CN104446078A - 一种沥青路面增强用秸秆纤维的制备方法 - Google Patents

一种沥青路面增强用秸秆纤维的制备方法 Download PDF

Info

Publication number
CN104446078A
CN104446078A CN201410796157.XA CN201410796157A CN104446078A CN 104446078 A CN104446078 A CN 104446078A CN 201410796157 A CN201410796157 A CN 201410796157A CN 104446078 A CN104446078 A CN 104446078A
Authority
CN
China
Prior art keywords
stalk
straw
enhancing
bituminous pavement
minutes
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201410796157.XA
Other languages
English (en)
Other versions
CN104446078B (zh
Inventor
刘开平
李刚
温久然
马玉薇
孙志华
汤骅
李祖仲
李洁
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Changan University
Original Assignee
Changan University
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Changan University filed Critical Changan University
Priority to CN201410796157.XA priority Critical patent/CN104446078B/zh
Publication of CN104446078A publication Critical patent/CN104446078A/zh
Application granted granted Critical
Publication of CN104446078B publication Critical patent/CN104446078B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种沥青路面增强用秸秆纤维的制备方法，包括如下步骤：1)将秸秆进行机械压榨劈裂；2)将压榨劈裂的秸秆用表面活性剂溶液浸泡4～6小时，滤除自由水分，然后干燥至秸秆含水量在50～70％，最好在62～66％；3)将步骤2)中含水50～70％的秸秆切短至0.5～2厘米；4)将步骤3)中切短至0.5～2厘米的秸秆在叶片式打浆机上强力打散3～5分钟，随后加入2～5％的处理药剂继续打散1～2分钟，得到该沥青路面增强用秸秆纤维。其制备工艺简单，工作人员便于操作，制造成本较低；制备出来的秸秆纤维性能较好。

Description

一种沥青路面增强用秸秆纤维的制备方法
技术领域
本发明涉及植物纤维制备领域具体为一种沥青路面增强用秸秆纤维的制备方法。
背景技术
路面设计对于沥青混凝土高级公路路面视作弹性体系，不考虑应力卸载-塑性变形数量，但这些不可恢复变形或多或少的存在，加入大量均匀分散的细微纤维能很好的提高路面作为弹性层状体系进行分析计算的可靠度。均匀分散的纤维改善了细微沥青混凝土的均质性、整体工作性能，提高公路表面沥青混合料的稳定性，从而提高了沥青混凝土路面的抗冲磨能力，提高了结构层的疲劳寿命，而现有的植物植物纤维制备方法过于复杂，成本制造相对较高。
发明内容
本发明的目的在于提供一种沥青路面增强用秸秆纤维的制备方法，以解决上述背景技术中提出的问题。
为实现上述目的，本发明提供如下技术方案：
一种沥青路面增强用秸秆纤维的制备方法，包括如下步骤：
1)将秸秆进行机械压榨劈裂；
2)将压榨劈裂的秸秆用表面活性剂溶液浸泡4～6小时，滤除自由水分，然后干燥至秸秆含水量在50～70％，最好在62～66％；
3)将步骤2)中含水50～70％的秸秆切短至0.5～2厘米；
4)将步骤3)中切短至0.5～2厘米的秸秆在叶片式打浆机上强力打散3～5分钟，随后加入2～5％的处理药剂继续打散1～2分钟，得到该沥青路面增强用秸秆纤维。
作为优选，所述的处理药剂为乳化沥青中加入10～40％脂肪酸稀土盐，加热至60～80℃，并保温10～30分钟，再加入5～15％的钛酸酯偶联剂，继续加热至80～90℃，并保温10～20分钟，冷却制备而成。
与现有技术相比，本发明的优点：该沥青路面增强用秸秆纤维的制备方法，其制备工艺简单，工作人员便于操作，制造成本较低；制备出来的秸秆纤维性能较好。
具体实施方式
实施例1
一种沥青路面增强用秸秆纤维的制备方法，包括如下步骤：
1)将秸秆进行机械压榨劈裂；
2)将压榨劈裂的秸秆用表面活性剂溶液浸泡4.5小时，滤除自由水分，然后干燥至秸秆含水量在62％；
3)将步骤2)中含水62％的秸秆切短至1厘米；
4)将步骤3)中切短至1厘米的秸秆在叶片式打浆机上强力打散3分钟，随后加入2.5％的处理药剂继续打散1分钟，得到该沥青路面增强用秸秆纤维。
本实施例中所述的处理药剂为乳化沥青中加入30％脂肪酸稀土盐，加热至80℃，并保温25分钟，再加入10％的钛酸酯偶联剂，继续加热至90℃，并保温20分钟，冷却制备而成。
实施例2
一种沥青路面增强用秸秆纤维的制备方法，包括如下步骤：
1)将秸秆进行机械压榨劈裂；
2)将压榨劈裂的秸秆用表面活性剂溶液浸泡5小时，滤除自由水分，然后干燥至秸秆含水量在64％；
3)将步骤2)中含水50～70％的秸秆切短至1.5厘米；
4)将步骤3)中切短至1.5厘米的秸秆在叶片式打浆机上强力打散4分钟，随后加入3.5％的处理药剂继续打散1.5分钟，得到该沥青路面增强用秸秆纤维。
本实施例中所述的处理药剂为乳化沥青中加入30％脂肪酸稀土盐，加热至80℃，并保温25分钟，再加入10％的钛酸酯偶联剂，继续加热至90℃，并保温20分钟，冷却制备而成。
实施例3
一种沥青路面增强用秸秆纤维的制备方法，包括如下步骤：
1)将秸秆进行机械压榨劈裂；
2)将压榨劈裂的秸秆用表面活性剂溶液浸泡6小时，滤除自由水分，然后干燥至秸秆含水量在66％；
3)将步骤2)中含水66％的秸秆切短至2厘米；
4)将步骤3)中切短至2厘米的秸秆在叶片式打浆机上强力打散5分钟，随后加入5％的处理药剂继续打散2分钟，得到该沥青路面增强用秸秆纤维。
本实施例中所述的处理药剂为乳化沥青中加入30％脂肪酸稀土盐，加热至80℃，并保温25分钟，再加入10％的钛酸酯偶联剂，继续加热至90℃，并保温20分钟，冷却制备而成。
以上实施例仅为介绍本发明的优选案例，对于本领域技术人员来说，在不背离本发明精神的范围内所进行的任何显而易见的变化和改进，都应被视为本发明的一部分。

Claims (2)

1.一种沥青路面增强用秸秆纤维的制作方法，其特征在于，包括如下步骤：
1)将秸秆进行机械压榨劈裂；
2)将压榨劈裂的秸秆用表面活性剂溶液浸泡4～6小时，滤除自由水分，然后干燥至秸秆含水量在50～70％；
3)将步骤2)中含水50～70％的秸秆切短至0.5～2厘米；
4)将步骤3)中切短至0.5～2厘米的秸秆在叶片式打浆机上强力打散3～5分钟，随后加入2～5％的处理药剂继续打散1～2分钟，得到该沥青路面增强用秸秆纤维。
2.根据权利要求1所述的一种沥青路面增强用秸秆纤维的制作方法，其特征在于，所述的处理药剂为乳化沥青中加入10～40％脂肪酸稀土盐，加热至60～80℃，并保温10～30分钟，再加入5～15％的钛酸酯偶联剂，继续加热至80～90℃，并保温10～20分钟，冷却制备而成。
CN201410796157.XA 2014-12-18 2014-12-18 一种沥青路面增强用秸秆纤维的制备方法 Expired - Fee Related CN104446078B (zh)