在于所述重质碳酸钙与硬脂酸的混合质量比为1000：6～8。
5.根据权利要求1或2或3或4所述生产方法，其特征在于所述改性处理的温度为125℃。
CN201410656245.XA 2014-11-18 2014-11-18 油漆用超细活性重质碳酸钙的生产方法 Pending CN104448937A (zh)